• Journal of Welding and Joining
• /
• v.33 no.3
• /
• pp.54-61
• /
• 2015

In this study, effect of laser power on hardness and microstructure of SKD61 Hot Die steel of which surface was melted and hardened with Yb:YAG disk laser was investigated. Beam speed was fixed at 70 mm/sec and distance between them was 0.8 mm about Laser surface melting. The only thing that was changed laser power. Laser powers were 2.0, 2.4 and 2.8 kW. No defect was found under all conditions. As the laser power increased, the penetration depth were deepened and the bead width was also widened. There was no hardness deviation of fusion zone at same laser power and it was higher than that of heat affected zone. In addition, the more laser power increased, the more hardness in fusion zone decreased. Fusion zone was macroscopically dendrite structure. However, core matric in dendrite was lath martensite of 100 nm size. There were $M_{23}C_6$ of 500 nm and the VC and $Mo_2C$ of a nano meters on boundary of dendrite.

• Proceedings of the KWS Conference
• /
• 2010.05a
• /
• pp.93-93
• /
• 2010

환경 규제 및 배출가스 규제에 의하여 차량 경량화를 위해 점차적으로 Al합금의 차체 및 부품적용 비율이 점차 확대되고 있다. 이에 따라 알루미늄의 레이저 용접 시 출력, 초점거리, 용접 속도 등 공정 변수의 상관관계와 용접 결함 현상에 의한 관심이 집중된 연구가 많이 발표되었으며, 알루미늄 5000계열의 경우 박판 용접 시 기공, 균열 등 과 같은 결함 현상을 방지하기 위하여, Twin spot laser, Laser-TIG hybrid 등과 같은 공법 적용을 제안되었다. 본 연구에서는 Yb:YAG laser welding 시 Mg 함량이 높은 AA5J32을 소재를 이용하여 박판 겹치기 용접 시 Back side spiking 결함 방지를 위한 레이저 빔 출력 파형을 설계하여 실험을 수행하였다. 또한 파형의 특성에 따라 나타나는 겹치기 용접부의 기계적 특성과 기공에 대해 알아 보고자 하였다.

• Journal of Welding and Joining
• /
• v.29 no.6
• /
• pp.4-8
• /
• 2011

• Proceedings of the Korean Vacuum Society Conference
• /
• 2016.02a
• /
• pp.201.1-201.1
• /
• 2016

본 연구에서는 펄스형으로 운전하는 플라즈마를 대상으로 하거나 플라즈마 특성의 빠른 변동을 파악하기 위해 1 kHz 이상의 반복율, 5 pulse burst mode와 2 J/pulse 이상의 발진특성을 갖는 Nd:YAG 레이저를 기반으로 하는 광원을 개발하기 위하여 레이저와 전원장치를 설계하였다. 전체 시스템은 MOPA(Master Oscillator Power Amplifier)형태로 구성하고 발진기는 FBG(Fiber Bragg Grating)을 반사경으로 사용한 Yb fiber 레이저를 설계하였다. 또한 설계한 레이저를 작동시킬 전원장치를 연구하였다. 정확한 스위칭과 턴온, 턴오프를 구현하기 위하여 IGBT 스위치를 적용하였고 적절한 저항을 조합하여 전류가 시간에 따라 상승하다가 스위치 턴오프에 급격히 감소하는 형태의 레이저 다이오드 구동에 적합한 삼각파와 비슷한 전류파형을 설계하였다. 추후 설계한 두 장치를 제작하여 테스트를 거친 후, VEST 내부 플라즈마 진단에 적용할 계획이다.

• Korean Journal of Optics and Photonics
• /
• v.21 no.3
• /
• pp.123-128
• /
• 2010

Sum frequency generation was utilized to obtain a yellow laser with the wavelength of 578.4 nm for a probe laser of an Yb lattice clock. The output of an Nd:YAG laser with wavelength of 1319 nm and that of an Yb-fiber laser with wavelength of 1030 nm were passed through a waveguided periodically-poled lithium niobate (WG-PPLN) for sum frequency generation. It is required that the probe laser has a linewidth of the order of 1 Hz to fully resolve the Yb lattice clock transition. Thus, the linewidth of the probe laser was reduced by stabilizing the frequency to a super-cavity. This was made of ULE with a low thermal expansion coefficient, and was mounted on an active vibration-isolation table at the optimal point for the reduced sensitivity to vibration. Also, this was installed in a vacuum chamber, and the temperature was stabilized to 1 mK level. This system was installed in an acoustic enclosure to block acoustic noise. The finesse of the super-cavity was measured to be 380 000 from the photon life time of the cavity.

