• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.19 no.1
• /
• pp.105-112
• /
• 2018

This paper proposes a method for fabricating heatable glass using the conduction characteristics of metal thin films deposited on the surface of Low-e(Low emissivity) glass. The heating value of Low-e glass depends on the Joule heat caused by Low-e glass sheet resistance. Hence, its prediction and design are possible by measuring the sheet resistance of the material. In this study, silver electrodes were placed at 50 mm intervals on a soft Low-e glass sample with a low emissivity layer of 11 nm. This study measured the sheet resistance using a 4-point probe, predicted the power consumption and heating value of the Low-e glass, and confirmed the heating performance through fabrication and experience. There are two conventional methods for manufacturing heatable glass. One is a method of inserting nichrome heating wire into normal glass, and the other is a method of depositing a conductive transparent thin film on normal glass. The method of inserting nichrome heating wire is excellent in terms of the heating performance, but it damages the transparency of the glass. The method for depositing a conductive transparent thin film is good in terms of transparency, but its practicality is low because of its complicated process. This paper proposes a method for manufacturing heatable glass with the desired heating performance using Low-e glass, which is used mainly to improve the insulation performance of a building. That is by emitting a laser beam to the conductive metal film coated on the entire surface of the Low-e glass. The proposed method is superior in terms of transparency to the conventional method of inserting nichrome heating wire, and the manufacturing process is simpler than the method of depositing a conductive transparent thin film. In addition, the heat characteristics were compared according to the patterning of the surface thin film of the Low-e glass by an emitting laser and the laser output conditions suitable for Low-e glass.

• 한국신재생에너지학회:학술대회논문집
• /
• 2011.05a
• /
• pp.121.2-121.2
• /
• 2011

Aluminum-doped Zinc Oxide (AZO) is considered as an excellent candidate to replace Indium Tin Oxide (ITO), which is widely used as transparent conductive oxide (TCO) for electronic devices such as liquid crystal displays (LCDs), organic light emitting diodes (OLEDs) and organic solar cells (OSCs). In the present study, AZO thin film was applied to the transparent electrode of a channel-shaped flexible organic solar cell using a low-temperature selective-area atomic layer deposition (ALD) process. AZO thin films were deposited on Poly-Ethylene-Naphthalate (PEN) substrates with Di-Ethyl-Zinc (DEZ) and Tri-Methyl-Aluminum (TMA) as precursors and $H_2O$ as an oxidant for the atomic layer deposition at the deposition temperature of $130^{\circ}C$. The pulse time of TMA, DEZ and $H_2O$, and purge time were 0.1 second and 20 second, respectively. The electrical and optical properties of the AZO films were characterized as a function of film thickness. The 300 nm-thick AZO film grown on a PEN substrate exhibited sheet resistance of $87{\Omega}$/square and optical transmittance of 84.3% at a wavelength between 400 and 800 nm.

• Transactions on Electrical and Electronic Materials
• /
• v.13 no.5
• /
• pp.241-244
• /
• 2012

Antimony doped tin oxide (ATO) thin films on glass substrate were prepared by the chemical solution deposition (CSD) method, using sol-gel solution synthesized by non-alkoxide precursors and the sol-gel route. The crystallinity and electrical properties of ATO thin films were investigated as a function of the annealing condition (both annealing environments and temperatures), and antimony (Sb) doping concentration. Electrical resistivity, carrier concentration, Hall mobility and optical transmittance of ATO thin films were improved by Sb doping up to 5~8 mol% and annealing in a low vacuum atmosphere, compared to the undoped tin oxide counterpart. 5 mol% Sb doped ATO film annealed at $550^{\circ}C$ in a low vacuum atmosphere showed the highest electrical properties, with electrical resistivity of about $8{\sim}10{\times}10^{-3}{\Omega}{\cdot}cm$, and optical transmittance of ~85% in the visible range. Our research demonstrates the feasibility of low-cost solution-processed transparent conductive oxide thin films, by controlling the appropriate doping concentration and annealing conditions.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2001.11a
• /
• pp.525-528
• /
• 2001

ZnO:Al thin film can be used as a transparent conducting oxide(TCO) which has low electric resistivity and high optical transmittance for the front electrode of amorphous silicon solar cells and display devices. This study of electrical, crystallographic and optical properties of Al doped ZnO thin films prepared by Facing Targets Sputtering (FTS), where strong internal magnets were contained in target holders to confine the plasma between the targets, is described. Optimal transmittance and resistivity was obtained by controlling flow rate of O$_2$ gas and substrate temperature. When the of gas rate of 0.3 and substrate temperature 200$^{\circ}C$ , ZnO:Al thin film had strongly oriented c-axis and lower resistivity(<10$\^$-4/Ω-cm).

