• The Plant Pathology Journal
• /
• v.26 no.4
• /
• pp.421-423
• /
• 2010

New sources of barley (Hordeum vulgare L.) resistant to spot blotch, caused by Cochliobolus sativus, are needed to provide effective resistance because of the rapid change pathotype patterns of C. sativus in fields. The purposes of our study were to develop a method to screen barley for resistance to spot blotch disease and then use this methodology to screen barley genotypes for resistance to the major virulent pathotype Pt4 in barley populations in Syria. A transparent tape method, in which a conidial suspension of C. sativus was dropped onto transparent tape and placed, treated-side down, on the second leaf surface of barley plants. Disease symptoms of fungus were easily detected on the leaves covered by the transparent tape after 48h of inoculation. The transparent tape method was repeatable and the disease scores obtained were correlated (r = 0.91, P = 0.001) with those obtained by the seedling assay. This method may be beneficial in various plant pathology breeding programs.

• Journal of the Korean Ceramic Society
• /
• v.41 no.4
• /
• pp.277-283
• /
• 2004

To fabricate green sheet of transparent dielectric for PDP front panel, dispersion of transparent dielectric slurry, density, and mechanical properties of green sheets have been investigated as a function of amount and composition of organic additives. Measurements of sedimentation and viscosity were employed to determine a proper dispersant and its amount for a well dispersed transparent dielectric powders in non-aqueous system. Green sheets, having various ratios of transparent dielectric powders to transparent dielectric powders＋ binder＋plasticizer and binder to binder＋plasticizer, were fabricated. All the tape casting slurries showed shear thinning effect, that is, the apparent viscosity decreased with the increase of shear rate. It was found that the amount and composition of organic additives were main variables to affect densities and mechanical properties of transparent dielectric green sheets for PDP.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.17 no.10
• /
• pp.1107-1113
• /
• 2004

Dry film method for large size of PDP(Plasma Display Panel) module has been actively investigated. This method for lead-free transparent dielectric formation depends on green sheet technology. By adjusting the composition of transparent dielectric powders and organics, uniformly dispersed slurry was fabricated, Viscosity of the slurry exhibited pseudoplastic behavior for tape casting, Cast green sheets were tested under tensile condition at room temperature. It was found that the increase in transparent dielectric powder and binder ratio leads to decrease in strain to failure of green sheets from 120 % to 34 % and from 255 % to 4 %, respectively. Tensile strength of green sheets decreased abruptly with increase of transparent dielectric powder ratio, with minimum at 0.13 MPa. On the other hand, tensile strength increased continuously from 0.1 MPa to 2.4 MPa with increase of binder ratio. The green sheets were attached on the glass substrate and heated by following firing schedule. As a result, the best result was obtained when fired at 580 $^{\circ}C$ for 15 min and had transmittance of 78 % in visible range 550 nm.

• Journal of the Microelectronics and Packaging Society
• /
• v.27 no.3
• /
• pp.73-76
• /
• 2020

Silver nanowires (AgNWs) intrinsically possess high conductivity, ductility, and network structure percolated in a low density, which have led to many advanced applications of transparent and flexible electronics. Most of these applications require patterning of AgNWs, for which photolithographic and printing-based techniques have been widely used. However, several drawbacks such as high cost and complexity of the process disturb its practical application with patterning AgNWs. Herein, we propose a novel method for the patterning of AgNWs by employing UV-curable adhesive tape with a structure of liner/adhesive layer/polyolefin (PO) film and UV irradiation to simplify the process. First, the UV-curable adhesive tape was attached to AgNWs/polyurethane (PU), and then selectively exposed to UV irradiation by using a photomask. Subsequently, the UV-curable adhesive tape was peeled off and consequently AgNWs were patterned on PU substrate. This facile method is expected to be applicable to the fabrication of a variety of low-cost, shape-deformable transparent and wearable devices.

• Journal of the Korean Ceramic Society
• /
• v.44 no.10
• /
• pp.548-553
• /
• 2007

Ceramic green sheets consisting Bi-based glass frit were fabricated for an application to PDP transparent dielectric front panel. The dispersion condition of the slurry for tape casting was pre-examined, and two kinds of hinder and plasticizer were used in the non-aqueous slurry system. In the fabrication process for the frit film, the properties such as dry and firing shrinkage, elongation, and transmittance were examined at the condition of various mixing ratio of plasticizers. In the mixing ratio of polyethylene glycol to dibutyl phthalate of 3:5wt%, a good adhesion, elongation and transmittance were observed at the firing temperature of $580^{\circ}C$. The photograph for the cross section of the interface was also showed a dense microstructure.

