Annealing experiments on albite powders, thin sections, and TEM specimens have been performed utilizing an optical microscope heating stage. Sample orientations were determined by optical microscope and XRD, and then confirmed by TEM diffraction patterns. Partial melting of samples occurred at $1030^{\circ}C$-l2 hr for powder, but at $1060^{\circ}C$-12 hr for TEM specimen. It is difficult to get TEM images of albite microstructures above this temperature due to thickening and the amorphous phase of the melted part. Correlative studies between optical microscopy and TEM indicated that the $1050^{\circ}C$-12 hr annealing in ambient condition was most adequate to observe tweed microstructures in albite through TEM. In situ TEM heating experiments for direct observation of tweed microstructures in albite may require annealing at slightly higher temperatures than $1050^{\circ}C$ considering the high vacuum condition inside TEM.

• Journal of the Korean Society for Heat Treatment
• /
• v.11 no.1
• /
• pp.27-34
• /
• 1998

Effects of different heat treatments on microstructure and damping capacity of Cu-55%Mn alloy were investigated to find an optimum heat treatment condition for a maximum damping capacity. The alloy showed the high level of damping capacity in case of the aging at 375 and $400^{\circ}C$. This is ascribed to the FCC${\rightarrow}$FCT martensitic transformation and microstructural changes from mottled to tweed band type. The damping capacity had a maximum value of 0.33 in logarithmic decrement when the alloy was aged at $375^{\circ}C$ for 14 hours followed by 20 times of thermal cycling between room temperature and $250^{\circ}C$. The refinement of tweed structure by thermal cycling is thought to be responsible for the highest damping capacity.