• 한국자동차공학회논문집
• /
• 제10권2호
• /
• pp.186-192
• /
• 2002

The fatigue crack propagation characteristics were investigated on dissimilar friction weld of two kind of heat-resisting steels (STR3 and STR35) commonly used in valve materials for vehicles. A small circular artificial defect was machined to induce fatigue crack at bonded line, heat affected zone and base metal of the weld on the surface of the specimens. From the results of the experiment, the fatigue limits of the materials STR3 and STR35 were obtained to be 429.0MPa and 409.4MPa respectably. The STR35 base metal and 1.0mm HAZ specimens showed 190% and 82% higher fatigue life than STR3 base metal. And the fatigue life of 1.0mm HAZ specimen was shown 99% on STR3 and 29% on STR35 higher than that of their base metal. But the fatigue life of weld interface specimen was shown 18% on STR3 and 72% on STR35 lower than that of their base metal because of the weld interface separation.

• Journal of Welding and Joining
• /
• 제26권5호
• /
• pp.60-65
• /
• 2008

Ferritic stainless steels of the 400 series have been available for automotive exhaust system, heat exchanger, radiater etc. in various industrial because heat resistance, corrosion resistance and strength are excellent. Especially, automotive exhaust system is required good heat resistance because typical temperature of exhaust system exposed during operation of engine is reach up to $800^{\circ}C$. However, research for effect of high temperature in ferritic stainless steels is not enough. In this study, high temperature tensile properties of lap weld of ferritic stainless steels(STS 429) were investigated. In accordance with heat input, lap welds had been produced and were evaluated at high temperature($800^{\circ}C$) to compare high temperature tensile properties. In addition, room temperature tensile tests were carried out for non-aging and aging specimens. As a result of R.T tensile test, non-aging specimens were fractured in base metal except for low heat input specimen and aging specimens were fractured in weld metal. Also high temperature tensile test were carried out by aging specimen. After high temperature tensile test, fracture of aged specimen was occurred in base metal except for low heat input specimen. Fracture surface of low heat input specimen in weld metal was confirmed as brittle fracture with observation using scanning electron microscope(SEM). Significant decrease in ultimate tensile strength (between 82 and 85%) was observed for aged ferritic stainless steels(STS 429) when tested at high temperature.

• 한국철도학회논문집
• /
• 제9권4호
• /
• pp.371-378
• /
• 2006

This study investigates the effects of the material properties and the fatigue behaviors in the SM490A material butt weld specimens due to the heat-treatment and the grinding. In the fatigue behavior, the heat-treatment affects the fatigue life. The S-N curves of both matrix specimen and butt weld specimen are reversed at some cycle by the existence or nonexistence of heat-treatment. The grinding on the bead makes the fatigue limit decrease in the all specimens. But the reinforcement removed, the fatigue limit increases at the high cycle. Also, this study investigates the fatigue life estimation by examining butt weld bead profiles. The butt weld beads, which are welded by semi-robot method, have non-uniform bead profiles described by $\theta,\;\rho$ and h. The stress concentration factors $K_t$, are changed by each different $\theta,\;\rho$ and h from 1.395 to 2.863. Hence, the sensitivity of $K_t$ is changed by each $\theta,\;\rho$ and h. As $\theta$ becomes lower and $\rho$ and h become higher, $K_t$ increases. The fatigue life can he estimated very closely for the AAY specimens without residual stress using only butt weld bead profiles. But, fur the AAN specimens with residual stress, the fatigue life must be estimated by considering both the weld bead profiles and the residual stress data.

• 대한기계학회논문집A
• /
• 제24권10호
• /
• pp.2597-2602
• /
• 2000

The most effective means of evaluating remaining life is through the creep testing of samples removed from the component. But sampling of large specimen from in-service component is actually impossible. So, sampling device and small-specimen creep tester have been applied. Sampling device has been devised to extract mechanically small samples by hemispherical, diamond -coated cutter from the surface of turbine rotor bores and thick-walled pipes without subsequent weld repairs requiring post weld heat treatment. A method of manufacturing small creep specimen, 2min gage diameter and 10min gage length, using electron beam welding to attach grip section, has been proven. Small-specimen creep tester has been designed to control atmosphere to prevent stress increment by oxidation during experiment. To determine whether the small specimens successfully reproduce the behavior of large specimens, creep rupture tests for small and large specimens have been performed at identical conditions. Creep rupture times based on small specimens have closely agreed within 5% error compared with that of large specimen. The errors in rupture time have decreased at longer test period. This comparison validates the procedure for fabricating and testing on small specimen. This technique offers potential as an efficient method for remaining life assessment by direct sampling from in -service high temperature components.

