• Journal of Welding and Joining
• /
• v.34 no.5
• /
• pp.6-12
• /
• 2016

This study was performed bead welding of pure titanium by using fiber laser. Since titanium is very sensitive to oxidation and nitriding during welding, it is important to compose the shielding equipment compared with different material. Thus side and coaxial shield nozzle, rail and chamber type shielding equipment are widely used to protect effectively the weld during welding. Experiments were performed by changing nozzle angle and distance using side and coaxial shield nozzle. The bead colors of gold, brown, blue, purple and yellowish white were obtained by changing variables of shield nozzle, and then its weldability was investigated. As experiment result, sound and not brominated beads were formed when side nozzle angle and distance were respectively $45^{\circ}$ and 10 mm.

• Laser Solutions
• /
• v.16 no.3
• /
• pp.11-21
• /
• 2013

As parts are becoming more complex and smaller with the development of new materials, high-quality laser precision processing is getting the limelight. Laser enables quick processing and less deformation of materials. It also enables welding with diverse materials. In this study, the pole rod and tap for the secondary battery were laser-welded using cross and coaxial nozzles. The results of the comparative analysis of cross and coaxial nozzles according to the processing parameters showed that the coaxial nozzle had more sensitive welding characteristic to the nozzle position or pressure than the cross nozzle. This indicated that the processing parameters should be carefully determined for the welding with the coaxial nozzle. The pole rod and tap were welded together in a form of T joint to improve the output of the secondary battery, and the cross nozzle had a better welding characteristic than the coaxial nozzle.

• Journal of Welding and Joining
• /
• v.29 no.3
• /
• pp.58-63
• /
• 2011

Bead shape control with gas force process has been developed to overcome the concave back bead in pipe orbital welding. However, It is impossible to make a convex back bead using the existing gas nozzle, because it has high gas-consuming and low gas force. The purpose of this paper, to develop optimum shape of nozzle which to reduce the consumption of gas, maximizing the shield gas force with low cost and high productivity coincide the Green welding. In this paper venturi-type nozzle was compared with existing CP-type nozzle by TIG pulse welding in overhead position. As a result, CP-type occurs the wormholes in the overhead position, but the Venturi-type without the pore and formed a good bead appearance.

• Journal of Welding and Joining
• /
• v.29 no.3
• /
• pp.51-57
• /
• 2011

Bead shape control with gas force process has been developed to overcome the concave back bead in pipe orbital welding. However, It is impossible to make a convex back bead using the existing gas nozzle, because it has high gas-consuming and low gas force. The purpose of this paper, to develop optimum shape of nozzle which to reduce the consumption of gas, maximizing the shield gas force with low cost and high productivity coincide the Green welding. In this paper venturi-type nozzle was designed by using the Venturi meter and compared velocity, pressure, arc shape in the flat position with existing CP-nozzle. As a result, Venturi-type nozzle's maximum velocity and pressure was improved at the same flow rate. Also heat input was increased by the arc contraction in the flat position.

• Journal of Korean Society of Industrial and Systems Engineering
• /
• v.41 no.3
• /
• pp.186-193
• /
• 2018

Modern manufacturing industries is to produce both precise and robust mechanical parts without failure while they are in service. In order to prevent a part failure for its lifetime, a mechanical design for a part should be examined on a basis of mechanical simulation. A nozzle plate, being a key part in steam engines, changes flow directions of steam in a turbine used in power plant. This paper is to the design and test for part safety and durability. Currently, nozzle plates are fabricated by welding nozzles to their plates. Welding causes some defects on the used materials while they are being manufactured. Another major defect is un-even pitches between welded nozzles. Welding causes phase changes because of high melting temperature of metal. This leads to decay on the welding spots, which weakens their structural strength and then, may lead to early damages on mechanical structures. This research proposes assembly-typed nozzle plate without welding. From the beginning, nozzle and plate are designed for insertion-typed assembly. Nozzle head and foot are designed in accordance with the grooves on outer ring and inner ring of a plate to make mating surfaces. Then the nozzle plate should be proved for structural and fatigue safety before they are put in manufacturing. This research adopts commercial softwares for modeling and mechanical simulation. The test result shows that the design with smaller mating area and deeper insertion produces higher safety in terms of structure and durability. From the conclusion, this paper proposes the assembly-typed nozzle plate to replace the welding typed.

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 2012.10a
• /
• pp.131-132
• /
• 2012

• 대한공업교육학회지
• /
• v.33 no.1
• /
• pp.282-296
• /
• 2008

Present automobile robot welding use $CO_2$ inert gas as a shielding fluid. The inert gas is spreading out and consumable. This present welding mechanism interfered with the welding nozzle. After welding several places have welding defects. Therefore, to reduce the $CO_2$ inert gas and to avoid interference with the material and to increase production modified nozzle which composed of cap and tip are needed. Suggested modified nozzle assembly composed of two stages i.e. $1^{st}$ and $2^{nd}$ stage. At the second stage it has 8 holes which is 3mm of diameter around the circumference. On the base of experimental results the inert $CO_2$ gas discharge reduced to 47% and welding defects decreased also. Modified two stage welding cap can be applied to the present robot welding machine and save the prime cost.

