• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.11 no.6
• /
• pp.486-492
• /
• 1998

The amorphous Co-based magnetic films have a large saturation flux density, a low coercive force, and a zero magnetostriction constant. Therefore, they have been studied for application to magnetic recoding heads and micro magnetic devices. However, it was found that the magnetic anisotropy was changed for each film fabrication processes. In this study, we investigated how to control the anisotropy of sputtered amorphous $Co_{89}Nb{8.5}Zr{2.5}$ films. After deposition, the rotational field annealing ant the uniaxial field annealing were performed under the magnetic field of 1.5 kOe. the annealing was done at the temperature range from 400 to $600^{\circ}C$ for one hour. As-deposited amorphous $Co_{89}Nb{8.5}Zr{2.5}$ thin film had saturation magnetization ($4\piM_5$) of 0.8 T, coercive force($_IH_C$) of 1.5 Oe, and anisotropy field($H_k$) of 11 Oe. The amorphous $Co_{89}Nb{8.5}Zr{2.5}$ thin films annealed by rotational field annealing at $500^{\circ}C$ for one hour was found to be isotropy, and $4\piM_5$ of 0.9 T was obtained from these films, Also, the magnetic anisotropy of as-deposited films could be controlled by uniaxial field annealing at $400^{\circ}C$ for one hour. Anisotropy field($H_k$) of 17 Oe and $4\piM_5$ of 1.0 T were obtained by this method.

• Journal of the Korean Magnetics Society
• /
• v.11 no.4
• /
• pp.163-167
• /
• 2001

The rotation of uniaxial anisotropy field of 700 ${\AA}$ thick sputtered NiFe thin film due to magnetic annealing was investigated. NiFe film was annealed in a magnetic field which is perpendicular to the initial induced uniaxial anisotropy field. The NiFe film becomes nearly isotropic after 1 hour annealing at 160 $^{\circ}C$. With increase of annealing temperature over 160 $^{\circ}C$, the film gets uniaxial anisotropy field again. An abrupt increase of H$\sub$c/ was observed with annealing temperature over 400 $^{\circ}C$. The X-ray diffraction analysis and Auger electron spectroscopy with Ar ion etching showed extensive grain growth in NiFe film with (111) texturing and interdiffusion with adjacent Au electrode layer by 400 $^{\circ}C$ magnetic annealing.

• Journal of Magnetics
• /
• v.10 no.4
• /
• pp.133-136
• /
• 2005

The NiMn/NiFe bilayer structure which was short time annealed in order to induce unidirectional anisotropy were studied as a function of annealing temperature. The maximum exchange bias field of NiMn/NiFe bilayer was presented at $250^{\circ}C$ after short time annealing process with no external field. The appearance of exchange bias was due to phase transformation of NiMn layer. In plane angular dependence of a resonance field distribution which measured by FMR was analysed as a combined effect of unidirectional anisotropy and uniaxial anisotropy. The resonance field and the line width from FMR measurement were also analysed with annealing temperature.

• Journal of the Korean Magnetics Society
• /
• v.12 no.2
• /
• pp.46-50
• /
• 2002

Soft magnetic Mumetal thin film was fabricated under magnetic field at various substrate temperatures. High vacuum annealing was carried out at 200$\^{C}$ during 1 hr. The in-plane anisotropy of Mumetal thin film was determined from hysteresis loops measured by VSM when the sample axis varied from the field direction from 0°to 180°. As the substrate temperature increases, the coercivity in easy direction decreases, but uniaxial anisotropy deviates from the field direction. After vacuum annealing at 200$\^{C}$ for 1 hr, the uniaxial anisotropy is improved irrespective of substrate temperature. When the substrate temperature was 50$\^{C}$, the anisotropy field is 4.3 Oe. As the substrate temperature increases anisotropy field decreases. Uniaxial anisotropy of Mumetal thin film was formed best at 50$\^{C}$ before and after annealing.

• Proceedings of the KIEE Conference
• /
• 1996.07a
• /
• pp.193-195
• /
• 1996

In amorphous transformer core, magnetic field annealing is required for inducing uniaxial magnetic anisotropy to circular direction of the core. Generally annealing temperature is about foot, so insulator using in solenoid bed must have a high temperature stability, mechanical strength and good machinability. In this study, we made the magnetic field annealing apparatus using insulators, conductors, connectors and power supply. And then tested the apparatus in annealing process of 50 kVA amorphous transformers.

• Proceedings of the Korean Magnestics Society Conference
• /
• 2001.04a
• /
• pp.56-57
• /
• 2001

• Journal of the Korean Magnetics Society
• /
• v.21 no.1
• /
• pp.10-14
• /
• 2011

We have measured the ferromagnetic resonance (FMR) signal in as deposited and $400^{\circ}C$ annealed CoFeB/MgO thin film to investigate the annealing effect on magnetic anisotropies and FMR linewidth (${\Delta}H_{PP}$). The uniaxial anisotropy field ($H_{K1}$) was only observed in the as deposited sample. Whereas, in the $400^{\circ}C$ annealed sample, the biaxial anisotropy field ($H_{K2}$) was additionally observed in accompany with uniaxial anisotropy field ($H_{K1}$). The appearance of biaxial anisotropy fields was originated from the crystalline growth of bcc CoFeB(001) from the MgO(001) interface and by the B diffusion during thermal annealing. Also, the ${\Delta}H_{PP}$ of $400^{\circ}C$ annealed sample was increased compared with that of as deposited sample, which was due to the broad distribution of the magnetization axis by the biaxial anisotropy.

• Electrical & Electronic Materials
• /
• v.8 no.4
• /
• pp.443-450
• /
• 1995

A directional coupler which on the X-cut $LiNbO_3$ substrate is fabricated by using proton exchange method and self-aligned method. After proton exchange process, the waveguide is formed by annealing process. The relation ship between refractive index change of waveguide and maximum output was studied along with the annealing time. A self-aligned method was used to simplify the fabrication process of the waveguide and to maximize the efficiency of electric field. The on-off state of modulator has been observered with the switching of the directional coupler by the electric field effect and also the switching voltage of the directional coupler has been measured with 8.0 [V].

• Proceedings of the KIEE Conference
• /
• 1998.07d
• /
• pp.1498-1499
• /
• 1998

Thin film inductors of 10 mm ${\times}$ 10 mm with spiral pattern of 14 turns were fabricated by sputtering, photo-masking, and etching processes. Their impedence characteristics and annealing after effects were investigated. After magnetic annealing, the impedence characteristics of the inductors were improved at comparatively low frequencies, but the tendencies of it for thr frequency changes were almost same. These improvement was caused by the annihilation of the internal stresses of films, Uniaxial field annealed thin film inductor had an inductance of 1000 nH, resistance of 6 $\Omega$, and quality factor of 1 at 2 MHz.

• The Transactions of the Korean Institute of Electrical Engineers
• /
• v.40 no.5
• /
• pp.496-500
• /
• 1991

The effects of annealing with and without magnetic field on magnetic properties of amorphous Fe-B-Si cores have been investigated as a function of toroidal stress. By decreasing the toroidal stress, the magnetic properties of the amorphous ribbon have beenimproved. Near 180 domain walls exist in the thermally annealed toroidal cores, but the domain walls exist in the thermally annealed toroidal cores, but the domain walls are not parallel to the longitudinal direction of the ribbon. In the specimen annealed with a magnetic field strength of 10 Oe in the longitudinal ribbon length axis, the domains are nearly parallel to the longitudinal direction due to the field induced uniaxial anisotropy resulting in further increase in the remanent magnetization and decrease in the coercive force and loss.