• 한국해양공학회지
• /
• 제22권6호
• /
• pp.46-51
• /
• 2008

The effect of the addition of Co and N and subzero treatment on tensile strength and damping capacity was investigated in Fe-Cr-Mn alloy. Austenite was transformed into martensite by cold rollins increasing the degree of cold rollins led to an increase in the volume fraction of martensite. The damping capacity linearly increased with increasing volume fraction of ${\varepsilon}$ martensite in cold rolled specimens and subzero treated specimens after cold rolling. The volume fraction of ${\varepsilon}$ martensite, tensile strength and damping capacity was also increased by the addition of Co, while this treatment decreased the elongation. However, the volume fraction of ${\varepsilon}$ martensite, elongation and damping capacity were reduced by the addition of N, although the tensile strength increased. Tensile strength and damping capacity werealso increased by subzero treatment, while elongation decreased.

• 열처리공학회지
• /
• 제34권3호
• /
• pp.116-121
• /
• 2021

This study was carried out to investigate the effect of transformation induced martensite on the tensile properties of Fe-20Mn-12Cr-3Ni-3Si alloy. α' and ε-martensite were formed by cold rolling, and these martensite were formed with according to the specific direction, surface relief and partially intersection. With an increasing degree of cold rolling, amount of α'-martensite was slowly increased, whereas amount of ε-martensite was rapidly increased. Volume fraction of ε-martensite formed by cold working was large than α'-martensite. Tensile strength was rapidly increase and elongation was rapidly decreased with an increasing of degree of cold rolling. This means that tensile strengh and elongation was greatly influenced by the volume fraction of ε-martensite formed by cold rolling then α'-martensite.

• 열처리공학회지
• /
• 제32권2호
• /
• pp.61-67
• /
• 2019

This study was carried out to investigate the effect of thermo-mechanical treatment on the tensile properties of Fe-20Mn-12Cr-3Ni-3Si alloy with deformation induced martensite transformation. ${\alpha}^{\prime}$ and ${\varepsilon}$-martensite, dislocation, stacking fault were formed, and grain size was refined by thermo-mechanical treatment. With the increasing cycle number of thermo-mechanical treatment, volume fraction of ${\varepsilon}$ and ${\alpha}^{\prime}$-martensite, dislocation, stacking fault were increased, and grain size decreased. In 5-cycle number thermo-mechanical treated specimens, more than 10% of the volume fraction of ${\varepsilon}$-martensite and less than 3% of the volume fraction of ${\alpha}^{\prime}$-martensite were attained. Tensile strength was increased and elongation was decreased with the increasing cycle number of thermo-mechanical treatment. Tensile properties of thermo-mechanical treated alloy with deformation induced martensite transformation was affected to formation of martensite by thermo-mechanical treatment, but was large affected to increasing of dislocation and grain refining.

• 한국재료학회지
• /
• 제30권6호
• /
• pp.315-320
• /
• 2020

This study deals with the yielding behavior and strain aging properties of three bake hardening steels with dual-phase microstructure, fabricated by varying the annealing temperature. Bake hardening and aging tests are performed to examine the correlation of martensite volume fraction with yielding behavior and strain aging properties of the bake hardening steels with dual-phase microstructure. The volume fraction of martensite increases with increasing annealing temperature. Room-temperature tensile test results show that the yielding behavior changes from discontinuous-type to continuous-type with increasing volume fraction of martensite due to higher mobile dislocation density. According to the bake hardening and aging tests, the specimen with the highest fraction of martensite exhibited high bake hardening with low aging index because solute carbon atoms in ferrite and martensite effectively diffuse to dislocations during the bake hardening test, while in the aging test they diffuse at only ferrite due to lower aging temperature.

• 한국해양공학회지
• /
• 제27권4호
• /
• pp.9-13
• /
• 2013

The tensile properties of high manganese austenitic stainless steel with the two phase structures of deformation-induced martensite and reversed austenite were studied. Reversed austenite with an ultra-fine grain size of less than $0.3{\mu}m$ was obtained by reversion treatment. The two phases structures of deformation-induced martensite and reversed austenite were obtained by an annealing treatment in the range of $500^{\circ}C-700^{\circ}C$ for various times in 70% cold- rolled high-manganese austenitic stainless steel. The volume fraction of the reversed austenite increased rapidly with increases in the annealing temperature and time. In the stainless steel with the two phases of austenite and martensite, the strength decreased rapidly, while the elongation increased slowly and then rapidly increased with an increase in the volume fraction of the reversed austenite. Therefore, the strength and elongation were strongly controlled by the volume fraction of reversed austenite. A good combination of high strength and elongation could be obtained by the mixed structure of reversed austenite and deformation-induced martensite.