• Journal of Welding and Joining
• /
• v.24 no.2
• /
• pp.48-56
• /
• 2006

The fatigue strength of the welds is affected by such factors as the weld geometry, microstructures, tensile properties and residual stresses caused by fabrication. It is very important to evaluate the structural integrity of the welds in nuclear power plant because the weldment undergoes the most of damage and failure mechanisms. In this study, the fatigue assessments for a reactor vessel outlet nozzle with the weldment to the piping system are performed considering the welding residual stresses as well as the effect of local brittle zone in the vicinity of the weld fusion line. The analytical approaches employed are the microstructure and mechanical properties prediction by semi-analytical method, the thermal and stress analysis including the welding residual stress analysis by finite element method, the fatigue life assessment by following the ASME Code rules. The calculated results of cumulative usage factors(CUF) are compared for cases of the elastic and elasto-plastic analysis, and with or without residual stress and local brittle zone effects, respectively. Finally, the fatigue life of reactor vessel outlet nozzle weld is slightly affected by the local brittle zone and welding residual stresses.

• Proceedings of the KWS Conference
• /
• 2009.11a
• /
• pp.25-25
• /
• 2009

종래의 위보기 자세에서 용접은 중력이 모재의 표면으로 향하고 있어 용융금속이 중력에 의해 표면방향으로 흘러내리게 되어 용접 실시가 불가능하였다. 이에 Shield Gas Force, Trailing Gas Force 그리고 Ahead Gas Force를 적절히 적용하여 Position Welding에서 중력으로 인해 Molten Metal이 처지는 문제를 극복하여 생산성 향상으로 연결할 수 있음을 선행 실험을 통해 확인하였으나 기존의 C(Convergent)형, CP(Convergent Divergent)형 및 P(Parrallel)형 가스 노즐은 용접조건에 따라 실드 가스의 소모량이 많고, 토출되는 실드가스력이 부족하여 용접시 볼록한 이면 비드 형성을 위한 용융 풀을 효과적으로 제어 할 수 없다. 따라서 본 연구에서는 동일량의 실드 가스 공급시 가스 노즐을 통해 토출되는 실드가스의 소모를 줄이고 실드가스력을 극대화하여 저가의 고생산성을 가진 친 환경 용접기술(Green welding)에 부합하는 CDP(Convergent Divergent Parrallel)형 가스 노즐을 제작하여 기존의 CP형 가스 노즐과 비교 분석하였다. 또한 Overhead Position에서의 비드형상제어와 Flat Position에서 방풍효과를 비교해 보았다. 그 결과 CDP Nozzle은 CP Nozzle보다 동일한 유량에서 풍속은 3.5배, 냉각능력은 1.5배, 가스압력은 6.25배로 우수한 성능을 확인할 수 있었고, Overhead Position에서 가스 유량을 동일하게 하여 용접하였을 때 CP Nozzle의 경우 오목한 이면비드가 나타났지만 CDP Nozzle의 경우 볼록하게 양호한 이면비드 형상이 나타났고, Flat Position에서의 방풍효과 비교실험에서 CDP Nozzle에서는 깊고 균일한 용입을 CP Nozzle에서는 불안정한 용입이 나타났는데 이는 CDP Nozzle의 경우 풍속에 의한 Arc Blow가 적게 발생하여 상대적으로 더 나은 용입을 확인하였다.

• Journal of Welding and Joining
• /
• v.29 no.2
• /
• pp.34-39
• /
• 2011

Nickel-based austenitic alloys such as Alloy 82 and 182 had been employed as the weld metals in nuclear power plants (NPPs) due to their high corrosion resistance as well as good mechanical properties. However, since the 2000s, the occurrence of primary water stress corrosion cracking has been reported in conjunction with these alloys in domestic and oversea NPPs. In the present work, we assumed an imaginary crack at the inner surface of a surge nozzle weld that had previously experienced the outside repair welding, and constructed its finite element model. Finite element analysis was performed with respect to the heat transfer, and then to the residual stress for obtaining the total applied stress distributions. These stress distributions were finally converted to the stress intensity factors for estimating crack growth rate. From the comparison of crack growth rate curves for the cases of no repair welding and outside repair welding, it was found that the outside repair welding did not exhibit negative effect on the crack growth for the surge nozzle under consideration in this work; in both cases, the cracks stopped growing before they became the through-wall cracks.