• Journal of the Korea Furniture Society
• /
• v.19 no.3
• /
• pp.172-179
• /
• 2008

The objective of this study was to investigate the influence of the water repellents' treatment on the water absorptivity and the dimensional stability of Korean red pine wood(Pinus densiflora). The alkylketene dimer(AKD), fluororesin emulsion(Wood-seal, WS), and paraffin wax emulsions(PW25, PW40, and PW1200) were used as water repellents. PW40 and WS were proved as excellent water repellents for pine wood, because the samples treated with these agents showed high contact angles and large reduction in water absorptivities. Also, the dimensional stability(antiswelling efficiency) of pine wood was considerably improved by water repellents treatments, such as PW40 and WS at the pressure of 2MPa. The water repellent treated woods with WS, PW40, and PW1200 at the pressure of 2MPa were relatively stable to the wet-dry cyclic leaching test.

• Journal of the Korean Applied Science and Technology
• /
• v.13 no.2
• /
• pp.47-53
• /
• 1996

The procedure to prepare an acrylic emulsion water repellents by blending of arcylic copolymer, activated polyethylene, wax, and emulsifiers was published in the previous paper. After the treatment of the prepared water repellents on a cotton fabrics with and without textile finishing resin, washability, contact angle, tearing strength, and crease recovery were tested. As the result, there were remarkable improvements in physical properties. Proper curing temperature of the synthesized water repellents impellents was $150^{\circ}C$ : proper using concentration was 5wt% : sodium acetate was the best catalyst for water repellents among the used, and proper concentration was 1.0wt%.

• Journal of the Korea Concrete Institute
• /
• v.16 no.4 s.82
• /
• pp.477-484
• /
• 2004

As a part of durability improvement of concrete-structure, penetrating water repellency of liquid type is applied to concrete surface. Besides, a related standard is made recently, but the standard has been prescribe for initial settlement state of penetrating water repellency of liquid type, to the exclusion of performance variation depending time and outdoor environment factor. For measurement of performance variation, we measured the weight of outdoor exposure specimen every regular intervals and check a measured value against a measured value of different condition specimen. Moreover, after the application of penetrating water repellent, measured a adhesive strength in tension between cement-polymer modified waterproof coatings and surface of specimen. The applied penetrating water repellent is a emulsified silicon type with a deep penetration depth. In view of the results so far achieved, the more a Quantity of application and active solid content does get, the deeper penetrating water repellency of emulsion type Penetrate get longer and supplied moisture increase in quantity, a penetrating water repellency of liquid type penetrates more deep, but a quantity of water absorption increase gradually. Perhaps this result is caused by a reduction of active solid content on concrete surface, because active ingredient is moved into the concrete by dissolution.

• Clean Technology
• /
• v.18 no.2
• /
• pp.170-176
• /
• 2012

A series of acrylic copolymers containing perfluoroalkyl acrylate were synthesized by 2-step emulsion polymerization of variety of acrylate monomers (ethyl acrylate, butyl acrylate or methyl methacrylate) with perfluoroalkyl ethyl acrylate (PFA) and glycidyl methacrylate (GMA) monomers. This study focused on effects of monomer compositions (the kind of acrylate monomer, contents of PFA and GMA) and composition of surfactants [(sodium dodecyl sulphate/nonylphenol 10mole ethoxylate (NP-10)] and initiator content on the contact angles and surface free energy. It was found that the copolymer having an optimum composition (BA : 87 wt%, GMA : 8.7 wt% and PFA : 4.3 wt%) was shown to be quite surface active [surface free energy : 19.89 mN/m and contact angles : $103.5^{\circ}$ (water) and $78.7^{\circ}$ (methylene iodide)] in the solid state. This result suggests that the optimal copolymer containing fluorinated monomer synthesized in this study have high potential as a low surface energy material, which may have high oil- and water-repellent surface and have been proposed as acrylic syntan for leather and also as soil-resistant/oil and water repellent coating for textiles and wood etc.

• Journal of the Korean Applied Science and Technology
• /
• v.35 no.2
• /
• pp.502-508
• /
• 2018

The acrylate copolymer having good coating, water-repellent and adhesion properties was designed and prepared. We prepared copolymers with high yield of > 95% using methyl methacrylate(MMA), 2,2,2-trifluoroethyl acrylate (FMA) and 2-hydroxyethyl methacrylate monomers(HEMA) by either bulk or emulsion polymerization techniques. The $^1H-NMR$ spectrum was used to identify chemical structure and DSC and DMA analysis were conducted. As a result, the glass transition temperature decreased by $3^{\circ}C$ as FMA content increased from 5% to 10%, and decreased by $2{\sim}8^{\circ}C$ when HEMA content increased from 5 % to 10 %. The physical properties were measured using Instron and TGA. As FMA or HEMA content increased by 10%, tensile strength decreased from 29 MPa to 22 MPa and Td decreased from $200^{\circ}C$ to $180^{\circ}C$ in both bulk and emulsion. The contact angle relatively decreased as hydrophilic HEMA content increased.

• Polymer(Korea)
• /
• v.29 no.5
• /
• pp.433-439
• /
• 2005

The copolymers were prepared by the emulsion copolymerization of fluoroalky lacrylate-stearylacrylate-m-isopropenyl-${\alpha},\;{\alpha}'$-dimethylbenzyl isocyanate (TMI) in order to obtain water repellent polymers. The respective copolymerization rates of the three monomers considerably depended upon the use of the nonionic emulsifier and the nonionic-cationic mixed emusifier, and the optimum conditions were obtained. The particle sizes of the copolymers were in the range of 105 to 222nm. The particle sizes of the copolymers prepared by the use of the mixed emulsifiers were smaller than those of the copolymers prepared by the use of the nonionic emulsifier. The reactions of both TMI-N-methyl acetamide and TMI-cellobiose did not take place. However, the reaction of TMI-n-butylamine occurred. The water contact angles before and after washing three times for nylon and poly(ethylene terephthalate) (PET) fabrics coated with the copolymer prepared by the use of mixed emulsifier were about $139^{\circ}\;and\;133^{\circ}$ Therefore, the copolymer showed good durable repellency for nylon and PET.