• 한국재료학회지
• /
• 제3권1호
• /
• pp.84-94
• /
• 1993

GFRP복합재료의 피로거동은 하중형식, 재질 및 섬유의 강화구조, 환경적인 인자들의 영향을 크게 받는것으로 알려져 있다. 본 연구에서는GFRP의 피로거동에 미치는 증류수 흡습의 영향을 알아보기 위해 chopped strand glass mat강화 불포화 polyester수지 복합재료의피로특성을 조사하였다. 피로균열은 건조재와 흡습재 모두 피로 cycle초기에 발생하며 그 후 균열성장이 점차 둔화되는 영역과 가속되는 영역으로 나뉘어졌다. 또한 증류수의 흡습은 섬유와 기지재 사이의 결합력을 저하시키며 그로 인해 균영성장방향에 수직인곳에서의 fiber pull-out 발생과 균열성장방향에 있는 섬유들에서의 debonding이 증가하여 피로강도가 저하하였다.

• 상하수도학회지
• /
• 제34권2호
• /
• pp.149-159
• /
• 2020

Cured-in-place-pipe(CIPP) is the most adopted trenchless application for sewer rehabilitation to extend the life of the existing sewer without compromising both direct construction and indirect social costs especially applied in the congested urban area. This technology is globally and domestically known to be the most suitable for partial and full deteriorated pipe structure rehabilitation in a sewer system. The typical design of CIPP requires a significant thickness of lining to support loading causing sewage flow interruption and increasing material cost. This paper presents development of a high strength glass fiber composite lining material for the CIPP application and structural test results. The test results exhibit that the new glass fiber composite lining material has 12 times of flexural strength, 6.2 times of flexural modulus, and 0.5 Creep Retention Factor. These test results can reduce lining design thickness 35% at minimum. Even though taking into consideration extra materials such as outer and inner films for actual field applications, the structural capacity of the composite material significantly increases and it reduces 20 percent or more line thickness as compared to the conventional CIPP. We expect that the newly developed CIPP lining material lowers material costs and minimizes flow capacity reduction, and fully replaceable to the conventional CIPP lining materials.

• 대한환경공학회지
• /
• 제28권6호
• /
• pp.661-666
• /
• 2006

칼슘함량이 낮은 F급 플라이 애쉬와 알칼리 활성화 용액으로 구성된 페이스트의 압축강도 특성에 대한 연구를 수행하였다. 수산화나트륨과 물유리 그리고 물을 혼합하여 제조한 이들 활성화 용액은 매우 높은 $OH^-$ 농도를 가지고 있다. 알칼리 활성화 용액의 조성과 온도는 플라이 애쉬-시멘트 페이스트의 압축강도 발현에 대한 현저한 영향 인자임을 보여주었다. 50 MPa 이상의 압축강도는 플라이 애쉬를 각각 $60^{\circ}C$에서 48시간과 $85^{\circ}C$에서 24시간 양생하여 얻었다. 본 연구결과, F급 플라이 애쉬/NaOH/물유리의 무게 비율 25:8:2와 활성화 용액/플라이 애쉬의 무게 비율 0.6/1.0은 높은 강도를 가진 페이스트를 위한 적정 혼합비율로 나타났다.

• 한국지반환경공학회 논문집
• /
• 제21권11호
• /
• pp.11-20
• /
• 2020

연약지반 차수 및 보강용 그라우트에 대하여 다양한 양생조건에서 초기 및 장기재령에 걸쳐 내구성에 대한 검토를 수행하였다. 그라우트는 물유리계, 급결광물계 및 아크릴고분자계를 대상으로 하였으며, 양생조건은 수도수(청수) 양생, 인공해수 양생 및 대기 양생으로 하고, 시험은 재령별 일축압축강도와 길이변화량 및 중량변화량에 대하여 수행하였다. 인공해수는 MgCl₂와 MgSO₄ 수용액을 각각 제조하여 사용하였다. 급결광물계와 아크릴고분자계는 수도수와 인공해수에서는 내구성에 큰 변화가 없이 안정적으로 양생되는 반면 물유리의 경우 수도수에 비해 인공해수조건에서 매우 급격한 내구성 저하가 발생되었다. 대기 양생조건에서는 모든 경우에서 수도수 양생에 비해 내구성이 저하되는데, 특히 급결광물계와 물유리계에서 중량감소가 각각 약 62% 및 60%로 큰 내구성 저하가 발생되었다.

• 공학논문집
• /
• 제3권1호
• /
• pp.199-205
• /
• 1998

유리병을 대량생산하는 자동 병유리 제병공장에서의 배합공정상 가장 큰 문제점은 원료의 대부분을 차지하는 Cullet Quality Control 이다. 판유리조성은 병유리조성과 차이가 크지만, 판유리 파유리의 조성은 거의 일정하고 순수 판유리 파유리만을 얻을 수 있으므로 Cullet Quality Control이 용이하다. 또한 원료가 저가이므로 원가절감을 달성 할 수는 있으나, 판유리 파유리의 사용량을 용출량 대비 25%이상 증가시키면 조성과 점도의 차이로 인하여 로내 유리물의 유동성이 떨어져 용해로 Bottom 온도가 저하되고 유리의 균질성이 나빠진다. 따라서 용해로의 Dead Corner부분의 Devitrification 발생이 증가하게 되고 유리병의 생산효율을 저하시키는 원인이 된다. 이 문제점을 해결하기 위한 실험을 다음의 3가지 방법으로 실시하여 보았다. 즉 연구를 위하여 용융온도를 높이는 방법과 Booster를 사용하는 방법, Bubbler를 사용하는 방법으로 하였다. 그 결과 Booster 사용시 판유리 파유리 혼입율 90%, Bubbler 사용시 혼입율 70%, 용융온도를 $1480^{\circ}C$에서 $1560^{\circ}C$ 증가시 혼입율 60%로 혼입율을 감소시킬 수 있는 결과를 얻었다. 여기서 용융온도를 증가시키는 방법은 용해로 수명단축과 연료비 상승에 문제점이 있으므로 현실적으로 적용이 불가능한 방법이며, Booster 사용방법은 용해로 Bottom 부위의 용융 유리에 열을 가하여 열대류에 의해 유동성을 증진시키므로 유리의 균질화에는 양호 하나 전기에너지 소비가 많은 단점이 있다. Bubbler 사용방법은 압축공기에 의한 물리적인 대류 증진방법으로 균질화 면에서는 Booster보다는 못하나 가장 경제적인 장점이 있는 방법임을 알 수 있었다.

