• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.16 no.3
• /
• pp.121-126
• /
• 2006

HVOF thermal spray coating of Co-alloy T800 is progressively replacing the classical hard coatings such as chrome plating because of the very toxic $Cr^{6+}$ ion known as carcinogen causing lung cancer. For the study of the possibility of replacing of chrome plating, the wear properties of HVOF Co-alloy T800 coatings are investigated using the reciprocating sliding tester both at room and at an elevated temperature of $1000^{\circ}F\;(538^{\circ}C)$. The possibility as durability improvement coating is studied for the application to the high speed spindles vulnerable to frictional heat and wear. Wear mechanisms at the reciprocating sliding wear test are studied for the application to the systems similar to the sliding test such as high speed spindles. Wear debris and frictional coefficients of T800 coatings both at room and at an elevated temperature of $1000^{\circ}F\;(538^{\circ}C)$ are drastically reduced compared to those of non-coated surface of parent substrate Inconel 718. This study shows that the coating is recommendable for the durability improvement coatings on the surfaces vulnerable to frictional heat. The sliding surfaces are weared by the mixed mechanisms such as oxidative wear, abrasion by the sliding ball slurry erosion by the mixture of solid particles and small drops of the melts and semi-melts of the attrited particles cavitation by the relative motions among the coating, sliding ball, the melts and semi-melts. and corrosive wear. The oxide particles and the melts and semi-melts play roles as solid and liquid lubricant reducing the wear and friction coefficient.

• Journal of the Korean institute of surface engineering
• /
• v.39 no.5
• /
• pp.240-244
• /
• 2006

Tribaloy 800 (T800) powder is coated on the Inconel 718 substrate by the optimal High Velocity Oxy-Fuel (HVOF) thermal spray coating process developed by this laboratory. For the study of the possibility of replacing of the widely used classical chrome plating, friction, wear properties and sliding wear mechanism of coatings are investigated using reciprocating sliding tester both at room and at an elevated temperature of $1000^{\circ}F\;(538^{\circ}C). Both at room temperature and at $538^{\circ}C$, friction coefficients and wear debris of coatings are drastically reduced compared to those of non-coated surface of Inconel 718 substrate. Friction coefficients and wear traces of both coated and non-coated surfaces are drastically reduced at higher temperature of $538^{\circ}C$ compared with those at room temperature. At high temperature, the brittle oxides such as $CoO,\;Co_3O_4,\;MoO_2,\;MoO_3$ are formed rapidly on the sliding surfaces, and the brittle oxide phases are easily attrited by reciprocating slides at high temperature through complicated mixed wear mechanisms. The sliding surfaces are worn by the mixed mechanisms such as oxidative wear, abrasion, slurry erosion. The brittle oxide particles and melts and partial-melts play roles as solid and liquid lubricant reducing friction coefficient and wear. These show that the coating is highly recommendable for the durability improvement coating on the surfaces vulnerable to frictional heat and wear.

• Journal of Power System Engineering
• /
• v.9 no.2
• /
• pp.57-64
• /
• 2005

This paper is the study on dry sliding wear behavior of carbon fiber reinforced epoxy matrix composites against lay-up orientation. Tests were investigated on the effect of the lay-up orientation, fiber sliding direction, load and sliding velocity when circumstance keep continuously at $21^{\circ}C$, 60%RH. Pin-on-disk dry sliding wear tests for each experimental condition were carried out with a carbon fiber reinforced plastic pin on stainless steel disk in order to search the friction and wear characteristics. The wear rates and friction coefficients against the stainless steel counterpart were experimentally determined and the wear mechanisms were microscopically observed. The effect on friction and wear behavior are observed differently, according to various conditions. When sliding took place against counterpart, the highest wear resistance and the lowest friction coefficient were observed in the $[0]_{24s}$ lay-up orientation at anti-parallel direction.

• Proceedings of the KSME Conference
• /
• 2004.11a
• /
• pp.302-307
• /
• 2004

The major flow-induced vibration mechanisms such as fluid-elastic and turbulence excitation can cause the various types of wear of the steam generator tubes in unclear power plant. It is generally accepted that the tube wear due to vibration is affected by the presence of gap clearance between tube and support plate. Connors showed that the tube wear depth could be estimated by using the relationship between wear volume and sliding distance for contact time. Au-Yang predicted the wear depth by using the nonlinear characteristics of normal work rate to contact time. In this study the effect of gap size on the steam generator tubes wear is analyzed by deriving the wear depth versus normal work rate relationship from these previous results.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.25 no.11
• /
• pp.1720-1729
• /
• 2001

Wear characteristics of Nylon and acetal pinions against steel gears for different pitch line velocities was studied with a power circulating gear test rig under unlubricated condition. Specific wear rate was measured as a function of tooth number, module, tooth width and total revolution. The worn tooth surfaces were examined with a profile projector. The Nylon pinion showed lower specific wear rate than the acetal pinion. However, the Nylon pinion was fractured at high tooth loads, whereas the acetal pinion exhibited a steady wear behavior. The wear characteristics of Nylon pinion varied significantly with the Pitch line velocity. Wear occurred most severely at the tooth tip and the region immediately below the pitch line of pinion. The dominant wear mechanisms were adhesion and abrasion.