• 대한기계학회논문집
• /
• 제10권3호
• /
• pp.316-325
• /
• 1986

본 연구에서는 이상배합조직강에 있어서 피로균열진전거동의 미시조직 의존 성을 밟히기 위하여 제이상 마르텐사이트가 모상 페라이트를 둘러싼 마르텐사이트페라 이트 복합조직강을 준비하고 미시조직이 각각 다른 4종류의 시험편에 대하여 피로시험 을 실시한후 이에 의해 얻어진 피로균열진전속도를 균열휨과 균열닫힘을 통하여 검토 하였다.

• 한국재료학회지
• /
• 제28권3호
• /
• pp.129-134
• /
• 2018

This study was carried out to investigate the effect of grain size on the damping capacity of the Fe-26Mn-4Co-2Al damping alloy. ${\alpha}^{\prime}$ and ${\varepsilon}-martensite$ were formed by cold working, and these martensites were formed with a specific direction and surface relief. With an increase in grain size, the volume fraction of ${\alpha}^{\prime}$ and ${\varepsilon}-martensite$ increased by decrement the austenite phase stability. This volume fraction more rapidly increased in cold-rolled specimen than in the specimen that was not cold-rolled. The damping capacity also increased more with the augmentation an increased grain size and more rapidly increased in cold-rolled specimen than in the specimen that was not cold rolled. The effect of grain size on the damping capacity was larger in the cold-rolled specimen than the specimen that was not cold-rolled. Damping capacity linearly increased with an increase in volume fraction of ${\varepsilon}-martensite$. Thus, the damping capacity was affected by the ${\varepsilon}-martensite$.

• 동력기계공학회지
• /
• 제9권1호
• /
• pp.70-75
• /
• 2005

The damping property of Fe-12Cr-22Mn-X alloys has been investigated to develop high damping and high strength alloy. Particularly, the effect of the phase of austenite, alpha and epsilon martensite, which constitute the structure of the alloys Fe-12Cr-22Mn-X alloys, on the damping capacity at room temperature has been investigated. Various fraction of these phases were formed depending on the alloy element and cold work degree. The damping capacity is strongly affected by ${\varepsilon}$ martensite while the other phase, such as ${\alpha}'$ martensite, actually exhibit little effect on damping capacity. In case of Fe-12Cr-22Mn-3Co alloy, the large volume fraction of ${\varepsilon}$ martensite formed at about 30% cold rolling, and in case of Fe-12Cr-22Mn-1Ti alloy, formed at about 20% cold rolling and showed the highest damping capacity. Damping capacity showed higher value in Fe-12Cr-22Mn-1Ti alloy than one in Fe-12Cr-22Mn-3Co alloy.

• 한국주조공학회지
• /
• 제8권3호
• /
• pp.310-321
• /
• 1988

This study is aimed to investigate the effects of the multi-phase(ferrite-bainite-martensite) on the strengthening and toughening in ductile cast iron. All the specimen were austenitized at eutectoid transformation temperature range(${\alpha}+{\gamma}$) for 1hr and austempered at $300^{\circ}C$ and $400^{\circ}C$ for various holding time, and then quenched in iced water for multi - phase (${\alpha}-B-M$). When the volume fraction of martensite is below 15%, excellent maximum fracture load can be obtained due to strengthening by the fine martensite, but, with increasing of volume fraction over 15%, it was decreased drastically. The martensite size became finer and the shape of it changed from bar to spherical type with increasing of austempering holding time. The higher the austenitizing temperature is, the more preferential is the formation of austenite phase around the graphite nodules improving strength and toughness of austempered ductile cast iron.

• 한국재료학회지
• /
• 제28권10호
• /
• pp.583-589
• /
• 2018

This study investigates the effect of fatigue stress on the damping capacity in a damaged Fe-22Mn-12Cr-3Ni-2Si-4Co damping alloy under fatigue stress. ${\alpha}^{\prime}$ and ${\varepsilon}-martensite$ forms by fatigue stress in the damaged Fe-22Mn-12Cr-3Ni-2Si4-Co damping alloy under fatigue stress. The ${\alpha}^{\prime}$ and ${\varepsilon}-martensite$ forms with the specific direction and surface relief, or they cross each other. With an increasing fatigue stress, the volume fraction of ${\alpha}^{\prime}-martensite$ and ${\varepsilon}-martensite$ increases. With an increasing fatigue stress, the damping capacity increases with an increase in the volume fraction of ${\varepsilon}-martensite$. The increase in the damping capacity in the damaged Fe-22Mn-12Cr-3Ni-2Si-4Co alloy under fatigue stress strongly affects the increase of ${\varepsilon}-martensite$ formed by fatigue stress, but the damping capacity of the damaged Fe-22Mn-12Cr-3Ni-2Si-4Co damping alloy under fatigue stress is strongly controlled by a large amount of ${\alpha}^{\prime}-martensite$.