• Journal of Welding and Joining
• /
• v.19 no.5
• /
• pp.512-519
• /
• 2001

Sink roll has been used in molten Zn-0.2%Al alloy bath of continuous galvanizing line in sinking and stabilizing process of the steel strip in molten metal bath. In this process, although the scraper scraps off the sink roll surface, the dross compounds is builded up on the sink roll surface and the life time of the sink roll is shorten by the dross compounds. The present study was investigated the application of the spray coating layer on sink roll body for improving durability In molten Zn-0.2%Al alloy. Through the durability tests in molten Zn-0.2%Al alloy with various ceramic and cermet coating layer, the optimum bond and top coating material was obtained. As the results, the system of STS430F base metal, WC-l7Co bond and $ZrO_2-SiO_2$ top coating was clarified to be the best quality of durability in molten Zn-0.2%Al alloy.

• Journal of Powder Materials
• /
• v.7 no.2
• /
• pp.63-70
• /
• 2000

Thermal spray coating process has proven to be effective at producing hard, dense, wear resistance coatings on the relatively mild substrates. Among several spraying techniques, HVOF (High Velocity Oxygen Fuel) and plasma coating processes, which are preferentially used for the wear resistance application such as capstans, have been applied in this study. The effects of pre-treatment, it-process and post-treatment parameters on the wear and mechanical properties of WC+12%Co, Cr3C2 and Al2O3 powder coatings have been investigated and correlated with the microstructures. The results indicated that the carbide coating was more preferable to the oxide coatings and the post-treatments consisting of vacuum annealing and sealing on carbide coatings led to significant improvements in wear resistance, adhesive strength and coating phase stabilization over the other processing techniques in this application.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2007.11a
• /
• pp.171-172
• /
• 2007

초고속용사법(HVOF)은 우수한 강도와 높은 경도를 가지는 치밀한 후막형성이 가능하고 피로특성 및 열충격에 대한 저항성이 양호하여 종래에 사용되어 오던 전기도금등을 통한 표면처리 방법을 대체시키고 있다. 항공기엔진의 주요부품, 초고속 air bearing spindle등의 내구성향상을 위한 WC계 분말을 이용한 표면처리의 공정을 다구찌실험계획법을 이용해 최적조건을 선정하였다.

• Journal of Welding and Joining
• /
• v.18 no.3
• /
• pp.51-59
• /
• 2000

Sink roll has been used in molten 55%Al-Zn alloy bath of continuous galvanizing line for sinking and stabilizing working steel strip in molten metal bath. In the process, the sink roll body inevitably build up dross compounds and pitting on the sink roll surface during 55%Al-Zn alloy coated strip production, and the life time of the sink roll is shorten by build up dross compounds and pitting. The present study examined the application of thermally sprayed ceramic coatings method on sink roll body for improving erosion resistance at molten 55% Al-Zn pool. In this experiment, the stainless steels such as STS 316L and STS 430F were used as the substrate materials. The CoNiCr and WE-Co powder were selected as bond coating materials. Moreover $Al_2O_3-ZrO_2-SiO_2 and ZrO_2-SiO_2$ powders selected as the top coating materials. Appearances of the specimens before and after dipping to molten 55%Al-Zn pool were compared and analyzed. As a result of this study, STS430F of substrate, WC-Co of bond spray coatings, $ZrO_2-SiO_2$ power of top spray coatings is the best quality in erosion resistance test at molten 55%Al-Zn pool

• Transactions of the Korean Society of Machine Tool Engineers
• /
• v.15 no.1
• /
• pp.49-55
• /
• 2006

The effect of coating temperature with regard to surface properties of TiN-coated layer on hard metal(WC-Co) are experimentally investigated. Hardness, surface roughness, TiN coating thickness and adsorption force were measured in order to evaluate the effect of coating temperature. The two-way ANOVA method is used in order to evaluate the experimental data. In AIP processing, It is concluded that the furnace temperature in the range of $400^{\circ}C\~500^{\circ}C$ affected to a little increasing the number of production with the coating temperature.

• Journal of the Korean Vacuum Society
• /
• v.15 no.1
• /
• pp.110-116
• /
• 2006

The mechanical property and cutting performance of the cutting tools coated with nanoscale nyktukatered nitride film have been investigated. $Ti_{0.54}Al_{0.46}N-CrN$ and $Ti_{0.84}Al_{0.16}N-NlN$ systems, which showed super-lattice in nanoscale multilayered coating, were deposited on WC-Co insert by UBM sputtering, The superlattice coatings with different bilayer periods were manufactured by controlling deposition parameters. The superlattice formation and hardness of the nanoscale multilayered nitride film and the cutting performance of the insert coated with the film were examined. The hardness and cutting performance were dependent on the bilayer periods of the coatings. The flank wear of the inserts with superlattice coatings were decreased over $20\%$, compared to those of commonly used cutting tools coated with TiAIN single phase.

