• 한국분말재료학회지
• /
• 제25권3호
• /
• pp.240-245
• /
• 2018

This study focuses on the fabrication of a WC/Co composite powder from the oxide of WC/Co hardmetal scrap using solid carbon in a hydrogen gas atmosphere for the recycling of WC/Co hardmetal. Mixed powders are manufactured by mechanically milling the oxide powder of WC-13 wt% Co hardmetal scrap and carbon black with varying powder/ball weight ratios. The oxide powder of WC-13 wt% Co hardmetal scrap consists of $WO_3$ and $CoWO_4$. The mixed powder mechanically milled at a lower powder/ball weight ratio (high mechanical milling energy) has a more rapid carbothermal reduction reaction in the formation of WC and Co phases compared with that mechanically milled at a higher powder/ball weight ratio (lower mechanical milling energy). The WC/Co composite powder is fabricated at $900^{\circ}C$ for 6 h from the oxide of WC/Co hardmetal scrap using solid carbon in a hydrogen gas atmosphere. The fabricated WC/Co composite powder has a particle size of approximately $0.25-0.5{\mu}m$.

• 한국분말재료학회지
• /
• 제11권2호
• /
• pp.111-117
• /
• 2004

The oxidation behavior of 91 WC-9Co hardmetal in weight percentage has been studied in the present work as a part of the development of recycling process. The morphological and compositional changes of the WC-Co hardmetal with oxidation time at 90$0^{\circ}C$ were analyzed by using surface observation and X-ray diffraction. respective]y. As the oxidation time increased, the WC-Co hardmetal was continuously expanded to form porous oxide mixtures of $CoWO_4$ and $WO_3$. The morphology of porous oxide mixture was basically dependent on initial shape of the WC-Co hardmetal. From thermo-gravimetric (TG) analysis, it was found that the oxidation rate was increased with increasing oxidation temperature and oxygen content in the flowing atmospheric gas. The fraction of oxidation versus time curves showed S-curve relationship at a given of oxidation temperature. These oxidation behaviors of the WC-Co hardmetal were discussed in terms of previously proposed kinetic models.

• 한국분말재료학회지
• /
• 제12권2호
• /
• pp.112-116
• /
• 2005

In the present study, the focus is on the analysis of carbothermal reduction of oxide powder prepared from waste WC/Co hardmetal by solid carbon under a stream of argon for the recycling of the WC/Co hard-metal. The oxide powder was prepared by the combination of the oxidation and crushing processes using the waste $WC-8 wt.\%Co$ hardmetal as the raw material. This oxide powder was mixed with carbon black, and then this mixture was carbothermally reduced under a flowing argon atmosphere. The changes in the phase structure and gases discharge of the mixture during carbothermal reduction was analysed using XRD and gas analyzer. The oxide powder prepared from waste $WC-8wt.\%Co$ hardmetal has a mixture of $WO_{3} and CoWO_{4}$. This oxide powder reduced at about $850^{\circ}C$, formed tungsten carbides at about $950^{\circ}C$, and then fully transformed to a mixed state of tungsten carbide (WC) and cobalt at about $1100^{\circ}C$ by solid carbon under a stream of argon. The WC/Co composite powder synthesized at $1000^{\circ}C$ for 6 hours from oxide powder of waste $WC-8wt.\%Co$ hardmetal has an average particle size of $0.3 {\mu}m$.

• 한국분말재료학회지
• /
• 제23권5호
• /
• pp.372-378
• /
• 2016

This study focuses on the development of an alkaline leaching hydrometallurgy process for the recovery of tungsten from WC/Co hardmetal sludge, and an examination of the effect of the process parameters on tungsten recovery. The alkaline leaching hydrometallurgy process has four stages, i.e., oxidation of the sludge, leaching of tungsten by NaOH, refinement of the leaching solution, and precipitation of tungsten. The WC/Co hardmetal sludge oxide consists of $WO_3$ and $CoWO_4$. The leaching of tungsten is most affected by the leaching temperature, followed by the NaOH concentration and the leaching time. About 99% of tungsten in the WC/Co hardmetal sludge is leached at temperatures above $90^{\circ}C$ and a NaOH concentration above 15%. For refinement of the leaching solution, pH control of the solution using HCl is more effective than the addition of $Na_2S{\cdot}9H_2O$. The tungsten is precipitated as high-purity $H_2WO_4{\cdot}H_2O$ by pH control using HCl. With decreasing pH of the solution, the tungsten recovery rate increases and then decrease. About 93% of tungsten in the WC/Co hardmetal sludge is recovered by the alkaline leaching hydrometallurgy process.