• Korean Journal of Optics and Photonics
• /
• v.10 no.4
• /
• pp.301-305
• /
• 1999

The phase matching conditions of the new optical crystal grown by Czochralski pulling method, YCOB($YCa_4O(BO_3)_3$) with wavelength were suggested, and the second harmonic generation efficiency for the fundamental of Nd:YAG laser of 1064 nm was investigated. The variation of nonlinearity with rare earth ion doping was also investigated by measuring the second harmonic generation efficiencies of $Yb^{3+}$ + $Nd^{3+}$and ion doped YCOBs.

• Journal of Welding and Joining
• /
• v.31 no.3
• /
• pp.66-75
• /
• 2013

In this study, the effect of coating thickness($20{\mu}m$ and $30{\mu}m$) on microstructure and tensile properties in Yb:YAG disk laser welds of Al-Si-coated boron steel (1.2mmt) was investigated. In the case of as welds, the quantity of ferrite was found to be higher in base metal than that in HAZ (Heat Affected Zone) and fusion zone, indicating, fracture occurrs in base metal, and the fracture position is unrelated to the coating thickness. Furthermore, yield strength, tensile strength of base metal and welded specimens showed similar behavior whereas elongation was decreased. On the other hand, base metal and HAZ showed existence of martensite after heat treatment, the fusion zone indicated the presence of full ferrite or austenite and ferrite during heat treatment ($900^{\circ}C$, 5min), After water cooling, austenite was transformed to martensite, and the quantity of ferrite in fusion zone was higher as compared with in base metal, resulting in sharply decrease of yield strength, tensile strength and elongation, which leads to fracture occured at fusion zone. In particular, results showed that because the concentration of Al was higher in 30um coating layer specimen than that of 20um coating specimen, after heat treatment, producing a higher quantity of ferrite was higher after heat treatment in the fusion zone; howevers, it leads to a lower tensile property.

• Laser Solutions
• /
• v.18 no.2
• /
• pp.5-10
• /
• 2015

A tailor welded blank (TWB) is a welded blank comprised of two or more sheets with different properties - thickness, strengths or formabilities. TWBs are applied to the body panels to reduce weight and cost of the part. In this research, ultra high strength steel and high ductility steel were joined and laser tailor welded blanks were implemented. Yb:YAG laser welding tests were conducted with various welding conditions, and mechanical and geometrical characteristics of weldments were evaluated.

• Journal of Welding and Joining
• /
• v.33 no.5
• /
• pp.53-60
• /
• 2015

Laser surface Melting Process is getting hardening layer that has enough depth of hardening layer as well as no defects by melting surface of substrate. This study used CW(Continuous Wave) Yb:YAG and STD11. Laser beam speed, power and beam interval are fixed at 70mm/sec, 2.8kW and 800um respectively. Hardness in the weld zone are equal to 400Hv regardless of melting zone, remelting zone overlapped by next beam and HAZ. Similarly, microstructures in all weld zone consist of dendrite structure that arm spacing is $3{\sim}4{\mu}m$, matrix is ${\gamma}$(Austenite) and dendrite boundary consists of ${\gamma}$ and $M_7C_3$ of eutectic phase. This microstructure crystallizes from liquid to ${\gamma}$ of primary crystal and residual liquid forms ${\gamma}$ and $M_7C_3$ of eutectic phase by eutectic reaction at $1266^{\circ}C$. After solidification is complete, primary crystal and eutectic phase remain at room temperature without phase transformation by quenching. On the other hand, microstructures of substrate consist of ferrite, fine $M_{23}C_6$ and coarse $M_7C_3$ that have 210Hv. Microstructures in the HAZ consist of fine $M_{23}C_6$ and coarse $M_7C_3$ like substrate. But, $M_{23}C_6$ increases and matrix was changed from ferrite to bainite that has hardness above 400Hv. Partial Melted Zone is formed between melting zone and HAZ. Partial Melted Zone near the melting zone consists of ${\gamma}$, $M_7C_3$ and martensite and Partial Melted Zone near the HAZ consists of eutectic phase around ${\gamma}$ and $M_7C_3$. Hardness is maximum 557Hv in the partial melted zone.

• Electrical & Electronic Materials
• /
• v.7 no.4
• /
• pp.289-293
• /
• 1994

Thin films of YB $a_{2}$C $u_{3}$$O_{7-x}$ supercondYB $a_{2}$C $u_{3}$$O_{7-x}$uctor were prepared on (100) SrTi $O_{3}$ substrates by pulsed laser deposition using visible light laser. Q-switched Nd:YAG(532 nm, 30 ns) pulsed laser was used for deposition. The effects of substrate temperature and oxygen pressure during deposition on films were studied. Critical current density of 2.93*10$^{6}$ A/c $m^{2}$ at 77K and Tc(zero)=91.7K were obtained from the film prepared with Tsub=745.deg. C and $P_{02}$=200 mTorr. XRD analysis showed that the grown film has c-axis normal orientation to the substrate surface and has single phase. Surface morphology of the film has been improved by interfering the plume ejected from YB $a_{2}$C $u_{3}$$O_{7-x}$ target.arget.t.