• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2008년도 추계학술대회 논문집 Vol.21
• /
• pp.287-288
• /
• 2008

에폭시-층상실리케이트 나노콤포지트의 균질분산과 층상실리케이트내로 침투되는 박리정도를 향상시키기 위해 친환경적 분산기법인 물리적방법으로 Homogenizer와 Power Ultrasonic를 적용한 기법을 실시하였다. Homogenizer의 최적속도를 얻기 위해 분산시킨 나노콤포지트의 박리정도, 유리천이온도를 구할 수 있었고, Homogenizer와 Ultrasonic을 동시에 적용하여 최적시간을 구하기 위해 적용된 나노콤포지트를 절연파괴 강도의 Weibull Plots을 통하여 판단할 수 있는 좋은 결과를 얻을 수 있었다.

• 한국응용과학기술학회지
• /
• 제24권3호
• /
• pp.264-271
• /
• 2007

Effect of dispersion methods for Vapor Grown Carbon Fibers (VGCF) in epoxy caused the change in mechanical properties of VGCF/epoxy nanocomposites, such as tensile modulus and tensile strength. The influence of VGCF types - atmospheric plasma treated (APT) VGCF and raw VGCF - and their contents was discussed in detail. Treating VGCF with atmospheric plasma enhanced the surface energy, therefore improved the bonding strength with epoxy matrix. Two different methods used to disperse VGCF were ultrasonic and mechanical homogenizer methods. When using dispersion solutions, the VGCF demonstrated good dispersion in ethanol in both homogenizer and ultrasonic method. The uniform dispersion of VGCF was investigated by scanning electron microscopy (SEM) which showed well-dispersion of VGCF in epoxy matrix. The tensile modulus of raw VGCF/epoxy nanocomposites obtained by ultrasonic method was higher than that of one obtained by homogenizer method. APT VGCF/epoxy nanocomposites showed higher tensile strength than that of raw VGCF/epoxy nanocomposites.

• 한국복합재료학회:학술대회논문집
• /
• 한국복합재료학회 2003년도 추계학술발표대회 논문집
• /
• pp.29-32
• /
• 2003

Multi -walled carbon nanotube(MWNT)/poly(methyl methacrylate) composites were fabricate d through film casting. Manufacturing process was established using a ultrasonic cleaner and a homogenizer. Acetone was used as a solvent to melt PMMA and mix with MWNT. The ultrasonic cleaner performed an important role in producing MWNT/MMA nanocomposites. Ultrasonic energy was utilized to disperse MWNT in acetone. Also, melting PMMA in acetone and mixing MWNT and PMMA were achieved using the homogenizer. It was confirmed that the nanohlbes were well dispersed in PMMA according to SEM images.

• 한국음향학회지
• /
• 제41권1호
• /
• pp.9-15
• /
• 2022

기존의 나노입자 현탁액의 분산과정의 한계를 극복하여 단분산된 나노입자만으로 이루어진 현탁액을 얻기 위하여, 기존의 방법으로 전분산 처리된 현탁액을 다시 초음파 무화효과 및 사이클론을 이용하여 여과하는 방법을 제안하였다. 평균직경 250 nm인 Al₂O₃나노입자로 0.5 wt%인 현탁액을 만들어 초음파세척기 및 호모지나이저를 이용하여 각각 전처리 분산된 현탁액에 대하여 제안한 여과법을 적용하였다. 그 결과 초음파세척기로 전처리 분산한 경우 단분산된 나노입자 현탁액으로 여과하기 위해서는 종속 연결된 사이클론이 3개가 요구되는 반면, 호모저나이저로 전처리 분산된 현탁액의 경우는 2개의 사이클론으로도 가능함을 확인 하였다. 초음파 무화기 주파수의 조정과 사이클론의 설계 변경에 의해 다양한 종류의 나노입자에 대한 여과가 가능할 것으로 기대된다.

