• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2000년도 하계학술대회 논문집
• /
• pp.715-718
• /
• 2000

We studied about electrical, chemical and mechanical characteristics of XLPE by dicumyl peroxide(DCP) and trimethylolpropane triacrylate(TMPTA) content ratio. DCP content was changed from 1.0 to 2.Sphr increasing 0.5phr. TMPTA content was changed 0.5 to 1.5phr increasing 0.5phr. Thermal analysis (DSC) was carried out in order to observe tendency of Tg according to DCP and TMPTA content. Tensile strength was measured in order to observe mechanical strength. In experimental results, content DCP 2.0phr and TMPTA 1.0phr has highest breakdown strength. Content DCP 2.0phr and TMPTA 0.5phr has lowest dielectric constant. Tendency of Tg did not affected by DCP and TMPTA content. Breakdown strength and Specific inductive capacity was measured.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2005년도 하계학술대회 논문집 Vol.6
• /
• pp.127-128
• /
• 2005

UV-curable pressure sensitive adhesives were prepared by blending acrylic copolymer, copolymerized with butyl acrylate (BA), acrylic acid (AA) and vinyl acetate (VAc) by solution polymerization, triethyl amine (TEA) and trimethylolpropane triacrylate (TMPTA). The PSAs were evaluated by peel strength with varying contents of TMPTA and UV dose, and also glass transition temperature($T_g$) of PSAs were measured. When exposed on UV irradiation, the PSAs showed the decreased peel strength and increased $T_g$. And following UV irradiation, the PSAs did not leave any residue on wafer after peel off PSA.

• Macromolecular Research
• /
• 제16권2호
• /
• pp.149-154
• /
• 2008

UV-curable electrolytes inks were prepared by dissolving [2-[(methacryloyloxy)ethyl]dimethyl]propylaminium bromide (MEPAB), 1,5-[bis(2-methacryloxyethyl)dimethyl ammono]penthane dibromide (MDAPD), hexafunctional reactive oligomer (SP1013), trimethylolpropane triacrylate (TMPTA) and a photoinitiator in methanol/2-methoxyethanol. The compositions of the electrolyte inks were MEPAB/MDAPD/SP1013/TMPTA=6/24/17.2/12.8, 15/15/17.2/12.8 and 24/6/17.2/12.8. Humid-membranes were deposited on a gold electrode/alumina electrode using an ink-jet printer equipped with a UV lamp followed by immediate UV curing. The humidity-sensing characteristics including hysteresis, frequency and temperature dependence, response time and water durability were estimated.

• 폴리머
• /
• 제36권5호
• /
• pp.668-676
• /
• 2012

본 연구에서는 실리카 나노입자를 bis[3-(trimethoxysilyl)propyl]amine(BTMA) 실란 커플링제로 표면 개질한 후, 실리카에 도입되는 2차 아미노기인 -NH기와 Michael 부가반응이 가능한 acrylate기를 가지는 trimethylolpropane ethoxylate triacrylate(TMPET)와 3-(acryloyloxy)-2-hydroxypropyl methacrylate(AHM)로 표면 처리를 하여 반응성(meth)acrylate기를 가지는 brush를 도입하는 연구를 수행하였다. 1분자에 Michael 부가반응성이 있는 acrylate기를 3개 갖는 TMPET와 1분자에 반응성이 있는 acrylate기와 반응성이 없는 methacrylate기를 각각 1개씩 갖는 AHM을 사용하여, 처리 몰(mol)수의 변화가 실리카 표면에 도입되는 (meth)acrylate기에 미치는 영향을 Fourier transform infrared spectroscopy(FTIR), elemental analysis(EA) 및 고체 상태 cross-polarization magic angle spinning(CP/MAS) nuclear magnetic resonance spectroscopy(NMR)법을 사용하여 분석하였다. BTMA로 개질된 실리카를 TMPET로 처리하면, 액체상태의 순수 TMPET와 순수 BTMA의 반응과는 달리 TMPET 1분자당 3개씩 결합있는 acrylate기 대부분이 BTMA의 -NH기와 Michael 부가반응이 일어나는 것을 확인하였다. 따라서 BTMA로 처리한 실리카에 Michael 부가반응으로 반응성 (meth)acrylate기를 도입하기 위하여서는 AHM과 같이 Michael 부가반응성이 있는 acrylate기와 Michael 부가반응성이 없는 methacrylate기를 각각 1개씩 가지는 AHM을 사용하는 것이 필요함을 확인하였다.

