• Journal of the Mineralogical Society of Korea
• /
• v.27 no.4
• /
• pp.183-195
• /
• 2014

In order to study the mineralogical characteristics of a cathodic deposition-metallic powder, electrowinning experiments were carrier out on different electrolytic solutions at varying electric distances and electric currents. Under the same experimental conditions, Cu recovery was obtained much more effectively using a sodium chloride electrolyte than with a sulfuric acid electrolyte. In XRD analysis, copper ($Cu^0$), chalcanthite and cuprite were identified in the sulfuric acid electrolyte, while copper, nantokite and chalcanthite were observed in the sodium chloride electrolyte. In the sodium chloride electrolyte solution, increasing the electric distance and the electric current increased the Cu recovery rate, anode weight and anodic corrosion. The results of XRD analysis with non-pulverized cathodic deposition-metallic powder showed the average copper crystallite size was increased by increasing the electric current and decreasing the electric distance. It is suggested that the mass transfer was controlled with diffusion on the boundary between the electrode and the electrolytic solution due to the formation of dendrite copper.

• Journal of the Korean Ceramic Society
• /
• v.39 no.5
• /
• pp.452-459
• /
• 2002

This paper addresses the hydrothermal reactivity of blast furnace slag and fly ash with lime, respectively. The test conditions were CaO-to-$SiO_2$ ratio (C/S), autoclaving temperature ($140{\circ}C$ and $180{\circ}C$) and time (20 to 60h). The study was carried out in terms of the hydrothermal reactivity between $SiO_2$ contained in each hydraulic material and (pure) lime and the compressive strength of autoclaved specimens. Porosity measurement and the XRD analysis were also made in order to ascertain the hydraulicity of the siliceous materials. Compressive strength of the specimens was interpreted in terms of porosity and the reactivity of CaO and $SiO_2$. And the XRD analysis showed the C/S change of the hydrates in the course of autoclaving process. $SiO_2$ in the blast furnace slag was more reactive with CaO than that in the fly ash and consequently the blast furnace slag specimens resulted in much higher compressive strength. A maximum compressive strength of $807kg/cm^2$ was obtained for the blast furnace slag at the autoclaving condition of $180{\circ}C$ and 40 h, while only $397kg/cm^2$ was maximally to achieve with fly ash.

• Journal of the Korea Concrete Institute
• /
• v.28 no.3
• /
• pp.349-356
• /
• 2016

This report presents the results of an investigation on the early strength development of pastes high volume slag cement (HVSC) activated with different concentration of sodium carbonate ($Na_2CO_3$). The ordinary Portland cement (OPC) was replaced by ground granulated blast furnace slag (GGBFS) from 50% to 90% by mass, the dry powders were blended before the paste mixing. The $Na_2CO_3$ was added at 0, 2, 4, 6, 8 and 10% by total binder (OPC+GGBFS) weight. A constant water-to-binder ratio (w/b)=0.45 was used for all mixtures. The research carried out the compressive strength, ultrasonic pulse velocity (UPV), water absorption and X-ray diffraction (XRD) analysis at early ages(1 and 3 days). The incase of mixtures, V5 (50% OPC + 50% GGBFS), V6 (40% OPC + 60% GGBFS) and V7 (30% OPC + 70% GGBFS) specimens with 6% $Na_2CO_3$, V8 (20% OPC + 80% GGBFS) and V9 (10% OPC + 90% GGBFS) specimens with 10% $Na_2CO_3$ showed the maximum strength development. The results of UPV and water absorption showed a similar tendency to the strength properties. The XRD analysis of specimens indicated that the hydration products formed in samples were CSH and calcite phases.