• Journal of Industrial Convergence
• /
• v.21 no.8
• /
• pp.35-42
• /
• 2023

Recently, electronic devices with bendable electronic devices based on flexible substrates are being sold, and therefore, the purpose of this study is to evaluate the possibility of flexible substrates of conductive transparent tapes. As a transparent electrode, carbon nanotube (CNT) was formed by the coating method developed by the research team, and samples coated up to 5 times were fabricated. The surface resistance and transmittance of the substrate were measured, and both resistance and transmittance decreased as the number of CNT coatings increased. After the tape was detached from the glass, the surface resistance slightly increased in all samples, and the transmittance increased by about 10% in all measured wavelength ranges because the glass was removed. Next, the tape coated with CNT twice was used to a bending test 20,000 times under the condition of a radius of curvature of 2 mm. The electrical and optical properties before and after bending did not change, which means that there was no change in CNT properties due to bending.

• 한국초전도학회:학술대회논문집
• /
• v.9
• /
• pp.315-318
• /
• 1999

Bi$_{2}Sr_{2}CaCu_{2}O_{\delta}$ superconducting films were rapidly fabricated on copper tape by liquid reaction between a Cu-free precursor and Cu tape (LiReac-PreCu) method. Those thick films were well oriented along the c-axis. The precursor was made by melt-quenched technology using twin roller. The melt-quenched films were transparent and glossy yellow in appearance. These films which were the compostion of Bi$_2SrCaO_y$, Bi$_3Sr_2CaO_z$ were placed on copper tape and then heated at various temperatures for several minutes in air. They were analyzed using X-ray powder diffraction, SEM, a DC four-probe method. The mechanism of superconducting phase formation . from the melt-quenched precursor on Cu tape was studied

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.6 no.6
• /
• pp.497-501
• /
• 2005

Dry film method was applied to fabricate lead-free transparent dielectric fur PDP(Plasma Display Panel). From various slurry compositions, it was able to find out the. best composition for producing high density green sheet. The slurry exhibited shear thinning characteristics which are known to be suitable fur producing a high quality green sheet. The thermal expansion coefficient of the fabricated transparent dielectric was measured to be $97{\times}10^{-7}/^{\circ}C$ which is close to the value of the glass substrate(PD-200). Cross sectional SEM of the transparent dielectric layer on PD-200 showed that the two layers were well attached each other with no observable gaps between them.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 1995.11a
• /
• pp.302-305
• /
• 1995

ITO(indium tin oxide) that is both conductive in electricity and transparent to the visible ray is called transparent conducting thin film. Nowaday, according to the development of flat panel display such as LCD(Liquid Crystal display, EL(electolumine- scence display), PDP(plasma display panel), ECD(electrocromic display), the higher quality in the low temperature process has been asked to reduce the production cost and to have a good uniformity on a large substrate. In this study, we prepared indium tin oxide(ITO) by a cylindrical DC magnetron sputtering with Indium-tin (9:1) alloy target instead of indium-tin oxide target. To reduce the defact in ITO, the effect on ITO by varing the magnetic field intensity and the applied voltage ares studied. the resistivity of the film deposited in oxygen partial pressure of 5% and substrate temperature of 140$^{\circ}C$. is 1.6${\times}$10$\^$-1/$\Omega$$.$cm with 85% optical transmission in viaible ray.

• Current Photovoltaic Research
• /
• v.2 no.1
• /
• pp.14-17
• /
• 2014

In this paper, indium reduced materials for transparent conductive electrodes (TCE) were fabricated and their physical properties were evaluated. Two of materials, indium-zinc-tin oxide (IZTO) and aluminum (Al) were selected as TCE materials. In case of IZTO nanoparticles, composition ratios of In, Zn and Sn is 8:1:1 were synthesized. Size of the synthesized IZTO nanoparticles were less than 10 nm, and specific surface areas were about $90m^2/g$ indicating particle sizes are very fine. Also, the IZTO nanoparticles were well crystallized with (222) preferred orientation despite it was synthesized at the lowered temperature of $300^{\circ}C$. Composition ratios of In, Zn and Sn were very uniform in accordance with those as designed. Meanwhile, Al was deposited onto glass by sputtering in a vacuum chamber for mesh architecture. The Al was well deposited onto the glass, and no pore was observed from the Al surface. The sheet resistance of Al on glass was about $0.3{\Omega}/{\square}$ with small deviation of $0.025{\Omega}/{\square}$, and adhesion was good on the glass substrate since no pelt-off part of Al was observed by tape test. If the Al mesh is combined with ink coated layer which is consistent of IZTO nanoparticles, it is expected that the good and reliable metal mesh architecture for TCE will be formed.