• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.34 no.9
• /
• pp.1317-1323
• /
• 2010

In this study, the weld residual stress distribution at a dissimilar-metal welded plate of low alloy carbon steel and stainless steel, which are widely used in nuclear power plants, was characterized. A plate mock-up with butt welding was fabricated using SA 508 low alloy steel and Type 304 stainless steel plates and the residual stresses were measured by the X-ray diffraction method after electrolytic polishing of the plate specimen. Finite element analysis was carried out in order to simulate the butt welding of dissimilar metal plate, and the calculated weld residual stress distribution was compared with that obtained from the measured data. The characteristics of the three-dimensional residual stress distribution in a butt weld of dissimilar metal plates were investigated by comparing the measured and calculated residual stress data.

• Journal of Welding and Joining
• /
• v.17 no.1
• /
• pp.88-96
• /
• 1999

The effects of root gap on welding residual stress and deformation are dealt with the multi-pass weldment with three kinds(0, 6, 30mm) of root gap by F.E.M common code, and then compared with experiment data. In this analysis, an 100% ramp heat input model was used to avoid numerical convergence problem due to an instantaneous increase in temperature near the fusion zone, and the effect of a moving arc in a two dimensional plane was also included. During the analysis, a small time increment was applied in a period with instantaneous temperature fluctuation while a large time increment was used in the rest period. The residual stress is distributed as symmetric types and maximum value is also equivalent when the weldment with 0mm and 6mm root gap is welded. In the case of 30mm root gap welding, the distribution of the residual stress extends over a wide range as asymmetric types due to the built-up weld, and most of the residual stress is biased in the side of a built-up weld part. In case of 0mm gap welding and 6mm gap welding, a little angular distortion occurs, but the level of deformation is small. When the weldment with 30mm root gap is welded, the angular deformation of the asymmetric types, however, occurs larger than the other specimens. The experimental and the analytic results show good coincidence and indicate that the welding residual stress and deformation distribution of 30 mm root gap specimen may be asymmetric and the amplitude is larger than those of root gap specimen under standard.

• Journal of Ocean Engineering and Technology
• /
• v.26 no.5
• /
• pp.5-10
• /
• 2012

In this study, carbon steel (A53) is used as the material for the pipes in a marine plant and ship industry. Welds are necessary to join the carbon steel, and the effect of this welding on the properties of the carbon steel has been studied by many researchers. In this study, the dynamic behavior of welded carbon steel was studied using an acoustic emission (AE) technique, which is a nondestructive test. There are numerous AE parameters that can be used to analyze the damage behavior of carbon steel by external loading. The AE parameters of energy, cumulative count, amplitude, and AE event were used, and each parameter was differentiated according to the degree of damage to the carbon steel. The energy showed a high level at the elastic range of the load curve, while the amplitude had the highest value at the hardening region. The cumulative count showed a growth tendency similar to the loading curve. In addition, an ultrasonic technique and hardness test were applied to evaluate the mechanical properties according to the base zone, HAZ region, and weld zone of the weld specimen. The velocity and attenuation ratio showed little change between zones, and an evaluation of the ultrasonic waves on each zone of the specimen was found to be a useful method to clarify the mechanical properties of the carbon steel.

• Journal of the Korean Society for Nondestructive Testing
• /
• v.29 no.6
• /
• pp.586-590
• /
• 2009

Poisson's ratio, one of elastic constants of elastic solids, has not attracted attention due to its narrow range and difficult measurement. Transverse wave velocity as well as longitudinal wave velocity should be measured for nondestructive measurement of Poisson's ratio. Rigid couplants for transverse wave is one of obstacle for scanning over specimen. In the present work, a novel measurement of Poisson's ratio distribution was applied. Immersion method was employed for the scanning over the specimen. Echo signals of normal beam longitudinal wave were collected, and transverse wave modes generated by mode conversion were identified. From transit time of longitudinal and transverse waves, Poisson's ratio was determined without the information of specimen thickness. Poisson's ratio distribution of the carbon steel weldment was mapped. Heat affected zone of the weldment was clearly distinguished from base and filler metals.

• Transactions of the Korean Society of Machine Tool Engineers
• /
• v.16 no.2
• /
• pp.37-43
• /
• 2007

In this paper, laser vision sensor is used to detect some defects any $co_{2}$ welded specimen in hardware. But, as the best expression of defects of welded specimen, the concept of segment splitting method and mean distance are introduced in software. The developed GUI software is used for deriding whether any welded specimen makes as proper shape or detects in real time. The criteria are based upon ISO 5817 as limits of imperfections in metallic fusion welds.

