• Journal of Advanced Marine Engineering and Technology
• /
• v.34 no.2
• /
• pp.303-309
• /
• 2010

Copper tube rolling process using the planetary rolling mill has been studied by using finite element method. This rolling is process that makes copper tube by three-roll with mannesmann method. Also, rolling process has started from the cold working and finished to the hot working. This rolling process has more advantage that make reduction of process and cost than existing extrusion. This process includes various and complex process parameters. Each of the process parameters affects forming result. Therefore, all of the process parameters should be considered in copper tube rolling. Rolling process for copper tube was successfully simulated and it should be useful to determine optimal rolling condition.

• 유체기계공업학회:학술대회논문집
• /
• 2001.11a
• /
• pp.373-380
• /
• 2001

Solid Oxide Fuel Cells (SOFCs) have received considerable attention because of the advantages of high effiiciency, low pollution, cogeneration application and excellent integration with simplified reformer In this paper, we reported development of anode-tubular SOFC by wet process. For making tubular cell, Ni-cermet YSZ anode tube was fabricated using extrusion process, and YSZ electrolyte layer and LSM-YSZ composite, LSM, LSCF cathode layer were coated onto the anode supported tube using slurry dipping process and sintered by co-firing process. By using this tubular cell, we fabricated single cell consisted of the various cathode layers and 4 cell stack with an effective area of $75 cm^2$ per single cell, and evaluated their performance characteristics.

• Korean Journal of Animal Reproduction
• /
• v.19 no.3
• /
• pp.181-189
• /
• 1995

In this study, methods on fabrication of microtool and setting of micromanipulator were examined and relationship between first polar body extrusion rate and maturation time of follicular oocyte, enulceation rae and repetition of trial, and enucleation rate and maturation period were investigated. The results are as follows: 1. Suitable outside diameter of micropipette tube was 1mm. Holding pipette with less than diameter of oocyte was fitred for manipulation, and zona dissection needle was easily operated when its sharp-point had diameter of about 8 ${\mu}{\textrm}{m}$ and length of 300${\mu}{\textrm}{m}$. The injection pipette with 20~35${\mu}{\textrm}{m}$ outside diameter was adequate for injection of blastomere into perivitelline space. 2. Separation of blastomere was effective when zona pellucida had cut with zonadissection needle and the embryo was pipetted gently with the pipette that had narrower diameter than that of embryo until separation of blastomeres had completed. 3. The extrusion rate of first polar body was 78% during 20~24% hours incubation for maturation. 4. According to repetitions of micromanipulation, the enucleation rate was increased to 85% and the time required for enucleation of a oocyte was shortened to 3 min. 5. The extrusion rate of first polar body and enucleation rate were 82 and 76% respectively, in the group of the oocytes cultured for 22 hours. However in the group cultured for 24 hours, the extrusion rate of first polar body and enucleation rate were 53 and 100% respectively.

• Korean Journal of Materials Research
• /
• v.12 no.9
• /
• pp.691-695
• /
• 2002

A low temperature anode-supported tubular solid oxide fuel cell was developed. The anode-supported tube was fabricated using extrusion process. Then the electrolyte layer and the cathode layer were coated onto the anode tube by slurry dipping process, subsequently. The anode tube and electrolyte were co-fired at $140^{\circ}C$, and the cathode was sintered at $1200^{\circ}C$. The thickness and gas permeability of the electrolyte depended on the number of coating and the slurry concentration. Anode-supported tube was satisfied with SOFC requirements, related to electrical conductivity, pore structure, and gas diffusion limitations. At operating temperature of $800^{\circ}C$, open circuit voltage of the cell with gastight and dense electrolyte layer was 1.1 V and the cell showed a good performance of 450 mW/$\textrm{cm}^2$.

• Nuclear Engineering and Technology
• /
• v.51 no.4
• /
• pp.1069-1074
• /
• 2019

A novel fabrication method of oxide dispersion strengthened (ODS) steel cladding tubes for advanced fast reactors has been investigated using the cold spray powder-based materials deposition process. Cold spraying has the potential advantage for rapidly fabricating ODS cladding tubes in comparison with the conventional multi-step extrusion process. A gas atomized spherical 14YWT (Fe-14%Cr, 3%W, 0.4%Ti, 0.2% Y, 0.01%O) powder was sprayed on a rotating cylindrical 6061-T6 aluminum mandrel using nitrogen as the propellant gas. The powder lacked the oxygen content needed to precipitate the nanoclusters in ODS steel, therefore this work was intended to serve as a proof-of-concept study to demonstrate that free-standing steel cladding tubes with prototypical ODS composition could be manufactured using the cold spray process. The spray process produced an approximately 1-mm thick, dense 14YWT deposit on the aluminum-alloy tube. After surface polishing of the 14YWT deposit to obtain desired cladding thickness and surface roughness, the aluminum-alloy mandrel was dissolved in an alkaline medium to leave behind a free-standing ODS tube. The as-fabricated cladding tube was annealed at $1000^{\circ}C$ for 1 h in an argon atmosphere to improve the overall mechanical properties of the cladding.