• 공업화학
• /
• 제1권2호
• /
• pp.224-231
• /
• 1990

백금촉매의 분산을 향상시키기 위하여 카본블랙의 표면처리, 용매, 계면활성제 및 초음파분산기에 따른 효과를 고찰하였다. 카본블랙을 산화처리하여 카본블랙 표면에 친수성기인 작용기들을 도입함으로써 작용기들이 염화백금산 이온의 anchorage center역할을 하여 이 염화백금산을 환원시킬 때 백금입자(이온)의 이동이나 성장을 억제시켜 미립화 시킬 수 있다고 생각되었다. 혼합용매, 계면활성제, 초음파분산기 등을 이용한 경우, 염화 백금산이온이 anchorage center 역할을 하고 있는 작용기들에 까지 잘 스며들어감으로써 백금촉매의 분산성이 향상됨을 알았다. 혼합용매에 초음파분산기를 사용하여 공기산화시킨 카본블랙에 백금촉매를 담지시킨 결과, 분산성이 가장 우수하였으며 입자크기는 $30A^{\circ}$ 이하로 미립화 되었다.

• 한국재료학회지
• /
• 제19권3호
• /
• pp.156-162
• /
• 2009

Lubricant-based nanofluids were prepared by dispersing carbon nanoparticles in gear oil. In this study, the effects of the particle size, shape and dispersity of the particles on the tribological properties of nanofluids were investigated. Dispersion experiments were conducted with a high-speed bead mill and an ultrasonic homogenizer, and the surfaces of the nanoparticles were simultaneously modified with several dispersants. The effective thermal conductivity of the nanofluids was measured by the transient hot-wire method, and the tribological behaviors of the nanofluids were also investigated with a disk-on-disk tribo-tester. The results of this study clearly showed that the combination of the nanoparticles, the deagglomeration process, the dispersant and the dispersion solvent is very important for the dispersity and tribological properties of nanofluids. Lubricant-based nanofluids showed relatively low thermal conductivity enhancement, but they were highly effective in decreasing the frictional heat that was generated. For nanofluids containing 0.1vol.% graphite particles in an oil lubricant, The friction coefficient in the boundary and fluid lubrication range was reduced to approximately 70% of the original value of pure lubricant.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2008년도 추계학술대회 논문집 Vol.21
• /
• pp.361-362
• /
• 2008

에폭시 메트릭스에 $10{\pm}5nm$ SiO2 입자를 함량별 (1,3,5,7,9wt%)로 혼합하여 초음파 및 균질기를 이용한 분산을 실시하여 나노콤포지트를 제조하였다. 엉킴이 있는 나노입자를 물리적분산법을 이용하여 분산시킬 수 있었고, 그 결과 여러특성을 연구하였다. 기계적 굴곡강도 특성은 나노입자 충진함량 증가에따라 증가되는 경향을 나타내었고, 무충진 에폭시수지에 비하여 상대적으로 높은 굴곡강도를 나타내었다. 나노입자의 충진함량 증가에따라 절연파괴강도는 1wt%에서 가장 높는 절연파괴강도를 기록하였고 함량증가에 따라 약간 감소되는 경향을 보이고 있다. 이는 여러 연구자의 경향과 대체로 유사함을 알 수 있었다.

• 한국재료학회지
• /
• 제17권9호
• /
• pp.493-499
• /
• 2007

Oil-based nanofluids were prepared by dispersing nonconducting fibrous $Al_2O_3$ and spherical AlN nanoparticles in transformer oil. In this study, the effects of wet grinding and surface modification of particles on thermal and electrical properties of nanofluids were investigated. Grinding experiments were conducted with high-speed bead mill and ultrasonic homogenizer and nanoparticles were surface modified by oleic acid and polyoxyethylene alkyl acid ester(PAAE) in n-hexane or transformer oil, at the same time. It is obvious that the combination of nanoparticle, dispersant and dispersion solvent is very important for the dispersity of nanofluids. For nanofluids containing 1.0vol.% AlN particles in transformer oil, the enhancement of thermal conductivity was 11.6% compared with pure transformer oil. However, the electric-insulating property of AlN nanofluids was very low due to used dispersant itself. Therefore, the effect of the dispersant on thermal/electrical/physical properties of the transformer oil should be considered before selecting a proper dispersant.