• Journal of Welding and Joining
• /
• v.33 no.4
• /
• pp.17-23
• /
• 2015

Laser-gas metal arc hybrid welding has been considered as an alternative process of gas metal arc welding for offshore pipe laying. Fiber delivered high power lasers which enable deep penetration welding were recently developed but high power welding characteristics were not fully understood yet. In this study, the influence of shielding gas composition on welding phenomena in high power laser welding was investigated. Bead shapes, melt ejection and dropping were observed after autogenous laser welding with 100% Ar, Ar-20% $CO_2$, Ar-50% $CO_2$, and 100% $CO_2$ shielding gas. Process parameter window was widest with Ar-50% $CO_2$ shielding gas and the penetration was deepest with 100% $CO_2$ shielding gas. The melt dropping was not observed when Ar-50% $CO_2$ or 100% $CO_2$ shielding gas was supplied.

• Journal of the Korean Society for Precision Engineering
• /
• v.24 no.5
• /
• pp.35-43
• /
• 2007

Laser welding of metals has been widely used to improve a wear resistance and a corrosion resistance of the industrial parts. The objective of this research works is to investigate the influence of the process parameters, such as the welding for metals with CW Nd:YAG lasers. The bead-on-plate welding tests are carried out for several combinations of the experimental conditions. In order to quantitatively examine the characteristics of the butt welding, the welding quality of the cut section, stain-stress behavior and the hardness of the welded part are investigated. From the results of the investigation, it has been shown that the optimal welding condition without defects in the vicinity of the welded area and with a good welding quality is 1325W of the laser power, and 1.4m/min of laser welding speed.

• Journal of Welding and Joining
• /
• v.31 no.3
• /
• pp.49-53
• /
• 2013

Recently, studies about application of magnesium alloy sheet to automotive bodies are on the increase. For application to automotive bodies, researches about characteristics of resistance spot welding of magnesium alloy sheet are essential. Electrode life of resistance spot welding of magnesium alloy is very short due to sticking of magnesium alloy to copper alloy electrode. To increase electrode life, most effective method is inserting cover plate between electrode and magnesium sheet. But application of cover plate to actual process is difficult and decreases welding productivity. Process tape supplied automatically as cover plate can minimize lose of productivity and increase welding quality. In this study, resistance spot welding of magnesium alloy is carried out with applying process tape. Acceptable welding current region according to electrode force and welding time is determined.

• Journal of Welding and Joining
• /
• v.21 no.3
• /
• pp.30-34
• /
• 2003

This paper describes the heat distribution characteristics of ASTM A131DH36 high tensile steel for ship structures in 5㎾ $CO_2$ laser welding. In general, high energy of laser beam concentrates on the small area of the weldment instantaneously; therefore, this heat transfer mechanism induces the rapid changes of temperature and mechanical characteristics in laser welds this mechanism. So temperature distribution analysis is important to understand mechanical characteristics of laser welds. Authors have conducted finite element simulation to analyze the heat distribution characteristics in laser welds. The result of simulation has been verified by comparing with the metallurgical experiment result. From the result of this study, we can accurately predict the heat distribution characteristics in laser welds by using numerical simulation.

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 2002.05a
• /
• pp.565-568
• /
• 2002

Welding variables and conditions in gas metal arc welding (GMAW) effect on the weld quality and productivity, extensive research efforts have been made to analyze the welding variables and conditions. In this study dynamic behavior of GMAW system is investigated using the characteristic equations of the power supply, wire and welding arc. Characteristic equation of wire is modified to include the effect of droplets attached at the electrode tip. The dynamic characteristics of arc length, current, voltage with respect to the step, ramp inputs of CTWD was simulated, seam tracking procedure using arc sensor was simulated with variable V-Groove geometries and weaving frequencies. From results of simulation, some predictions about dynamic characteristics of GMAW and welding process are available. The proposed simulator and results appear to be utilized to determine the proper welding conditions, to be improved by considering power supply dynamic characteristics.

