• Journal of the Korea institute for structural maintenance and inspection
• /
• v.22 no.2
• /
• pp.68-75
• /
• 2018

In this study, to solve the problems of the conventional crack repair and injection method, high elasticity latex was used as the material of the storage tube to withstand the high pressure in the center part differently from the general port. When the repair solution was injected into the crack part, The TPS method was developed so that the air existing in the TPS can be discharged. In addition, a new infusion port in which a valve blocking the backflow of the remediation solution was installed at the injection port was developed and the physical characteristics of the port were analyzed. As a result of the evaluation, it was found that the filling rate of the remedial solution was improved compared to the existing ordinary injector method, and the cracks were completely filled in the test conditions. Compressive strength and tensile strength after repair showed about 20% decrease after repair in case of using ordinary injector method, while TPS method showed about 2~7% increase after repair. The results of this study showed that the injection port method using the elastic storage tube increased the injection performance and the quality after repair compared to the conventional injector method. The result of this study is expected to be utilized as the basic data for application and commercialization of the result to the practical structure.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.18 no.4
• /
• pp.504-510
• /
• 2017

This paper presents an AC-DC power module design and evaluates its efficiency and reliability when used for electronics appliances. This power module consists of a PWM control IC, power MOSFETs, a transformer and several passive devices. The module was tested at an input voltage of 220V (RMS) (frequency 60 Hz). A test was conducted in order to evaluate the operation and power efficiency of the module, as well as the reliability of its protection functions, such as its over-current protection (OVP), overvoltage protection (OVP) and electromagnetic interference (EMI) properties. Especially, we evaluated the thermal shut-down protection (TSP) function in order to assure the operation of the module under high temperature conditions. The efficiency and reliability measurement results showed that at an output voltage of 5 V, the module had a ripple voltage of 200 mV, power efficiency of 73 % and maximum temperature of $80^{\circ}C$ and it had the ability to withstand a stimulus of high input voltage of 4.2 kV during 60 seconds.

• Korean Journal of Plant Resources
• /
• v.14 no.3
• /
• pp.251-258
• /
• 2001

Predehydration effects for cryopreservation in -196$^{\circ}C$ liquid nitrogen were studied in Korean native Aquilegia buergeriana var. oxysepala Kitamura and A. flabellata var. pumila Kudo seeds. Aquilegia species seeds were adjusted to moisture contents between 3.2 and 9.7% by air dry treatments. Seeds were placed in paper envelopes after submerged in liquid nitrogen and rewarming in 38 $^{\circ}C$ water. Seeds moisture contents by duration of drying were identified as controlling factors in the survival of Aquilegia species seeds for cryopreservation. Aquilegia species seeds having approximate 5% moisture content were able to withstand cooling to -l96$^{\circ}C$. Undehydrated seeds of Aquilegia buergeriana var. oxysepala Kitamura after being cryopreservated in liquid nitrogen have a 10.9% of moisture content and show 52.5% in germination. But, Aquilegia buergeriana var. oxysepala Kitamura seeds dehydrated by drying for 60 min. to have 6.0% of moisture content before cryopreservation show 84.7% in germination test. Properly dehydrated seeds after being stored in liquid nitrogen showed over 60% in germination rate and also shows an uniform sprouting time,11~13 days in average. Any morphologically deformity in germinating beds has not been observed. Results from this study suggest that Aquilegia species seeds can cryopreservation in liquid nitrogen if the seed moisture content is controled by a proper amount of dehydration.

• The Journal of Korean Academy of Prosthodontics
• /
• v.55 no.2
• /
• pp.144-150
• /
• 2017

Purpose: The aim of this in vitro study is to investigate load bearing capacity of esthetic abutments according to the type of material and wall thickness. Materials and methods: 70 specimens equally divided into seven groups according to their abutment wall thicknesses. The abutments prepared with titanium 0.5 mm wall thickness were used as a control group (Ti-0.5), whereas zirconia abutments and resin nano ceramic abutments with wall thickness 0.5 mm, 0.8 mm and 1.0 mm were prepared as test groups (Zir-0.5, Zir-0.8, Zir-1.0 and RNC-0.5, RNC-0.8, RNC-1.0). All specimens were tested in a universal testing machine to evaluate their resistance to fracture and all of them underwent thermo-cycling before loading test. Mean fracture values of the groups were measured and statistical analyses were made using two-way ANOVA. Results: Zir-1.0 showed the highest mean strength ($2,476.3{\pm}342.0N$) and Zir-0.8 ($1,518{\pm}347.9N$), Ti-0.5 ($1,041.8{\pm}237.2N$), Zir-0.5 ($631.4{\pm}149.0N$) were followed. The strengths of RNC groups were significantly lower compared to other two materials (RNC-1.0 $427.5{\pm}72.1$, RNC-0.8 $297.9{\pm}41.2$) and the strengths of all the test groups decreased as the thickness decreases (P < .01). RNC-0.5 ($127.4{\pm}35.3N$) abutments were weaker than all other groups (P < .05). Conclusion: All tested zirconia abutments have the potential to withstand the physiologic occlusal forces in anterior and posterior regions. In resin nano ceramic abutments, wall thickness more than 0.8 mm showed the possibility of withstanding the occlusal forces in anterior region.

