• 품질경영학회지
• /
• 제44권3호
• /
• pp.509-526
• /
• 2016

Purpose: We would like to find the alternative method for the weathering test on rubber coated fabrics and adhesive-coated fabrics for the military products, KS M 0706 (Sunshine carbon arc) to KS M ISO 4892-2 (Xenon arc). Methods: We measured the tensile strength of adhesive-coated fabrics and adhesive products treated with sunshine carbon arc and xenon arc during 100, 150 and 200 hours, respectively. All of the results were treated with statistical test, ANOVA method. We also validate the surface modifications caused by treatment method and time by using FT-IR ATR and, SEM. Results: In case of the thick adhesive-coated fabrics (app. 1 mm), there was no distinctive difference on tensile strength by treatment method and time. In case of the thin mask hood (app. 0.22 mm) and TENT (app. 0.5 mm), there was distinctive difference on tensile strength. Especially, carbon arc showed a huge lowering properties. We could validate the curing from light and moisture, and the functional group change from cross-linking and oxidation using FT-IR ATR. In case of IBS, there was a surface cracks on SEM images. In case of mask hood, there was no distinctive differences, except for a particle falling from decreased affinity between rubber and particles caused by carbon arc. Conclusion: We concluded that there was no problems for changing xenon arc weathering test with same treatment time on IBS, KM7, K21 and adhesive products. In case of TENT and mask hood, there was a difference in tensile strength in accordance with the change of the treated time and method.

• 한국표면공학회지
• /
• 제47권2호
• /
• pp.57-62
• /
• 2014

The biogas holder is composed of an outer membrane and an inner membrane which are subject to outdoor exposure and gas exposure respectively. The influence of weathering conditions on the photo-degradation of a biogas holder was investigated. Tests were performed under three different methods - outdoor exposure tests (Seosan, Arizona), accelerated tests (Xenon-are lamp) with the outer-membrane of biogas. Moreover, the changes in the aging process were monitored using color difference, gloss, the contact angle and an optical microscope. Changes in physical properties, such as decrease reduction in gloss, decrease in the contact angle, increase in color difference were observed in the aging process. The comparison between membrane 3B, 4B and membrane 5B under xenon-arc were discussed. Membrane 5B was very sensitive to ultraviolet (UV) ray. There were many difficulties in the outdoor exposure test due to acid rain, dust, and stain resistance.

• 공업화학
• /
• 제28권1호
• /
• pp.35-41
• /
• 2017

외부에 노출된 재료는 자외선, 열, 온도, 습도 등의 다양한 환경 인자에 의해 성능저하가 일어나게 되며, 열화속도 및 사용수명에 대한 예측은 매우 중요한 문제이다. 본 연구에서는 가장 많이 사용되고 있는 색상 중 흰색, 초록색 재귀반사시트를 가지고 미국 아리조나, 인도 첸나이, 프랑스 세너리, 한국 서산 등 4개 지역에서 옥외폭로시험 및 제논아크촉진시험을 통하여 재귀반사시트 반사성능의 변화율을 측정하였다. 서산지역 및 제논아크 촉진시험을 통하여 얻어진 반사성능 값을 통해 회귀분석을 이용하여 가속계수를 구하였다. 또한, solar uv 프로그램을 이용하여 다양한 기후지역별 가속계수를 구할 수 있었으며, 그 결과 서산지역을 기준으로 프랑스 세너리 1.04배, 미국 아리조나 1.82배, 인도 첸나이 1.92배의 가속계수를 확인할 수 있었다.

