• Transactions of the Korean Society of Pressure Vessels and Piping
• /
• v.14 no.1
• /
• pp.58-65
• /
• 2018

The purpose of this study is to develop a Half Nozzle Repair(HNR) process to prevent the leakage from welds on small bore piping in Reactor Coolant System. The Codes & Standards of tempered bead and design requirements of J-Groove welds are reviewed. Automatic machine GTAW welding and machining equipments are developed to perform HNR process. Single pass welding and overlay welding equipments are conducted in order to obtain the optimal temper bead welding process parameters with Alloy 52M filler wire. Coarse grain heat affected zone(CGHAZ) is formed by rapid cooling rate in heat affected zone after welding. Accordingly, a proper temper bead technique is required to reduce CGHAZ in 1-Layer of welds by 2- and 3-Layers. Mock-up tests show that the developed HNR process is possible to meet ASME Code & Standard requirements without any defect.

• Journal of Welding and Joining
• /
• v.33 no.3
• /
• pp.68-74
• /
• 2015

Superduplex stainless steels are important materials to the oil and gas industry, especially for off-shore production. TIG welding of super duplex stainless steels to obtain the optimal phase balance between austenite and ferrite is mainly achieved by controlling the cooling rate and the weld chemistry. The latter depends on the filler wire chosen and the shielding gas used. If TIG welding of superduplex stainless steels is performed with argon shielding gas only, then nitrogen gets lost from the weld pool, which can result in a ferrite-rich weld metal, with an inferior corrosion resistance than parent metal. In the present study, nitrogen permeation model from the shield gas which gets into the weld metal in DCEN-TIG welding has suggested. This plasma stream model shows characteristics of permeation of nitrogen ions into the molten metal due to the strong physical effect of plasma stream which formed by the arc pressure rather than the permeation of nitrogen ions caused by electric effect.

• Journal of the Microelectronics and Packaging Society
• /
• v.6 no.3
• /
• pp.45-50
• /
• 1999

Copper has been widely used for the electronic parts, and especially spot welded one for the leads of condenser or resistor. However, copper is generally hard to be spot welded because of its low electrical resistivity. For this experiment, Sn-37%Pb solder which has relatively higher resistivity was coated on the Cu-sheet to improve the spot weldability of copper. As the experimental variables welding pressure was varied from 100 to 200kgf, welding time from 20 to 50ms, and welding current from 100 to 2500A. Experimental results showed that the solder coated Cu-sheet can be spot welded under the conditions of 400~2200A welding current, 100~200kgf pressure and 20-50ms welding time. The tensile shear strength of the spot welded joint increased with welding current up to the critical current, and after the critical value decreased with current.

• Transactions of Materials Processing
• /
• v.12 no.3
• /
• pp.214-220
• /
• 2003

In the case of hollow cylinder extrusion using porthole die, the effects of extrusion parameters-temperature, the speed of extrusion, the shape of the die and mandrel-on metal flow in porthole die extrusion of aluminum have been investigated. There have been few studies about condenser tube extruded by porthole die. This study was designed to evaluate metal flow, welding pressure, extrusion load, tendency of mandrel deflection according to variation of chamber length in porthole die. The welding chamber height in condenser tube was calculated by using finite element method. Forming analysis results for condenser tube would provide useful information for the optimal design of porthole die.

• Journal of the Korean Society of Clothing and Textiles
• /
• v.36 no.6
• /
• pp.583-591
• /
• 2012

This study selected three model designs used for air injection type welding clothes designed for insulation purposes and analyzed the performance of each design. The bending characteristics were analyzed in order to identify the flexibility of the welded areas; subsequently, the seam breaking strength and water pressure resistance were analyzed to identify the bonding strength. In addition, two types of waterproof fabric, polyurethane (PU) coated 2 layer and PU laminated 2 layer fabrics, were used for a performance analysis, according to fabric processing specifications. The circle type showed the highest flexibility in the terms of bending characteristics that influence wearability and were followed by the wave and the straight type. In terms of breaking strength, the straight type showed the highest breaking strength, followed by the wave and the circle type. The water pressure resistance analysis found that the wave type was superior to the straight type in terms of water pressure resistance. The wave type is deemed to be a design type suitable for maximizing performance, provided that the issue of stabilization in the welding production process is addressed. Looking at the bending characteristics of waterproof fabric for each specification, the laminating waterproof cloth outperformed the coated waterproof cloth in terms of flexibility. However, in terms of seam breaking strength, the coated waterproof cloth outperformed the laminated cloth. In contrast, the water pressure resistance of the laminated waterproof fabric was found to be higher than the coated waterproof fabric, leading to the conclusion that the bonding strength of the laminated waterproof fabric is higher than that of the coated waterproof fabric based on the assumption of injecting air.

• Transactions of the Korean Society of Machine Tool Engineers
• /
• v.16 no.6
• /
• pp.29-36
• /
• 2007

The present study examined the mechanical properties of the friction welding of Ni-Cr-Mo to SM45C. Friction welding was conducted at welding conditions of 2,000 rpm, friction pressure of 100MPa, friction time of 0.8, 1.0, 1.2, 1.4, 1.6, 1.8, 2.0 seconds, upset pressure of 150MPa, and upset time of 3.0 seconds. When the friction time was 1.6 seconds, the maximum tensile strength of the friction weld happened to be 1,020MPa, which is 120% of the base material's tensile strength(850MPa). At the same condition, the maximum shear strength was 438MPa, which is equivalent to 103% of the base material's shear strength(425MPa). At the same condition, the maximum vickers hardness was Hv490 at Ni-Cr-Mo nearby weld interface, which is higher Hv40 than condition of the friction time 0.8 seconds, and the maximum vickers hardness was Hv305 from weld interface of SM45C, which is higher Hv12 than condition of the friction time 0.8 seconds. The results of microstructure analysis show that the structures of two base materials have fined and rearranged along a column due to heating and axial force during friction, which has affected in raising hardness and tensile strength.

• Transactions of Materials Processing
• /
• v.19 no.8
• /
• pp.452-459
• /
• 2010

It was investigated that two plates of aluminum can be welded by hot extru-shear welding process with extru-shear welding dies, and that the welding strength and metal flow on the welding section were analyzed by computer simulation according to the welding variables such as inclined angle of cutter and overlapped length of plates and temperature of plates. It was known by computer simulation that welding strength on the welding section of plates could be influenced by the inclined angle of cutter and overlapped length of plates and temperature of plates. And it was known by experiments that two plates of aluminum can be welded on the end sections by hot extru-shear welding process using extru-shear welding dies, and that welding strength is the highest when inclined angle of dies is $70^{\circ}$, and overlapped length is 1.2 mm, and temperature is $520^{\circ}$, when aluminum 5052 two plates with 1.6 mm thickness are used as welding material.

• Proceedings of the KWS Conference
• /
• 1999.10a
• /
• pp.153-156
• /
• 1999

• Proceedings of the KWS Conference
• /
• 1999.10a
• /
• pp.157-159
• /
• 1999

• Proceedings of the KWS Conference
• /
• 2000.10a
• /
• pp.271-273
• /
• 2000