• Journal of the Korean institute of surface engineering
• /
• v.36 no.2
• /
• pp.116-121
• /
• 2003

Ti-Si-N coating layers were deposited onto WC-Co substrates by a hybrid system of arc ion plating (AIP) and sputtering techniques. The tribological behaviors of Ti-Si-N coating layers with various Si contents were investigated by the dry sliding wear experiments, which were conducted at three different sliding speeds, 0.1, 0.3, 0.5 m/s, against the steel and alumina balls. In the case of steel ball, the average friction coefficient slightly decreased with increasing the sliding speed regardless of Si content due to adhesive wear behavior between coating layer and steel ball. At constant sliding speed, the average friction coefficient decreased with increase of Si content. On the contrary, in the case of alumina ball, the average friction coefficient increased with increasing the sliding speed regardless of Si content, indicating that the abrasive wear behavior was more dominant when the coating layers slide against alumina ball. Through these experimental results, it was found that the tribological behaviors of Ti-Si-N coating layers were effected by factors such as Si content, sliding speed, and kinds of counterpart materials rather than the hardness of coating layer.

• Korean Journal of Materials Research
• /
• v.18 no.10
• /
• pp.558-563
• /
• 2008

TiAlN films were deposited on WC-5Co substrates with different buffer layers by D.C. magnetron sputtering. The films were evaluated by microstructural observations and measuring of preferred orientation, hardness value, and adhesion force. As a process variable, various buffer layers were used such as TiAlN single layer, TiAlN/TiAl, TiAlN/TiN and TiAlN/CrN. TiAlN coating layer showed columnar structures which grew up at a right angle to the substrates. The thickness of the TiAlN coating layer was about $1.8{\mu}m$, which was formed for 200 minutes at $300^{\circ}$. XRD analysis showed that the preferred orientation of TiAlN layer with TiN buffer layer was (111) and (200), and the specimens of TiAlN/TiAl, TiAlN/CrN, TiAlN single layer have preferred orientation of (111), respectively. TiAlN single layer and TiAlN/TiAl showed good adhesion properties, showing an over 80N adhesion force, while TiAlN/TiN film showed approximately 13N and the TiAlN/CrN was the worst case, in which the layer was destroyed because of high internal residual stress. The value of micro vickers hardness of the TiAlN single layer, TiAlN/TiAl and TiAlN/TiN layers were 2711, 2548 and 2461 Hv, respectively.

• Transactions of the Korean Society of Automotive Engineers
• /
• v.14 no.4
• /
• pp.99-106
• /
• 2006

High velocity oxygen-fuel thermal spray coating of the WC-Co cermet material is a well-established process for modifying the surface properties of the structural components exposed to the corrosive and wear attacks, and also these coating are well-known method to improve the fatigue strength of material. In this study, HVOF coated SM490B are prepared to evaluation of the effect of coating on tension and fatigue crack growth behavior. The pre-crack of the fatigue crack growth test specimens machined at deposited material area, heat affected zone and boundary, respectively. Through these test, the following results are obtained: 1) Tensile strength was about 498 MPa, and fracture occurred on base metal area. 2) The fatigue crack of coated specimens propagated more rapidly than non-coated specimen in all specimens. 3) In the same coating thickness specimens, the specimens with pre-crack at boundary more rapidly propagated than the specimens with pre-crack at HAZ and deposited material area. These results can be used as basic data in a structural integrity evaluation of rolled SM490B weldments considering HVOF coating.

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 2005.10a
• /
• pp.178-181
• /
• 2005

Quaternary Ti-Si-C-N coatings were deposited on WC-Co substrates by a hybrid coating system of arc ion plating (AIP) and sputtering techniques using Ti and Si targets, in an $Ar/N_2/CH_4$ gaseous mixture. The crystallinity, bending status, and microstructure of the Ti-Si-C-N coatings were measured by X-ray diffractometer (XRD) and X-ray photoelectron spectroscope (XPS), The micro-hardness of Ti(C,N) and Ti-Si-N coatings were about 30 and 40 GPa, respectively. As the Si was incorporated into Ti(C,N) coatings, the Ti-Si-C-N coatings having Si content of $8.9\;at.\%$ showed the maximum hardness value of about 55 GPa. In this work, the microstructure and mechanical properties of Ti-Si-C-N coatings were systematically investigated.