• 한국가구학회지
• /
• 제13권1호
• /
• pp.27-37
• /
• 2002

This study was investigated with the surface properties such as physical and accelerated tests of wood-based floorings. In physical test, hardness and abrasion resistance values of laminate floorings were higher than those of others. The center line average surface roughness($R_a$) of imported laminate flooring was highest value($1.34{\mu}m$) and that of imported solid wood flooring was lowest value($0.62{\mu}m$). In cold resistance and moist heat resistance, no defects were found on the surface of all flooring (crack, blistering, peeling, and gloss loss etc.) after testing. Wet-cold-dry cycle test showed that plywood flooring appeared some cracks. In accelerated weathering test, color difference increased with increasing Xenon arc light irradiation

• 한국신뢰성학회:학술대회논문집
• /
• 한국신뢰성학회 2002년도 정기학술대회
• /
• pp.157-164
• /
• 2002

본 연구에서는 실생활에 응용되는 Chloroprene계 고무에 대하여 30개월 동안 옥외 폭로를 행하였으며 동시에 Xenon-arc Type의 촉진 내후성시험기를 이용하여 그에 따른 내후성의 변화를 평가하였다. 폭로기간에 따른 인장강도와 신장률의 변화를 측정하였고 폭로면의 표면층에 대하여 FT-IR과 SEM을 사용하여 화학적 특성 및 미세구조를 분석하였다. 태양복사와 습도에 노출된 고무의 표면은 매우 짧은 기간에 파괴되었고, 고무 내부에 존재하는 가교제들의 용출을 확인할 수 있었으며, 산소와의 결합으로 내부층보다 고무의 표면에서 더 많은 가수분해와 광분해가 이루어진다는 것을 확인할 수 있었다. 이와 같은 표면층의 변화와 파괴는 고무의 기계적 성질에도 의미 있는 영향을 주었다.

• 공업화학
• /
• 제24권2호
• /
• pp.138-143
• /
• 2013

화학적 열화를 빠르게 유도할 수 있는 단파장의 자외선(254 nm)을 고밀도 폴리에틸렌의 표면에 조사하여, 생성된 carbonyl band의 변화로부터 기계적 물성 변화를 예측할 수 있는 지에 대한 가능성을 연구하였다. 오랜 시간이 요구되는 자연 태양광에 의한 옥외폭로시험이나, 제논-아크 광원에 의한 광 열화 대신에 광양자 에너지가 높은 UVC 램프를 사용함으로써, 유도되는 광열화의 화학적 특성이 동일한 기계적 물성 변화를 유발하는지를 확인하는 것에 본 연구의 의미가 있다. 인장시험과 크리프-파괴시험으로 진행된 고밀도 폴리에틸렌의 기계적 강도는 CI 변화에 유사한 양상을 보였으며, 특히 항복강도와 신장률은 자외선 노출시간과 밀접한 관계가 있음을 보여주었다. 따라서 빠른 표면 열화를 유발하는 UVC 램프를 활용한 카르보닐 지수와 기계적 물성 변화의 관계를 통하여 장시간이 요구되는 옥외에서의 기계적 물성변화를 보다 빠르게 파악할 수 있는 방법을 제시하였다.

• 보존과학회지
• /
• 제25권4호
• /
• pp.373-381
• /
• 2009

야외 전시되는 철제문화재 보존을 위해서 유물 표면을 피복처리 하는 것은 부식방지의 대표적인 방법이다. 근대문화유산 제78호 경의선장단역증기기관차는 보존조치 후 노천에서 전시될 예정이라서 기관차의 재부식 예방에 효과적인 표면 피복재를 내후성 실험을 통해 선별하였다. 실험재료는 기관차 표면 피복에 주로 사용되는 미정질 왁스 2종과 봉밀왁스를 기반으로 제조한 혼합왁스를 선별하였다. 실험방법은 3종의 왁스를 기관차 시편에 각각 피복하고 ISO 4892-1981 기준에 따라 제논아크촉진내후성시험기 속에서 1000시간 내후성 시험을 한 후 그 변화상을 비교 조사하였다. 실험결과 봉밀 왁스는 400시간 이후부터 표면에 백화현상이 발생하면서 노화하였고 미정질 왁스 2종은 800시간 이후부터 변화를 보였다. 시험전과 후 수분접촉각의 변화 역시 봉밀 왁스 보다 미정질 왁스가 적게 나타났다. 따라서 미정질 왁스 중 특히 고온형이 내후성과 수분 차단력이 가장 뛰어난 것으로 확인되어서 이것으로 증기기관차의 표면을 피복하게 되었다.