• Composites Research
• /
• v.12 no.3
• /
• pp.1-7
• /
• 1999

New hybrid composite material CPAL(Carbon Patched ALuminum alloy), an Al2024-T3 plate doubleside reinforced with carbon/epoxy laminates were made. Fatigue crack growth tests were carried out at R=0.2, 0.5 in the CPAL specimens. The retardation mechanism and behavior of fatigue crack growth were examined basing on investigation of the crack and the delamination using a X-Ray and a ultrasonic C-Scan. The fatigue crack growth rates of CPAL specimens were remarkedly retarded compared to that of the Al2024-T3 specimen. The retardations amounts of the fatigue crack growth rates get higher in $0^{\circ}$/$90^{\circ}$ CPAL specimen than in $\pm$$45^{\circ}$ CPAL specimen, and get higher at R=0.2 than at R=0.5. The retardation of fatigue crack growth rates in CPAL specimen was generated by the crack bridging mechanism, that is the behavior that the fibers in CFRP layers decrease the COD in the Al2024-T3 plate.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2008.11a
• /
• pp.201-201
• /
• 2008

박형초음파모터의 구조는 그림 1(a) 와 같이 크로스형태의 앓은 스테이터에 윗면과 아랫면에 각각 8 개의 압전세라믹이 부착된 형태이다. 압전세라믹의 분극방향은 로터와 접촉하는 스테이터의 A, B, C, D 네 개의 타점에서 순차적인 타원변위가 생성되도록 결정된다. 유한요소해석프로그램인 ATILA 5.2.4를 사용하여 최적설계를 한 결과 폭 3[mm], 길이 18[mm], 두께 1.8[mm], Brass 재질, Mid surface clamp 조건에서 입력전압 18[Vrms] 일 때 0.3[${\mu}m$]의 변위를 보였다. 최적설계된 모델을 제작하였고, 정확한 실험결과를 얻기 위해서 푸쉬풀게이지, x-y스테이지, rpm 메타, 토크게이지를 이용하여 실험테이블을 구성하였다. 그림 1(b) 는 마이크로컨트롤러를 이용한 구동 드라이버를 보여준다. 한 주기에서 1/4분주의 순차적인 네 개의 구형파를 생성하고, 이를 push-pull회로를 동하여 90도의 위상차가 나는 정현파를 생성하여 초음파 모터의 구동전원으로 사용한다. 엔코더와 AD 컨버터를 이용하여 정속도 운전을 위한 피드백 제어가 된다. 제안된 구동드라이버를 이용하여 측정한 결과, 구동 주파수 88.6[kHz], 입력전압 [40Vrms], preload 0.2 [N]에서 130 [rmp] 의 속도와 25 [gfcm] 의 토크특성을 보였다. 압력전압을 증가시킬수록 속도는 선형적인 증가를 보였고, 토크는 이와 반대로 감소하는 특성을 보였다. 피드백 제어회로가 없는 경우에는 preload 변화에 따른 극심한 속도 변화를 보였고, 피드백 제어를 하였을 경우에는 0.2~0.4[N]의 범위에서 정속도 운전이 가능함을 확인하였다. 기존의 주파수발생기와 파워 엠프를 이용한 구동장비와의 특성비교에서도 큰 차이를 보이지 않았으며, 장시간의 운전에도 안정적인 구동이 가능함을 확인하였다.

• The Transactions of the Korean Institute of Electrical Engineers D
• /
• v.55 no.2
• /
• pp.68-71
• /
• 2006

Active thermography has been used for several years in the field of remote non-destructive testing. It provides thermal images for remote detection and imaging of damages. Also, it is based on propagation and reflection of thermal waves which are launched from the surface into the inspected component by absorption of modulated radiation. For energy deposition, it use external heat sources (e.g., halogen lamp or convective heating) or internal heat generation (e.g., microwaves, eddy current, or elastic wave). Among the external heat sources, the ultrasound is generally used for energy deposition because of defect selective heating up. The heat source generating a thermal wave is provided by the defect itself due to the attenuation of amplitude modulated ultrasound. A defect causes locally enhanced losses and consequently selective heating up. Therefore amplitude modulation of the injected ultrasonic wave turns a defect into a thermal wave transmitter whose signal is detected at the surface by thermal infrared camera. This way ultrasound thermography(UT) allows for selective defect detection which enhances the probability of defect detection in the presence of complicated intact structures. In this paper the applicability of UT for fast defect detection is described. Examples are presented showing the detection of defects in PCB material. Measurements are performed on various kinds of typical defects in PCB materials (both Cu metal and non-metal epoxy). The obtained thermal image reveals area of defect in row of thick epoxy material and PCB.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2005.11a
• /
• pp.169-170
• /
• 2005

