• Journal of Welding and Joining
• /
• 제33권4호
• /
• pp.30-36
• /
• 2015

Austenite stainless steel(SA213-TP347H) has widely been used for the superheater & reheater tube in USC(ultra-supercritica) coal boiler because of its high creep rupture strength and anti-oxidation. But recently, the short-term failures have happened frequently in heat affected zone for only 4,000~15,000hours of service. Many investigations have been conducted to understand the failure mechanism. The root cause of failure was comfirmed to "strain induce participation hardening crack" or "reheat cracking". This mechanism often occurred due to weld residual stress and precipitation of the Cr, Nb carbides in the stabilized stainless steel such as TP347H. This paper presents an analysis of failure tube and effect of the sample tubes that conducting stabilizing heat treatment in site after 11,380hours & 16,961hours of service. Visual inspection was performed. In addition, microscopic characteristics was identified by O.M, SEM, and hardness test was carried out to find out the heat treatment effects. Failures seem to happen because of being not conducted stabilizing heat treatment in site. And another cause is inadequate weld parameter such as pass, ampere, voltage, inter-pass temperature. Thus, this paper has the purpose to describe that how to prevent similar failures in those weld-joints.

• 한국산학기술학회논문지
• /
• 제11권9호
• /
• pp.3155-3160
• /
• 2010

최근 자동차 산업은 고효율 자동차의 개발에 박차를 가하고 있으며 이에 따라 차체 경량화 및 내식성 방지를 위한 고강도강 및 도금강의 사용이 증가하고 있다. 이에 따라 본 연구에서는 자동차 차체에 쓰이는 3종의 다른 강판에 대하여, 겹침 순서에 따른 용접 특성을 시뮬레이션 기법을 이용하여 분석하였다. 자동차 차체에 많이 사용되는 EDDQ 급의 도금강판 0.7t와 인장강도 440 MPa급의 440R 1.2t, 그리고 AHSS (Advanced High Strength Steel)인 DP 590 0.2t 판재에 대하여 겹치기 순서에 따른 용접 특성을 시뮬레이션 하였고, 너겟 성장 곡선 및 전류에 따른 너겟의 크기로 그 용접성을 분석하였다. 또한 용접 시 발생되는 각 접촉부의 접촉저항을 이용하여 겹침순서에 따른 너겟의 크기를 분석하였으며, 이를 통해 최적의 겹치기 순서를 제안할 수 있었다.

• Journal of Welding and Joining
• /
• 제15권1호
• /
• pp.101-108
• /
• 1997

손상된 터어빈 로터강의 보수 용접에 있어서 용접부의 크립 파단 수명과 탄화물간의 관계가 연구되었다. 탄화물은 탄화물 추출 복제법을 이용하여 확인되었으며 로터강에는 Molybdenum 주성분의$M_2C$, Vanadium 주성분의 $M_4C_3$, 및 Chromium 주성분의 $M_{23}C_6$와 $M_7C_3$ 탄화물이 존재하였다. 한편 ICHAZ에서 파단된 시험편의 파단면에서는 구상의 조대한 Molybdenum 주성분의 $M_6C$ 탄화물이 발견되었다. 조대한 Molybdenum 주성분의 $M_6C$ 탄화물의 석출은 탄화물 주위에 고용경화 원소인 Molybdenum 농도를 떨어뜨려 기공 발생 원인을 제공하였다. CGHAZ에서 파단된 용접부의 파단면에서는 조대한 $M_6C$ 와 $M_{23}C_6$가 발견되었다.

• 대한토목학회논문집
• /
• 제4권3호
• /
• pp.19-25
• /
• 1984

용접구조에 있어서 가장 위험한 단면은 용접부이며 대부분의 파괴가 용접부로부터 발생하였다. 따라서 용접부의 파괴거동을 확인하는 것은 파괴방지를 위하여 중요한 요소라 할 수 있다. 본 연구는 용접부의 파괴거동에 관한 기초적인 연구로서 용접부의 국부적인 인성분포와 다층용접의 효과 및 잔류응력제거풀림의 효과를 조사하였다. 연구에 사용된 기본소재로서는 피로이력을 갖고 있는 강재와 피로이력이 없는 강재를 선택하였다. 용접부에서 미사용강재(피로이력이 없는 강재)모재, 열영향부 용착금속의 파괴인성이 각각 차이가 있었고 용착금속은 균열저지능력으로서 파괴인성이 가장 작아서 파괴발생원이 될수 있음을 확인하였다. 특히 본연구의 대상강재인 기사용강재(피로이력을 갖고 있는 강재)는 파괴인성이 용착금속 보다 작아서 균열이 존재하는 경우 가장 취약한 단면이 될수 있다는 것을 확인하였다. 다충용접은 용접부에 결합이 존재하지 않는다면 안정개선에 효과가 있음을 확인하였고 또한 잔류응력제거 풀림은 본연구에 관한 한은 효과가 없는 것으로 밝혀졌다.

