• Korean Journal of Materials Research
• /
• v.20 no.7
• /
• pp.379-384
• /
• 2010

The usual ceramic process of mixing and milling in state of oxides $ZrO_2$ and $CeO_2$ was adopted in this study in a wet process to manufacture Ce-TZP. $CeO_2$-$ZrO_2$ ceramics containing 8~20 mol% $CeO_2$ were made by heat treatment at $1250\sim1500^{\circ}C$ for 5hr. The maximum dispersion point of every slurry manufactured with a mixture of $ZrO_2$ and $CeO_2$ was neat at pH10. A stable slurry with average particle size of 90 nm can be manufactured when it is dispersed with the use of ammonia water and polycarboxylic acid ammonium. The sintered Ce-TZP ceramics manufactured with the addition of $CeO_2$ in a concentration of less than 10 mol% progressed to the fracture of the specimen due to the existence of a monoclinic phase of more than 30% at room temperature. More than 99% of the tetragonal phase was created for the sintered body with the addition of $CeO_2$ beyond 18 mol%, but the degradation of the mechanical properties on the entire specimen was brought about due to the $CeO_2$ existing in a percentage above 3%. Consequently, the optimal Ce-TZP level combined in the oxide state was identified to be 16 mol% of $CeO_2$ contents.

• Journal of the Korean Ceramic Society
• /
• v.38 no.9
• /
• pp.834-838
• /
• 2001

Attempts were made to improve mechanical properties of zirconia-based electrolyte by preparing yttria-stabilized cubic zirconia/alumina composite. It was performed by precipitating Yag precursor in aqueous m-zirconia slurry. The powder was separated and then followed by heat treatment with expecting yttria to react with m-$ZrO_2$ to give yttria stabilized zirconia and alumina to be dispersed homogeneously. When 17.8wt% Yag(6.3mol% $Y_2O_3$) was used, fracture toughness and strength were substantially improved from 1.44MPa${\cdot}m^{1/2}$ and 270Mpa for YZ8Y to 3.62MPa${\cdot}m^{1/2}$ and 447MPa respectively, but electrical conductivity at $^{\circ}$C in air was decreased from 0.126 to 0.057${\Omega}^{-1}cm^{-1}$. It seemed due to the presence of small amount of tetragonal zirconia. But when 21.58wt% Yag(8.0mol% $Y_2O_3$) was added, fracture toughness of 2.93MPa${\cdot}m^{1/2}$ and flexural strength of 388MPa were obtained with electrical conductivity of ${\Omega}^{-1}cm^{-1}$.

• Journal of the Korean Electrochemical Society
• /
• v.7 no.2
• /
• pp.94-99
• /
• 2004

Anode-supported flat tubular solid oxide fuel cell (SOFC) was investigated to increase the cell power density. The anode-supported flat tube was fabricated by extrusion process. The porosity and pore size of Ni/YSZ ($8mol\%$ yttria-stabilized zirconia) cermet anode were $50.6\%\;and\;0.23{\mu}m$, respectively. The Ni particles in the anode were distributed uniformly and connected well to each other particles in the cermet anode. YSZ electrolyte layer and multilayered cathode composed of $LSM(La_{0.85}Sr_{0.15})_{0.9}MnO_3)/YSZ$ composite, LSM, and $LSCF(La_{0.6}Sr_{0.4}Co_{0.2}Fe_{0.7}O_3)$ were coated onto the anode substrate by slurry dip coating, subsequently. The anode-supported flat tubular cell showed a performance of $300mW/cm^2 (0.6V,\; 500 mA/cm^2)\;at\;500^{\circ}C$. The electrochemical characteristics of the flat tubular cell were examined by ac impedance method and the humidified fuel enhanced the cell performance. Areal specific resistance of the LSM-coated SUS430 by slurry dipping process as metallic interconnect was $148m{\Omega}cm^2\;at\;750^{\circ}C$ and then decreased to $148m{\Omega}cm^2$ after 450hr. On the other hand, the LSM-coated Fecralloy by slurry dipping process showed a high area specific resistance.

