The effect of the wear of contact tips on the weld beads made by a Gas Metal Arc Welding(GMAW) process was studied. In order to correlate between the wear of tips and beads, the droplet transfer was investigated by a high speed camera and waveform shapes, and the condition of beads was examined by a low magnification camera as well. It was found that the worn contact tip had caused to shift the contact point between the tip and the welding wire which resulted in nonuniform beads. In addition, the worn contact tip had changed the welding resistance and brought about the arc instability during welding.

• Proceedings of the KIEE Conference
• /
• 2004.11c
• /
• pp.135-137
• /
• 2004

In this study we'll deal with the small-sized metalized film capacitors with large capacity which head have $5mm{\times}5mm{\times}2.5mm$ dimension. The lead wire is used to weld at both sides of capacitors. At that time the position gap between the welding machine and lead wire supplier would cause the welding error. Also, during the tapping processing of metalized film capacitors, the interval error among the capacitors, the length error of lead frame attached at the capacitors, and the straightness distortion of the lead frame could happen. As mentioned, four kinds of error parameters will be measured and analyzed by using the automatic visual inspection system that is implemented with CCD camera, optical parts, background lighting, and image processing algorithms. Finally we are able to achieve success rate above 99% to detect the welding faults of capacitors in the field test.

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 2000.05a
• /
• pp.763-766
• /
• 2000

The Rapid Prototyping and Tooling technology has been developed. However, most commercial ones currently use resins or waxes as the raw materials. These days. the direct metal deposition methods are researched as a true rapid prototyping and tooling technology. A fundamental study on rapid prototyping and tooling with wire welding technology using $CO_2$ laser radiation was carried out in this paper. The main focus is to develop a simple commercial rapid prototyping and tooling system with the exiting laser welding technology. The process is investigated as a function of laser parameters and process variables. Basic parts were fabricated as out-put and their microstructure, hardness and tensile strength are examined for the reliability. In addition, Its advantages and disadvantages are discussed as a rapid prototyping and tooling system.

• Journal of Welding and Joining
• /
• v.3 no.1
• /
• pp.40-45
• /
• 1985

Wire meling characteristics were examined with variation of gas formers such as $MgCO_3, CaCO_3 and Li_ 2CO_ 3$ by self-shielded flux cored arc welding. The flux cored wire of overlap type was welded by DCRP. The results obtainedareas follows. 1) Drop type was observed with no gas former, repelled type with MgCO_3$ added and short circuit type with $Li_2CO_3$ added. The variation of transfer mode was related to the blowing force of $CO_2$ gas and the surface tension of the slag. 2) Droplet size increased with adding gas formers due to the effect of $CO_2$ gas cushion. 3) Core spikes were observed more frequently with increasing the amount of gas formers.

• Journal of Welding and Joining
• /
• v.20 no.3
• /
• pp.54-59
• /
• 2002

Overlays is a treatment of the surface and near-surface regions of a material to allow the surface to perform functions that are distinct from those frictions demanded far the bulk of the material. Welding, thermal spray, quenching, carburizing and nitration have been used as the surface treatment. Especially, weld overlay is a relatively thick layer of filler metal applied to a carbon or low-alloy steel base metal for the purpose of providing a wear resistant surface. In this study, weld overlay was performed by MAG welding on the base metal(SS400) with filler metal which contain composite powders($Cr_3C_2+Mn+Mo+NbC$) and solid wire(JIS-YGW11). Characteristics of hardness and wear resistance on overlays were analyzed by EDS, EPMA, XRD and microstructures. Carbide formations were $M(Cr, Fe)_7C_3$ and NbC phases. And carbide volume fraction, hardness and specific wear resistance of overlays were increased with increasing powder feed rate and decreasing wire fred rate. Hardness and wear resistance were almost proportioned to carbide volume fraction of overlay.

