• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2001년도 추계학술대회 논문집 Vol.14 No.1
• /
• pp.288-291
• /
• 2001

It is very important to select suspension solution for forming electrophoretic deposited YBCO thick mm, because it is heavily affected to its superconducting properties. In this paper, high-temperature superconductor films of $YBa_{2}Cu_{3}O_{7-x}$ were fabricated by electrophoretic deposition (EPD) from alcohol-based suspension such as iso-propanol, iso-butanol, and their mixture. For the formation of YBCO dense and adherent coating on a silver wire by EPD, 1 % PEG(1000) 2 ml, as a additive for making their surface crack-free, was used for electrophoresis. As a results, the cracks were considerably decreased and the superconducting critical current density $(J_e)$ without/with PEG was $1200A/cm^2$ and $2020A/cm^2$, which films deposited in mix iso-propanol and iso-butanol suspension.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2001년도 추계학술대회 논문집
• /
• pp.288-291
• /
• 2001

It is very important to select suspension solution for forming electrophoretic deposited YBCO thick film, because it is heavily affected to its superconducting properties. In this paper, high-temperature superconductor films of YBa$_2$Cu$_3$$O_{7-x}$ were fabricated by electrophoretic deposition (EPD) from alcohol-based suspension such as iso-propanol, iso-butanol, and their mixture. For the formation of YBCO dense and adherent coating on a silver wire by EPD, 1% PEG(1000) 2 $m\ell$, as a additive for making their surface crack-free, was used for electrophoresis. As a results, the cracks were considerably decreased and the superconducting critical current density (J$_{c}$) without/with PEG was 1200 A/$\textrm{cm}^2$ and 2020 A/$\textrm{cm}^2$, which films deposited in mix ism-propanol and iso-butanol suspension.ion.

• 한국세라믹학회지
• /
• 제36권2호
• /
• pp.203-209
• /
• 1999

Si 기판위에 Ba2YCu3O7-$\delta$ 고온초전도체를 응용하기 위해 요구되는 buffer층으로 유망한 재료인 LaAlO3 단일상 분말을 고상반응법과 자발착한 연소반응법으로 제조하였다. 제조된 LaAlO3 분말의 입자형태와 결정상태는 scanning electron microscope (SEM)과 X-ray diffractometer (XRD)를 이용하여 분석하였다. 분말의 비표면적과 소결특성은 각각 Brunauer-Emmett-Teller(BET) 방법과 dilatometer를 측정하였다. 고상반응법으로 LaAlO3 분말을 제조할 때에는 하소온도를 150$0^{\circ}C$까지 높게 하여도 단일상을 얻는 것이 어려웠으나 자발착한 연소반응법에 의한 분말제조는 $650^{\circ}C$의 저온에서 하소하여도 쉽게 얻을 수 있었다. Dilatometer 측정을 통하여 분석해 보면, 고상반응법에 의한 분말보다 자발착한 연소반응법에 의한 분말로 제조된 소결체가 고상반응법에 의한 소결체에 비해 1.4배나 큰 소멸밀도(98.87%)를 가졌다. 이렇게 소결밀도에서 큰 차이가 나는 것은 자발착한 연소방법에 의한 분말의 평균 입자크기가 nano crystal size이고 비표면적 값(56.54 $m^2$/g)이 매우 크기 때문이다. 두가지 방법으로 제조된 분말을 이용, LaAlO3 layer를 스크린 프린팅과 소결법으로 Si 기판상에 제조하였으며 자발착한 연소합성법으로 제조된 분말은 110$0^{\circ}C$에서 우수한 소결특성을 나타내었다.