• 한국응용과학기술학회지
• /
• 제28권2호
• /
• pp.240-246
• /
• 2011

UV-Curable hybrid coatings were synthesized to improve the surface properties of plastic film. Organic-inorganic coating solutions were prepared by the sol-gel method using urethane-acrylate oligomer, acrylate monomer, photo initiator and tetraethoxysilane (TEOS). Methacryloyloxypropyltrimethoxysilane(MPTMS) was used as a silane coupling agent to improve chemical interaction between inorganic phases and UV curable acrylate. In this study, the surface hardness and adhesive properties were improved with the use of inorganic component. The experimental results showed that UV-Curable hybrid films containing aliphatic urethane oligomer, hexanedioldiacrylate, trimethylolpropanetriacrylate, hydroxy dimethyl acetophenone exhibited good surface properties. Also, the optimum curing conditions were investigated.

• Korean Chemical Engineering Research
• /
• 제50권3호
• /
• pp.421-426
• /
• 2012

불소계 아크릴레이트 2,2,2-trifluoroethylmethacrylate을 사용한 자외선 경화형 유-무기 하이브리드 코팅 막에 있어서 무기물 및 사용되는 유기 단량체의 종류 및 조성이 내 오존성 및 표면 특성에 미치는 영향에 대해 연구하였다. 코팅액은 금속 알콕사이드인 tetraethoxysilane(TEOS)와 실란 커플링제인 methacryloyloxypropyltrimethoxysilane(MPTMS)로 구성된 유-무기 혼성 용액에 2,2,2-trifluoroethylmethacrylate와 자외선 경화를 위한 유기물을 첨가하여 제조되었다. 코팅막은 코팅액을 기재위에 바 코팅 한 후 자외선 경화를 통해 제조되었다. 제조된 코팅 막의 내 오존성은 TEOS의 함량이 증가할수록 내 오존성과 표면경도는 향상되었다. 또한, 불소 함량이 증가할수록 내 오존성은 향상되었지만 표면 경도는 다소 떨어졌다. 우레탄 아크릴레이트를 첨가한 코팅 막은 높은 연필경도를 나타내었다. 코팅 막의 투과도는 TEOS와 2,2,2-trifluoroethylmethacrylate의 함량에 큰 영향을 받지 않았다. 더욱이, 코팅 막은 90% 이상의 높은 투과도를 나타내었다.

• 반도체디스플레이기술학회지
• /
• 제12권2호
• /
• pp.79-84
• /
• 2013

Nanoimprint lithography (NIL) is the next generation photolithography process in which the photoresist is dispensed onto the substrate in its liquid form and then imprinted and cured into a desired pattern instead of using traditional optical system. There have been considerable attentions on NIL due to its potential abilities that enable cost-effective and high-throughput nanofabrication to the display device and semiconductor industry. Although one of the current major research trends of NIL is large-area patterning, the technical difficulties to keep the uniformity of the residual layer become severer as the imprinting area increases more and more. In this paper, with the rolling type imprinting process, a mold, placed upon the $2^{nd}$ generation TFT-LCD glass sized substrate($370{\times}470mm^2$), is rolled by a rubber roller to achieve a uniform residual layer. The prediction of residual layer thickness of the photoresist by rolling of the rubber roller is crucial to design the rolling type imprinting process, determine the rubber roller operation conditions-mpressing force & feeding speed, operate smoothly the following etching process, and so forth. First, using the elasticity theory of contact problem and the empirical equation of rubber hardness, the contact length between rubber roller and mold is calculated with consideration of the shape and hardness of rubber roller and the pressing force to rubber roller. Next, using the squeeze flow theory to photoresist flow, the residual layer thickness of the photoresist is calculated with information of the viscosity and initial layer thickness of photoresist, the shape of mold pattern, feeding speed of rubber roller, and the contact length between rubber roller and mold previously calculated. Last, the effects of rubber roller operation conditions, impressing force & feeding speed, on the residual layer thickness are analyzed with consideration of the shape and hardness of rubber roller.

