• 한국재료학회:학술대회논문집
• /
• 한국재료학회 2003년도 춘계학술발표강연 및 논문개요집
• /
• pp.83-83
• /
• 2003

The stochiometric mix of evaporating materials for the CuInSe$_2$ single crystal thin films was prepared from horizontal furnace. To obtain the single crystal thin films, CuInSe$_2$ mixed crystal was deposited on thoroughly etched semi-insulating GaAs(100) substrate by the Hot Wall Epitaxy (HWE) system. The source and substrate temperature were 62$0^{\circ}C$ and 41$0^{\circ}C$, respectively. The crystalline structure of single crystal thin films was investigated by the photoluminescence and double crystal X-ray diffraction (DCXD). The carrier density and mobility of CuInSe$_2$ single crystal thin films measured from Hall effect by van der Pauw method are 9.62$\times$10$^{16}$ cm$^{-3}$ , 296 $\textrm{cm}^2$/V.s at 293 K, respectively From the photocurrent spectrum by illumination of perpendicular light on the c-axis of the CuInSe$_2$ single crystal thin film, we have found that the values of spin orbit splitting ΔSo and the crystal field splitting ΔCr were 6.1 meV and 175.2 meV at 10 K, respectively. From the photoluminescence measurement on CuInSe$_2$ single crystal thin film, we observed free excition (Ex) existing only high quality crystal and neutral bound exiciton (D$^{\circ}$,X) having very strong peak intensity. Then, the full-width-at -half-maximum(FWHM) and binding energy of neutral donor bound excition were 7 meV and 5.9 meV, respectivity. By Haynes rule, an activation energy of impurity was 59 meV.

• 한국결정성장학회지
• /
• 제9권2호
• /
• pp.197-206
• /
• 1999

수평 전기로에서 $AgInSe_2$다결정을 합성하여 HWE(Hot Wall Epitaxy) 방법으로 $AgInSe_2$ 단결정 박막을 반절연성 GaAs(100) 위에 성장하였다. $AgInSe_2$단결정 박막은 증발원과 기판의 온도를 각각 $610^{\circ}C$, $450^{\circ}C$로 성장하였다. 이때 성장된 단결정 박막의 두께는 3.8$\mu\textrm{m}$였다. 단결정 박막의 결정성의 조사에서 20 K에서 측정한 광발광 스펙트럼은 884.1nm(1.4024eV) 근처에서 excition emission 스펙트럼이 가장 강하게 나타났으며, 또한 이중결정 X-선 회절곡선(DCXD)의 반폭치(FWHM)도 125arcsec로 매우 작은 값으로 측정되어 최적 성장 조건임을 알 수 있었다. Hall 효과는 van der Pauw 방법에 의해 측정되었으며, 온도에 의존하는 운반자 농도와 이동도는 293K에서 각각 $9.58{\times}10^{22} electron/m^3,\; 3.42{\times}10^{-2}m^2/V{\cdot}s$였다. $AgInSe_2$단결정 박막의 광전류 단파장대 봉우리들로부터 20K에서 측정된 $\Delta$Cr(Crystal field splitting)은 0.12eV, $\Delta$So(spin orbit coupling)는 0.29 eV였다. 20K에서 얻어진 광발광 봉우리들 중에서 881.1nm(1.4071 eV)와 882.4nm(1.4051 eV)는 free exciton$E_x$의 upper polariton과 lower polariton인$E_x^U$와 $E_x^L$를 의미하며, 884.1nm(1.4024 eV)는 donor-bound exciton emission에 의한 $I_2$봉우리를, 885.9nm(1.3995 eV)는 acceptor-bound exciton emission에 의한 $I_1$ 봉우리를 각각 나타내었다. 또한 887.5nm(1.3970 eV)에서 관측된 봉우리는 DAP(donor-acceptor pair)에 기인하는 광발광 봉우리로 해석되었다.

