• The Journal of Advanced Prosthodontics
• /
• 제15권5호
• /
• pp.238-247
• /
• 2023

PURPOSE. The purpose of this study was to assess the effect of resin cement shade on the color of different novel ultratranslucent monolithic zirconia and lithium disilicate veneer materials. MATERIALS AND METHODS. For a total of 40 specimens, flat cylindrical discs with a 9-mm diameter and 0.5-mm thickness were created using CAD/CAM technology. The specimens were divided into five groups according to their material (n = 8) (e.max, Prettau, Aidite, Shofu and Dima) using A1 shade. Resin discs with the same diameter and shade as the specimens served as tooth-colored substructures. Three shades (neutral, light and warm) of resin cement try-in pastes (Variolink Esthetic LC) were used as the luting cement material. The color of each material group was measured before and after cementation using the three cement shades, and the CIE L^*a^*b^* coordinates were obtained with a spectrophotometer. Values for the translucency parameter (TP) and color change delta E (E) before (baseline) and after cementation of each specimen were determined. To compare differences among the material groups within each shade of cement and among various shades of cement within each material, the data were analyzed using one-way ANOVA and post hoc testing. RESULTS. Color coordinates L^*, a^* and b^* significantly changed after the application of try-in pastes relative to baseline values, with a noticeable decrease in lightness (L^*) (P < .05). A significant color change (ΔE) was observed in all tested materials after cementation, with ΔE values exceeding 3.3 (P < .05). Although TP changed after cementation for most materials tested, these changes were not statistically significant (P > .05). Shofu and Dima ceramics showed the lowest TP values, while Aidite and Prettau showed the highest TP values. For e.max, translucency decreased after cementation with neutral and warm shades, and it significantly increased after cementation with a light shade. CONCLUSION. The shade of cement significantly altered the final color of the ceramic veneer material to a level above the threshold at which the clinical perception of color change occurred (> 3.3). The TP was not influenced by the cement shade. The translucency levels of the novel ultratranslucent multilayer monolithic zirconia ceramics Aidite and Prettau were higher than that of the lithium disilicate e.max material.

• 대한치과보철학회지
• /
• 제61권3호
• /
• pp.179-188
• /
• 2023

목적. 이 연구의 목적은 알루미나 입자 공기분사 및 프라이머 표면처리가 각각 두 가지 종류의 지르코니아(3 mol% yttria-stabilized tetragonal zirconia polycrystal; 3Y-TZP, 5 mol% partially stabilized zirconia; 5Y-PSZ)와 레진시멘트의 전단응력에 미치는 영향을 평가하는 것이다. 재료 및 방법. 완전 소결된 14.0×14.0×2.0 mm 크기의 두가지 다른 종류의 지르코니아 시편(3Y-TZP, 5Y-PSZ)을 각각 40개씩 제작하고 400, 600, 800 그릿의 실리콘 카바이드 종이로 연마 후 에폭시 레진에 매립하였다. 이들을 각각 4개의 대조군, 50 ㎛ 알루미나 입자 공기분사 사용군, 프라이머 사용군, 50 ㎛ 알루미나 입자 공기분사와 프라이머로 표면을 처리한 한 후 레진시멘트(PANAVIA V5)로 접착하였다. 그 후 증류수(37℃)에 24시간 보관 후 전단결합강도 실험을 시행, Kolmogorov-Smirnov & Shapiro-Wilk test를 사용해서 정규성을 확인한 후, 모수적 방법인 이원배치분산분석을 사용하여 지르코니아 종류 및 표면처리 방법에 따른 전단결합강도의 상호작용 및 통계적 차이를 분석하였다. 이후 Dunnett T3를 이용해 사후검정을 하였다. 결과. 이배치분산분석 결과 지르코니아 종류에 따른 전단결합강도는 각 군간에 유의미한 차이를 보이지 않았지만(P > .05), 표면처리 방법에 따른 전단결합강도는 50 ㎛ 알루미나 입자 공기분사 사용군, 프라이머 사용군, 50 ㎛ 알루미나 공기 분사와 프라이머를 사용한 군에서는 유의미한 상관관계를 보였다(P < .05). Dunnett T3 사후검정 결과 지르코니아의 종류에 상관없이 전단결합강도는 샌드블라스팅 & 프라이머 > 프라이머 > 샌드블라스팅 > 대조군 순서로 나타났다(P < .05). 결론. 본 연구 결과에 따르면 지르코니아 종류에 따른 전단결합 강도 차이는 없었다. 지르코니아 표면의 기계적 화학적 표면처리를 동시에 했을 때 가장 높은 전단결합강도를 보였다.