• Journal of Welding and Joining
• /
• v.19 no.6
• /
• pp.608-613
• /
• 2001

In this study, the rotary bending fatigue test was carried out with two kinds of base metal, martensite stainless steel STR3 and austenite stainless steel STR35 and the dissimilar friction welded material with them. To compare the fatigue fifes according to the notch positions, the small circular defect was worked on the bonded line, 1.0mm and 0.5mm distance form the bonded line. The fatigue limits of the STR3 and STR35 base metal were 429.0MPa and 409.4MPa respectably. In comparison with fatigue life at the same notch positions, the STR35 specimens showed about 190% for base metal, 82% for 1.0mm distance notched specimens higher than that of the STR3. But the fatigue life of the 0.5mm distance notched STR35 specimen showed about 35% lower than that of the STR3 specimen. And the bonded line notched specimen was much lower fatigue life than the other specimens because of separation of the bonded line.

• Transactions of the Korean Society of Automotive Engineers
• /
• v.11 no.1
• /
• pp.143-150
• /
• 2003

Experimental research has been carried out to investigate the characteristics of the fatigue crack initiation and propagation behavior of Tailor Welded Blank(TB) sheet used for vehicle body. We used three types of specimens which were machined of the same base metal: one is 1.4mm thick, another is 1.6mm thick, and the third(TB specimen) is laser-welded of two specimens(1.4mm and 1.6mm thick ones). The results of tensile and hardness test indicate that the yield strength of the TB specimen is the highest, and the hardness around welding bead is higher than that of base metal. Fatigue strength and fatigue limit of the TB specimen are much superior to those of the base metal up to $10^6$ cycles. The fatigue crack propagation of the heat-affected zone of the TB specimen is slower than that of the base metal. Welding bead has the fastest crack Propagation in the low stress intensity factor range$(\DeltaK)$ region, but the slowest in the high $\DeltaK$ region. The fatigue propagation characteristic of the TB specimen is relatively stable in comparison with that of the base metal in the high ${\Delta}K$ region around over $28MPa\sqrt{m}$.

• Journal of Ocean Engineering and Technology
• /
• v.30 no.4
• /
• pp.334-340
• /
• 2016

The combustion chamber of a diesel engine is often exposed to a more serious wear and corrosion environment than other parts of the engine because its temperature increases as a result of using heavy oil of low quality. Therefore, repair and built-up welding methods must be performed on worn or corroded parts of the piston crown, exhaust valve, etc. from an economical point of view. In this study, Inconel 718 filler metal was used in repair welding on the groove of a forged steel specimen for a piston crown, along with built-up welding on the surface of another forged steel specimen. Then, the corrosion characteristics of the weld metal zone for the repair welding and the deposited metal zone for the built-up welding were investigated using electrochemical methods in a 35% H₂SO₄ solution. The deposited metal zone indicated better corrosion resistance than the weld metal zone, showing a nobler corrosion potential, higher impedance, and smaller corrosion current density. It is considered that metal elements with good corrosion resistance were generally included in the filler metal, and these elements were also greatly involved in the deposited meta by built-up welding, whereas the weld metal consisted of metal elements mixed with both the filler metal and base metal elements because of the molten pool produced by the repair welding. Finally, it is considered that the hardness of the weld metal was increased by the repair welding, whereas the built-up welding improved the corrosion resistance of the deposited metal.

• Corrosion Science and Technology
• /
• v.16 no.2
• /
• pp.49-58
• /
• 2017

Many research efforts on the effect of nitrogen on the corrosion resistance of stainless steels have been reported, but little research has been conducted on the effect of nitrogen for the weldment of stainless steels by the seal-weld method. Therefore, this work focused on the determining the corrosion resistance of tube/tube sheet mock-up specimen for sea water condensers, and elucidating the effect of shielding nitrogen gas on its resistance. The pitting corrosion of autogenously welded specimen propagated preferentially along the dendritic structure. Regardless of the percent of shielding nitrogen gas, the analyzed nitrogen contents were very much lower than that of the bulk specimen. This can be arisen because the nitrogen in shielding gas may partly dissolve into the weldment, but simultaneously during the welding process, nitrogen in the alloy may escape into the atmosphere. However, the pitting resistance equivalent number (PREN) of the interdendrite area was higher than that of the dendrite arm, regardless of the shielding gas percent; and the PREN of the interdendrite area was higher than that of the base metal; the PREN of the dendrite arm was lower than that of the base metal because of the formation of (Cr, Mo) rich phases by welding.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.9 no.3
• /
• pp.605-610
• /
• 2008

Through welding fabrication, user can feel unsatisfaction of surface quality because of welded defects, Generally speaking, these are called weld defects. For checking these defects effectively without time loss effectively, weldability estimation system setup is an urgent thing for detecting whole specimen quality. In this study, by laser vision camera, catching a rawdata on welded specimen profiles, treating vision processing with these data, qualitative defects are estimated from getting these information at first. At the same time, for detecting quantitative defects, whole specimen weldability estimation is pursued by multifeature pattern recognition, which is a kind of fuzzy pattern recognition. For user friendly, by weldability estimation results are shown each profiles, final reports and visual graphics method, user can easily determined weldability. By applying these system to welding fabrication, these technologies are contribution to on-line weldability estimation.