• Journal of Conservation Science
• /
• v.34 no.1
• /
• pp.39-50
• /
• 2018

This study replicated traditional smelting methods to produce iron blooms from sand iron. The metallurgical properties of the slag and the iron blooms were analyzed. The sand iron materials used in the smelting experiments, which were based on ancient documents, were collected from Gyeong-Ju and Pohang. Analysis by WD-XRF and XRD showed that Gyeong-Ju's sand iron contains a high-titanium, with magnetite, and Pohang's sand iron contains a low-titanium, which magnetite and ilmenite were mixed. Analysis of the slag with XRD, and the micro-structure with metal microscopes and SEM-EDS, confirmed that the major compounds in the slag of the Gyeong-Ju's sand iron were fayalite and $w\ddot{u}stite$, and those in the slag of the Pohang's sand iron were titanomagnetite and fayalite. The differences in the main constituents were confirmed according to the Ti quantity. Finally, we observed the microstructures of the iron blooms. In the case of the iron bloom produced from Gyeong-Ju's sand iron, the outside was found to be dominantly a pearlite of eutectoid steel, while the inside was a hypo-eutectoid steel where ferrite and pearlite were mixed together. While, the major component of the iron bloom produced from Pohang's sand iron was ferrite, which is almost like pure iron. However, there were many impurities inside the iron blooms. Therefore, this experiment confirmed that making ironware required a process that involved removing internal impurities, refining, and welding. It will be an important data to identify the characteristics of iron by-products and the site through traditional iron-making experiments under various conditions.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.24 no.3
• /
• pp.96-103
• /
• 2020

As a basic study for the application of natural zeolite as a concrete admixture, the compressive strength, activity factor, Ca(OH)₂ quantitative analysis and XRD experiments were investigated. It is thought that SiO₂, which is abundant in natural zeolite, affects the strength development by reacting with the hydration product of cement in all specimens in which natural zeolite was added according to powder level and substitution rate. As the substitution rate increases, the compressive strength decreases, which is considered to be due to the decrease in the amount of C₃S and C₂S minerals in the clinker, which affects the strength expression compared to the cement content of the reference mortar. The XRD crystal structure did not show a significant difference from the reference mortar, and it was confirmed that the Z2-10 (Blaine: 15,600㎠ / g) specimen with 10% substitution of natural zeolite was the best among the experimental levels. Substitution amount for use as concrete admixture is 10% substitution is most ideally seen.

• Applied Chemistry for Engineering
• /
• v.16 no.6
• /
• pp.768-771
• /
• 2005

The deposition of silicon nitride ($SiN_x$) thin films was carried out on $SiO_2/Si$ substrate at room temperature by reactive dc magnetron sputtering. The analysis of deposited $SiN_x$ films using x-ray photoelectron spectroscopy indicated that the composition of $SiN_x$ films was Si-rich. The deposited $SiN_x$ thin films were annealed by varying annealing temperature and time. X-ray diffraction (XRD) analysis was performed in order to examine the crystallization of Si in $SiN_x$ thin films. The optical and electrical properties of $SiN_x$ thin films were measured for the observation of Si nanodot. As a result, we observed the XRD peaks that might be the Si crystals. As the annealing time and annealing temperature increased, the photoluminescence intensity of $SiN_x$ films gradually increased. The capacitance-voltage characteristics of $SiN_x$ film measured before and after annealing indicated that the trap effect of electrons or holes occurred due to the existence Si nanodots in the $SiN_x$ thin films.

• Conservation Science in Museum
• /
• v.30
• /
• pp.89-100
• /
• 2023

Museum collections are comprised of a variety of materials, and different scientific examinations are being conducted according to the types and production properties of the materials, but insufficient research has been carried out on ultra-small artifacts. To identify the material characteristics of the white ultra-small materials excavated from Geumnyeongchong tomb, this study carried out a wide range of non-destructive analyses (specific gravity, microscopy, nano-computed tomography (Nano-CT), scanning electron microscopy-energy dispersive X-ray spectroscopy (SEM-EDS), X-ray diffraction (XRD), and Raman spectroscopy) and compared the said artifacts with the Goryeo-era burial accessories examined in prior research. Non-destructive analysis confirmed the presence of aragonite, which mainly consists of calcium carbonate (CaCO₃) as the constituent mineral, and identified the material used for the ornaments as the gemstone pearl based on its growth lines. This study concludes that pearls began to be used in the ancient Korean Peninsula in the 6^th century. It is expected that scientific examinations of the white ultra-small artifacts will yield information about the social culture of the time.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.14 no.9
• /
• pp.4185-4190
• /
• 2013

