• Composites Research
• /
• 제31권5호
• /
• pp.202-208
• /
• 2018

In this paper, mechanical and hygroscopic properties of teak sawdust and recycled polypropylene (RPP) composites are evaluated and compared with virgin polypropylene (VPP) matrix based composites. Verities of composites are prepared by variation in the plastic types, wood plastic ratio and the addition of coupling agent in the formulations. Mixing of wood sawdust and polypropylene is done by a twin screw extruder, and then sheets of wood plastic composites (WPCs) are produced by using the compression molding method. The results show that recycled matrix composites exhibit better tensile, flexural strength with low impact strength than virgin matrix based composites. Recycled composites show low water absorption and thickness of swelling than virgin matrix based composites. The results confirm that wood content in the polymer matrix affects the performance of composites while presence maleated polypropylene (MAPP) improves the properties of the composites significantly. Developed RPP matrix composites are as useful as VPP matrix composites and have the potential to replace the wood and plastics products without any adverse effect of the plastics on the environment.

• Journal of the Korean Wood Science and Technology
• /
• 제33권2호통권130호
• /
• pp.40-55
• /
• 2005

This study was carried out to discuss the feasibility of wood and plastic wastes as the raw materials for wood particle-plastic composites. For this purpose, composites were manufactured from coarse and fine wood particles and polypropylene fibers by nonwoven web process. And the effect of wood particle size on the performance of the composites were analyzed according to ASTM D 1037-93. In the physical properties of composites, water absorption decreased with the increase of target density and polypropylene fiber content. And the composites with fine wood particles appeared to have slightly lower water absorption than those with coarse wood particles. Thickness swelling did not vary significantly with the increase of target density but increased with the increase of wood particle content. And the composites with fine wood particles were significantly lower in thickness swelling than those with coarse wood particles. In the mechanical properties of composites, dry and wet MOR showed the increasing tendency with the increase of polypropylene fiber content and target density. Dry and wet MOE showed the increasing tendency with the increase of target density but only wet MOE exhibited the increasing tendency with the increase of polypropylene fiber content. Composites with fine wood particles appeared to be generally higher in wet MOR and MOE than those with coarse wood particles. In conclusion, composites with fine wood particles showed generally higher performance than those with coarse ones. Also, composites were significantly superior to control particleboards in the performance, especially in water absorption and thickness swelling.

• Journal of the Korean Wood Science and Technology
• /
• 제42권5호
• /
• pp.499-509
• /
• 2014

Wood filler is a porous and anisotropic material having different size, shape, and aspect ratio. The use of wood fillers such as wood particle, wood flour, and wood pulp in wood plastic composites (WPCs) are growing rapidly because these wood fillers give improved strength and stiffness to WPCs. However, the wood fillers have originally poor compatibility with plastic matrix affecting the mechanical properties of WPCs. Therefore, to improve compatibility between wood and plastic, numbers of physical and chemical treatments were investigated. While the various treatments led to improved performances in WPC industries using petroleum-based plastics, full biodegradation is still issues due to increased environmental concerns. Hence, bio-based plastics such as polylactide and polyhydroxybutyrate having biodegradable characteristics are being applied to WPCs, but relatively expensive prices of existing bio-based plastics prevent further uses. As conventional processing methods, extrusion, injection, and compression moldings have been used in WPC industries, but to apply WPCs to engineered or structural places, new processing methods should be developed. As one system, co-extrusion technique was introduced to WPCs and the co-extruded WPCs having core-shell structures make the extended applications of WPCs possible.

• 한국가구학회지
• /
• 제27권4호
• /
• pp.392-398
• /
• 2016

Wood-plastic composites (WPCs) composed of mainly wood flour and thermoplastics have attracted considerable attentions due to advantages of cost effectiveness, high durability, and microbial resistance. However, relatively poor fire resistance of WPCs from low thermal stability of wood and plastics prevents further uses. This study investigated the effect of expandable graphite (EG) and aluminium hydroxide (AH)/magnesium hydroxide (MH) on the properties of WPCs. The combined incorporation of both EG and metal hydroxide (i.e., AH or MH) into formulations leads to higher flexural modulus of filled composites compared to neat PP and WPC. In thermal properties, EG played an important role in improving thermal stability of filled composites by suppressing thermal decompositions of wood and PP. Moreover, EG showed better water absorption features. From this research, it can be said that EG and metal hydroxides have potentials as effective reinforcement, flame retardant, and moisture barrier.

• 한국화재소방학회논문지
• /
• 제24권6호
• /
• pp.120-125
• /
• 2010

주거 건축 및 가구산업의 자재로써 합성목재(Wood-Plastic Composites)는 점차 각광받고 있다. 본 연구에서는 합성목재의 연소특성을 살펴보기 위하여 한계산소지수 측정(ASTM D 2863) 및 콘칼로리미터 시험(ISO 5660-1)을 실시하였으며 또한 일반목재인 적송과 방부 처리를 한 방부목에 대하여도 동일한 시험을 통하여 합성목재와의 연소특성을 비교.검토하였다. 한계산소지수 측정결과 합성목재가 적송 및 방부목에 비해 낮게 측정되었다. 콘칼로리미터 시험결과 합성목재의 열방출률이 가장 높았고 또한, 최대 열방출률 및 평균 열방출률, 총 방출열량도 적송 및 방부목에 비해 높게 나타났다.