• 한국결정성장학회지
• /
• 제11권4호
• /
• pp.138-147
• /
• 2001

수평 전기로에서 $ZnIn_{2}S_{4}$ 다결정을 합성하여 HWE(Hot Wall Epitaxy)방법으로 $ZnIn_{2}S_{4}$ 단결정 박막을 반절연성 GaAs(100) 기판 위에 성장시겼다. $ZnIn_{2}S_{4}$ 단결정 박막은 증발원의 온도를 $610^{\circ}C$, 기판의 온도를 $450^{\circ}C$로 성장시켰고 성장 속도는 0.5$\mu\textrm{m}$/hr로 확인되었다. $ZnIn_{2}S_{4}$ 단결정 박막의 결정성의 조사에서 $10^{\circ}$K에서 광발광 (photoluminescence) 스펙트럼이 433nm (2.8633 eV)에서 exciton emission 스펙트럼이 가장 강하게 나타났으며, 또한 이중결정 X-선 요동곡성 (DCRC)의 반폭치(FWHM)도 133 arcsec로 가장 작아 최적 성장 조건임을 알 수 있었다. Hall 효과는 van der Pauw 방법에 의해 측정되었으며, 온도에 의존하는 운반자 농도와 이동도는 $293^{\circ}$K에서 각각 $8.51{\times}10^{17}electron{\textrm}{cm}^{-3}$, 291$\textrm{cm}^2$/V-s 였다. $ZnIn_{2}S_{4}$ 단결정 박막의 광전류 단파장대 봉우리들로부터 $10^{\circ}$K에서 측정된 ${\Delta}$Cr(crystal field splitting)은 0.1678 eV, ${\Delta}$So (spin orbit coupling)는 0.0148eV였다. $10^{\circ}$K의 광발광 측정으로부터 고품질의 결정에서 볼 수 있는 free exciton 과 매우 강한 세기의 중성 주개 bound exciton 등의 피크가 관찰되었다. 이때 증성 주개 bound exciton 의 반치폭과 결합 에너지는 각각 9meV와 26meV였다. 또한 Haynes rule에 의해 구한 불순물의 활성화 에너지는 130meV였다.

• 한국결정성장학회지
• /
• 제10권3호
• /
• pp.189-198
• /
• 2000

수평전기로에서 $CuGaSe_2$다결정을 합성하여 HWE(Hot Wall Epitaxy) 방법으로 $CuGaSe_2$단결정 박막을 반절연 성 GaAs(100)기판 위에 성장하였다. $CuGaSe_2$단결정박막은 증발원의 온도를 $610^{\circ}C$, 기판의 온도를 $450^{\circ}C$로 성장하였다. 이때 성장된 단결정 박막의 두께는 2.1$\mu\textrm{m}$였다. 단결정 박막의 결정성의 조사에서 20K에서 광발광(photoluminescence) 스펙트럼이 672.6nm(1.8432 eV)에서 exciton emission 스펙트럼이 가장 강하게 나타났으며, 또한 이중결정 X-선 요동곡선(DCRC)의 반폭치(FWHM)도 138 arcsec로 가장 작아 최적 성장 조건임을 알 수 있었다. Hall 효과는 van der Pauw 방법에 의해 측정되었으며, 온도에 의존하는 운반자 농도와 이동도는 293 K에서 각각 $4.87{\times}10^{23}$ electron/$m^{23}$ , $1.29{\times}10^{-2}$$\m^2$/v-s였다. $CuGaSe_2$ 단결정 박막의 광전류 단파장대 봉우리들로부터 20K에서 측정된 $\Delta$Cr(crystal field splitting)은 약 0.0900 eV $\Delta$So(spin orbit coupling)는0.2493 eV였다. 20K에서 광발광 봉우리의 667.6nm(1.8571 eV)는 free exciton($E_x$), 672.6nm(1.8432 eV)는 acceptor-bound exciton 인 $I_2$와 679.3nm(1.8251 eV)는 donor-bound exciton인 $I_1$였다. 또한 690.9nm(1.7945 eV)는 donor-acceptor pair(DAP) 발광 $P_0$이고 702.4nm(1.7651 eV)는 DAP-replica $P_1$, 715.0nm(1.7340 eV)는 DAP-replica $P_2$, 728.9nm(1.7009 eV)는 DAP-replica $P_3$, 741.9nm(1.6711 eV)는 DAP-replica $P_4$로 고찰된다. 912.4nm(1.3589 eV)는 self activated(SA)에 기인하는 광발광 봉우리로 고찰되었다.

