To perform the permanent disposal of metal hydroxide waste from electro-kinetic decontamination, it is necessary to secure the technology for its solidification. The integrity tests on the fabricated solidification should also meet the criteria of the Korea Radioactive Waste Agency. We carried out the solidification of metal hydroxide waste using cement solidification. The integrity tests such as the compressive strength, immersion, leach, and irradiation tests on the fabricated cement solidifications were performed. It was also confirmed that these requirements of the criteria of Korea Radioactive Waste Agency on these cement solidifications were met. The microstructures of all the cement solidifications were analyzed and discussed.

• 한국세라믹학회지
• /
• 제39권12호
• /
• pp.1133-1137
• /
• 2002

폐콘크리트 미분말과 고로 슬래그를 사용하여 유해 산업폐기물 고화용 시멘트를 제조한 후 수화성상과 압축강도를 평가하고 이 시멘트를 COREX 슬러지에 첨가하여 고화처리 하였다. 폐콘크리트 미분말과 슬래그 미분말을 1:1로 하고 여기에 포틀랜드 시멘트와 반수석고를 각각 10% 첨가하여 만든 고화용 시멘트로 사용 가능한 강도를 발현하고 있었다. 이 시멘트로 COREX 슬러지를 고화한 경우에 7일에서 140 kgf/$cm^2$을 상회하는 강도를 보여 폐슬러지를 고화시켜 안정화하는데 응용할 수 있음을 확인하였다.

• 자원리싸이클링
• /
• 제18권3호
• /
• pp.3-10
• /
• 2009

무기성 산업폐기물을 이용한 $CO_2$ 고형화 연구는 폐콘크리트 시멘트 미분말 등 무기성 산업폐부산물의 성분 중의 CaO 또는 MgO 성분과 지구온난화의 주범인 $CO_2$와 반응시켜 탄소를 안정적으로 고형화시켜 대기 중의 $CO_2$의 발생을 저감시키는 연구이다. 본 고에서는 산업 현장 및 도시에서 발생되는 $CO_2$의 대기 방출을 저감시킴과 동시에 산업폐부산물의 유효 자원화를 위한 $CO_2$ 고형화 연구의 국내외 기술 동향을 파악하고, 이를 통해 한국형 $CO_2$ 저감 및 활용 기술을 제시하고자 한다.

• 방사성폐기물학회지
• /
• 제16권2호
• /
• pp.183-193
• /
• 2018

현재, 한국원자력연구원은 부산 기장에 연구용 원자로(Ki-Jang Research Reactor, KJRR)를 건설 계획하고 있다. 원자로를 운영하면 중 저준위 방사성폐기물이 발생하므로 방사성 폐기물을 안전하게 처리 하는 것이 중요하다. 현재, 다양한 형태의 방사성 폐기물을 처리 할 수 있는 시멘트 고화 방법을 일반적으로 사용하고 있으며, 방사성 폐기물 처분시설 인수 기준(압축 강도, 유리수, 침수 및 침출시험 등)을 만족해야 한다. 특히, 폐기물에 함유된 방사성 세슘이 유출 될 경우 범 국제적인 문제를 야기하므로, 고화체 인수 기준 중에서 침출시험이 가장 중요한 인자이다. 시멘트 고화 방법은 다른 고화 방법 보다 공정이 간단하며 비용이 적게 들지만, 침출 저항성이 낮다. 이에 본 연구는 시멘트 고화체 세슘 침출 저항성 증진을 위하여 기장 연구용 원자로(KJRR) 모사폐액과 대표적인 세슘 흡착제인 제올라이트와 황토를 혼합하여 기장로 모의폐액 시멘트를 제조하였다. 제올라이트와 황토가 시멘트 고화체와 결합되어 있는 것을 SEM-EDS를 통하여 정량적으로 확인하였다. 침출 시험은 ANS 16.1 방법에 의해 90일동안 진행하였다. 기장로 모의폐액 시멘트의 세슘(3000 ppm)을 첨가하여 90일간의 침출시험 후 침출수의 세슘 농도 분석 결과, 제올라이트와 황토가 포함된 모의폐액 시멘트는 제올라이트와 황토를 첨가하지 않은 대조군에 비해 최대 27.90%, 21.08%의 세슘 침출 저항성 정도를 나타내는 것을 확인하였다. 또한, 제올라이트와 황토가 포함된 기장로 모의폐액 시멘트는 인수 기준(압축강도, 유리수 유무, 침수 및 침출 지수)을 통과 하는 것을 확인하였다.

• 방사성폐기물학회지
• /
• 제5권4호
• /
• pp.297-308
• /
• 2007

폐액증발기 농축폐액의 폴리머고화를 위하여 붕산 함유 건조분말에 액상규산나트륨을 과립화제로 활용하여 점적 형태로 분사하고 평균 $2{\sim}4mm$ 크기의 과립을 제조하는 농축폐액 과립화 설비를 제작하였다. 또한 폐수지 폴리머 고형화에 대해 미국 원자력규제위원회(NRC)의 인증을 받은 신규 고화기술을 과립화된 농축폐액에 성공적으로 적용하였다. 상기 고화설비는 기계적인 혼합 대신 중력을 이용한 in-situ 고화처리 방식으로 폐기물의 추가적인 부피증가가 없고 폐기물 적재량을 최대화할 수 있다. 생산된 폴리머 고화체의 성능평가를 위해 화재시험, 압축강도시험, 침출 및 침수시험, 방사선조사시험, 열순환시험을 표준시험법에 따라 수행하였다.

• 한국방사성폐기물학회:학술대회논문집
• /
• 한국방사성폐기물학회 2018년도 춘계학술논문요약집
• /
• pp.192-193
• /
• 2018

• 환경위생공학
• /
• 제18권4호
• /
• pp.36-44
• /
• 2003

The cement-based system among S/S(Solidification/Stabilization) is widely used to treat hazardous wastes. In this study, tannery sludge was solidified to evaluate the stabilization effects of using admixtures in the cement-based S/S. Fly ash as substitute also used to increase the strength of the S/S of hazardous waste. The compressive strength measurement and leaching experiment of chromium metal of solidified mortar were carried out to compare and evaluate the physical and chemical characteristics of solidified hazardous waste sludge. From the result of this study, there was increased of compressive strength by using AEW-3(early-hardening AE water reducing agent), and leaching concentration of chromium became low enough to satisfy the regulatory criteria. The successful solidification for the organic contaminant and heavy metal in hazardous waste should enable to treat by cement-based system using early-hardening AE water reducing admixture and fly ash as substituted cement.

• Advances in environmental research
• /
• 제3권4호
• /
• pp.337-353
• /
• 2014

The determination of the effectiveness of the immobilization of blasting dust (waste generated in galvanic activities) in cement matrix, as well of mechanical, physical and microstructural properties of concrete paving blocks produced with partial replacement of cement was the objective of this work. The results showed that blasting dust has high percentage of silica in the composition and very fine particle size, characteristics that qualify it for replacement of cement in manufacturing concrete blocks. The replacement of Portland cement by up to 5% residues did not cause a significant loss in compressive strength nor increase in water absorption of the blocks. Chemical tests indicated that there is no problem of leaching or solubilization of contaminants to the environment during the useful life of the concrete blocks, since the solidification/stabilization process led to the immobilization of waste in the cement mass. Therefore, the use of blasting dust in the manufacture of concrete paving blocks is promising, thus being not only an alternative for proper disposal of such waste as well as a possibility of saving raw materials used in the construction industry.