• 한국세라믹학회지
• /
• 제44권3호
• /
• pp.162-168
• /
• 2007

Silica wet gels were prepared ken water glass ($29\;wt%\;SiO_{2}$) by using Amberlite as a ion exchange resin. After washing in distilled water, the wet gels were further aged in a solution of TEOS/EtOH to strengthen of 3-dimensional network structure. As increase TEOS content in aging solution, BET surface area and porosity of the ambient dried silica aerogels were significantly decreased, and average pore diameter was also decreased 30 nm to -10 nm. Also, higher density and compressive strength were obtained in case of higher TEOS content. This is due to precipitation of $SiO_{2}$ nano particles by TEOS. Hence, TEOS addition plays an important role of both strengthening and stiffness of silica wet gel network. By adding over 30 vol% TEOS, a crack-free monolithic silica aerogel tiles were obtained and its density, compressive strength, and thermal conductivity were shown $0.232g/cm^{3}$, 7.3 MPa, and 0.029 W/mk, respectivly.

• 한국세라믹학회지
• /
• 제34권1호
• /
• pp.13-22
• /
• 1997

은 이온과 구리 이온을 동시에 함유하는 살균용 인산염계 수용성 유리를 용융법으로 제조하였다. 분말상의 유리 시편을 상온의 증류수에 넣어 조성과 시간에 따른 용해 특성을, bulk상 시편에 대해서는 용해 전.후의 표면변화를 각각 관찰하였고, 살균 효과 및 세포독성을 평가하였다. 은 이온:구리 이온=1:1인 조성에서 최대 용해량을 나타내었으며 용해거동은 초기부터 total dissolution이 지배적이었다. 시간의 경과에 따라 용해는 진행이 되지만, 표면에 생성되는 새로운 층은 관찰되지 않았다. Pseudomonas sp, e. coli, staphylococcus aureus, 및 salmonella균에 대한 살균 효과는 용해량의 증가에 따라 증가하여 우수한 살균효과를 나타내었다. L929 세포에 대한 독성 실험 결과, 은 이온의 농도가 10ppm이상에서만 독성을 나타내었다.

• 한국표면공학회지
• /
• 제29권6호
• /
• pp.781-787
• /
• 1996

Silicom oxide films with good water repellency were prepared by rf plasma-enhanced CVD (rf-PECVD) using four kinds of organosilicon compound, which had different number of methyl ($CH_3$) groups, and oxygen as gas sources. The differences in the deposition rates, film composition and film properties were studied in detail. Water repellency depended on the number of $CH_3$ groups in the organosilicon compounds and the partial pressure of oxygen in the plasma. The highest contact angle for water drops, about 95 degrees, was obtained when trimethy lmethoxy silane (TMMOS) was used. The contact angle decreased with the amount of oxygen gas introduced into the plasma. The dissociation of $CH_3$ groups by adding oxygen was comfirmed by Fourier transform infrared spectroscopy(FTIR) and X-ray photoelectron spectroscopy (XPS). The optical properties were estimated by double-beam spectroscopy and ellipsometry. The transmittance of the glass plate coated by the film prepared with tetramethoxy silane (TMOS) was about 90% and the refractive index of film was 1.44. This value was smaller than the refractive index of a glass plate(soda lime glass, refractive index is 1.515) and this film played a role of anti-refractive coating.

• 과학교육연구지
• /
• 제45권3호
• /
• pp.326-335
• /
• 2021

본 연구에서는 무지개의 생성 원리를 분석할 수 있는 무지개 발생 장치를 개발하였다. 무지개는 물방울에 대한 빛의 분산 및 반사와 굴절에 의해 형성되지만, 물방울 한 개로만 무지개를 만들 수 없다. 따라서 본 연구에서는 여러 물방울들이 만드는 빛의 경로를 통해 무지개를 관측할 수 있는 장치를 만들어 무지개 생성 원리에 대해 학생들이 보다 쉽게 이해하도록 하였다. 물방울이 만드는 무지개는 유리구슬을 이용하여 재현하였고, 관찰자의 위치와 광원의 고도 등과 같은 무지개 생성과 관련된 다양한 변인을 변화시키며 무지개를 구현하였다.

• 한국정보디스플레이학회:학술대회논문집
• /
• 한국정보디스플레이학회 2007년도 7th International Meeting on Information Display 제7권2호
• /
• pp.1699-1702
• /
• 2007

We will discuss encapsulation of OLEDs on both flexible and rigid glass substrates. Accelerated testing at 6CC/90RH and 85C/85RH is compared and acceleration factors for OLED and Calcium test samples are discussed.We have tested the stability and performance of our barrier coating to much higher temperatures: up to 140 C. Water Vapor Transmission rates at temperatures from 60 to 140 C are presented. Rates and methods for low cost manufacturing on a large scale are analysed