• Transactions of the Korean hydrogen and new energy society
• /
• v.17 no.2
• /
• pp.204-211
• /
• 2006

The electrolyte in the solid oxide fuel cell must be dense enough to avoid gas leakage and thin enough to reduce the ohmic resistance. In order to manufacture the thin and dense electrolyte layer, 8 mol% $Y_2O_3$ stabilized-$ZrO_2$ (8YSZ) electrolyte layers were coated on the porous tubular substrate by the novel vacuum slurry dip-coating process. The effects of the slurry concentration, presintering temperature, and vacuum pressure on the thickness and the gas permeability of the coated electrolyte layers have been examined in the vacuum slurry coating process. The vacuum-coated electrolyte layers showed very low gas permeabilities and had thin thicknesses. The single cell with the vacuum-coated electrolyte layer indicated a good performance of $495\;mW/cm^2$, 0.7 V at $700^{\circ}C$. The experimental results show that the vacuum dip-coating process is an effective method to fabricate dense thin film on the porous tubular substrate.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2009.11a
• /
• pp.18.2-18.2
• /
• 2009

Ceramics have some properties that are unmatched by other kind of materials like metals or polymers. The ability of high thermal and chemical resistance and in case of being superior in specific mechanical properties makes the ceramic materials suitable for arange of applications. The microstructure and morphology of a material arguably permit the use of many advanced application otherwise difficult to achieve.Porous structures have some important applications in biomedical and environmental field. For human hard tissue reconstruction and augmentation procedure suitable biomaterials are used with a desirable porosity. A range of porous bioceramics were fabricated with tailored design to meet the demand of specific applications. Channeled and interconnected porosity was introduced in alumina, zirconia, and hydroxyapatite or tri calcium phosphate ceramics by different methods like multi-pass extrusion process, bubble formation in viscous slurry,slurry dripping in immiscible liquid, sponge replica method etc. The detailed microstructural and morphological investigations were carried out to establish the unique features of each method and the developed systems. For environmental filters the porous structures were also very important. We investigated a range of channeled and randomly porous silicon based ceramic composites to enhance the material stability and filtration efficiency by taking advantage of the material chemistry of the element. Detailed microstructural and mechanical characterizations were carried out for the fabricated porous filtration systems.

• The Journal of Korean Academy of Prosthodontics
• /
• v.49 no.2
• /
• pp.120-127
• /
• 2011

Purpose: The purpose of this study was to examine the effects of chromium chloride addition on coloration, mechanical property and microstructure of 3Y-TZP. Materials and methods: Chromium chloride was weighed as 0.06, 0.12, and 0.25 wt% and each measured amount was dissolved in alcohol. $ZrO_2$ powder was mixed with each of the individual slurry to prepare chromium doped zirconia specimen. The color, physical properties and microstructure were observed after the zirconia specimen were sintered at $1450^{\circ}C$. In order to evaluate the color, spectrophotometer was used to analyze the value of $L^*$, $C^*$, $a^*$ and $b^*$, after placing the specimen on a white plate, and measured according to the International Commission on Illumination (CIE) standard, Illuminant D65 and SCE system. The density was measured in the Archimedes method, while microstructures were evaluated by using the scanning electron microscopy (SEM) and XRD. Fracture toughness was calculated Vickers indentation method and indentation size was measured by using the optical microscope. The data were analyzed with 1-way ANOVA test (${\alpha}$ = 0.05). The Tukey multiple comparison test was used for post hocanalysis. Results: 1. Chromium chloride rendered zirconia a brownish color. While chromium chloride content was increased, the color of zirconia was changed from brownish to brownish-red. 2. Chromium chloride content was increased; density of the specimen was decreased. 3. More chromium chloride in the ratio showed increase size of grains. 4. But the addition of chromium chloride did not affect the crystal phase of zirconia, and all specimens showed tetragonal phase. 5. The chromium chloride in zirconia did not showed statistically significant difference in fracture toughness, but addition of 0.25 wt% showed a statistically significant difference (P<.05). Conclusion: Based on the above results, this study suggests that chromium chlorides can make colored zirconia while adding in a liquid form. The new colored zirconia showed a slight difference in color to that of the natural tooth, nevertheless this material can be used as an all ceramic core material.