본 연구에서는 초음파 센서에 응용 가능한 $0.4Pb(Ni_{1/3}Nb_{2/3})O_3-0.6Pb(Zr_xTi_{1-x})O_3+0.5Wt%$ $MnO_2$ 세라믹스에 Zr/(Ti+Zr)비를 0.37에서 0.41로 변화시킨 조성을 1175 $\sim$ 1200$^{\circ}C$ 온도에서 소결하여 이의 결정구조 및 미세조직을 분석하였고, 압전, 유전 특성을 고찰하였다. 본조성에서 x=0.385 조성에서 최대 유전상수 값 3490 이 나타났으며, 그 이상의 첨가에서는 감소하였다. 상경계 영역인 x=0.385 조성에서 $\varepsilon$r, $K_p$, $d_{33}$ 값이 최대값을 나타내었다. $0.4Pb(Ni_{1/3}Nb_{2/3})O_3-0.6Pb(Zr_xTi_{1-x})O_3+0.5Wt%$ $MnO_2$, 세라믹스에서는 kp 와 $d_{33}$ 는 Zr/(Ti+Zr)비 0.385조성까지 증가하였다가 그 이상 조성에서 감소하였다. $1175^{\circ}C$에서 2시간 소결한 x=0.385조성에서 $\varepsilon$r=3490, kp=0.71, Qm=476의 우수한 압전 특성을 나타내었다.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.29 no.8
• /
• pp.483-488
• /
• 2016

Ultrasound imaging by using piezoelectric materials, such as lead zirconium titanate (PZT) has been one of the most preferred modes of imaging in the medical field due to its simple, low cost and non-ionizing radiation in comparison to other imaging techniques. Recently, the market demand for portable ultrasound is becoming larger with applications in developing countries, disaster area, military, and emergency purposes. However, most of ultrasound probes used is bulky and high power consumable, so unsuitable for such applications. In this study, the 3 layered ceramic specimen consisted of 128 pitches of $420{\mu}m$ in width and $450{\mu}m$ in thickness were prepared by using the Ti-rich PZT compositions co-fired at $1,050^{\circ}C$. Their electrical and ultrasound pulse-echo properties were investigated and compared to the single layer specimen. The 3 layered ultrasound probe showed 1.584 V of Vp-p, which is 3.2 times higher than single layered one, implying that it would allow effectively such a portable ultrasound probe system. The result were discussed in terms of higher capacitance, lower impedance and higher dielectric coefficient of the 3 layered ultrasound probe.

• Restorative Dentistry and Endodontics
• /
• v.26 no.5
• /
• pp.379-386
• /
• 2001

This study was performed to evaluate the sealing ability of various retrograde filling materials by using bacterial penetration and dye penetration test. One hundred and forty extracted human teeth with single, straight canals and mature apiece were collected and used for this study. All canals were instrumented using an engine driven Ni-Ti file (ProFile). After removing 3mm from the apex of tooth, a standardized 3mm root end cavity was prepared using an ultrasonic instrument. The 70 teeth were randomly divided into 7 groups : 6 groups for retrograde filling using Super-EBA, ZOE, Chelon-Silver, IRM, ZPC and amalgam. The 7th group was used as a negative control. Nail varnish was applied to all external root surfaces to the level of the reseated root ends to prevent lateral microleakages. The specimens were then sterilized in an ethylene oxide sterilizer for 24 hours. 2 mm of the reseated root was immersed in a culture chamber containing a Tripticase Soy Broth with a phenol red indicator. The coronal access of each specimen was inoculated every 72 hours with suspension of Proteus vulgaris. The culture media were observed every 24hours for color change indicating bacterial contamination. The specimens were observed for 4weeks. The remaining 70 teeth were submitted to a dye penetration test. The canals of all teeth were first sealed with AH26 and obturated using an Obtura II system. Root resection, root end preparation and retrograde filling was performed as above. All specimens were suspended in 2% methylene blue dye for 72 hours before being ion gitudinally split. The degree of dye penetration was then measured using a stereomicroscope at 10 magnification and evaluated. The results were as floows : 1. In the bacterial penetration, the degree of leakage was the lowest in the Super-EBA, followed by, in ascending order, ZOE, Chelon-Silver IRM and ZPC. The amalgam showed highest bacterial leakage of all(p<0.01). 2. In the dye penetration, the degree of microleakage was the lowest in the Chelon-Silver and Super-EBA, followed by, in ascending order, IRM, ZPC. The ZOE and amalgam showed the highest microleakage of all (p<0.05). These results suggested that the eugenol based cement, Super-EBA, have excellent sealing ability as a retrograde filling material.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.29 no.2
• /
• pp.90-94
• /
• 2016