• Journal of the Korean Wood Science and Technology
• /
• 제34권5호
• /
• pp.79-87
• /
• 2006

Value-added utilization of the disposed ash trees due to the infestation by Emerald Ash Borer (EAB) was explored by converting them into particleboards (PBs) and wood-plastic composites (WPCs). The experimental result showed that PB panels could be successfully manufactured from the ash wood but compaction ratio need to be higher than 1.3 in order to meet the standard requirements listed by American National Standards Institute (ANSI). Ash wood plastic composites with high density polyethylene (HDPE) and polypropylene (PP) were also prepared with additives by extrusion. Physical and mechanical properties of ash wood plastic composite compared favorably to those made of pine and maple.

• 한국안전학회지
• /
• 제27권1호
• /
• pp.26-31
• /
• 2012

Wood-plastic composites represents a growing class of materials used by the residential construction industry and furniture industry. In this study, the effect of flame retardants on the flammability and mechanical properties of wood flour-high density polyethylene(HDPE) composites were studied. we were manufactured wood flour-HDPE composites by modular intermeshing co-rotating twin screw extruder with L/D ratio of 42. The flame retardant properties were used limiting oxygen index(LOI) and mechanical properties were measured by universal testing machine(UTM). The Morphological analysis of composites were analyzed by Scanning electron microscope(SEM). It was found that Ammonium polyphosphate can effectively reduce the flammability of the wood flour-HDPE composites. Marginal reduction in the mechanical properties of the composites was found with addition of flame retardants. SEM images showed that the coupling agent improved wood flour-HDPE interfacial bonding.

• 접착 및 계면
• /
• 제3권4호
• /
• pp.1-9
• /
• 2002

본 연구의 목적은 목분과 폴리프로필렌으로 제조한 목질-고분자 복합재료의 점탄성적 성질에 미치는 결합제, 기핵제의 영향에 대해 고찰하는데 있으며, 목분과 결합제간의 esterification 반응이 목질-고분자 복합재의 기계적 성질에 미치는 영향 또는 고찰하고자 한다. 복합재는 목분 60%와 폴리프로필렌 40%를 혼합하여 제조하였으며, DMTA (Dynamic mechanical thermal analysis)를 사용하여 damping peaks (than ${\delta}$), storage modulus (E'), loss modulus (E")를 측정하였다. 또한 XPS (X-ray Photolectron Spectroscopy)를 사용하여 목분에 MAPP를 처리하기 전과 후의 상태를 고찰하였다. DMA 시험은 온도범위 $-20{\sim}100^{\circ}C$에서 여러가지 주파수 (1, 5, 10, 25 HZ) 조건과, 승온속도 $5^{\circ}C/min$으로 실시하였다. 이 시험결과를 토대로 복합재의 활성화에너지를 구하여 결합제와 기핵제가 목분과 고분자물질간 계면의 성질에 미치는 영향을 고찰하였다.

• Journal of the Korean Wood Science and Technology
• /
• 제21권2호
• /
• pp.31-37
• /
• 1993

Composites of styrene polymers with woody fibers were prepared, and the effect of compatibilizers on their mechanical properties was evaluated. To improve the compatibility of wood fibers and the matrix polymers, styrene-maleic anhydride copolymer(SMA) and maleic anhydride-modified polymers were used as compatibilizers. As results, maleic anhydride-modified polystyrene and SMA were proved to improve the tensile strength of the molded composites, and also were evaluated as good compatibilizers for the wood fiber polystyrene composite. Cellulosic fiber (dissolving pulp) provided better reinforcement than lignocellulosic fiber(thermomechanical pulp). On the contrary in the case of the composite of wood fiber and acrylonitrile-butadiene styrene copolymer(ABS), SMA and maleic anhydride-modified acrylonitrile-butadiene-styrene copolymer(MABS) did not act as compatibilizers. However, MABS was evaluated as a good polymer matrix to make wood fiber reinforced composite. The tensile properties of the composites of wood fiber and MABS were superior than those of wood fiber-ABS composites.

• 한국가구학회지
• /
• 제27권2호
• /
• pp.137-144
• /
• 2016

Wood plastic composite (WPC) is a green composite made of wood flour and thermoplastics to provide better performance by removing the defects of both wood and plastics. However, relatively low thermal stability and poor fire resistance of wood and plastics included in WPC have been still issues in using WPC as a building material for interior applications. This study investigated the effect of environmentally-friendly flame retardants (EFFRs) on the mechanical, thermal, morphological, and water absorption properties of wood flour (WF)/talc/polypropylene (PP) composites in comparison with neat PP. The whole EFFRs-filled WF/talc/PP composites showed higher values in flexural strength, flexural modulus, and impact strength compared to neat PP. In thermal properties, aluminum hydroxide (AH)-filled composite showed a $36^{\circ}C$ reduction in maximum thermal decomposition temperature ($T_{max}$) compared to neat PP, but magnesium hydroxide (MH) played an important role in improving thermal stability of filled composite by showing the highest $T_{max}$. From this research, it can be said that MH has potentials in reinforcing PP-based WPCs with improvement of thermal stability.