• Journal of Welding and Joining
• /
• v.18 no.2
• /
• pp.184-184
• /
• 2000

In this study, the lap welding between austenitic stainless steel and carbon steel was carried out using arc spot welding process and weldability of welded specimens was estimated. From the tensile-shear strength test, micro Vickers hardness test, and microstructure observation, specimen of 6.5mm(hole of upper plate) showed the best results in terms of tensile-shear strength and nugget shape. And there was an unmixed zone in fusion boundary between the carbon steel base metal and bulk weld metal. This zone had very thin width with the hard microstructure. The shape of weld nugget in arc spot welding of dissimilar metal welds was predicted by searching thermal history of a weld joint through a three-dimensional finite element model. From the numerical analysis, predicted the shape of weld nugget showed good agreement with the experiment(Received August 24, 1999)

• Journal of Welding and Joining
• /
• v.18 no.2
• /
• pp.57-63
• /
• 2000

In this study, the lap welding between austenitic stainless steel and carbon steel was carried out using arc spot welding process and weldability of welded specimens was estimated. From the tensile-shear strength test, micro Vickers harness test, and microstructure observation, specimen of $psi6.5mm$(hole of upper plate) showed the best results in terms of tensile-shear strength and nugget shape. And there was an unmix zone in fusion boundary between the carbon steel base metal and bulk weld metal. This zone had very width with the hard microstructure. The shape of weld nugget in arc spot welding of dissimilar metal melds was predicted by searching thermal history of a weld joint through a three-dimensional finite element model. From the numerical analysis, predicted the shape of weld nugget showed good agreement with the experiment.

• Journal of Welding and Joining
• /
• v.33 no.2
• /
• pp.69-77
• /
• 2015

High strength steels have been continually being developed to improve in fuel economy in automotive and ensure safety of passengers. New bonding and welding methods have been required for improving weldability on high strength steels. In this study, resistance spot welding and Weld-bond with nugget diameters of 4.0mm, 5.0mm, 6.0mm and 7.0mm were produced and tested, respectively. In order to confirm the effect of nugget diameters on tensile shear characteristic of the Weld-bond, tensile shear characteristics of Weld-bond were compared with those of resistance spot welding and adhesive bonding. Peak load of Weld-bond were increased as the nugget diameter increases. After appearing maximum peak load continuous fracture followed with second peak owing to load being carried by resistance spot weldment. Fracture modes of the adhesive layer in Weld-bond fractures were represented by mixed fracture mode, which are cohesive failure on adhesive part and button failure at resistance spot welds. The results showed that the tensile shear properties can be improved by applying Weld-bond on TRIP steel, and more apparent with nugget diameter higher than 5${\surd}$t.

• Transactions of the Korean Society of Mechanical Engineers
• /
• v.17 no.2
• /
• pp.393-406
• /
• 1993

In resistance spot welding process, size of molten nuggest have been utilized to assess the integrity of the weld quality. However real-time monitoring of the nugget size is an extremely difficult problem. This paper describes the design of an artificial neural networks(ANN) estimator to predict the nugget size for on-line use of weld quality monitoring. The main task of the ANN estimator is to realize the mapping characteristics from the sampled dynamic resistance signal to the actual negget size through training. The structure of the ANN estimator including the number of hidden layers and nodes in a layer is determined by an estimation error analysis. A series of welding experiments are performed to assess the performance of the ANN estimator. The results are quite promissing in that real-time estimation of the invisible nugget size can be achieved by analyzing the dynamic resistance signal without any conventional destructive testing of welds.

• Journal of Welding and Joining
• /
• v.12 no.3
• /
• pp.109-117
• /
• 1994

Spot welding has wide used with a high work efficiency in the automotive and aerospace industries. Up to the present, the technique mainly used to test spot welds on production lines has been entirely depended upon destructive chisel or peel testing. Therefore, it's being very important assignment to secure the NDE technique which can be evaluate spot weld quality with more efficiency and high reliability. This paper discusses the feasibility of UNDE techniques to evaluate spot weld quality. For the sake of the approach to the quantitative measurement of nugget diameter and the discrimination of a the corona bond from nugget, ultrasonic c-scan image and distribution of reflective echo amplitude was measured by immersion method with the mechanical and the electronic scanning of point-focussed ultrasonic beam(25 MHz). As the results of this study, corona bond which is the most dangerous types of interface defects can be successfully detected, as well as expulsion and voids. Ultrasonic testing results were confirmed and compared by optical microscope and SAM(Scanning Acoustic Microscope) observation of the spot-weld cross section. The results show that the nugget diameter can be successfully measured with the accuracy of 0.8 mm.