• 한국결정성장학회지
• /
• 제10권6호
• /
• pp.425-433
• /
• 2000

수평 전기로에서 $CuGaTe_2$다결정을 합성하여 HWE 방법으로 $CuGaTe_2$단결정 박막을 반절연성 GaAs (100) 위에 성장하였다. $CuGaTe_2$단결정 박막은 증발원과 기판의 온도를 각각 $670^{\circ}C$, $410^{\circ}C$로 성장하였다. 이때 단결정 박막의 결정성이 10K에서 측정한 광발광 스펙트럼은 954.5 nm(1.2989 eV) 근처에서 exciton emission 스펙트럼이 가장 강하게 나타났으며, 또한 이중결정 X-선 요동곡선(DCRC)의 반폭치(FWHM)도 139arcsec로 가장 작게 측정되어 최적 성장 조건임을 알 수 있었다. Hall효과는 van der Pauw 방법에 의해 측정되었으며, 온도에 의존하는 운반자 농도와 이동도는 293 K에서 각각 $8.72{\times}10{23}$개 $\textrm m^3$, $3.42{\times}10^{-2}$ $\textrm m^2$/V.s였다. 상온에서 $CuGaTe_2$단결정 박막의 광흡수 특성으로부터 에너지 띠간격이 1.22 eV였다. Bandedge에 해당하는 광전도도 peak의 온도 의존성은 varshni 관계식으로 설명되었으며, varshni 관계식의 상수값은 $E_g$(0) = 1.3982 eV, $\alpha$ = $4.27{\times}10^{-4}$eV/K, $\beta$ = 265.5K로 주어졌다. $CuGaTe_2$단결정 박막의 광전류 단파장대 봉우리들로부터 10K에서 측정된$\Delta$cr(crystal field splitting)은 0.0791 eV, $\Delta$s.o(spin orbit coupling)는 0.2463 eV였다. 10K에서 광발광 봉우리의 919.8nm(1.3479 eV) free exciton($E_x$), 954.5nm(1.2989 eV)는 donor-bound exciton 인 $I_2(D^0,X)$와 959.5nm(1.2921 eV)는 acceptor-bound exciton 인 $I_1(A_0, X)$이고, 964.6nm(1.2853 eV)는 donor-acceptor pair(DAP) 발광, 1341.9nm(0.9239 eV)는 self activated(SA)에 기인하는 광발광 봉우리로 고찰되었다.

• 한국결정성장학회지
• /
• 제25권5호
• /
• pp.173-181
• /
• 2015

A stoichiometric mixture of evaporating materials for $BaIn_2S_4$ single crystal thin films was prepared from horizontal electric furnace. To obtain the single crystal thin films, $BaIn_2S_4$ mixed crystal was deposited on thoroughly etched semi-insulating GaAs(100) substrate by the Hot Wall Epitaxy (HWE) system. The source and substrate temperatures were $620^{\circ}C$ and $420^{\circ}C$, respectively. The crystalline structure of the single crystal thin films was investigated by double crystal X-ray diffraction (DCXD). The carrier density and mobility of $BaIn_2S_4$ single crystal thin films measured from Hall effect by van der Pauw method are $6.13{\times}10^{17}cm^{-3}$ and $222cm^2/v{\cdot}s$ at 293 K, respectively. The temperature dependence of the energy band gap of the $BaIn_2S_4$ obtained from the absorption spectra was well described by the Varshni's relation, $E_g(T)=3.0581eV-(3.9511{\times}10^{-3}eV/K)T^2/(T+536K)$. The crystal field and the spin-orbit splitting energies for the valence band of the $BaIn_2S_4$ have been estimated to be 182.7 meV and 42.6 meV, respectively, by means of the photocurrent spectra and the Hopfield quasicubic model. These results indicate that the splitting of the ${\Delta}so$ definitely exists in the ${\Gamma}_5$ states of the valence band of the $BaIn_2S_4/GaAs$ epilayer. The three photocurrent peaks observed at 10 K are ascribed to the $A_1$-, $B_1$-exciton for n = 1 and $C_{24}$-exciton peaks for n = 24.