• 공업화학
• /
• 제16권3호
• /
• pp.342-347
• /
• 2005

하이퍼브랜치 폴리올(HBP-16, 32, 64)과 acrylic acid로부터 광경화형 하이퍼브랜치 아크릴레이트를 합성하였고, 그 물성을 조사하였다. TGA로 측정한 UV 경화필름의 열안정성은 관능기 수가 증가할수록 좀더 높은 온도로 이동하였다. 또한 아크릴 레이트의 관능기 수가 증가할수록 경도, 내마모성, 인장강도가 우수하였으며, 내후성 테스트에서는 아크릴레이트의 관능기수가 증가할수록 황변 지수 값이 증가하는 결과를 보여주었다.

• 한국인쇄학회지
• /
• 제16권3호
• /
• pp.61-80
• /
• 1998

To investigate in influence of photosensitizer used with benzophenone(BP) in the curing rate and physical properties of UV curable hard coating on plastic, we prepared UV curable clear and pigmented coatings with DEA, DMA, NPM and TEA as photosensitizer, respectively. The curing rate calculated from the decrease of the absorbance of acrylic double bond measured by FT-IR spectroscopy increased s follows; DEA>DMA>NPM>TEA. this order could be explained by the reactivity of diethylamino group of DEA and the ease of formation of activated complex between BP and photosensitizer during the curing process. In UV curable pigmented coatings, the order of curing rate increased as follows; DEA>DMA>TEA>NPM. It was found that the curing rate of the pigmented coating can be increased by light scattering of TiO$_2$. The hardness of coating film cured by photosensitization of DEA and DMA is higher than other photosensitizers due to the crosslinking reaction of DEA and DMA radical bound to polymer backbone.

• 마이크로전자및패키징학회지
• /
• 제29권2호
• /
• pp.107-112
• /
• 2022

본 연구에서는 용제를 전혀 사용하지않고 UV경화가 가능한 실버 페이스트를 개발하였다. 무용제(solvent-free) 타입으로 개발한 실버 페이스트의 점도 및 점탄성 측정하였다. 그리고 스크린인쇄로 패턴을 인쇄한 후에 UV경화로 전극도막을 형성시켰다. 형성된 전극도막의 전도성, 연필경도, 접착력에 대해서 평가하였다. 마지막으로 전극도막의 경화특성은 TGA 및 FT-IR로 평가하였다. 이러한 결과를 정리하면 전도성, 접착력, 경화특성에 대해서는 Paste(4), 즉 1.2 ㎛의 구형 실버 파우더와 50 nm 실버 파우더를 72:8%로 혼합한 실버 페이스트가 가장 우수한 물성이 얻어짐을 알 수 있었다.

• Journal of the Korean Wood Science and Technology
• /
• 제34권2호
• /
• pp.58-67
• /
• 2006

The relationship between acoustic property and coating hardness of musical instruments was investigated using a sound level meter and a pendulum hardness tester. Urethane topcoat, oil stain, natural oil varnish, and UV-curable epoxy acrylate coatings were applied on four different substrates: Paulownia coreana, Pinus koraiensis, Castanea crenata var. dulcis and Pinus densiflora. The influence of the coating type on the acoustic properties was stronger than that of the substrate. In the case of an oil stain formed with tacky coating layer, the sound pressure level (SPL) and surface hardness decreased with increasing of coating thickness. In the other coatings, SPL decreased and hardness increased as the coating layer thickened. However, SPL began to increase again at coating thickness above $100{\mu}m$.

• 접착 및 계면
• /
• 제13권4호
• /
• pp.156-162
• /
• 2012

UV 경화형 우레탄아크릴레이트 수지와 유기화클레이를 혼합한 후 UV를 조사하여 경화시킴으로써 폴리우레탄-클레이 나노복합체를 제조하였다. 유기화클레이로서는 Closite20A (C20A) 및 이를 실란처리하여 표면에 아크릴기를 도입한 아크릴변성 C20A를 사용하였다. XRD와 TEM 분석으로부터 제조된 나노복합체는 삽입형 나노복합체이며, 아크릴 변성시킨 C20A가 변성시키지 않은 C20A에 비해 더 잘 분산되는 것을 알 수 있었다. DMTA, 연필경도분석, PET 필름에의 부착성 시험으로부터 클레이 첨가에 의해 유리전이온도와 저장탄성률 및 연필경도가 증가하고 PET 필름에의 부착성이 향상되며, 이러한 물리적 특성의 증가는 아크릴 변성시킨 C20A를 함유한 나노복합체에서 더 크게 발현됨을 알 수 있었다. 또한, 클레이 첨가에 의해 UV경화 시 수반되는 수축을 저하시킬 수 있음을 알았다. 한편, 제조된 나노복합체는 우수한 광투과도를 나타내었으나, 광택도는 나노입자를 함유하지 않은 경우에 비해 다소 저하되었다.

