• Journal of the Korean Magnetics Society
• /
• v.3 no.3
• /
• pp.201-207
• /
• 1993

Starting ingot of $Pr_{15}Fe_{77}B_{8}$ were prepared by vacuum induction melting under argon atmosphere. The ingot were induction melted in a quartz crucible and then ejected as a molten alloy throuth a 0.6 mrn orifice onto a rotating cop¬per wheel. An anisotropic magnet was prepared from ribbon by hot deformation techniques. A fully dense precursor magnet first made by pressing ribbons at $680^{\circ}C$ under a pressure of $21.8\;kg/mm^{2}$. A substantially oriented magnets were obtained by die-upset under various conditions. As the compression ratio increases, the $B_{r}$ value increases pronouncedly though $_{i}H_{c}$ decreases. Also, XRD analyses show increased diffraction peak from (006). From these results, it can be known that the magnetic easy axis was formed along the compression axis. As the die-upset speed increases, $_{i}H_{c}$ increases though $B_{r}$ decreases. The $B_{r}$ increases up to $750^{\circ}C$ of die-upset temperature and above this temperature decreases. The value of $4{\pi}M_{s}$ of the $Pr_{15}Fe_{77}B_{8}$ alloy prepared is found to be 11.8 KG. When the alloy was compressed by 0.8 under the die-upset speed of 0.05 m/sec at $750^{\circ}C$, $B_{r}$ was 11.0 KG indicating that the alloy has excellent magnetic anistropy. However, this alloy has some limitation because of low $_{i}H_{c}$.

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 2009.05a
• /
• pp.310-313
• /
• 2009

Several high nitrogen stainless steel ingots(100kg) were fabricated with changing Ni and $[N]_2$ contents by Pressurized Vacuum Induction Melting(P_VIM). After free forging process, chemical compositions, microstructure and mechanical properties were estimated. Hardness was increased with the increase of $[N]_2$ content. Furthermore, microstructure including a lot of tempering twins was observed with optical microscope. Mechanical properties were estimated as function of solution treatment temperature and cooling method(air/water) under duration time of 1 hr on sample that were fabricated with Ni content under the atmospheric $[N]_2$ pressure. At solution treatment range of $1050{\sim}1100^{\circ}C$, hardness was decreased with the increase of solution temperature and there were little discrepancy of microstructure and hardness with cooling method. Computer simulation was carried out in order to inspect pass schedule in cold rolling process. When the condition of simulation was roll speed of 2.5mpm, rolling rate $15{\sim}17%$ per pass, it was ascertained that the formation such as deformation by sticking and lamellar sliver etc. was restricted from a simulation.

• Korean Journal of Materials Research
• /
• v.3 no.2
• /
• pp.175-184
• /
• 1993

Abstract Co-and/or AI-added Nd-Fe-B-based magnetic alloys were fabricated by using vacuum induction melting frunace, and melt-spun ribbons were made of the magnetic alloys with single roll rapid quenching method. The variation of magnetic properties of the melt-spun ribbons as a function of Cuwheel velocity (Vs) were investigated. Bonded magnets were made of the optimally quenched ribbon fragments, and the magnetic properties of the melt-spun ribbons and the bonded magnets were studied, relating to the microstructure and crystalline structure. Cu-wheel surface velocity had a strong effect on the magnetic properties of the melt-spun ribbons, and the maximum properties were obtained around Vs =20m/sec. The optimally quenched ribbon had a cellura-type microstructure, in which fine N$d_2$F$e_14$B grains were surrounded by thin Nd-rich phase. In case of a 2.1at% AI-added melt-spun ribbon, the magnetic properties were as follows: iHc, Br, and (BH)max were 15.5KOe, 7.8KG and 8.5MGOe respectively. And resin bonded magnets were fabricated by mixing optimally quenched ribbon fragments with 2.5wt % polyamide resin, compacting and binding at room temperature. The iHc, Br and (BH)max of bonded magnet were lO.2KOe, 4.4KG and 3.3MGOe respectively. And hot-pressed magnets were made by pressing the overquenched ribbons at high temperature. The magnetic properties of hot-pressed magnets were better than those of bonded magnets, and when the holding time was 8 minutes, the iHc, Br, and (BH)max of the hot-pressed magnet were 1O.8KOe, 7.3KG and 8.0MGOe respectively. Domain structure was mainly maze pattern, which means that the easy magnetization axis could be aligned, and the domain width of the hot-pressed magnets was smaller than that of bonded magnets.

• Journal of the Korean Institute of Gas
• /
• v.26 no.6
• /
• pp.16-23
• /
• 2022

In this study, characteristics of effect on hydrogen gas was investigated to hydrogen embrittlement by disk and tensile tests. The developed and commercial alloy was fabricated to a plate material made from an alloy ingot. The prepared materials were processed in the form of a disk to measure rupture pressure by hydrogen and helium gas at a rate of 0.1 to 1,000 bar/min. In the hydrogen pre-charged tensile test, a specimen was hydrogenated using an anode charging method, and the yield strength, ultimate tensile strength, elongation, and reduction in area rate were carried by a strain rate test. Also, the microstructure was observed to the fracture surface of the tensile test specimen. As a result, the developed materials satisfied endurable hydrogen embrittlement, and the fractured surface showed a brittleness fracture surface with a depth of several ㎛, but dimple due to ductile fracture could be observed.