• Journal of Welding and Joining
• /
• v.15 no.3
• /
• pp.79-87
• /
• 1997

This study was performed to evaluate basic characteristics of electron beam welding process for a 9% Ni steel plate. The principal welding process parameters, such as working distance, accelerating voltage, beam current and welding speed were investigated. The AB (Arata Beam) test method was also applied to characterize beam size and energy density of the electron beam welding process. The electron beam size was found to decrease with the increase of accelerating voltage and the decrease of working distance. So, in case of high voltage (150kV), spot size and energy density of electron beam were revealed to be 0.9mm and $6.5\times10^5W/\textrm{cm}^2$ respectively. The accelerating voltage among the welding parameters was found to be the most important factor governing the penetration depth. When the accelerating voltage of electron beam was low ($\leq$90kV), beam current and welding speed did not affect on the penetration depth significantly. However, in case of high voltage ($\geq$120kV), the depth of penetration increased very sensitively with the increase of beam current and the decrease of welding speed.

• Journal of Welding and Joining
• /
• v.10 no.4
• /
• pp.250-258
• /
• 1992

In order to clarify the mechanical behavior of welding crack and to evaluate the mechanical characteristics of welded parts in thick plate, it is very important to accurately predict the welding deformation and residual stress including transient state before welding. In this paper, the theory of a three-dimensional elasto-plastic problem for the analysis of mechanical phenomenon of welding joint on the plate is developed into an efficient and accurate method based on the finite element method, and then several examples are considered by using the proposed model. The results of numerical analyses are discussed in the viewpoint of the mechanical characteristics of the distribution of three-dimensional welding residual stresses, plastic strains and their production mechanism on the thick plate.

• Journal of Industrial Technology
• /
• v.21 no.A
• /
• pp.329-336
• /
• 2001

In this study, a series of fatigue tests are carried out in order to estimate quantitatively the characteristics of fatigue crack growth rate for high strength steels of SM570, POSTEN60, and POSTEN80 steel, that is, the influence on fatigue crack growth rate according to the welding line, the characteristics of fatigue crack growth according to the welding method and the kinds of steel, and the characteristics of fatigue crack growth for base metal, heat affected zone and weld metal. From the test results, in case that the notch if parallel to welding line, it knows that the retardations of fatigue crack growth rate in crack tip at early stage increase remarkably than in case that the notch is perpendicular to welding line due to compressive residual stress. And the characteristics of fatigue crack growth rate according to welding method are that the dispersion of fatigue crack growth rate in case of FCAW method is smaller than that of SAW method. Also, it knows that the fatigue crack growth rate converges in high stress intensity factor range.

• Journal of Welding and Joining
• /
• v.20 no.6
• /
• pp.732-740
• /
• 2002

• Journal of the Korean Society of Manufacturing Technology Engineers
• /
• v.21 no.2
• /
• pp.349-353
• /
• 2012

As the world wind energy market grows rapidly, the productions of wind power generation equipment have recently increased, but manufacturers are not able meet this requirement. Particularly offshore wind energy industry is one of the most popular renewable energy sectors. To generalize welding processes, the welding automation is considered for steel structure manufacturing in offshore wind energy to get high quality and productivity. Welding technology in construction of the wind towers is depended on progress productivity. In addition, the life of wind tower structures should be considered by taking account of the natural weathering and the load it endures. The root passes are typically deposited using Gas Tungsten Arc Welding(GTAW) with a specialized backing gas shield. Not only the validation consists of welders experienced in determining the welding productivity of the baseline welding procedure, but also the standard testing required by the ASME section IX and API1104 codes, toughness testing was performed on the completed field welds. This paper presents the welding characteristics of the root-pass welding of high tensile steel in manufacturing of offshore wind tower. Based on the result from welding experiments, optimal welding conditions were selected after analyzing correlation between welding parameters(peak current, background current and wire feed rate) and back-bead geometry such as back-bead width(mm) and back-bead height performing root-pass welding experiment under various conditions. Furthermore, a response surface approach has been applied to provide an algorithm to predict an optimal welding quality.