• 한국식품영양학회지
• /
• 제26권1호
• /
• pp.85-91
• /
• 2013

국내산 복숭아의 저장성 증진을 위하여 저선량(0~3.0 $kJ/m^2$)의 UV-C를 조사하고, 저장기간 동안 부패율, 이화학적 변화 및 기호도의 변화를 측정하였다. 부패율의 경우, 대조군은 4일 이후부터는 부패된 복숭아를 보이기 시작하였으며, 저장 8일에는 50.00%의 부패율을 나타내었다. 저선량의 UV-C 처리군은 대조군보다 낮은 부패율을 보였으며, 특히 1.0 및 2.0 $kJ/m^2$의 UV-C 처리군이 가장 낮은 부패율을 나타내었다. 무게 변화의 경우, 대체적으로 대조군 및 UV-C 처리군 모두 저장기간 동안 큰 차이를 보이지는 않았다. pH 변화에서는 UV-C 처리에 의한 차이를 보이지 않았으며, 저장기간 중 pH가 증가하였으나 모든 실험군에서 차이가 없는 것으로 나타났다. 경도의 경우, UV-C 처리 직후에는 모든 실험군에서 차이가 없었으나, 저장 중 대조군의 변화가 가장 많았으며, UV-C 처리군의 경도 변화는 적은 것으로 나타났다. 색도 변화(명도, 적색도 및 황색도)에서는 UV-C 처리 및 저장 중 모든 실험군에서 큰 차이를 보이지는 않는 것으로 나타났다. 맛, 향, 색에 대한 기호도의 변화에서는 UV-C 처리에 의한 변화를 보이지 않았으며, 저장 중 기호도는 감소하였으나 모든 실험군에서 차이가 없는 것으로 나타났다. 조직감 및 종합적 기호도에서는 UV-C 처리에 의한 변화를 보이지 않았으나 저장 중 대조군의 기호도값이 가장 많이 감소하였고, UV-C 처리군의 변화는 적은 것으로 나타났다. 전반적으로 대조군보다는 저선량의 UV-C 처리군이 기호도가 높은 것으로 나타났다.

• 청정기술
• /
• 제16권4호
• /
• pp.245-253
• /
• 2010

대구경 강관 표면 보호를 위해 사용되는 필라멘트 와인딩 공정에 불포화 폴리에스터 (unsaturated polyester: UP)를 이용한 자외선 (ultraviolet) 경화 방법을 적용하고자, UP를 이용한 최적의 UV 경화 조건을 찾아보았다. 기존의 유기계 과산화물을 개시제로 사용한 열경화 방법에서는 개시제의 불안정성, 휘발성 유기물 발생, 열에 약한 대상물질의 변형 등 문제점이 발생하므로 이에 대한 개선책으로 UV 경화방법을 시도하였다. UV 경화에 사용되는 다양한 개시제 중에서 비교적 침투력이 높아서 두꺼운 고분자 층 형성이 가능한 개시제 2 종(Irgacure 819 및 Darocure 1173)을 선정하여 이들의 조합비율에 따라 경화된 UP 고분자에 대한 열역학적, 기계적 물성을 비교 분석하여 우수한 경화조건 (개시제 함량 1.5 phr, 혼합 비율 1:1.2, UV 램프로는 갈륨램프)을 찾아내었다. 또한 UP 광경화수지의 경도, 충격강도, 굴곡강도 향상을 위해 유리섬유를 수지 내에 적층하여 복합재료를 제조하고 이들의 특성을 비교한 결과 충격강도가 매우 향상되었다.