• 한국정밀공학회지
• /
• 제21권4호
• /
• pp.161-169
• /
• 2004

In this study, we investigated fatigue crack growth behavior of laser welded sheet metal due to a single overload. Fatigue specimens were made using butt joint of cold rolled sheet metal that was welded by $CO_2$ laser. The fatigue crack propagation tests were performed in such a way that fatigue loading was parallel to the weld line while crack propagation was perpendicular to the weld line. Single overload was applied when fatigue crack tip was arrived near the weld line. The distances between the crack tip and the weld line at which a single overload was applied were 6, 4 and 2mm. The effect of specimen thickness and overload ratio on the fatigue behavior was determined. The plastic zone size of crack tip due to the single overload was determined from the finite element analysis. For investigating fatigue crack growth behavior, we used different thickness specimen 0.9mm and 2.0mm, and variable overload ratio applied fatigue crack propagation test. Also we used finite element analysis for investigating the plastic zone size of crack tip when single overload applied

• Journal of Welding and Joining
• /
• 제24권2호
• /
• pp.42-47
• /
• 2006

While it is known that the weld toe grinding method may give 3.4 times of fatigue strength improvement, this improvement may significantly vary according to weld bead shapes and loading modes. Although tremendous interest have been given in improving fatigue strength improvement for ship structures, quantitative results are yet in need. In this context, a series of fatigue tests is carried out for a type of test specimen that are typically found in ship structures. Weld burr grinding is carried out using a electric grinder in order to remove surface defects and improve the weld bead profile. The test results are compared with the same type of test specimen without applying the fatigue improvement technique in order to obtain a quantitative measure of the fatigue strength improvement. On the other hand, both hot spot stress and structural stress methods are employed to compare the effectiveness of the two methods in evaluating the fatigue strength improvement of welded structures.

• 한국레이저가공학회지
• /
• 제2권2호
• /
• pp.18-26
• /
• 1999

An innovative real-time weld monitoring technique using chromatic filtering of the thermal radiation from a weld pool is developed. The thermal radiation from the weld pool is focused on an aperture and the transmitted thermal radiation is monitored at two wavelengths with high-speed single-element detectors. Due to the chromatic aberration introduced in the focusing optics, the transmittance curve of thermal radiation varies by the wavelength. Owing to this difference in the transmittance, the local variation of thermal radiation from the weld pool can be monitored by processing the two spectroscopic signals from two detectors. In this paper, the algorithms to monitor the laser power on the weld specimen and the focus shift we investigated and the performances of laser power and focus monitoring are shown for a pulsed Nd:YAG laser welding. The monitoring of the weld pool size variation is also discussed.

• 한국기계가공학회지
• /
• 제2권4호
• /
• pp.53-60
• /
• 2003

Large sized marine structures are used under corrosion environment of seawater and applied by severe service loading such as an ocean current, a billow and a tempest. Marine structures are usually constructed by lots of thick wall steel pipes joining welded joints. The thickness of such as steel pipes is usually more than 40mm. The such as steels are called "Thermo-Mechanical Control Process steel (TMCP steel)" strengthened by a heat treatment in process of steel manufactures. The failure, especially crack initiation, of marine structures was starting at weld joints under service condition. Then they should be designed by basis of the fatigue strength under seawater corrosion environment of weld joints. To clarity the fatigue crack initiation behavior is important more than to clarify the crack propagation behavior on the strength design of marine structures, because it is very difficult to find out the crack initiation and propagation phenomena and then even if it will be able to find out, it is considered that the refit of the damaged parts of welded joints have a technical difficulty under the sea. Therefore, it is most important to clarify the corrosion fatigue crack initiation behavior under the seawater condition. But, there is one big difficulty to make a test for thick plate specimen, for example thicker than 40mm. Because, it is need large capacity loading apparatus to test such as thick plate specimen. In this research, the new configuration specimen for fatigue crack initiation tests was proposed. Using this new specimen, it is easy to carry out the fatigue clack initiation tests with relatively low cyclic loading and to observe a fatigue crack initiation behavior.

• 한국철도학회논문집
• /
• 제7권2호
• /
• pp.85-92
• /
• 2004

This paper consists of two parts. One is finite element analysis of the redistribution of residual stresses of weld specimen by cutting. This work is necessary to predict the actual residual stress distribution of weld specimens used in fatigue test. The other subject is to calculate the relaxation of residual stress and the strain field induced by cyclic loading. To obtain fatigue life of weldment, the value of strain amplitude at each position is necessary, for example in the strain-life approach, and the numerical results can be used to verify experimental strain measurements. Thermo mechanical finite element analyses were conducted on the commercial package ABAQUS.

• 대한기계학회논문집A
• /
• 제29권8호
• /
• pp.1153-1160
• /
• 2005

Many methods of spot weld modeling have been developed to increase efficiency and guarantee the robustness fer the CAE analysis. In this research they are introduced and the performance is compared in a viewpoint of stiffness and durability. For evaluating the performance a multi-spot welded specimen as well as two single welded specimen is used. The results show that the CWELD element considering 'patch to patch' is stiffer than other modeling methods in stiffness and more conservative in durability. It also offers simple modeling and since it is much easier to maintain the orrhogonality of the BAR element expressing a nugget, we can obtain more exact reaction forces and moments in a nugget. Therefore the CWELD element is the most excellent in the assessment of durability.