• 한국분말야금학회:학술대회논문집
• /
• 한국분말야금학회 2006년도 Extended Abstracts of 2006 POWDER METALLURGY World Congress Part 1
• /
• pp.334-335
• /
• 2006

WC/WC interface in VC mono-doped WC-10mass%Co submicro-grained hardmetals of $0.5\;{\mu}m$ was investigated together with WC/Co interface by using HRTEM and XMA. The thickness of V-rich layer and the analytical value of V at WC/WC interface were almost the same as those at WC/Co interfaces. These results, etc., suggested that the V-rich layers at both interfaces were not generated by an equilibrium segregation mechanism in the sintering stage, but generated by a preferential precipitation mechanism during the solidification of Co liquid phase in the cooling stage. Based on this suggestion, we succeeded in developing a nano-grained hardmetal with 100 nm $(0.1\;{\mu}m)$.

• 한국분말야금학회:학술대회논문집
• /
• 한국분말야금학회 2006년도 Extended Abstracts of 2006 POWDER METALLURGY World Congress Part 1
• /
• pp.344-345
• /
• 2006

The linear intercept (LI) method was used to quantitatively measure the intercepts of WC grains in nano-grained WC-10Co hardmetal. When the surveyed intercept numbers of WC grain exceeded 200, the statistic data for the mean grain size of WC were reproduced. The discriminative minimal grain size of used LI method was 12 nm; the maximum intercept of WC grain was 109 nm; the average intercept of WC grains was 45 nm and the corresponding 3D mean grain size of WC was 70 nm which is agreeable with the XRD outcome.

• 한국분말재료학회지
• /
• 제9권4호
• /
• pp.273-279
• /
• 2002

In this study, the WC-10 wt.%Co nanopowders doped by grain growth inhibiter were produced by three different methods based on the spray conversion process. Agglomerated powders with homeogenous distribution of alloying elements and with internal particles of about 100-200 nm in diameter were synthesized. The microstructural changes and sintering behavior of hardmetal compacts were compared with doping method and sintering conditions. The microstructure of hardmetals was very sensitive to doping methods of inhibitor. Nanostructured WC-Co hardmetal powder compacts containing TaC/VC doped by chemical method instead of ball-milling shown superior sintering densification, and the microstructure maintained ultrafine scale with rounded WC particles.

• 한국재료학회:학술대회논문집
• /
• 한국재료학회 2003년도 추계학술발표강연 및 논문개요집
• /
• pp.35-35
• /
• 2003

• 한국분말재료학회지
• /
• 제14권5호
• /
• pp.315-319
• /
• 2007

Pure WC or WC with low Co concentration less than 0.5 wt.% is studied to fabricate high density WC/Co cemented carbide using vacuum sintering and post HIP process. Considering the high melting point of WC, it is difficult to consolidate it without the use of Co as binder. In this study, the effect of lower Co addition on the microstructure and mechanical properties evolution of WC/CO was investigated. By HIP process after vacuum sintering, hardness and density was sharply increased. The hardness values was $2,800kgf/mm^2$ using binderless WC.

• 자원리싸이클링
• /
• 제19권4호
• /
• pp.41-50
• /
• 2010

초경공구의 제조공정에서 발생하는 WC-Co 초경합금 슬러지로부터 텅스텐의 순환활용을 위한 기초연구가 수행되었다. 왕수를 사용하여 슬러지로부터 코발트를 침출함과 동시에 탄화텅스텐을 텅스텐산으로 변환시켜 회수하였다. 왕수농도, 반응온도와 시간, 광액농도 등이 코발트의 침출과 텅스텐산의 생성에 미치는 영향을 조사하였으며 최적조건을 도출하였다. 왕수농도 100 vol.%, 반응온도 $100^{\circ}C$, 반응시간 60분에서슬러지의 광액농도가 400 g/L에 도달할 때 까지 슬러지로부터 코발트의 완전한 추출이 이루어졌으나, 슬러지에 존재하는 모든 탄화텅스텐이 텅스텐산으로 완전히 전환되는 것은 광액농도가 150 g/L 이하일 때 이었다. 생성된 텅스텐산을 암모니아 용액에 용해함으로서 금속 불순물들을 불용성 잔사로 제거하는 것이 가능하였다. 증발결정 공정을 통하여 정제된 암모늄 텅스테이트 용액으로부터 99.85%의 순도를 가지는 암모늄 파라텅스테이트($(NH_4)_{10}{\cdot}H_2W_{12}O_{42}{\cdot}4H_2O$)를 얻을 수 있었다.