This study was undertaken to investigate the dry wear characteristics and mechanism of KP-4M steel for plastic molding against SKD 61 hardened by heat treatment. The wear test was carried out under different conditions such as sliding speed, contact pressure, sliding distance, with frictional tester of pin on disc type. The wear loss on variation of sliding speed was little in lower speed range below 0.5 m/sec and in higher speed range above 1.5 m/sec,'but wear loss was high in intermediate speed range. The critical sliding speed, which showed the maximum value of specific wear rate, became lower with increased contact pressure. Increasing the contact pressure, the critical sliding distance Lcr which the wear mechanism changes from severe wear to mild wear was increased due to the decrease of oxidation reaction velocity. Through this study we suggested a model of generation and elimination process of wear debris of KP-4M steel for plastic molding.

• Transactions of the Korean Society of Mechanical Engineers
• /
• v.14 no.2
• /
• pp.399-406
• /
• 1990

This paper is studied to know corrosive wear mechanism of STS304 steel on atmospherical temperature against mating material as the same. The corrosive test was carried out by rubbing the annular surface of two test pieces in distilled water and NaCl aqueous solution. The corrosive wear mechanism was investigated by S.E.M. The experimental results show that there is one Lcr transferring from severe wear to mild wear on change of NaCl concentration and atmospherical temperature, and which is the other still remaining in server wear state. It was found that the critical sliding distance Lcr shorten with increasing NaCl concentration but it is longer with ascending atmospherical temperature and the mild wear state still continues under the condition of high generation rate and elimination rate of the corrosive product. Considering upon the result, the model of corrosive wear mechanism is proposed.

• Tribology and Lubricants
• /
• v.20 no.1
• /
• pp.7-13
• /
• 2004

High strength steels are widely used as tribo-materials in the field. Previous study revealed that for mild steel, the states of strain on the worn surface measured by X-ray diffraction has a good relationship with the state of wear. The objective of this study is to identify the relationship between the state of strain on the worn surface and the state of wear in high strength steels. Sliding wear tests were carried out using several hardened steels. X-ray diffraction tests were conducted to analyze the state of strain on the worn surface during wear. The experimental results indicated that the state of strain on worn surface in the hardened steel shows the same tendency as in the mild steel. It is clear that change of half value width on the worn surface as a function of sliding speeds is broadly similar in shape to wear characteristics curve and its magnitude has a good relationship with the wear rate at two different wear modes in the hardened steel.

• Tribology and Lubricants
• /
• v.20 no.3
• /
• pp.125-131
• /
• 2004

Nano-wear behavior of amorphous carbon films was studied by Atomic Force Microscopy. The a-C films are deposited on Si(100) substrate by DC magnetron sputtering method. The influences of different surface roughness on the nano-wear are investigated. Nano-wear tests were carried out using a very sharp diamond coated tip. Its spring constant was 1.6 N/m and radius of curvature was 110 nm. Normal force used in the wear tests ranged 0 to 400 nN. It was found that surface depression occurred during scratching because of plastic deformation and abrasive wear (cutting St ploughing). Wear depth increased linearly with normal force. Changing the surface roughness variables according to the bias pulse control, the less surface roughness decreased the wear depth. The thickness did not affect the wear resistance.

• Tribology and Lubricants
• /
• v.33 no.1
• /
• pp.31-35
• /
• 2017

Recently, international attention has been focused on the development of non-traditional energy resources such as shale gas and oil sands, due to the steep increase in the demand for natural resources. The materials incorporated in an oil gas plant module experience extreme environments, and are prone to various problem such as fracture, corrosion and abrasion due to low-temperature brittleness. In order to improve the plant life, it is necessary to perform characteristics study and performance evaluation of the materials. In particular, this paper explains the main set of materials which are most frequently used in oil sands plant project. In order to investigate wear characteristics, the authors carried out abrasive wear tests of TP 316, stainless steel and SS 400, structural rolled steel. For the analysis of the abrasive wear resistance of an oil sands plant, the authors carried out the test according to ASTM G 105 "Standard Test Method for Conducting Wet Sand/Rubber Wheel Abrasion Test" standard guidelines. The authors have derived the results from the data associated with the loss of mass with respect to wear rate. During the test, for a given wear length for 10,000 revolutions, the rotational speed and applied force of the rubber wheel were varied.

