• Journal of Advanced Marine Engineering and Technology
• /
• v.37 no.4
• /
• pp.368-377
• /
• 2013

The Urea-SCR system commercialized shows a remarkable performance to reduce NOx emission in heavy duty diesel engines. However, Urea-water solution injected upstream a mixer, which is set up inside a exhaust pipe to promote exhaust gas-atomized droplet mixing, bumps up against the wall of a exhaust pipe as the droplets flow downstream through the exhaust gas. The urea deposited on the wall of the exhaust pipe is changed into the Urea-salt, resulting in the decreased life-time of the SCR catalysts. Therefore, the development of the urea deposition avoidance technologies is being treated as an important issue of the Urea-SCR systems. An experimental study was carried out to investigate the effects of the wall flow characteristics around the mixer-housing assembly with the variation of the mixer housing surrounding and supporting the mixer, which is designed to increase the wall flow and then to reduce droplet deposition. The flow characteristics was investigated by using a hot-wire anemometry for 2-D simplified duct model, and the housing tilt angles and the position of the mixer were changed : angle of $0^{\circ}$, $1^{\circ}$, $2^{\circ}$, $3^{\circ}$, and mixer positions of 0L, 0.5L, 1L. The results showed that the wall flow onto the exhaust pipe was improved with changing the tilt angle of the mixer housing, and the wall flow improved more when the position of the mixer was on 1L.

• Korean Journal of Air-Conditioning and Refrigeration Engineering
• /
• v.25 no.5
• /
• pp.261-268
• /
• 2013

Technologies for preventing contaminants deposition are a key issue in a modern duct system. When particulate matters deposit inside the exhaust pipes, which are widely used in the Urea-SCR system to reduce $NO_x$ emission from heavy duty diesel engines, many problems arise associated with increased flow resistance and corrosion. Therefore, the development of the urea deposition avoidance technologies is being treated as an important issue of the Urea-SCR system. An analytical study was carried out to investigate the effects of the wall flow around the mixer with the variation of the mixer housing surrounding and supporting the mixer, which is designed to increase the wall flow and then to reduce droplet deposition. The housing angles and the position of the mixer were changed：angles of $0^{\circ}$, $1^{\circ}$, $2^{\circ}$, and $3^{\circ}$, and mixer positions of 0 L, 0.5 L, and 1 L. The axial velocity distributions, maximum velocity, the half-width, and momentum distribution of the wall flow were investigated to examine the effect of the mixer-housing assembly geometry.

• Journal of ILASS-Korea
• /
• v.13 no.3
• /
• pp.134-142
• /
• 2008

In the case of heavy duty diesel engines, the Urea-SCR system is currently considered to reduce the NOx emission as a proved technology, and it is widely studied to get the high performance and durability. However, the nozzles to inject the urea-water solution into the exhaust pipe occur some problems, including the nozzle clogging, deposition of urea-water solution on the inner wall of the exhaust pipe, resulting in the production of urea salt. In this study, a swirl-type twin-fluid nozzle to produce more fine droplets was used as a method to solve the problems. The effect of the nozzle cap geometry, including the length to diameter ratio ($l_o/d_o$) and chamfer, on the spray characteristics were investigated experimentally. The length to diameter ratio of nozzle cap were varied from 0.25 to 1.125. The chamfer angle of the nozzle cap was constant at 90o. The mean velocity and droplet size distributions of the spray were measured using a 2-D PDA (phase Doppler analyzer) system, and the spray half-width, AMD (arithmetic mean diameter) and SMD (Sauter mean diameter) were analyzed. At result, The larger length to diameter ratio of nozzle cap were more small SMD and AMD. The effect of the chamfer did increase the radial velocity, while it did not affect the atomization effect.

• Proceedings of the Korean Society of Soil and Groundwater Environment Conference
• /
• 2004.09a
• /
• pp.450-452
• /
• 2004

Using factor analysis and bivariate comparisons of major components in ground water, three geochemical processes were identified as controlling factors of ground water chemistry; 1) natural mineralization by water rock interactions, 2) effect of seawater which includes salinization by seawater near seashores and deposition of sea salt, and 3) nitrate contamination by N fertilization. Contribution of rainfall was also estimated from the measured composition of wet deposition. The geochemical processes were separated using total alkalinity as an indicator for natural mineralization, Cl for effect of seawater, and nitrate for N fertilization. Relatively high correlation of major components with nitrate suggests that nitrification of nitrogenous fertilizers significantly affects ground water chemistry. Total cations derived from nitrate sources have good linearity for nitrate in equivalent basis with a slope of 1.8, which is a mean of proton production coefficients in nitrification of two major compounds in nitrogenous fertilizers, ammonium and urea. Contribution of nitrate sources to base cations, Cl, and SO$_4$ in ground water was determined considering maximum contribution of natural mineralization to estimate a threshold of the effect of N fertilization for ground water chemistry, which shows W fertilization has a greatest effect than any other processes in ground water with nitrate concentration greater than 50 mg/L for Ca, Mg, Na and with concentration greater than 30 mg/L for Cl and SO$_4$.

• Journal of the Korean Ceramic Society
• /
• v.28 no.4
• /
• pp.338-346
• /
• 1991

The alumina-titania composite powders coated with Al2O3 were prepared by the method of hydrolysis-deposition of mixed aluminium salt solution of Al2(SO)4-Al(NO3)3-Urea. The effects of coating-process parameters on the characteristics of coated composite powders were also investigated. As the content of TiO2 dispersed in deionized water increased, the coated composite powders were found to be more uniform in size and unagglomerated. When TiO2 powders were coated for 30 min, the optimum TiO2 content in the coating process was 400 mg/ι. The size of TiO2 particle was increased approximately from 0.7${\mu}{\textrm}{m}$ to 1.0${\mu}{\textrm}{m}$ through coating of Al2O3. The IEP of coated composite powders was pH=8.3 identical to the value of aluminium hydroxides and the zeta-potential showed nearly similar values each other. When heat treating coated composite powders at 130$0^{\circ}C$, only two phases of TiO2(rutile) and Al2TiO5 were observed. These results showed that the suface of TiO2 could be uniformly coated with the aluminium hydroxide.

• Journal of the Korean Ceramic Society
• /
• v.29 no.8
• /
• pp.667-673
• /
• 1992

The alumina-zirconia composite powders of core particle ZrO2 coated with Al2O3 were prepared by the hydrolysis-deposition of the mixed aluminum salt solution of Al2(SO4)3-Al(NO3)3-Urea. The effects of hydrolysis reaction and coating parameters on characteristics of coated powders and composites were also investigated. The degree of coating could be estimated from the ratio of tetra-/mono-ZrO2 present at the room temperature after heat-treating coated powders at 120$0^{\circ}C$ and the result of TEM observations. When the content of ZrO2 in the dispersed coating system, the coating time, and the volume ratio of water/solution were 50 mg/g, 180 min, and 5, respectively the coating efficiency was maximum (the ratio of tetra-/mono-ZrO2 was 87/13). The relative densities of coated Al2O3-ZrO2 composites sintered at 1$650^{\circ}C$ for 4 hrs were about 91~98% and the maximum ratio of tetra-/mono-ZrO2 in Al2O3-20wt% ZrO2 composites was 62/38.