• Journal of Welding and Joining
• /
• 제6권2호
• /
• pp.30-39
• /
• 1988

Generally, as the welded region of weld structures has the incomplete bead and welded deposit which are able to behave like the surface cracks occasinally, there is a high possibility that the fatigue fracture of the weld structures is due to the surface cracks on the wlded region. This study was done to investigate the effects of post weld heat treatment (PWHT) on the fatigue behaviors of the surface crack of the heat affected zone (HAZ) for the multi-pass welds under the repetitive pure bending moment. The obtained results are summarized as follows : 1. The crack grows to the depth direction initially as the number of cylces increase, the amount of crack length is increased for the surface dir3ction and cive versa for the depth direction. 2. The fatigue life is increased in a order of as weld, PWHT specimens and parent. 3. As the number of cycles increase, the crack length is increased to th surface direction. The increase of the depth length is blunted at the center of specimen thickness. 4. The fatigue crack growth of PWHT specimens to the surface direction is dependent upon the holding time and applied stress during PWHT. In order words, the crack growth rate decreases with the holding time and increases with the applied stress during PWHT. 5. As the crack grows, the aspect formed in the course of crack propagation approaches to semicircle for parent and ellipse with the largest semidiameter for PWHT ($1/4hr, 15kgf/mm^2$) 6. At depth direction, it is difficult to apply to the paris' equation because of the scattered data between the crack growth rate and the stress intensity factor range.

• Journal of Welding and Joining
• /
• 제32권2호
• /
• pp.48-53
• /
• 2014

This study was carried out to investigate the effect of postweld heat treatment(PWHT, 930, 1080, $1230^{\circ}C$) on the microstructure, phase formation, pitting corrosion and mechanical properties such as hardness, tensile strength and impact values of super duplex stainless steel(UNS S32750) multipass welds. Based on the microstructural examination and X-ray diffraction analysis, it was found that the ${\sigma}$ phase was formed in the welds heat treated at $930^{\circ}C$ in which the ferrite content greatly decreased into 5~10% in the welds. The secondary austenite was formed in the reheated zone of welds and redissolved into ferrite with increasing heat treatment temperatures. The tensile strength and impact values of welds heat treated at $930^{\circ}C$ were the lowest and revealed the brittle fracture surface. The weight loss by pitting corrosion increased with test temperatures. It was confirmed that pitting corrosion occurred mainly in secondary austenite of reheated zones. The postweld heat treatment temperature is recommended to be in the range of $1050{\sim}1150^{\circ}C$.

• 한국해양공학회지
• /
• 제26권5호
• /
• pp.73-80
• /
• 2012

It is well known that a considerable amount of scatter is shown in experimental results relating to fatigue crack growth even under identical and constant amplitude cyclic loading conditions. Moreover, flux cored arc welding (FCAW) is a common method used to join thick plates such as the structural members of large scale offshore structures and very large container ships. The objective of this study was to investigate the macro- and microscopic observations of the fatigue crack growth (FCG) behavior of the FCAWed API 2W Gr. 50 steel joints typically applied for offshore structures. In order to clearly understand the randomness of the fatigue crack growth behavior in the materials of three different zones, the weld metal (WM), heat affected zone (HAZ), and base metal (BM), experimental fatigue crack growth tests for each of five specimens were performed on ASTM standard compact tension (CT) specimens under constant amplitude cyclic loading. Special focus was placed on the fatigued fracture surfaces. As a result, a different behavior was observed at the macro-level, depending on the type of material property: BM, HAZ, or WM. The variability in the fatigue crack growth rate for WM was higher than that of BM and HAZ.