We executed the property changes of the sintered MgO (99.9% purity, 300nm size) specimens with addition to CaO content of 0.00wt%, 0.25wt%, and 0.50wt%, processed at 7GPa, for 5min, 600~$800^{\circ}C$. To investigate the micro-structure and physical property changes of the sintered MgO(-CaO), we employed a scanning electron microscopy(SEM), X-ray diffractomerty(XRD), Vickers hardness, and density. The SEM result showed that MgO powder of 300nm size was changed into sintered structure of 520nm by high pressure and low temperature sintering, regardless of the CaO contents. According to the XRD analysis, no CaO phase observed, while MgO peaks shift indicated the existence of CaO in the MgO matrix. The Vickers hardness result showed that hardness of sintered MgO-CaO increased by 12% compared pure MgO under the same temperature conditions. It implied that we can obtain the same hardness with $100^{\circ}C$ lowered sintering temperatures by addition of CaO. The density results showed that it was possible to obtain density of 98%, which is 5% greater than that of pure MgO at low temperature of $600^{\circ}C$.

• Journal of the Korea Institute of Building Construction
• /
• v.23 no.6
• /
• pp.693-702
• /
• 2023

This research explores the potential application of Liquid Red Mud(LRM), a byproduct of industrial processes, in the construction sector. We neutralized LRM(pH 10-12) using nitric acid, aiming to understand its viability in construction applications. The study involved substituting LRM(pH 7-8) in mortar formulations, varying by cement type. We assessed the properties of these mixtures by measuring flow, setting time, and compressive strength. Additionally, X-ray Diffraction(XRD) and Scanning Electron Microscopy(SEM) analyses were conducted to examine the chemical properties. Results indicated a reduction in flow value for LRM and LN(neutralized LRM) compared to the control (Plain ) across different cement types. The setting times(initial and final) for LRM and LN were notably shorter than Plain. In compressive strength tests, LRM replaced with slag cement showed enhanced initial strength, though long-term strength gains were marginal across different cement types. SEM analysis revealed distinct voids in Plain and LN, with LRM exhibiting a fibrous microstructure. XRD patterns in SN(slag neutralized) resembled those in OR(original red mud) and ON(original neutralized), with a notable peak at a 2θ value of 22°. The study concludes that unneutralized LRM, when substituted for slag cement in mortar, yields superior initial strength compared to its neutralized counterpart.

• Applied Microscopy
• /
• v.32 no.4
• /
• pp.311-317
• /
• 2002

There is great requirement on the TEM specimen preparation method with particle size selectivity as a prerequisite for the quantitative structure analysis on the materials such as gibbsite powder, which generally forms a large agglomerate and shows a variation of transition process depending on their sizes. In this experiment, we made an attempt to give a methodology for the TEM specimen preparation of powder with the size selectivity. After mixing 1 wt% gibbsite powder with ethanol solvent, gibbsite suspension was prepared by application of ball-milling and ultrasonification with addition of 0.25 vol% dispersion agent, Darvan C, which was diluted into distilled water by the ratio 1:19. Appling the static sedimentation method to gibbsite suspension after estimation of the sedimentation time by the measurement of accumulative concentration variation, we acquired TEM specimens with well-dispersed and size selected gibbsite particles in nm scale. Overall picture of each sample was taken by SEM and morphology of each dispersed particle was imaged by TEM. Raw and processed gibbsite powders were also examined by XRD to investigate whether they were suffered from phase change during the process or not.