• 한국원자력학회:학술대회논문집
• /
• 한국원자력학회 2004년도 요약집 춘계학술발표대회
• /
• pp.330-330
• /
• 2004

• 대한용접접합학회:학술대회논문집
• /
• 대한용접접합학회 2001년도 춘계학술발표대회 개요집
• /
• pp.198-200
• /
• 2001

• 대한용접접합학회:학술대회논문집
• /
• 대한용접접합학회 1996년도 특별강연 및 추계학술발표 개요집
• /
• pp.156-159
• /
• 1996

• Journal of Welding and Joining
• /
• 제26권4호
• /
• pp.41-43
• /
• 2008

• Journal of Welding and Joining
• /
• 제33권2호
• /
• pp.18-22
• /
• 2015

The importance of emotional quality of car is getting higher in these days. Noise takes great portion in emotional quality because it is detectable problem with just a few rides. The sources of car noise during operation are various and the related technical issues are vast. Sometimes weldments of auto body are referred as the source of noise and the suspicious weldment shows unsatisfactory welding quality in most cases. In this research, cases of noise making weldments are investigated to figure out the solution for welding quality improvement. They are categorized into several groups in according to the inferred types of the error source then appropriate solutions are suggested. Auto body has weldments of resistance spot welding and gas metal arc welding in general. Therefore the solutions are suggested as adjustment of welding process variables and related machineries. Inevitable error source is also referred which is originated from thermal expansion rate difference between ultra high strength steel and mild steel. This new approach is validated through simple calculation then more concrete investigation with numerical analysis is remained as further works to be done.

• Journal of Welding and Joining
• /
• 제19권1호
• /
• pp.58-64
• /
• 2001

The initiation and propagation lives of fatigue crack were studied for spot weldments composed of cold rolled steel plates(SPC$\times$SPC) and galvanized steel plates(GA$\times$GA) using DC potential drop method(DCPDM). Through the various test results, it was known that the fatigue crack initiation and propagation behaviors in all specimens could be definitely detected by DCPDM. The fatigue crack initiation life( $N_{i}$) detected by DCPDM in SPC$\times$SPC and GA$\times$GA spot weldments increased as the welding current and the nugget diameter( $N_{d}$) increased. The fatigue crack propagation life($\Delta$ $N_{f-i}$) declined as the difference of $N_{i}$ and the fatigue fracture life( $N_{f}$) also increased according to the decrease of fatigue load, $\Delta$P and the increase of nugget diameter. In the same spot weldments, the increase of nugget diameter came to increase fatigue crack propagation life owing to a decrease of stress concentration in front of nugget, especially the increasing extent for GA$\times$GA spot weldment was very high. In the welding current 6kA, $N_{f}$ for GA$\times$GA spot weldment decreased more than that of SPC$\times$SPC specimen due to zinc layer coated in steel plate and undersized nugget diameter. On the other hand, in 8kA and 10kA, the GA$\times$GA spot weldment showed higher $N_{f}$ in spite of lower $N_{i}$, than that of SPC$\times$SPC specimen except 3,000N fatigue load.ue load. load.d.

• 한국산학기술학회논문지
• /
• 제12권12호
• /
• pp.5405-5411
• /
• 2011

본 연구에서는 교량용 구조용 강재인 HSB600 강의 용접부에서 입열량 (1.5~3.6 kJ/mm)과 용접후 열처리(PWHT, $600^{\circ}C$, 40hr.)가 미세조직과 기계적 특성에 미치는 영향에 관해 연구하였다. HSB600 강재를 GMA용접을 실시하였다. 용접된 상태에서는 인장강도와 경도는 입열량이 증가할수록 저하되었으며 충격 흡수 에너지는 큰 차이를 보이지 않았다. 낮은 입열량인 1.5 kJ/mm에서 침상형 페라이트가 가장 많이 생성되었다. 용접후 열처리를 통해 경도와 인장강도가 저하되었고, 용착금속의 충격흡수에너지가 증가되었다.

• 대한기계학회:학술대회논문집
• /
• 대한기계학회 2005년도 창립60주년 기념 추계 학술대회
• /
• pp.120.1-120.1
• /
• 2005

• 비파괴검사학회지
• /
• 제1권1호
• /
• pp.22-31
• /
• 1981

• Journal of Welding and Joining
• /
• 제20권2호
• /
• pp.42-49
• /
• 2002