• Corrosion Science and Technology
• /
• 제12권1호
• /
• pp.27-33
• /
• 2013

According to its merits about high curing speed and low emission of volatile organic compounds, UV curable inorganic-organic coating technology has been developed as an alternative for toxic and carcinogenic chromate-based treatments for years. It is consistently observed that ultra-thin films offer excellent corrosion protection as well as paint adhesion to metals. Based on the tetra-ethylorthosilicate(TEOS) and methacryloxypropyl trimethoxysilane(MPTMS), inorganic sol was synthesized and formed hybrid networks with UV curable acrylic monomer, 6-hexanediol diacrylate(HDDA), trimethylolpropane triacrylate(TMPTA), pentaerylthritol triacrylate(PETA). Several methods were used to test their properties such as salt spray test, potentiodynamic measurement, tape peel test, etc. It was shown that anti-corrosive property and stability of storage were affected by the molecular ratios of inorganic and organic compounds. It was not only the stability of storage, but had a excellent anti-corrosive, paint adhesive, and anti-solvent properties in a final molar ratios of 0.6/0.04/0.86/0.005 (TEOS/MPTMS/Acetone/HNO3) and 0.08/0.106/0.081/0.02 (TMPTA/HDDA/PETA/photo initiator).

• 한국염색가공학회지
• /
• 제11권4호
• /
• pp.1-7
• /
• 1999

Urethane-acrylate propelymers for secondary coating of optical fiber and high - performance material were prepared from the 4,4'-diphenylmethane diisocyanate(MDI), poly(tetramethylene oxide)glycol(PTMG, Mw 650 or 1000), 1,6-hexanediol(HD), 2-hydroxyethyl acrylate(HEA), and dibutyltin dilaurate as a catalyst. UV-Curable polyurethane acrylates were formulated from the urethane-acrylate prepolymers, three types of reactive diluents(DTs) having mono-, di-, and trifunctional-phenoxyethyl acrylate(PEA), hexanediol diacrylate(HDDA), and trimethylolpropane triacrylate(TMPTA), and 1-hydtoxycyclohexyl phenyl ketone(Irgacure 184) as a photoinitiator. The UV-cured films of polyurethane acrylates were obtained by curing using a medium-pressure mercury lamp(U W/cm, $\lambda_{max}=365\;nm)$. In this work, the effects of molecular weights of polyol and diol with low molecular weight into polymer chain on mechanical and dynamic mechanical properties of UV-cured polyurethane acrylates were studied. The structure and properties of the films obtained from the UV photopolymerization of urethane-acrylate prepolymer were investigated by FT-IR spectroscopy, dynamic mechanical measurement, tensile testing, and X-ray diffractometry.

• Elastomers and Composites
• /
• 제57권3호
• /
• pp.100-106
• /
• 2022

Waterborne polyurethane-acrylate(WPUA) dispersions were prepared by surfactant-free emulsion polymerization in a two-step process. In the first step, polytetrahydrofuran, isophorone diisocyanate, dimethylol proponic acid, and 2-hydroxyethyl methacrylate were used to synthesize a vinyl-terminated polyurethane prepolymer. In the second step, styrene, methyl methacrylate, butyl acrylate, and different multi-functional crosslinkers were copolymerized. 1,6-hexanediol diacrylate, trimethylolpropane triacrylate, and pentaerythritol tetraacrylate were used as the crosslinkers, and their effect on the mechanical and thermal properties of WPUA was investigated. Overall, as the number of functional groups of the cross-linker increased, the gel fraction improved to 79.26%, the particle size increased from 75.9 nm to 148.7 nm, and the tensile strength was improved from 5.86 MPa to 12.40 MPa. In thermal properties, the glass transition temperature and decomposition temperature increased by 9.9℃ and 18℃, respectively. The chemical structures of the WPUA dispersions were characterized by Fourier-transform infrared spectroscopy. The synthesized WPUA has high potential for applications such as coatings, leather coatings, adhesives, and wood finishing.

• 공업화학
• /
• 제2권2호
• /
• pp.175-184
• /
• 1991

PVC 와 Polystyren 과 같은 고분자가 자외선에 노출될 때 이들 표면을 보호하고, 물성을 유지하기 위해서 자외선 경화 도료를 도장하지만, PVC 는 epoxy acrylate 에 대해서, 그리고 Polystyren 은 대부분의 UV도료에 부착력이 약하므로, 반응희석제의 조성을 변화시키거나, 다관능기 acrylate를 표면에 photografting 시키거나, 표면을 광화학적으로 활성화시켜 부착력을 향상시킴을 목적으로 하였다. 미리 침투시킨 광개시제에 의한 grafting이나 표면 활성화로 부착력은 현저히 증가하였고, 각 희석제에 있어 Tripropylene glycol diacrylate는 유연성 향상과 부착력 증가를 가져오나, 황변 현상과 표면 산화에 의한 경화 밀도의 증가로 grafting을 제외한 다른 도장 방법은 시간이 지남에 따라 도막의 부착력이 감소하였다. 여기에 비해 Trimethylol propane triacrylate 는 원래 다관능기에 의해 높은 경화 밀도를 가지고 이에 따른 단단한 도막 때문에 부착력에 문제가 있으나, 두가지 도장법에서는 오히려 다관능기에 의한 화학 결합으로 부착력이 향상되었다. 그리고, 고분자 표면의 표면 에너지를 활성화를 통해 증가시킴으로 해서 UV 도료의 상용성 문제를 grafting 과 표면 활성화를 통해 해결해 도료 배합의 다양화와 기능화를 가져올 것이 기대된다.