• Journal of the Korean Ceramic Society
• /
• v.52 no.5
• /
• pp.315-319
• /
• 2015

Yttria-stabilized zirconia (YSZ)-based micro tubular SOFC single cells were fabricated by electrophoretic deposition (EPD) process. Stable slurries for the EPD process were prepared by adding phosphate ester (PE) as a dispersant in order to control the pH, conductivity, and zeta-potential. NiO-YSZ anode support, NiO-YSZ anode functional layer (AFL), and YSZ electrolyte were consecutively deposited on a graphite rod using the EPD process; materials were then co-sintered at $1400^{\circ}C$ for 4 h. The thickness of the deposited layer increased with increasing of the applied voltage and the deposition time. A YSZ-based micro tubular single cell fabricated by the EPD process exhibited a maximum power density of $0.3W/cm^2$ at $750^{\circ}C$.

• Analytical Science and Technology
• /
• v.6 no.2
• /
• pp.225-229
• /
• 1993

ATZ was prepared by adding an alumina sol equivalent to 2wt% as $Al_2O_3$ to an aqueous slurry of alumina (AKP-30) and zirconia (TZ-2Y or TZ-0Y) in the range of 10-30ATZ, followed by gelation, calcination, and sintereing between $1450^{\circ}C{\sim}1550^{\circ}C$ for 2h. They showed excellent microstructure with alumina grains of <$0.5{\mu}m$ and>99% of the theoretical density. Fracture toughness of ${\sim}8MPa{\cdot}m^{1/2}$ was observed around 20ATZ which was higher than $6MPa{\cdot}m^{1/2}$ obtainable by ball-milling.

• Korean Chemical Engineering Research
• /
• v.49 no.6
• /
• pp.786-789
• /
• 2011

In order to estimate the possibility of applying electrolytes generally used in solid oxide fuel cells(SOFCs) to direct carbon fuel cells(DCFCs), properties of YSZ(yttria stabilized zirconia) electrolyte were evaluated. In this study, vacuum slurry coating method was adapted to coat thin layer on anode support substrate. After sintering the electrolyte at $1400^{\circ}C$ for 5hrs, microstructure was analyzed by using SEM image. Also, gas permeability and ionic conductivity were measured to find out the potential possibility of electrolyte for DCFCs. The YSZ electrolyte represented dense coating layer and low gas permeability value. The ionic conductivity of YSZ electrolyte was high over $800^{\circ}C$. After measurement of the electrolyte properties, direct carbon fuel cell was fabricated and its performance was measured at $800^{\circ}C$.

• Journal of the Korean Ceramic Society
• /
• v.42 no.12 s.283
• /
• pp.827-832
• /
• 2005

In this study, thin electrolyte layer was prepared by 8YSZ ($8mol\%$ Yttria-Stabilized Zirconia) slurry dip and sol coating onto the porous anode support in order to reduce ohmic resistance. 8YSZ polymeric sol was prepared from inorganic salt of nitrate and XRF results of xerogel powder exhibited similar results $(99.2\pm1wt\%)$ compared with standard sample (TZ-8YS, Tosoh Co.). The dense and thin YSZ film with $1{\mu}m$ thickness was synthesized by coating of 0.7M YSZ sol followed by heat-treatment at $600^{\circ}C$ for 1 h. Thin film electrolyte sintered at $1400^{\circ}C$ showed no gas leakage at the differential pressure condition of 3 atm.