• Journal of the Korean Society of Manufacturing Technology Engineers
• /
• v.5 no.4
• /
• pp.38-46
• /
• 1996

This paper discusses the feasibility of Ultrasonic Nondestructive Evaluation (UNDE) technique for sport weld quality. Ultrasonic c-scan image assisted by image processing technique was used for Nondestructive Evaluation(NDE) of spot weld quality. Ultrasonic testing results obtained were confirmed and compared by Optical Microscope and SAM(Scanning Acoustic Mircroscope) observation of the spot-weld cross section, The results show that the nugget dinameter can be successfully measured with the accuracy of 0.5mm. It was ascertained that ultrasonic c-scan technique is very effective method for the sake of the approach to the quantitative measurement of nugget diameter and the discrimination of the corona bond from nugget. Additional support for the above conclusions is provided by the results for galvanized steel. The ultrasonic results for galvanized welds generally correspond to the results for uncoated steel. Finally, it was found that the above-mentioned technique can be sufficiently applied to NDE method for securing the Quality Assurance(QA) of spot welded products in production line.

• Journal of Power System Engineering
• /
• v.17 no.4
• /
• pp.115-119
• /
• 2013

The resistance spot welding of high strength steel degrades the weldability because of its high strength with rich chemical composition and coating layer to protect from corrosion. And the weld Expulsion is prone to occur and severely affect the nugget guality when the initial gap between automatic borrowing galvanied steel sheets(SGARC35) and Zn-coateel trip steels(GA580TRIP and GA980 TRIP) exist in resistance spot welding(RSW). RSW is one of the most popular welding processes used to join sheet metals. but weld guality sometimes do creases due to welding condition. in this paper to verity tue weldability using spot welding with the hemispherically concaved electrode, tensile shear strength and cross-tensile strength were measured by a universal test machine. in addition, the nugget size on cross-sectional area of the weld was observed by optical and electron microscopy. As a result, the nugget size of this specimen is increased with increasing welding current and Max load of tensile-shear strength is increased with welding current is increasing.

• Journal of Welding and Joining
• /
• v.24 no.6
• /
• pp.39-43
• /
• 2006

A ferritic stainless steel, STS430, and a galvanized steel for case and frame of electronic goods are welded by resistance spot welding and resistance projection welding methods. In this study, resistance spot welding has been performed to investigate the weldability of dissimilar materials such as a ferritic stainless steel and a galvanized steel. Tensile load of the spot weld without heat treatment was 196 kN and brittle fracture occurred at interface between STS430 and nugget due to the high hardness, 380 Hv, in nugget. It was found that the hardness of as-welded nugget increased with higher cooling rate during resistance spot welding by comparing with GTA weld of same materials. Heat treatment by applying second current made nugget softened. Tensile load of heat treated weld increased and reached to 303 kN and fracture occurred at base metal, a galvanized steel.

• Journal of the Korean Society for Nondestructive Testing
• /
• v.25 no.3
• /
• pp.209-214
• /
• 2005

Spot welding is the most widely used in automotive and aerospace industries. The quality of weld depends upon the size of nugget between the overlapped steel plates. Recently, the thickness of the steel plates is much thinner and hence, it introduces the smaller size of nugget. Therefore, it is necessary not only to develop the criterion to evaluate the quality of weld but also to obtain the optimal welding conditions for the better performance. In this paper, the steel plates, 0.5 mm through 1.5 mm thickness, have been spot welded at different welding conditions and the nugget sizes are examined by ultrasonic technique (C-scan type). The relationships between the nugget sizes and the weldability have been investigated. The result of ultrasonic technique shows the good agreement with that of the tensile test.

• Journal of the Korean Society for Nondestructive Testing
• /
• v.14 no.2
• /
• pp.112-121
• /
• 1994

This paper discusses the feasibility of ultrasonic C-scan technique for nondestructive evaluation of spot weld quality. Ultrasonic evaluation for spot weld quality was performed by immersion method with the mechanical and the electronic scanning of point-focussed ultrasonic beam(25 MHz). For the sake of the approach to the quantitative measurement of nugget diameter and the discrimination of the corona bond from nugget, preliminary infinitesimal gap experiment by newton ring is tried in order to set up the optimum ultrasonic test condition. Ultrasonic image data obtained were confirmed and compared by optical microscope and SAM(Scanning Acoustic Microscope) observation of the spot-weld cross section. The results show that the nugget diameter can be measured with the accuracy of 1.0mm, and voids included in nugget can be detected to $10{\mu}m$ extent with simplicity and accuracy. Finally, it was found that it is necessary to make a profound study of definite discrimination of corona bond from nugget and the approach of quantitative evaluation of nugget diameter by utilizing the various image processing techniques.