• Progress in Superconductivity
• /
• v.13 no.3
• /
• pp.158-162
• /
• 2012

$Y(Pr)Ba_2Cu_4O_8$ system is one of the most studied high temperature superconductors. Substitution of Pr for Y in this system suppresses $T_c$ and superconductivity finally disappears at a high Pr doping. There are competing theories for the suppression of $T_c$ but systematic experimental results are very rare. In order to find the change in Fermi surface topology which can affect the superconductivity, we have performed angle-resolved photoemission studies on single crystal samples of $YBa_2Cu_4O_8$ and $PrBa_2Cu_4O_8$. While the Fermi surface of $YBa_2Cu_4O_8$ shows a similar topology to those of other cuprates, we observe only 1D like band structures in $PrBa_2Cu_4O_8$. We find no significant differences in the chain band for both samples.

• The Transactions of the Korean Institute of Electrical Engineers C
• /
• v.49 no.4
• /
• pp.210-218
• /
• 2000

For the fabrication of $YBa_2Cu_3O_x$ thick film, a substrate of $Y_2BaCuO_5$ was fabricated by adding $CeO_2$ into $Y_2BaCuO_5$ and two types of doping materials added with binder material were prepared. Each doping material was patterned on $Y_2BaCuO_5$substrate by the screen printing method and then was annealed at the temperature with a few step. It could be observed by X-ray diffraction patterns and SEM photographs that through the diffusion process of the $Y_2BaCuO_5$ and each doping material, the $YBa_2Cu_3O_x$ phase was formed. And with n additive of $CeO_2$ the thickness of formed $YBa_2Cu_3O_x$decreased. From the experiment of current limiting on thick film, the sample with thiner thickness of $YBa_2Cu_3O_x$ showed the more effective characteristics of current limiting.

• Bulletin of the Korean Chemical Society
• /
• v.12 no.6
• /
• pp.606-612
• /
• 1991

We have carried out an extended Huckel calculation to rationalize the role of $CuO_3$ chains and the size effect of the charged model clusters for the following charged model culsters : ${{Cu_6}{O_{21}}^{28-},\;{{Cu_6}{O_{22}}^{30-}\;,{{Cu_9}{O_{30}}^{39-}\;,{{Cu_9}{O_{32}}^{43-}\;,{{Cu_{12}{O_{38}}^{48-}\;,{{Cu_{15}{O_{50}}^{65-}\;,{{Cu_{18}{O_{54}}^{66-}\;,{{Cu_{18}{O_{55}}^{68-}\;,{{Cu_{24}{O_{70}}^{84-}\;and\;{{Cu_{27}{O_{78}}^{93-}$ for high-$T_c$ superconductor $YBa_2Cu_3O_7$: ${{Cu_6}{O_{18}}^{22-}\;,{{Cu_9}{O_{26}}^{31-}}\;,{{Cu_{12}{O_{32}}^{36-}\;,{{Cu_{15}{O_{42}}^{49-}\;,{{Cu_{18}{O_{46}}^{50-}\;,{{Cu_{24}{O_{60}}^{64-}\;and\;{{Cu_{27}{O_{66}}^{69-}$ for insulator $YBa_2Cu_3O_6$. The results show that the electronic structures and properties of the charged model clusters relating to high-$T_c$ superconductor are very sensitive to the size change of the clusters with various environmental effects, wherease those of the charged model clusters for insulator $YBa_2Cu_3O_6$ are monotonous to the size change. The $CuO_3$ chains along the b-direction may yield cooperative electronic coupling with the $CuO_2$ layers in determining both conducting and superconducting properties of $YBa_2Cu_3O_{7-x}$ system.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.29 no.2
• /
• pp.110-113
• /
• 2016

(YNdSm)-Ba-Cu-O system high Tc composite superconductors were directionally grown by zone melting process, having large temperature gradient, in air atmosphere. Cylindrical green rods of $(YNdSm)_{1.8}Ba_{2.4}Cu_{3.4}O_x$ [(YNS)1.8]composite oxides by CIP (cold isostatic pressing) method using rubber mold were fabricated. The microstructure and superconducting properties were investigated by XRD, TEM and SQUID magnetometer. The size of nonsuperconducting $(YNdSm)_2BaCuO_5$ inclusions of the melt-textured (YNS)1.8 sample with $CeO_2$ additive were remarkably reduced and uniformly distributed within the superconducting (YNS)1.8 matrix. (YNS)1.8 samples, with / without $CeO_2$ additive, showed an onset $T_c{\geq}90K$ and sharp superconducting transition. The critical current density $J_c$ value of the (YNdSm)1.8 superconductor with $CeO_2$ additive were 840 A, $1.2{\times}104A/cm^2$ in 77 K, 0 Tesla by direct current transport method.

• Journal of the Korean Institute of Telematics and Electronics
• /
• v.27 no.5
• /
• pp.724-728
• /
• 1990

The X-ray diffraction pattern, electrical resistance, density and critical temperature of a series of YBa2(Cu3-xNix)O7-\ulcornersamples (0\ulcorner\ulcorner.5) were investigated with the increase of the Ni content. The samples show a principal 1.2.3-like phase with well resolved orthorhombic peaks. The final pattern of the x=0.1 sample appears to be well reacted orthorhombic YBa2(Cu,Ni)3O7-\ulcornerwith minor impurities and an appreciable amorphous fraction. From the above results, we conclude that Ni does not play an important role for the superconductivity in the Y-Ba-Cu-O system.