• Journal of the Korean Ceramic Society
• /
• v.41 no.7
• /
• pp.560-566
• /
• 2004

To fabricate the continuously porous alumina bodies by multi-extrusion process, carbon powder and ethylene vinyl acetate were used as a pore forming agent and a binder, respectively. As the change of extrusion pass number, reduction ratio as well as the volume fraction of core and tube, the porous alumina bodies having various kind of pore size and porosity could be obtained. The porous bodies showed continuous pore shape, high specific surface as well as high bending strength, which were compared with those of commercial alumina bodies. In-vitro study was carried out using MG-63 osteoblast cells to investigate of their biocompatibility. As a result, the cells grew well on top and bottom as well as inside surface of pore. From the result of in-vivo study of 3-dimensional porous alumina bodies using rats, it was confirmed that any inflammatory response was not found in the subcutaneous tissue around porous body. Also the porous bodies removed from the rats were fully covered with well-developed fibrous tissues and showed the formation of new capillary blood vessels.

• Journal of the Korean Ceramic Society
• /
• v.42 no.4
• /
• pp.260-268
• /
• 2005

A heat-resisting diatomite protection tube, using diatomite as a main component, was manufactured through an extrusion molding of ceramic slurry in different component ratios. And its mechanical strength, carbon analysis and microstructural non-homogeneity were investigated. After fixing $60wt\%$ of porous diatomite whose particle size was $50\~100\;{\mu}m$, the optimum mixture ratio with composition variables by changing $1\;wt\%$ of each component that was silica sol$(4.3\~7.3\;wt\%)$ as an inorganic binder, CMC (Sodium CarboxyMethyl Cellulose $(6\~9\;wt\%)$) as an organic binder and paper powder$(4.7\~7.7\;wt\%)$ was obtained. As a result of the investigation on a composition containing $60\;wt\%$ diatomite, $5.3\;wt\%$ silica sol, and $7\;wt\%$ CMC, a heat-resisting protection tube that could be used as a molten steel probe for measuring the temperature and components of molten steel was developed. The bending strength, compressive strength, and elastic modulus of the protection tube developed, that contained $\le2.3\;wt\%$ carbon, were 7.1 MPa, 7.5 MPa, and 1090 MPa, respectively.

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 2001.05a
• /
• pp.36-39
• /
• 2001

Tubular hydroforming has attracted increased attention in the automotive industry recently. In this study, a professional finite element program for analysis and design of tube hydroforming processes has been developed, called HydroFORM-3D, which is based on a rigid-plastic model. With the developed program several hydroforming processes such as a tee extrusion, an automotive rear axle housing and lower arm are analyzed and designed. And also, the Oyane's ductile fracture integral I was calculated from the histories of stress and strain according to every element and then the forming limit of the hydroforming process could be evaluated. The pediction of the bursting failure and the plastic deformation during typical hydroforming processes shows to be reasonable so that this approach can be extended to other various tube hydroforming processes.

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 2009.10a
• /
• pp.332-337
• /
• 2009

Recently, boss and rib test based on backward extrusion process was proposed to quantitative evaluate the interfacial friction condition in bulk forming process. In this test, the tube-shaped punch with hole pressurizes the workpiece so that the boss and rib are formed along the hole and outer surface of the punch. It was experimentally and numerically revealed that the height of boss is higher than that of the rib under the severe friction condition. This work is focused on the effect of the punch design and friction condition on deformation pattern in boss and rib test. From the boss and rib test simulations, it was found that there is slight variation in both the heights of boss and rib according to the length of punch land, nose radius, and face angle. However the hole diameter of the punch and the clearance between the punch and die have a significant influence on the heights of the boss and rib. In addition, the effect of flow stress was also investigated on the deformation patterns through FE simulations.

• Transactions of Materials Processing
• /
• v.18 no.8
• /
• pp.640-645
• /
• 2009

Recently, boss and rib test based on backward extrusion process was proposed to quantitatively evaluate the interfacial friction condition in bulk forming process. In this test, the tube-shaped punch with hole pressurizes the workpiece so that the boss and rib are formed along the hole and outer surface of the punch. It was experimentally and numerically revealed that the height of boss is higher than that of the rib under the severe friction condition. This work is focused on the effect of the punch design and flow stress on deformation pattern in boss and rib test. From the boss and rib test simulations, it was found that there is slight variation in both the heights of boss and rib according to the length of punch land, nose radius, and face angle. However the hole diameter of the punch and the clearance between the punch and die have a significant influence on the calibration curves showing the heights of the boss and rib. In addition, the effect of flow stress on the calibration curves was investigated through FE simulations. It was found that there is no effect of strength coefficient of the workpiece on the calibration curves for estimation of friction condition. On the other hand, the strain-hardening exponent of the workpiece has a significant influence on the calibration curve.