The xAl-yCe oxide catalysts with different mol ratios of Al/(Al+Ce) were prepared by a co-precipitation method and Pt supported on xAl-yCe oxide catalysts were synthesized by an incipient wetness impregnation method. The catalysts were characterized by X-ray Diffraction (XRD), $N_2$ sorption, and $H_2$/CO-temperature programmed reduction ($H_2$/CO-TPR) to correlate with catalytic activities in co oxidation. Among the catalysts studied here, Pt/1Al-9Ce oxide catalyst showed the highest activity in dry and wet reaction conditions and the catalytic activity showed a typical volcano-shape curve with respect to Al/(Al+Ce) mol ratio. When the presence of 5% water vapor in the feed, the temperature of $T_{50%}$ was shifted ca. $30^{\circ}C$ to lower temperature region than that in dry condition. From CO-TPR, the desorption peak of $CO_2$ on Pt/1Al-9Ce oxide catalyst showed the highest value and well correlated the catalytic performance. It indicates that the Pt/1Al-9Ce oxide catalyst has a large amount of active sites which can be adsorbed by co and easy to supplies the needed oxygen. In addition, the amount of pentacoordinated $Al^{3+}$ sites obtained through $^{27}Al$ NMR analysis is well correlated the catalytic performance.

• Korean Chemical Engineering Research
• /
• v.46 no.4
• /
• pp.806-812
• /
• 2008

The ammonia decomposition reaction has been of increasing interest as a means of treating ammonia in flue gas in the presence of precious metal catalyst. Various catalysts, $Pt-Rh/Al_2O_3$, $Pt-Rh/TiO_2$, $Pt-Rh/ZrO_2$, $Pt-Pd/Al_2O_3$, $Pd-Rh/Al_2O_3$, $Pd-Rh/TiO_2$, $Pd-Rh/ZrO_2$, $Pt-Pd-Rh/Al_2O_3$, $Pd/Ga-Al_2O_3$, $Rh/Ga-Al_2O_3$, and Ru/Ga-$Al_2O_3$, were synthesized by using excess wet impregnation method. Using a homemade 1/4" reactor at $10,000{\sim}50,000hr^{-1}$ of space velocity in the presence of precious metal catalyst ammonia decomposition reactions were carried out to investigate the catalyst activity. The inlet ammonia concentration was maintained at 2,000 ppm, with an air balance. Both $T_{50}$ and $T_{90}$, defined as the temperatures where 50% and 90% of ammonia, respectively, are converted, decreased significantly when alumina-supported catalysts were applied. In terms of catalytic performance on the ammonia conversion in the presence of hydrogen sulfide, $Pt-Rh/Al_2O_3$ catalyst showed no effect on the poisoning caused by hydrogen sulfide. These results indicate that platinum-rhodium bimetallic catalyst is a useful catalyst for ammonia decomposition.

• Clean Technology
• /
• v.26 no.4
• /
• pp.286-292
• /
• 2020

This study confirmed the effect of the Cu/CeO2-X catalyst on the CO oxidation activity at low temperature through the catalyst's structure and reaction characteristics. The catalyst was prepared by the wet impregnation method. Cu/CeO2_X catalysts were manufactured by loading Cu (active metal) using CeO2 (support) formed at different calcination temperatures (300-600 ℃). Manufactured Cu/CeO2_X catalysts were evaluated for the low-temperature activity of carbon monoxide. The Cu/CeO2_300 catalyst showed an activity of 90% at 125 ℃, but the activity gradually decreased as the calcination temperature of the CeO2-X and Cu/CeO2_600 catalysts showed an activity of 65% at 125 ℃. Raman, XRD, H2-TPR, and XPS analysis confirmed the physicochemical properties of the catalysts. Based on the XPS analysis, the lower the calcination temperature of the CeO2 was, the higher the unstable Ce3+ species (non-stoichiometric species) ratio became. The increased Ce3+ species formed a solid solution bond between Cu and CeO2-X, and it was confirmed by the change of the CeO2 peak in Raman analysis and the reduction peak of the solid solution structure in H2-TPR analysis. According to the result, the formation of the solid solution bond between Cu and Ce has been enhanced by the redox properties of the catalysts and by CO oxidation activity at low temperatures.