• 한국원자력학회:학술대회논문집
• /
• 한국원자력학회 2005년도 춘계학술발표회
• /
• pp.437-438
• /
• 2005

• 한국원자력학회:학술대회논문집
• /
• 한국원자력학회 2004년도 추계학술발표회 발표논문집
• /
• pp.1028-1029
• /
• 2004

• 한국원자력학회:학술대회논문집
• /
• 한국원자력학회 2005년도 춘계학술발표회
• /
• pp.435-436
• /
• 2005

• 한국재료학회지
• /
• 제15권2호
• /
• pp.126-133
• /
• 2005

Mechanical properties of zirconium cladding were evaluated by ring tension test to simulate Reactivity-Initiated Accident (RIA) at high burnup situation as an out-reactor test. Zircaloy-4 cladding was hydrided up to 1000 ppm as well as oxidized up to $100\;{\mu}m$ to simulate high-burnup situation. After simulated high-burnup treatment, ring tension test was carried out from 0.01 to 1/sec to correlate with actual RIA event. The results showed that ductility and circumferential toughness decreased with the hydrogen content and oxide thickness. Hydride generated inside cladding acted as brittle failure. Oxygen influenced cladding tube by the reduction of load bearing area, oxygen embrittlement, and thermal aging. Correlation between in-reactor RIA parameter like fuel enthalpy and out-reactor toughness was performed and showed a reasonable result.

• 한국원자력학회:학술대회논문집
• /
• 한국원자력학회 2004년도 추계학술발표회 발표논문집
• /
• pp.907-908
• /
• 2004

• 한국원자력학회:학술대회논문집
• /
• 한국원자력학회 2004년도 추계학술발표회 발표논문집
• /
• pp.905-906
• /
• 2004

• 열처리공학회지
• /
• 제18권2호
• /
• pp.112-118
• /
• 2005

Study was focused on the effect of the cooling rate on the embrittlement behavior of Zircaloy-4 cladding simulated Loss Of Coolant Accident (LOCA) environment. Claddings were oxidized at given temperature and given time followed by various water quenching in the range of $0.6^{\circ}C$ and $100^{\circ}C$ per second. Cladding failed after water quenching above the threshold oxidation. Threshold oxidation was decreased as the cooling rate increased, which is due to the matensite structure formed during fast cooling rate.

• 열처리공학회지
• /
• 제18권5호
• /
• pp.288-296
• /
• 2005

The corrosion behaviors of Zr-based alloys were very sensitive to their microstructures which were determined by manufacturing process. The specimens of Zr-based alloy named as HANA-4 for nuclear fuel cladding were investigated in order to get the optimized manufacturing process such as the intermediate annealing temperature and cold working steps after the ${\beta}$ quenching. From the microstructural analysis, cold worked microstructure of the samples was changed to the recrystallized microstructure by performed process. The corrosion behaviors of HANA-4 alloy were affected by the different manufacturing process. The ${\beta}$-Zr phase was formed in the matrix and the Nb concentration in the ${\beta}$-Zr phase was increased as progressing the manufacturing process. So, it was found that the corrosion rate of HANA-4 alloy was affected by the Nb concentration in the matrix.

• 열처리공학회지
• /
• 제18권3호
• /
• pp.164-171
• /
• 2005

Iodine-Induced Stress Corrosion Cracking (ISCC) properties of Zircaloy-4 and HANA4 developed in KAERI for the high burn-up nuclear fuel cladding were evaluated. To confirm the effect of final heat treatment on ISCC resistance of Zr-alloy, stress relieved and recrystallized specimens were prepared and tested. With the pre-cracked specimen at internal surface, ISCC crack propagation rates and threshold stress intensity factor ($K_{ISCC}$) based on the fracture mechanics were measured by internal pressurization test at $350^{\circ}C$ in iodine environment. $K_{ISCC}$ of Zircaloy-4 and HANA4 cladding were $3.3MPa{\cdot}m^{1/2}$ and $4.4MPa{\cdot}m^{1/2}$, respectively. Pitting corrosion at the crack surface was observed and it seemed that TG crack propagation was derived from the pitting.

• 열처리공학회지
• /
• 제17권6호
• /
• pp.356-364
• /
• 2004

The hydrides in cladding affect the corrosion and tensile properties. In this study corrosion and tensile properties were evaluated with varying the hydrogen concentration. The charged hydrogen contents were ranged from 200 to 1000 ppm. The corrosion rate in water and LiOH solution increases with the hydrogen concentration. The hydride did not affect the corrosion mechanism in the pre-transition region, but in the post-transition region the corrosion rate was accelerated. Cladding E contained higher Niobium content was slowly accelerated compared with other claddings. The yield and ultimate strengths were independent on the hydrogen content. However, the total elongation decreased gradually with increasing the hydrogen content. SEM observation of fracture surface showed that an average of depth of voids decreased with increasing the hydrogen content and small secondary crack are observed.