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.22 no.2
• /
• pp.137-141
• /
• 2009

AZO transparent conductive thin films were grown on $SiO_2$/Si and glass substrates using diethylzinc (DEZ) and trimethylaluminium (TMA) as the precursor and $H_2O$ as oxidant by atomic layer deposition. The structural, electrical, and optical properties of the AZO films were characterized as a function of film thickness at a deposition temperature of $150^{\circ}C$. The AZO films with various thicknesses show well-crystallized phases and smooth surface morphologies. The 190-nm-thick AZO films grown on Coming 1737 glass substrates exhibit rms(root mean square) roughness of 8.8 nm, electrical resistivity of $1.5{\times}10^{-3}\;{\Omega}-cm$, and an optical transmittance of 84% at 600nm wavelength. Atomic layer deposition technique for the transparent conductive oxide films is possible to apply for the deposition on flexible polymer substrates.

• Proceedings of the KIEE Conference
• /
• 2009.07a
• /
• pp.1351_1352
• /
• 2009

We deposited $SnO_2$:F thin films by atomospheric pressure chemical vapor deposition(APCVD) on corning glass. $SnO_2$:F films were used as transparent conductive oxide (TCO) electrode for Si thin film solar cells. We have investigated structural, electrical and optical properties of $SnO_2$:F thin films and fabricated thin film Si solar cells by plasma enhanced CVD(PECVD) on $SnO_2$:F thin films The cells were characterized by I-V measurement using AM1.5 spectra. Conversion efficiency of our cells were between 5.61% and 6.45%.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2016.02a
• /
• pp.312.1-312.1
• /
• 2016

We have deposited ZnO thin films by ultraviolet (UV) enhanced atomic layer deposition using diethylznic (DEZ) and water (H2O) as precursors with UV light. The atomic layer deposition relies on alternating dose of the precursor on the surface and subsequent chemisorption of the precursors with self-limiting growth mechanism. Though ALD is useful to deposition conformal and precise thin film, the surface reactions of the atomic layer deposition are not completed at low temperature in many cases. In this experiment, we focused on the effects of UV radiation during the ALD process on the properties of the inorganic thin films. The surface reactions were found to be complementary enough to yield uniform inorganic thin films and fully react between DEZ and H2O at the low temperature by using UV irradiation. The UV light was effective to obtain conductive ZnO film. And the stability of TFT with UV-enhanced ZnO was improved than ZnO by thermal ALD method. High conductive UV-enhanced ZnO film have the potential to applicability of the transparent electrode.

• Proceedings of the IEEK Conference
• /
• 1998.06a
• /
• pp.391-394
• /
• 1998

The effect of the heat treatment of the AZO transparent conductive film prepared by rf magnetron sputtering was investigated. The variations of the electrical and optical properties with heat treatment ambient and temperature were studied. After the heat treatment in air above 300.deg. C, the resistivity of AZO films increased by 1 to 8 orders of magnitude. However, no significant change in the AZO films after th eheat treatment in vacuum was not observed.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2007.11a
• /
• pp.455-456
• /
• 2007

Optically transparent, highly conductive coating have been major theme of thin film science efforts for some years. In this work, t-MWNT(thin Multi-walled Carbon Nanotubes) are acid treated, then the stable dispersion of t-MWNTs in polar solvent such as alcohols, was achieved by sonication. The transparent conducting films are prepared using the one component solution of t-MWNT/epoxy binder via spray coating on glass substrate. The characterization of acid treated t-MWNTs was performed by Raman spectrometer. The opto-electrical properties of conducting films are analyzed by the binder concentration, and the effect of co-solvent on the compatibility and dispersibility of one component t-MWNT/epoxy binder solutions are discussed.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2006.06a
• /
• pp.103-104
• /
• 2006

Transparent conductive oxide (TCO) are necessary as front electrode for increased efficiency of LED. In our paper, transparent conducting alminum-doped Zinc oxide films (AZO) were prepared by rf magnetron sputtering on glass (corning 1737) substrate, were then annealed at temperature $400^{\circ}C$ for 2hr. The smooth AZO films were etched in diluted HCL (0.5%) to examine the surface morphology properties as a variation of the time. The surface morphology of AZO films increased as a time. We observed texture structure of AZO thin film etched for 1min.