In this work, [$Pb(Mg_{1/2}W_{1/2})_{0.03}(Ni_{1/3}Nb_{2/3})_x(Zr_{0.5}Ti_{0.5})_{0.97-x}O_3-BiFeO_3$] (x=0.02 to 0.12) composition ceramics were fabricated by the conventional soild state reaction method and their microstructure and piezoelectric properties were investigated according to PNN substitution. The addition of small amount of $BiFeO_3$, $Li_2CO_3$, and $CaCO_3$ were used in order to decrease the sintering temperature of the ceramics. The XRD (x-ray diffraction patterns) of all ceramics exhibited a perovskite structure. The sinterability of PMW-PNN-PZT-BF ceramics was remarkably improved using liquid phase sintering of $CaCO_3$, $Li_2CO_3$. However, it was identified from of the X-ray diffraction patterns that the secondary phase formed in grain boundaries decreased the piezoelectric properties. According to the substitution of PNN, the crystal structure of ceramics is transformed gradually from a tetragonal to rhombohedral phase. The x=0.10 mol PNN-substituted PMW-PNN-PZT-BF ceramics sintered at $920^{\circ}C$ showed the optimum values of piezoelectric constant($d_{33}$), piezoelectric figure of merit($d_{33{\cdot}}g_{33}$), planar piezoelectric coupling coefficient($k_p$) and density : $d_{33}=566$ [pC/N], $g_{33}=29.28[10^{-3}mV/N]$, $d_{33{\cdot}}g_{33}=16.57[pm^2/N]$, $k_p=0.61$, density=7.82 [$g/cm^3$], suitable for duplex ultrasonic sensor application.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2005.07a
• /
• pp.371-372
• /
• 2005

Supercapacitors are promising devices for delivering high power density. Digital communications, electric vehicles and other devices that require electrical energy at high power levels in relatively short pulses have prompted considerable research on supercapacitors. In recent years, solid electrolytes have been investigated for supercapacitors. Solid electrolytes are advantageous over liquid electrolytes in respect of easy handling and reliability without electrolyte leakage. In this preliminary study, an electrochemical supercapacitor in all solid configuration has been fabricated using CNF-DAAQ and poly-vinylidenefluoride(PVdF). A new type of Supercapacitor was constructed by using carbon nanofibers(CNFs) and DAAQ(l,5-diaminoanthraquinone) monomer. DAAQ was deposited on the carbon nanofibers by chemical polymerization with $(NH_4)_2S_2O_8$ as oxidant in the 0.1M $H_2SO_4$. Dried SPEEK powder was mixed with N-methyl pyrrolidone to make 10 wt.% solution in an ultrasonic bath, the slurry was cast over a glass substrate heated to $70^{\circ}C$ for solvent evaporation. And then we used solid electrolyte of SPEEK. The unit cell consist of DAAQ-CNF/electrolyte/Pt. From the analysis, it is clear that surface of carbon nanofibers was quite uniformly coated with DAAQ. The performance characteristics of the supercapacitors have been evaluated using Cyclic Voltammetry.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2006.06a
• /
• pp.329-330
• /
• 2006

본연구에서는 초음파 모터 등의 고출력 액츄에이터에 응용 가능한 $0.4Pb(Ni_{1/3}Nb_{2/3})O_3$-$0.6Pb(Zr_{0.405}Ti_{0.595})O_3$ + 0.25wt% $Fe_2O_3$ 조성시스템에 $MnO_2$ (0~1 wt.%)첨가하여 압전, 유전특성 및 미세구조에 관해 고찰하였다. 본조성을 $1125{\sim}1175^{\circ}C$ 온도에서 2시간 소결하여 시편을 제조하였으며 이의 결정구조 및 미세조직을 분석하였다. $MnO_2$ 첨가량 증가에 따라 압전 상수와 전기기계결함계수는 감소하였으며, 기계적 품질계수는 0.5 wt% 첨가시까지 증가하였으나 첨가량이 그 이상 증가함에 따라 감소하였다. 압전특성은 $1125^{\circ}C$에서 소결한 $MnO_2$ 0.5wt%조성에서 ${\varepsilon}r$ = 2040, kp = 0.66, $d_{33}$ = 504, Qm=438의 우수한 특성을 나타내었다.

• Earthquakes and Structures
• /
• v.10 no.3
• /
• pp.523-538
• /
• 2016

Besides their spiritual significance, minarets are humanity's cultural heritage to the future generations due to their historical and architectural attraction. Currently, many historical masonry minarets are damaged and destroyed due to several reasons such as earthquakes and wind. Therefore, safety of these religiously significant buildings needs to be thoroughly investigated. The utmost care must be taken into account while investigating these structures. Our study investigated earthquake behavior of historical masonry minaret of Haci Mahmut Mosque. Destructive and non-destructive tests were carried out to determine earthquake safety of this structure. Brick-stone masonry material properties of structure were determined by accomplishing ultrasonic wave velocity, Schmidt Hammer, uniaxial compression (UAC) and indirect tension (Brazilian) tests. Determined material properties were used in the finite element analysis of the structure. To validate the numerical analysis, Operational Modal Analysis was applied to the structure and dynamic characteristics of the structure were determined. To this end, accelerometers were placed on the structure and vibrations due to environmental effects were followed. Finite element model of the minaret was updated using dynamic characteristics of the structure and the realistic numerical model of the structure was obtained. This numerical model was solved by using earthquake records of Turkey with time history analysis (THA) and the realistic earthquake behavior of the structure was introduced.