• Journal of the Korean Society of Industry Convergence
• /
• v.14 no.2
• /
• pp.59-65
• /
• 2011

$CO_2$ Welding which uses $CO_2$ instead of inert gas is most widely used in industrial sites. Welding rod for $CO_2$ Welding is roughly divided into solid wire and flux cored wire. $CO_2$ Welding has higher efficiency than any other welding methods, and also economic and speedy to handle, that's why is used frequently for welding general structures. As most of studies about $CO_2$ Welding are focused on metallurgical changes of successful joints, they developed theories about the change of configuration on weld parts. This study is especially focused on not only the change of configuration on weld parts, but also the change of the penetrating depth through changing the position of welding torch. For inspection, applied AWS A5.20 E70-1 among welding wires and fixed moving angles of torch, but controled the values of voltage and the position of welding. Also Automatic Feed Mechanism is used for exact movement of material, specimen is a piece of steel for general structures. By measuring and analyzing the configuration of sliced section and the values of welding leg length and welding throat after welding, the outcome about the changes turned out.

• Journal of Welding and Joining
• /
• v.29 no.4
• /
• pp.30-34
• /
• 2011

• Journal of Welding and Joining
• /
• v.16 no.1
• /
• pp.17-24
• /
• 1998

본 내용에서는 solid wire(1.2 mm)를 대상으로 보호가스, 용접조건 및 용접재료 등이 용적이행현상에 미치는 영향을 용접 중 아크 신호의 변화와 고속카메라에 의한 용적이행현상 관찰 결과를 중심으로 기술하였다.

• Journal of Welding and Joining
• /
• v.18 no.2
• /
• pp.196-196
• /
• 2000

Formation of the weld defect, such as a blowhole and a pit in lap-jointed fillet arc welds has been a serious problem in arc welding of Zn-coated steel sheet. In this study, the relationship among welding conditions, welding materials and defect formation was investigated in order to minimize these defects in the CO₂ welds. In addition, the arc stability of the commercial welding wires was evaluated for revealing their effects on defect formation. Main conclusions obtained are as follows:1) There was no difference between shear tensile strength of the sound welds and that of the welds with blowholes whose diameters are less than 0.5mm. However, the welds with blowholes whose diameters are equal or larger than 0.5mm and pits exhibited tensile strength 10~20% and 30~40% lower than that of the sound welds respectively.2) The optimum welding condition to effectively prevent or reduce the weld defects formation are as follows:- The welding variables of 220A-23V-100cm/min and 120A-190V-30cm/min were recommended for minimizing the weld defects.- The gap between the two sheets at the lap-joint should be controlled to more than 0.2mm- Solid wire was less susceptible to the formation of the weld defects than the flux-cored wire.- The low welding current condition produced less weld defects than the hihg welding current condition.3) One of the reason why the amount of the defect was reduced at the low welding current was the gas discharging by the active agitation of the molten pool, due to an increasing in the number of the short circuit. (Received September 27, 1999)

• Journal of Welding and Joining
• /
• v.18 no.2
• /
• pp.69-76
• /
• 2000

Formation of the weld defect, such as a blowhole and a pit in lap-jointed fillet arc welds has been a serious problem in arc welding Zn-coated steel sheet. In this study, the relationship among welding conditions, welding materials and defect formation was investigated in order to minimize these defects in the CO₂welds. In addition, the arc stability of the commercial welding wires was evaluated for revealing their effects on defect formation. Main conclusions obtained are as follows: 1) There was no difference between shear tensile strength of the sound welds and that of the welds with blowholes whose diameters are less than 0.5mm. However, the welds with blowholes whose diameters are equal or large than 0.5mm and pits exhibited tensile strength 10∼ 20% and 30∼40% lower than that of the sound welds respectively. 2) The optimum welding condition to effectively prevent or reduce the weld defects formation are as follows: -The welding variables of 220A-23V-100cm/min and 120A-19V-30cm/min were recommended for minimizing the weld defects. -The gap between the two sheets at the lap-joint should be controlled to more than 0.2mm. -Solid wire was less susceptible to the formation of the weld defects than the flux-cored wire. -The low welding current condition produced less weld defects than the high welding current condition. 3) One of the reason why the amount of the defect was reduced at the low welding current was the gas discharging by the active agitation of the molten pool, due to an increasing in the number of the short circuit.