• Progress in Superconductivity
• /
• v.12 no.1
• /
• pp.36-40
• /
• 2010

We have studied the anisotropy of the London penetration depth of carbon doped $MgB_2$ single crystals, which was obtained from reversible magnetization measurements with the magnetic field both parallel and perpendicular to the c-axis. Similar to the pure $MgB_2$, the anisotropy of the upper critical field ${\gamma}_H$ decrease with temperature while the anisotropy of the London penetration depth ${\gamma}_{\lambda}$ slowly increases with temperature. However, the temperature dependence of ${\gamma}_H$ is drastically reduced and the value of ${\gamma}_{\lambda}$ becomes nearly ~1 as C is introduced. These results indicate that C substitution increases impurity scattering mainly in the $\sigma$ bands. The temperature dependence of the anisotropies agree well with the theoretical predictions with impurity scattering.

• Electrical & Electronic Materials
• /
• v.9 no.6
• /
• pp.578-583
• /
• 1996

The magnetic properties have been investigated for the system of $Y_{1-x}$Yb$_{x}$Ba$_{2}$Cu$_{3}$F$_{y}$O$_{y}$ with x=0.0, 0.1, 0.2, 0.3, 0.4 and 0.5. In the magnetic hysteresis measurements, the values of the magnetic critical current densities are in the range of 10$^{4}$-10$^{5}$ A/cm$^{2}$ at the maximum external field 1.4 T. The upper critical field is over 100 T. The critical current density is estimated by the magnetization width .DELTA.M through the Bean critical state model. As the field strength is increased, the .DELTA.M diminishes slowly. The .DELTA.M for the fluorinated sample also decreases slowly with increasing field. It is considered that the large J, value results from this type is due to enhanced pinning center in grain boundary.y.ary.y.

• Journal of Magnetics
• /
• v.16 no.1
• /
• pp.15-18
• /
• 2011

We have studied the $TiO_2$ doping effects on the flux pinning behavior of an $MgB_2$ superconductor synthesized by the in-situ solid-state reaction. From the field-cooled and zero-field-cooled temperature dependences of magnetization, the reversible-irreversible transition of $TiO_2$-doped $MgB_2$ was determined in the H-T diagram (the temperature dependence of upper critical magnetic field and irreversibility line). For comparison, the similar measurements are also obtained from SiC-doped $MgB_2$. The critical current density was estimated from the width of hysteresis loops in the framework of Bean's model at different temperatures. The obtained results manifest that nano-scale $TiO_2$ inclusions served as effective pinning centers and lead to the enhanced upper critical field and critical current density. It was concluded that the grain boundary pinning mechanism was realized in a $TiO_2$-doped $MgB_2$ superconductor.

• Progress in Superconductivity and Cryogenics
• /
• v.21 no.3
• /
• pp.18-21
• /
• 2019

We studied the effect of Fe ion irradiation on the upper critical field ($H_{c2}$) of 410 nm single-crystalline $MgB_2$ thin films. The irradiation energy was fixed at 140 keV when we increased the irradiation doses from $1{\times}10^{14}ion/cm^2$ to $4{\times}10^{14}ion/cm^2$. We found that $H_{c2}$ significantly increase with increasing irradiation dose, despite the low irradiation energy. The enhancement of $H_{c2}$ could be explained by the reduction of electron mean free path caused by defects induced from irradiation, leading to a decrease of coherence length (${\xi}$). We also discussed the effect of irradiation on temperature-dependent resistivity in details.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2010.08a
• /
• pp.172-172
• /
• 2010

$MgB_2$ doped with $TiO_2$ was prepared by the in-situ solid state reaction to study the effects of $TiO_2$ dopant on the flux pinning behavior of $MgB_2$ superconductor. From the field-cooled and the zero-field-cooled temperature dependences of magnetization, the realms of vortex-glass and vortex-liquid states of $TiO_2$-doped $MgB_2$ were determined in the H-T diagram (the temperature dependence of upper critical magnetic field and irreversibility line). The critical current density was estimated from the width of hysteresis loops in the framework of Beam's model at different temperatures. The results indicate that nano-scale $TiO_2$ inclusions play a role of the effective pinning centers and lead to the enhanced upper critical field and critical current density. It is suggested that the grain-boundary pinning mechanism is realized in $TiO_2$-doped $MgB_2$ superconductor.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2009.06a
• /
• pp.362-362
• /
• 2009

$MgB_2$ bulk samples were sintered at different ambient. In this work, high purity Ar gas was added with oxygen and hydrogen gas, which can be regarded as impurity in a sense, as a possible dopant in the $MgB_2$. It was found that oxygen in the sintering ambient leads to a decrease in the critical current density $J_c$ at self field and lower fields. However, we can obtained higher $J_c$ at higher fields. It was also noted that $MgB_2$ samples sintered with 5% hydrogen in Ar revealed the increased $J_c$ at all fields compared to those processed in pure Ar ambient. From the XRD and FESEM analysis, the impurity gas in Ar can refine the $MgB_2$ grain size and result in increased grain. boundary, which can act as a strong flux pinning sites in $MgB_2$ samples. Also discussed are the effects of sintering ambient on irreversibility field, $H_{irr}$ and the upper critical field, $H_{C2}$.

