• Journal of Welding and Joining
• /
• v.28 no.2
• /
• pp.47-53
• /
• 2010

According to the research report for the recent a few years, the dissimilar welding of Cu and STS 304 alloy have been presented that a weldability is very poor. This article present a study on Lap joint by Electron beam welding dissimilar materials. The weld metals was constituted between pure copper and STS 304 steel. The experiment was performed with 125mA welding current, 520mA focusing current. The Vacuum condition of chamber is 5${\times}$10-5torr and welding speed is 300mm/min. Showing the bead shape of weld metal, the thickness of the stainless 304 using as the protect materials is 3mm and the thickness of a copper is 15mm. The analysis about the microstructure were carried out in which it was observed with SEM. The results showed that complex heterogeneous fusion zone microstructure characterized both by rapid cooling and mixing of the molten metal, however the liquation crack was formated in the fusion line.

• Proceedings of the KWS Conference
• /
• 2009.11a
• /
• pp.239-242
• /
• 2009

Friction stir spot welding (FSSW), developed based on principle of friction stir welding, has been paid attention as a new solid-state spot welding process. Since FSSW can produce high-quality weld in Al alloys more easily than resistance spot welding, this process has been already used for construction of Al components in the automotive industries. Despite the large industrial interests in FSSW, fundamental knowledge on welding phenomena of this process has not been fully understood. In this study, FSSW phenomena, such as the consolidation mechanism, the microstructural evolution and the material flow, were examined in Al alloy 6061. This study clarified that the elliptical zone found in the vicinity of the pin hole on the cross section was characterized by the initially lapped surface of two sheets. Moreover, the following material flow was proposed; capture of the upper material with the threads on the pin surface, spiral flow along the tool rotation, and then release at the tip of the pin.

• Journal of the Korean Society for Precision Engineering
• /
• v.27 no.2
• /
• pp.40-49
• /
• 2010

The Purpose of this paper is to weld a rapid palatal expander using a continuous wave Nd:YAG laser. The rapid palatal expander has become a useful treatment method for severe maxillary transverse deficiencies and posterior crossbites. Rapid maxillary expansion is a well-established method to correct transverse maxillary deficiency and arch length discrepancy. The major process parameters studied in the present laser welding experiment were the positions of focus, laser power and travel speed of laser beam. We measured the fusion zone size and its shape using an optical microscope for the observation of cross-sectional area and tension stress of a rapid palatal expander welded. Through the experimental investigation, the optimum speeds and power of laser without deficiencies of weld cross-sectional area were obtained.

• Journal of Welding and Joining
• /
• v.12 no.1
• /
• pp.73-79
• /
• 1994

Low cycle fatigue test was performed by companion specimens method to compare the properties of cyclic strain for the weldments of controlled rolling steel CR60 and welding structural steel SM58Q. And the result does not showed any difference of low cycle fatigue life between weldments. Especially, the values of coefficient of cyclic plastic strain $C_{p}$ and exponent of cyclic plastic strain $K_{p}$ of heat affected zones of CR60 steel and SM58Q steel were same. And $C_{p}$ and $K_{p}$ of CR60 steel were equal to the values of weld it means a good combination between the base metal, the heat affected zone and the weld of CR60 steel.eel.eel.

• Journal of Welding and Joining
• /
• v.25 no.5
• /
• pp.36-44
• /
• 2007

This paper is the first part of the study on the accuracy improvement of numerical analysis of steel welds. The aim of this paper is to raise the accuracy of thermal analysis results, such as the shape and size of the weld cross section and the hardness distribution in HAZ(Heat-Affected Zone). It is known that the factors affecting on the accuracy are thermal properties, metallurgical properties and welding heat source model. It was found that the arbitrary distributed heat source model should be used to predict practical weld cross section shape and size. Also, in order to improve the prediction accuracy of HAZ hardness distribution, it was essential to consider 2 CCT(Continuous Cooling Transformation) diagrams in calculating volume fraction of transformed phases. One is the peak temperature being around melting temperature. The other is the peak temperature being around metallurgical transformation temperature.

• Journal of Industrial Technology
• /
• v.18
• /
• pp.117-124
• /
• 1998

In recently, according to increase the construction rate of steel bridge, it is necessary to develop the high strength, high toughness steel. Thus, this study show to evaluate the fatigue characteristic of SWS 570 B first used within a country. With the weld-joined compact tension specimens compared with each other, that is, transverse and lengthwise about the crack propagation, high and low in the input heat level, the fatigue test were performed. The log-log curves between the fatigue crack propagation rate da/dN and the transition range of the stress intensity factor ${\Delta}K$ ahead the crack tip were drawed, with these data. By using this curve, we obtained C and m which is material constant from Paris-Erdogan power law. The obtained results from this study indicate that fatigue crack growth rate of SWS 570 B is not influenced by softening effect which occurs in the HAZ(heat-affected zone) when high and low heat input weld is carried out. Softening effects, which affect fatigue properties, are shown that it is not affected to the fatigue growth rates significantly.