• The Journal of Korean Academy of Prosthodontics
• /
• v.60 no.2
• /
• pp.135-142
• /
• 2022

Purpose. This study aims to evaluate the combined effect of reduced thickness in different regions on the fracture resistance of monolithic zirconia crowns. Materials and methods. Seven nickel-chromium dies were generated from a 3D model of mandibular first molar using the digital scanner with the following geometries: 1.5 mm occlusal reduction, 1.0 mm deep chamfer. Based on the abutment model, Zirconia blocks (Luxen Zirconia) were selected to fabricate Sixty-three zirconia crowns with occlusal thicknesses of 0.3 mm, 0.5 mm, and 1.5 mm, and different axial thicknesses of 0.3 mm, 0.5 mm, and 1.0 mm. All crowns were cemented by resin cement. Next, the crowns were subjected to load-to-fracture test until fracture using an electronic universal testing machine. In addition, fracture patterns were observed with a scanning electron microscope (SEM). Two-way ANOVA and the Tuckey HSD test for post hoc analysis were used for statistical analysis (P < .05). Results. The mean values of fracture resistancerecorded was higher than the average biting force in the posterior region. The two-way ANOVA showed that the occlusal and axial thickness affected the fracture resistance significantly (P < .05). However, the effect of axial thickness on fracture resistance did not show a statistical difference when thicker than 0.5 mm. The observed failure modes were partial or complete fracture depending on the severity of crack propagation. Conclusion. Within the limitations of the present study, the CAD-CAM monolithic zirconia crown with extremely reduced thickness showed adequate fracture resistance to withstand occlusal load in molar regions. In addition, both occlusal and axial thickness affected the fracture resistance of the zirconia crown and showed different results as combined.

• Research in Community and Public Health Nursing
• /
• v.7 no.2
• /
• pp.420-436
• /
• 1996

The goal of this study is to explore different risk factors for smoking and look at the relationships between knowledge, attitudes, and behavioral intentions regarding smoking among schoolchildren, in order to reduce teenage smoking. To achieve this goal a self-administered questionaire regarding smoking was provided to schoolchildren in the 7th and 8th grades in one junior high school in Jerusalem. The schoolchildren were exposed to 10-12 hours of a smoking prevention intervention program. The questionaire focused primarily on the personal characteristics, social environment, knowledge, attitudes, practices, and behavioral intentions of the children. Crosstabs were performed on each variable to determine if significant associations exist among the different variables. The statistical computer, package, SPSS PC, was used to manipulate the data along with Chi-square test. The findings were as follows : About 11% of the children aged 12-14 have ever smoked or are smoking currently, and about 24.0% of those who ever smoked started smoking at the age of 10. Boys smoke more(p<.01), poorer students(by self-perception of school performance) smoke more, and those who had peers who were smokers were more likely to smoke(p<.05). The percentage of the children who reported that either father or mother smoked was about 30%, but no statistical association was found between parental smoking and children's smoking, although trends were noted in the expected direction, i.e. more smokers among children of smokers. Only 1.1% of the children intended to smoke in the future, and 98.0% of the children indicated that they can or they might be able to withstand social pressure. Seventy percent of the children demonstrated medium to high knowledge about smoking, Males, 8th graders, better students, and those without friends who smoke had higher social pressure showed more negative attitudes(p<.01). Those with non-smoking siblings showed more negative behavioral intentions regarding smoking(p<.01), and better students showed more negative behavioral intentions. Those who had higher knowledge scores showed more negative attitudes towards smoking, but not significantly so. Those who had very negative behavioral intentions showed highly significant negative attitudes towards smoking(p<.01).