• 한국결정성장학회지
• /
• 제18권5호
• /
• pp.217-224
• /
• 2008

수평 전기로에서 $ZnIn_2Se_4$ 단결정을 합성하여 HWE(Hot Wall Epitaxy)방법으로 $ZnIn_2Se_4$ 단결정 박막을 반절연성 GaAs(100) 기판에 성장시켰다. $ZnIn_2Se_4$ 단결정 박막의 성장 조건을 증발원의 온도 $630^{\circ}C$, 기판의 온도 $400^{\circ}C$였고 성장 속도는 0.5 $\mu m/hr$였다. $ZnIn_2Se_4$ 단결정 박막의 결정성의 조사에서 10K에서 광발광(photoluminescence) 스펙트럼이 682.7nm ($1.816{\underline{1}}eV$)에서 exciton emission 스펙트럼이 가장 강하게 나타났으며, 또한 이중결정 X-선 요통곡선(DCRC)의 반폭치(FWHM)도 128 arcsec로 가장 작아 최적 성장 조건임을 알 수 있었다. Hall 효과는 van der Pauw 방법에 의해 측정되었으며, 온도에 의존하는 운반자 농노와 이동도는 293 K에서 각각 $9.41\times10^{16}/cm^{-3}$, $292cm^2/V{\cdot}s$였다. $ZnIn_2Se_4$/SI(Semi-Insulated) GaAs(100) 단결정 박막의 광흡수와 광전류 spectra를 293 K에서 10K까지 측정하였다. 광흡수 스펙트럼으로부터 band gap $E_g(T)$는 varshni공식에 따라 계산한 결과 $E_g(T)=1.8622\;eV-(5.23\times10^{-4}eV/K)T^2/(T+775.5K)$ 이었으며 광전류 스펙트럼으로부터 Hamilton matrix(Hopfield quasicubic mode)법으로 계산한 결과 crystal field splitting energy ${\Delta}cr$값이 182.7meV이며 spin-orbit energy ${\Delta} so$값은 42.6meV임을 확인하였다. 10 K일 때 광전류 봉우리들은 n= 1, 27일때 $A_{1}-$, $B_{1}-$와 $C_{27}-exciton$ 봉우리임을 알았다.

• 센서학회지
• /
• 제11권5호
• /
• pp.309-318
• /
• 2002

수평 전기로에서 $CdIn_2S_4$ 다결정을 합성하여 HWE(Hot Wall Epitaxy)방법으로 $CdIn_2S_4$ 단결정 박막을 반절연성 GaAs (100)기판에 성장시켰다. $CdIn_2S_4$ 단결정 박막의 성장 조건은 증발원의 온도 $630^{\circ}C$, 기판의 온도 $420^{\circ}C$였고 성장 속도는 $0.5\;{\mu}m/hr$였다. $CdIn_2S_4$ 단결정 박막의 결정성의 조사에서 10 K에서 광발광(photoluminescence) 스펙트럼이 463.9 nm (2.6726 eV)에서 exciton emission 스펙트럼이 가장 강하게 나타났으며, 또한 이중 결정 X-선 요동 곡선(DCRC)의 반폭치(FWHM)도 127 arcsec로 가장 작아 최적 성장 조건임을 알 수 있었다. Hall 효과는 van der Pauw 방법에 의해 측정되었으며, 온도에 의존하는 운반자 농도와 이동도는 293K에서 각각 $9.01{\times}10^{16}/cm^3$, $219\;cm^2/V{\cdot}s$였다. $CdIn_2S_4$/SI(Semi-Insulated) GaAs(100) 단결정 박막의 광흡수와 광전류 spectra를 293K에서 10K까지 측정하였다. 광흡수 스펙트럼으로부터 band gap $E_g(T)$는 Varshni 공식에 따라 계산한 결과 $2.7116eV-(7.74{\times}10^{-4}eV/K)T^2$/(T+434K)이었으며 광전류 스펙트럼으로부터 Hamilton matrix(Hopfield quasicubic mode)법으로 계산한 결과 crystal field splitting ${\Delta}cr$값이 0.1291 eV이며 spin-orbit ${\Delta}so$값은 0.0248 eV임을 확인하였다. 10K일 때 광전류 봉우리들은 n = 1일때 $A_1$-, $B_1$-와 $C_1$-exciton 봉우리임을 알았다.