• Journal of Welding and Joining
• /
• 제1권2호
• /
• pp.45-52
• /
• 1983

Many pressure vessels for the hot H$\sub$2//H$\sub$2/S service are made of 2+1/4Cr-1Mo steel with austenitic stainless steel overlay to combat agressive corrosion due to hydrogen sulfide. Hydrogen dissolves in to materials during operation, and sometimes gives rise to unfore-seeable damages. Appropriate precautions must, therefore, be taken to avoid the hydrogen induced damages in the design, fabrication and operation stage of such reactor vessels. Recently, hydrogeninduced cracking (or Disbonding) was found at the interface between base metal and stainless weld overlay of a desulfurizing reactor. Since the stainless steel overlay weld metal is subjected to thermal and internal-pressure loads in reactor operation, it is desirable for the overlay weld metal to have high strength and ductility from the stand point of structural safety. In section III of ASME Boiler and Pressure Vessel Code, Post-Weld Heat Treatment(PWHT) of more than one hour per inch at over 1100.deg. F(593.deg. C) is required for the weld joints of low alloy pressure vessel steels. This heat treatment to relieve stresses in the welded joint during construction of the pressure vessel is considered to cause sensitization of the overlay weld metal. The present study was carried out to make clear the diffusion of carbon migration by PWHT in dissimilar metal welded joint. The main conclusion reached from this study are as follows: 1) The theoretical analysis for diffusion of carbon in stainless steel overlay weld metal does not agree with Fick's 2nd law but the general law of molecular diffusion phenomenon by thermodynamic chemical potential. 2) In the stainless steel overlay welded joint, the PWHT at 720.deg. C for 10 hours causes a diffusion of carbon atoms from ferritic steel into austenitic steel according to the theoretical analysis for carbon migration and its experiment. 3) In case of PWHT at 720.deg. C for 10 hours, the micro-hardness of stainless steel weld metal in bonded zone increase very highly in the carburized layer with remarkable hardening than that of weld metal.

• 대한용접접합학회:학술대회논문집
• /
• 대한용접접합학회 2009년 추계학술발표대회
• /
• pp.95-95
• /
• 2009

Zinc coatings provide the most effective and economical way of protecting steel against corrosion. There are three types of galvanizing lines typically used in production line in galvanizing industries,Galvanize (GI) coating (Zn-0.1-0.3%Al), Galfan coating (Zn-5%Al), Galvalume(GL) coating (45%Zn-Al). In continuous Galvanizing lines, the immersed bath hardware (e.g. bearings, sink, stabilizer, and corrector rolls, and also support roll arms and snout tip) are subjected to corrosion and wear failure. Understanding the reaction of these materials with the molten Zn alloy is becomes scientific and commercial interest. To investigate the reaction with molten Zn alloys, static immersion test performed for 4, 8, 16, and 24 Hr. Two different baths used for the static immersion, which are molten Zn and molten Zn-55%Al. Microstructures characterization of each of the materials and intermetallic layer formed in the reaction zone was performed using optical microscope, SEM and EDS. The thickness of the reaction layer is examined using image analysis to determine the kinetics of the reaction. The phase dominated by two distinct phase which are eutectic carbide and matrix. The morphology of the intermetallic phase formed by molten Zn is discrete phase showing high dissolution of the material, and the intermetallic phase formed by Zn-55wt%Al is continuous. Aluminum reacts readily with the materials compare to Zinc, forming iron aluminide intermetallic layer ($Fe_2Al_5$) at the interface and leaving zinc behind.

• 대한기계학회논문집
• /
• 제11권1호
• /
• pp.53-62
• /
• 1987

본 논문에서는 1 KW CW CO$_{2}$레이저 발생자장치를 사용하여 표면경화 처리 를 행할때 공정과 관련된 변수들이 용접부 및 표면경화층에 미치는 영향들을 이론과 실험을 통해서 규명하고, 이 결과들을 실제공정에 사용할 수 있는 기초자료로서 제시 하고자 한다. 이를 위해서 해석에 사용될 수 있는 유한요소법(Finite Element Meth- od)에 근거한 2차원 열유동 해석용 프로그램 및 데이타 처리 프로그램을 개발하고, 중 탄소강에 레이저 표면처리를 수행하여 실험 및 이론해석의 결과를 비교 검토하였다. 비교 검토하여 그 설정기준을 고찰하였다.