• 공업화학
• /
• 제26권4호
• /
• pp.439-444
• /
• 2015

본 연구에서는 차선도료로 MMA (methyl metacrylate) 수지계 열경화성 수지를 선정하여 차선의 내구성능과 재귀반사성능을 개선할 수 있는 최적의 열경화성 차선도료를 설계하고자 하였다. 특히 현장 적용성을 향상시키기 위하여 차선도료의 경화시간을 8 min으로 단축하기 위해 주재의 구성요소를 설계하였다. 실험 결과 MMA 모노머($Tg=105^{\circ}C$) 15.6 wt%에 PMMA (ploymethyl metacrylate, MW = 70,000, $Tg=60^{\circ}C$) 6.0 wt%와 TMPTA (trimethylolpropane triacrylate, MW = 338, $Tg=27^{\circ}C$) 1.2 wt%를 배합한 TSRM-6가 부착강도 등 도료물성이 우수하여 최적 배합비율로 결정하였다. 열경화성 차선도료의 도장조건은 분사 전 반드시 균일한 혼합이 이루어져야 하며 최적 설계된 TSRM-6에 우천용 유리알을 사용한 경우 마모시험 횟수 20만 회에서 야간재귀반사성능계수는 $431mcd{\cdot}m^{-2}{\cdot}lux^{-1}$ (건조 조건), $354mcd{\cdot}m^{-2}{\cdot}lux^{-1}$ (젖은 조건), $172mcd{\cdot}m^{-2}{\cdot}lux^{-1}$ (비오는 조건)으로 우수한 성능을 나타내었다.

• Korean Chemical Engineering Research
• /
• 제49권1호
• /
• pp.75-82
• /
• 2011

본 연구에서는 스테인레스 스틸(stainless steel)의 표면 코팅용 광경화 필름 개발을 위하여 isophorone diisocyanate (IPDI), polycaprolactone triol(PCLT), 2-hydroxyethyl acrylate(HEA), 그리고, 희석제로서 trimethylolpropane triacrylate (TMPTA)와 acrylic acid(AA)의 첨가비율을 달리한 광경화형 poly(urethane acrylate-co-acrylic acid)(PU-co-AA) 필름을 성공적으로 제조하였으며, 제조한 PU-co-AA 필름의 모폴로지, 접착특성, 기계적 특성, 전기적 특성 등에 대한 AA 첨가량의 영향을 조사하였다. 모든 PU-co-AA 필름은 비정형 구조를 나타내었으나, AA의 함량이 증가할수록 분자 규칙 및 패킹밀도는 감소하였다. 접착특성은 AA 함량 50% 이상에서는 접착력 5B 수준으로 스테인레스 스틸에 대한 우수한 접착특성을 나타내었으며, AA 함유량이 0%에서 66%까지 증가함에 따라 Pull-off strength법 접착력은 6~31 $kg_f/cm^2$ 로 선형적으로 증가하였다. 광경화 폴리우레탄 아크릴레이트의 접착력을 증가시키기 위한 유연한 사슬구조와 2관능기를 가진 AA의 도입은 다관능기의 TMPTA의 높은 가교밀도를 줄임으로써 효과적인 것을 확인할 수 있었으며, AA 함량이 증가함에 따라 접촉각의 감소와 젖음성의 향상을 확인하였다. 한편, 유연한 사슬 및 곁사슬 -COOH를 가진 AA의 도입은 규칙성 및 패킹밀도의 감소를 나타내며, 이는 PU-co-AA 필름의 경도 저하를 나타내며, 또한 AA의 분자 내의 작용기 -COOH는 고분자 필름 내의 분극현상을 증가시킴으로써 유전상수의 증가 경향을 나타내었다. 결론적으로 PU-co-AA 필름의 물리적 특성은 첨가한 AA의 함량에 크게 의존함을 확인할 수 있었다. 또한, 광경화 폴리우레탄 아크릴레이트에 아크릴산 AA의 도입은 사슬의 유연성 증가와 가교밀도의 감소 영향으로 스테인레스 스틸과의 접착력을 향상시키는데 매우 효과적인 방법임을 확인할 수 있었다.