Ultra-fine $\beta$-SiC powders were fabricated by self-propagating high temperature synthesis process (SHS) using microwave oven. The flexural strength, fracture toughness, and hardness of hot pressed sample at 200$0^{\circ}C$ for 60 min using synthesized SiC powders, which had 2 wt% of Al2O3 and 2.5 wt% of B4C content, showed 438 MPa, 4.15MPa.m1/2 and 28 GPa, respectively. The highest strength, fracture toughness, and hardness of composites containing 4wt% of Al2O3, which had highest relative density of 99.9%, showed 458 MPa, 4.6MPa.m1/2 and 36.2 GPa, respectively.

• 한국세라믹학회지
• /
• 제31권11호
• /
• pp.1283-1292
• /
• 1994

Ultra-fine $\beta$-SiC powders were fabricated by self-propagating high temperature synthesis process (SHS) using chemical furnace. The dependences of the C powders with different surface areas, the molar ratios of C/Si, the weight ratios of chemical fuel content, and pellet diameter-size on synthesis were investigated. Compositional and structural characterization of these powders was carried out by scanning electron micrograph and X-ray diffraction. The $\beta$-SiC powders which had C/Si mole ratio=1.05, 3 times chemical fuel contents, and pellet diameter=20 mm were optimum for synthesis efficiency. By optimizing process-variables, it is possible to fabricate $\beta$-SiC powders which have little secondary phases ($\alpha$-SiC).