• Applied Chemistry for Engineering
• /
• v.9 no.2
• /
• pp.165-171
• /
• 1998

The $Y_1Ba_2Cu_3O_{7-x}$(123) superconductor powders were prepared by pyrophoric synthesis method(PSM) using $Y_2O_3$(99.9%), $BaCO_3$(99.9%), and CuO(99.9%) powders. The phase formation and reaction kinetics of 123 superconductor manufactured with powders prepared in various pHs of pyrophoric synthetic solution have been studied through the experiments at various heat treatment temperatures and times. Inductively coupled plasma(ICP) spectroscopy and scanning electron microscopy(SEM) measurements were performed to examine the composition and morphology of the sample. X-ray diffraction(XRD) analysis was done to determine phase formation and conversion ratio of Y-Ba-Cu-O systems. The 123 powder prepared at pH 7(${\pm}0.3$) yields the best result in terms of purity, homogeneity, and reactivity. The activation energies(${\Delta}E_a$) of 123 phase formation were found to be 191 kJ/mol and 230kJ/mol in solid state reaction method and pyrophoric synthesis method, respectively.

• Journal of the Korean Magnetics Society
• /
• v.1 no.2
• /
• pp.15-21
• /
• 1991

The magnetic properties of the $Y_{1}Ba_{2}Cu_{3-x}Sn_{x}O_{7-y}$ superconductor were studied as a function of Sn concentration by utilizing both the vibrating sample magnetometer (VSM) and torque magnetometer. Unlike the cases where Fe and Co were substituted for Cu, the superconducting transition temperature was maintained above 90 K until x reached the value of 0.36. The lower critical field $H_{c1}(T)$ and upper critical field $H_{c2}(T)$ are measured as a function of temperature and external magnetic field, respectively. By aid of these results, $H_{c1}(0)$.($H_{c2}(0)$), the coherence length ${\varepsilon}_{0}$, the penetration depth ${\lambda}_{0}$, and the Ginzburg-Landau parameter k were oqtained. Flux pinning was also observed in the sample.

• Progress in Superconductivity
• /
• v.6 no.1
• /
• pp.89-94
• /
• 2004

The policrystalline$SmBa_2$$Cu_2$$O_{y}$ was synthesized by the solid state reaction method. The dependence of AC susceptibility on temperature and applied ac field was studied. The critical temperature $T_{c}$ is about 92 K. As the ac field is increased, the slope and the value of real part of susceptibility become smaller and the peak position of imaginary part $T_{P}$ was shifted to a lower temperature with peak broadening. Using Bean's model, we determined intergrain critical current density $J_{c}$ and obtained $44 A/{cm}^2$ at 75 K. From the relation of the $J_{c}$ (T)=($1-T/T_{c}$ )$^{\beta}$ we obtained $\beta$=0.8 and found that the Josephson junction type of the $SmBa_2$$Cu_2$$O_{y}$ is SIS junction. The peak of the imaginary part shifts to higher temperature with increasing frequency, f. from Arrhenius plot, we obtained the activation energy of about 0.96 eV.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 1996.11a
• /
• pp.174-176
• /
• 1996

In the YBCO matrix, 10wt.% Y$_2$BaCuO$\_$5/ (211 phase) was added, the final 211 content of YBCO made by MTG process could reach about 20wt.% which was the optimum value for the critical current density. And also 10wt.% Ag was added in the matrix of YBCO, which was nearly about the saturate solubility of silver in textured YBCO. SmBaCuO crystal was grown by the melted-condensed process. A 5${\times}$5${\times}$2㎣ single crystal of SmBaCuO was used to be the seed in the preparation of YBCO. It was proved the orientation of YBCO was the same as the orientation of the SmBaCuO seed. The oxygen absorption of bulk oriented YBCO was studied and the heat treatment of oxygen absorption would be in flowing oxygen, at 400$^{\circ}C$ for about 24 hours. the magnetic hysteresis loops were measured by Vibrating Smaple Magnetometer and the J$\_$c/ was calcuated by means of Bean's model.

• Journal of the Korean Ceramic Society
• /
• v.27 no.1
• /
• pp.48-54
• /
• 1990

YBa2Cu3O7-x(=YBCO) single crystals were grown by flux method and the growing process of crystals was investigated. YBCO and 3BaO-7CuO composition powders were mixed by the ratio of 25 : 75(wt%), and the mixtures were melted at 105$0^{\circ}C$ in a electric furnace with no temperature-gradient. Then the melt was cooled at a rate 2-1$0^{\circ}C$/h in the above furnace. YBCO single crystal plate with average size of $1.5\times$2.0$\times$0.1㎣ were obtained in the cavities between crucible and solidified ingot, and the single crystals were oriented to <001> direction. The ingots of flux parts were analyzed by XRD and EDS for the purpose of presuming the growing process of the crystals. It was assumed that the divorced eutectic reaction, by which YBCO crystals were grown first and then BaCuO2 and CuO crystals, occured in the case of cooling rate faster than 2$^{\circ}C$/h. When the cooling rate was 2$^{\circ}C$/h, it was assumed that quasi-equilibrium eutectic reaction occured, so that YBCO, BaCuO2 and CuO crystals were grown at the same time.