• Journal of Mechanical Science and Technology
• /
• v.15 no.9
• /
• pp.1274-1280
• /
• 2001

The fretting wear behavior of the contact between Zircaloy-4 tube and Inconel 600, which are used as the fuel rod cladding and grid, respectively, in PWR nuclear power plants was investigated in air. In the study, number of cycles, slip amplitude and normal load were selected as the main factors of fretting wear. The results indicated that wear increased with load, slip amplitude and number of cycles but was affected mainly by the slip amplitude. SEM micrographs revealed the characteristics of fretting wear features on the surface of the specimens such as stick, partial slip and gross slip which depended on the slip amplitude. It was found that fretting wear was caused by the crack generation along the stick-slip boundaries due to the accumulation of plastic flow at small slip amplitudes and by abrasive wear in the entire contact area at high slip amplitudes.

• Tribology and Lubricants
• /
• v.15 no.2
• /
• pp.212-217
• /
• 1999

The wear characteristics and wear mechanisms of dental composite resins were investigated. Composite resins such as Metafil, Silux Plus, Heliomolar and Palfique Estelite were selected as specimens and contents of filler in specimens in order to evaluate the effect of Prepolymerized Particle Fillers in friction and wear characteristics. Ball on flat wear tester was used for the wear test at room temperature. The friction coefficient of Metafil was quite high relatively, and the wear resistances of Silux Plus and Palfique Estelite were better than that of Metafil and Heliomolar at the same experimental condition. It was found that The main wear mechanism is plastic flow and abrasive wear by failure of filler's bond to the matrix.

• Proceedings of the Korea Committee for Ocean Resources and Engineering Conference
• /
• 2004.05a
• /
• pp.390-394
• /
• 2004

This is the study on dry sliding wear behavior of unidirectional carbon fiber reinforced epoxy matrix composite at ambient temperature. The wear rates and friction coefficients against the stainless steel counterpart specularly processed were experimentally determined and the resulting wear mechanisms were microscopically observed. Three principal sliding directions relative to the dominant fiber orientation in the composite were selected. Wren sliding took place against smooth and hard counterpart, the highest wear resistance and the lowest friction coefficient were observed in the antiparallel direction. When the velocity between the composite and the counterpart went up, the wear rate increased. The fiber destruction and cracking caused fiber bending on the contact surface, which was discovered to be dominant wear mechanism.

• Journal of the Korean Society of Fisheries and Ocean Technology
• /
• v.44 no.3
• /
• pp.250-256
• /
• 2008

Generally the side plate materials of FRP ship are composed of glass fiber and unsaturated polyester resin composites(GFRP composites). In this study, the effect of applied load and sliding speed on friction and wear characteristics of these materials were investigated at ambient temperature by pin-on-disc friction test. The cumulative wear volume, friction coefficient and wear rate of these materials for SiC abrasive paper were determined experimentally. The cumulative wear volume showed a tendency to increase nonlinearly with increase of sliding distance and was dependent on applied load and sliding speed for these composites. The friction coefficient of GFRP composites was increased as applied load increased at same sliding speed in wear test. It was verified by SEM photograph of worn surface that major failure mechanisms were microfracture, deformation of resin, cutting and cracking.

• Tribology and Lubricants
• /
• v.11 no.3
• /
• pp.11-23
• /
• 1995

The friction and wear behavior of $Al_{2}O_{3}$, SiC, and $Si_{3}N_{4}$ under the different sliding conditions were investigated. The cylinder-on-disc wear tester was used for a wear test method. Using the servo-motor, the sliding speed did not alternate due to the frictional forces. Three kinds of loads were selected to watch the variation of the wear rates and the frictional forces under a constant speed. Three kinds of sliding conditions were used to see the effects of the oxidation and the abrasion. The dominant wear mechanisms of $Al_{2}O_{3}$ were the abrasion and the formation of transfer layers. The abrasion has a great effect on the wear of SiC. The wear of $Si_{3}N_{4}$ was due to the asperity-failure and the oxidation. Also, the wear rate of each ceramic is shown to be related to the frictional power provided to the tribological system.