• 한국결정성장학회지
• /
• 제21권3호
• /
• pp.99-104
• /
• 2011

단결정 성장을 위한 $MgGa_2Se_4$ 다결정은 수평 전기로에서 합성하였으며, 결정구조는 rhombohedral이고 격자상수 $a_0$는 3.953 ${\AA}$, $c_0$는 38.890 ${\AA}$였다. $MgGa_2Se_4$ 단결정박막은 HWE(Hot Wall Epitaxy) 방법으로 반절연성 GaAs(100)기판에 성장시켰다. 단결정박막의 성장 조건은 증발원의 온도 $610^{\circ}C$, 기판의 온도 $400^{\circ}C$에서 진행되었으며 성장 속도는 0.5 ${\mu}m/h$였다. 단결정박막의 결정성은 이중 결정 x-선 회절곡선의 반폭치와 X-선 회절무늬의 ${\omega}-2{\theta}$로부터 구하여 최적 성장 조건을 알 수 있었다. Hall 효과는 van der Pauw 방법에 의해 측정되었으며, 온도에 의존하는 운반자 농도와 이동도는 293 K에서 각각 $6.21{\times}10^{18}/cm^3$, 248 $cm^2/v{\cdot}s$였다. $MgGa_2Se_4$/SI(Semi-Insulated) GaAs(100) 단결정 박막의 광흡수 스펙트럼을 10 K에서 293 K까지 측정하였다. 광흡수 스펙트럼으로부터 구한 에너지 갭 $E_g(T)$는 varshni 공식 $E_g(T)=E_g(0)=({\alpha}T^2/T+{\beta})$을 잘 만족함을 알 수 있었다. 여기서 $E_g(0)=2.34\;eV$, ${\alpha}=8.81{\times}10^{-4}\;eV/K$, ${\beta}=251\;K$였다.

• 한국재료학회지
• /
• 제11권5호
• /
• pp.419-426
• /
• 2001

AgGaSe$_2$ 단결정 박막은 수평 전기로에서 합성한 $AgGaSe_2$ 다결정을 증발원으로 하여, hot wall epitaxy (HWE) 방법으로 증발원과 기판 (반절연성-GaAs(100)) 의 온도를 각각 $630^{\circ}C$, $420^{\circ}C$로 고정하여 박막 결정 성장을 하였다. 10K에서 측정한 광발광 excition 스펙트럼과 이중결정 X-선 요동곡선 (DCRC) 의 반치폭 (FWHM )을 분석하여 단결정 박막의 최적 성장 조건을 얻었다. Hall효과는 van der Pauw 방법에 의해 측정되었으며, 온도에 의존하는 운반자 농도와 이동도는 293k에서 각각 4.89$\times$$10^{ 16}$/㎤, 129$\textrm{cm}^2$/V.s였다. 광전류 봉우리의 10K에서 단파장대의 가전자대 갈라짐 (splitting)에 의해서 측정된 $\Delta$C$_{r}$ (crystal field splitting)은 0.1762eV, $$\Delta$S_{o}$ (spin orbit splitting)는 0.2494eV였다 10K의 광발광 측정으로부터 고풍질의 결정에서 볼 수 있는 free excitors과 매우 강한 세기의 중성 주개 bound excitors등의 피크가 관찰되었다. 이때 중성 주개 bound ekciton의 반치폭과 결합에너지는 각각 BmeV와 14.1meV였다. 또한 Haynes rule에 의해 구한 불순물의 활성화 에너지는 141meV였다.rule에 의해 구한 불순물의 활성화 에너지는 141meV였다.