• Progress in Superconductivity and Cryogenics
• /
• v.17 no.3
• /
• pp.9-12
• /
• 2015

NbN thin films were deposited on thermally oxidized Si substrate at room temperature by using reactive magnetron sputtering in an $Ar-N_2$ gas mixture. Total sputtering gas pressure was fixed while varying $N_2$ flow rate from 1.4 sccm to 2.9 sccm. X-ray diffraction pattern analysis revealed dominant NbN(200) orientation in the low $N_2$ flow rate but emerging of (111) orientation with diminishing (200) orientation at higher flow rate. The dependences of the superconducting properties on the $N_2$ gas flow rate were investigated. All the NbN thin films showed a small negative temperature coefficient of resistance with resistivity ratio between 300 K and 20 K in the range from 0.98 to 0.89 as the $N_2$ flow rate is increased. Transition temperature showed non-monotonic dependence on $N_2$ flow rate reaching as high as 11.12 K determined by the mid-point temperature of the transition with transition width of 0.3 K. On the other hand, the upper critical field showed roughly linear increase with $N_2$ flow rate up to 2.7 sccm. The highest upper critical field extrapolated to 0 K was 17.4 T with corresponding coherence length of 4.3 nm. Our results are discussed with the granular nature of NbN thin films.

• Progress in Superconductivity and Cryogenics
• /
• v.20 no.1
• /
• pp.1-10
• /
• 2018

The improvement of critical current properties of $REBa_2Cu_3O_{7-x}$ (REBCO) coated conductors by introducing artificial pinning centers (APCs) is examined with respect to the field-angle anisotropy, high-field performance and relaxation property with time. Nano-rods along the c-axis introduced by PLD method and isotropic nano-particles introduced by TFA-MOD method are treated. The theoretical analysis is also shown to understand the effect of APCs quantitatively. The effects of superconducting layer thickness that influences the high-field performance and relaxation property are also discussed. It is shown that the upper critical field, which is another important factor to determine the high-field property, can be improved by introduction of APCs through electron scattering at interfaces with the superconducting matrix. The optimum critical current property can be obtained by properly designing the morphology and number density of APCs and the superconducting layer thickness.

• Progress in Superconductivity and Cryogenics
• /
• v.16 no.4
• /
• pp.31-35
• /
• 2014

The upper critical field ($H_{c2}$) was determined by applying a magnetic field along the ab plane and c axis for two single crystals of $BaFe_{2-x}Ru_xAs_2$ (x=0.48 and 0.75). The anisotropy of the $H_{c2}(0)$, ${\gamma}(0)=H_{c2}{^{ab}}(0)/H_{c2}{^c}(0)$, was ~1.6 for x=0.48 and ~2.3 for x=0.75. The angle-dependent resistance measured below $T_c$ allowed perfect scaling features based on anisotropic Ginzburg-Landau theory, leading to consistent anisotropy values. Because only one fitting parameter ${\gamma}$ is used in the scaling for each temperature, the validity of the ${\gamma}$ value was compared with that determined from ${\gamma}=H_{c2}{^{ab}}/H_{c2}{^c}$. The ${\gamma}$ obtained at a temperature close to $T_c$ was 3.0 and decreased to 2.0 at low temperatures. Comparing to the anisotropy determined for electron- or hole-doped $BaFe_2As_2$ using the same method, the present results point to consistent anisotropy in Ru-doped $BaFe_2As_2$ with other electron- or hole-doped $BaFe_2As_2$.

• Journal of the Korean Magnetics Society
• /
• v.1 no.2
• /
• pp.15-21
• /
• 1991

The magnetic properties of the $Y_{1}Ba_{2}Cu_{3-x}Sn_{x}O_{7-y}$ superconductor were studied as a function of Sn concentration by utilizing both the vibrating sample magnetometer (VSM) and torque magnetometer. Unlike the cases where Fe and Co were substituted for Cu, the superconducting transition temperature was maintained above 90 K until x reached the value of 0.36. The lower critical field $H_{c1}(T)$ and upper critical field $H_{c2}(T)$ are measured as a function of temperature and external magnetic field, respectively. By aid of these results, $H_{c1}(0)$.($H_{c2}(0)$), the coherence length ${\varepsilon}_{0}$, the penetration depth ${\lambda}_{0}$, and the Ginzburg-Landau parameter k were oqtained. Flux pinning was also observed in the sample.