• Journal of the Korean Society of Safety
• /
• v.14 no.4
• /
• pp.126-134
• /
• 1999

In this study, plasma source ion implantation was used to improve the wear properties of biocompatible titanium implant. In order to observe the effect of ion energy and dose on wear property of titanium implant, pin-on-disk type wear tests in Hank's solution were carried out. The friction coefficient of ion implanted specimens were increased from 0.47 to 0.65 under high energy and ion dose conditions. As increasing ion energy and ion dose, the amount of wear was reduced.

• Tribology and Lubricants
• /
• v.19 no.4
• /
• pp.211-216
• /
• 2003

This paper was studied on the corrosion and corrosion-wear behavior of chromium (Cr) plating in the acidic environments. In the various pH of acidic solutions, the electrochemical polarization test and wear-corrosion test of Cr plating were carried out. And thus potential, corrosion current density and corrosion-wear loss behaviour of Cr plating are investigated.

• Transactions of Materials Processing
• /
• v.19 no.6
• /
• pp.357-362
• /
• 2010

Dry sliding wear behavior of pure Fe and Cu which have BCC and FCC crystal structure, respectively, was investigated. The wear characteristics of the pure metals with different crystal structure were compared. Dry sliding wear tests were carried out using a pin-on-disk wear tester at various loads under the constant sliding speed condition of 0.15 m/s against a silica ball at room temperature. Sliding distance was fixed as 600 m for all wear tests. Wear rate of a specimen was calculated by dividing the weight loss of the specimen after the test by the specific gravity and sliding distance. Worn surfaces and wear debris were analyzed by SEM. The wear of both pure Fe and Cu proceeded with surface deformation, resulting in similar wear rates despite of their structure difference under the current test conditions. Wear rates of both metals were low if the surface deformation due to wear forms thick surface-deformation layer that is strain hardened beneath the wearing surface. The pure Cu specimens showed a lot of oxides on the worn surface when tested at low loads less than 5 N, which resulted in very low wear rate.

• International Journal of Costume and Fashion
• /
• v.15 no.2
• /
• pp.19-36
• /
• 2015

The purpose of this study is to research the purchasing behavior according to the pursuit benefit for outdoor wear and to present a direction to outdoor wear. Questionnaire survey was administered to 533 male and female adults in their 30s to 40s living in Seoul and Gyeonggido from May 1 to 15, 2014. Concerning the statistic treatment for data analysis, SPSS for Window 18.0 was used to carry out frequency analysis, factor analysis, reliability test, cluster analysis, ANOVA and Duncan test as post-test. Benefit was drawn out as 4 elements including 'showing off & brand benefit sought', 'fashion benefits sought', 'functionality benefits sought' and 'economic benefits sought'. Group analysis according to benefit showed that it was materialized to 'multiple benefit sought group', 'unconcern group', 'showing off & brand benefit sought group' and 'utility benefit sought group'. There is an academic significance in that this research found out the level of benefit in purchasing outdoor wear and the difference of purchasing behavior by consumer groups according to benefit. This result might be used efficiently by marketers in outdoor clothing industry in classifying consumers and establishing the marketing strategy to deal with it.

• Proceedings of the Korean Society of Tribologists and Lubrication Engineers Conference
• /
• 2004.11a
• /
• pp.306-311
• /
• 2004

The sliding wear characteristics of the crane sheave were investigated using a pin-on-disk rig tester The experiment was conducted using a high carbon steel wire that was upper material, also carbon steel castings and carbon steel for machine structural use that was disk material. There are various operating conditions in this work. At the room temperature, we carried out the wear test under a grease lubrication. The results of wear test showed that carbon steel for machine structural use have lower wear volume, also the wear curves are linearly increased with increasing of sliding velocity The wear mechanism of a disk is the abrasive, adhesion, and fatigue wear under lubrication.