• Journal of the Korean Society of Safety
• /
• v.12 no.2
• /
• pp.45-56
• /
• 1997

Fracture behavior of ex-serviced 1Cr-0.5Mo steel was measured at room($24^{\circ}C$) and elevated($538^{\circ}C$) temperature and compared with that measured with virgin 1Cr-0.5Mo steel. Compact C(T) specimens were machined from the base and welded test materials. In case of the C(T) specimens of the weld, fatigue precrack was introduced along the fusion line so that following crack growth should occurs along the region of heat affected zone. It was observed that the J-R curve of the serviced material was significantly lower than that of the virgin material at room temperature. Brittle fracture was observed in the serviced material. On the other hand, at elevated temperature no noticeable difference was found between the J-R curves of the virgin and the serviced material. The measured J-R curves were also compared with those of the 1.25Cr-0.5Mo steel obtained from the other literatures. Optical microscopy and SEM examination of the serviced material reveal the carbide in/along the grain boundary which shows material degradation due to long-term usage. An example of application of the measured J-R curves is shown.

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 2005.10a
• /
• pp.627-631
• /
• 2005

In this study, low fatigue behavior of laser welded sheet metal were investigated. Before welding, the cross section of butt joint was prepared only by fine shearing without milling process. Specimens were same sheet metal and welding condition that using automobile manufacturing company at present. Butt joint of cold rolled sheet metal was welded by $CO_2$ laser. It is used that welding condition such as laser welding speed was 5.5m/sec and laser output power was 5kW for 0.8mm and 1.2mm sheet metal. The laser weldments were machined same or different thickness and same or different material. In order to mechanical properties of around welding zone, hardness test was performed. Hardness of welding bead is about 2 times greater than base material. We performed the low cycle fatigue tests for obtaining fatigue properties about thickness and the weld line direction of specimen. The results of strain controlled low cycle fatigue test indicate that all specimens occur cyclic softening, as indicated by the decrease in stress to reach a prescribed strain.

• Journal of the Society of Naval Architects of Korea
• /
• v.40 no.3
• /
• pp.54-60
• /
• 2003

Fatigue strength of offshore structures or ship structures is significantly decreased due to corrosive environment condition such as sea water and/or coal, crude oil of cargoes, compared to that of on shore structures. In corrosive environment, fatigue strength of structures also depends on characteristics of weld material heat affected zone(HAZ). In this research work, rotary bending fatigue tests of parent material and HAZ of TMCP steel were performed in order to investigate the initiation and propagation of cracks both in air and in NaCl solution. Comparison of fatigue strength In relation with the salinity of NaCl were carried out as well. According to the test results weld material or HAZ of TMCP steel showed higher fatigue strength than that of the parent material. The fatigue strength of TMCP steel decreases drastically in NaCl solution compared to that of in air environment. In particular, more reduced fatigue strength is observed in 1% NaCl solution than in 3% NaCl solution.

• Journal of Welding and Joining
• /
• v.34 no.3
• /
• pp.61-68
• /
• 2016

Characteristics of dissimilar metal welds between alloy steel ASTM A387 Gr. 91 and carbon steel ASTM A516 Gr.70 made with Flux cored arc welding(FCAW) have been evaluated in terms of microstructure, mechanical strength, chemical analysis by EDS as well as corrosion test. Three heat inputs of 15.0, 22.5, 30.0kJ/cm were employed to make joints of dissimilar metals with E91T1-B9C wire. Post-weld heat treatment was carried out at $750^{\circ}C$ for 2.5 h. Based on microstructural examination, tempered martensite and lower bainite were formed in first layer of weld metal. The amount of tempered martensite was decreased and the amount of lower bainite was increased with increasing heat input and layer. Heat affected zone of alloy steel showed the highest hardness due to the formation of tempered Martensite and lower Bainite. Tensile strengths of dissimilar welds decreased with increasing heat inputs. Dissimilar welds seemed to have a good hot cracking resistance due to the low HCS index below 4. The salt spray test of dissimilar metals showed that the corrosion rate increased with increasing heat inputs due to the increase of the amount of lower Bainite.