• Corrosion Science and Technology
• /
• v.12 no.5
• /
• pp.203-208
• /
• 2013

The electrocoating for automotive bodies is pigmented with a mixture of titanium dioxide and kaolin. In this study, the effects of titanium dioxide and kaolin contents in coating on electrodeposition process, drying, and surface properties such as surface roughness, gloss, impact resistance and corrosion resistance were investigated. Titanium dioxide and kaolin in coating do not have a decisive effect on curing reaction during drying and corrosion resistance but on gloss, surface roughness, impact resistance and electrodeposition process of coating. According to its size and shape on coating surface, pigment contents increased during drying process. However, the contents of kaolin and $TiO_2$ in coating didn't affect the corrosion resistance on zinc phosphated substrate, and the curing properties.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2003.10a
• /
• pp.59-59
• /
• 2003

In recent, various functional coatings on artificial tooth implants have been conducted to enhance the bonding strength between implants and bones. Despite of these efforts, some previous reports argued that an adhesion strength between titanium implant and the final coatings like hydroxyapatite(HA) is weaker than the strength between coating and bone. In order to increase the adhesion force between the final coating and implant surface, TiN/DLC based functionally graded coating, which has higher mechanical strength than the titanium implant, was applied as a middle layer between titanium implant and final coating. Particularly we finally coated a biocompatible hydroxyapatite film on the DLC layer and examined the mechanical properties. As a result, TiN/DLC based functionally graded coating showed the higher adhesion strength compared with hydroxyapatite single layer coating on the titanium implant.

• The Journal of Korean Academy of Prosthodontics
• /
• v.45 no.5
• /
• pp.601-610
• /
• 2007

Statement of problem: The adhesion between titanium and ceramic is less optimal than conventional metal-ceramic bonding, due to reaction layer form on cast titanium surface during porcelain firing. Purpose: This study characterized the effect of titanium-ceramic adhesion after gold and TiN coating on cast and wrought titanium substrates. Material and method: Six groups of ASTM grade II commercially pure titanium and cast titanium specimens$(13mm{\times}13mm{\times}1mm)$ were prepared(n=8). The conventional Au-Pd-In alloy served as the control. All specimens were sandblasted with $110{\mu}m\;Al_2O_3$ particles and ultrasonically cleaned for 5min in deionized water and dried in air before porcelain firing. An ultra-low-fusing dental porcelain (Vita Titankeramik) was fused on titanium surfaces. Porcelain was debonded by a biaxial flexure test at a cross head speed of 0.25mm/min. The excellent titanium-ceramic adherence was exhibited by the presence of a dentin porcelain layer on the specimen surface after the biaxial flexure test. Area fraction of adherent porcelain (AFAP) was determined by SEM/EDS. Numerical results were statistically analyzed by one-way ANOVA and Student-Newman-Keuls test at ${\alpha}=0.05$. Results: The AFAP value of cast titanium was greatest in the group 2 with TiN coating, followed by group 1 with Au coating and the group 3 with $Al_2O_3$ sandblasting. Significant statistical difference was found between the group 1, 2 and the group 3 (p<.05). The AFAP value of wrought titanium was greatest in the group 5 with TiN coating, followed by the group 4 with Au coating and the group 6 with $Al_2O_3$ sandblasting. Conclusion: No significant difference was observed among the three groups (p>.05). The AFAP values of the cast titanium and the wrought titanium were similar. However the group treated with $Al_2O_3$ sandblasting showed significantly lower value (p<.05).

• International Journal of Oral Biology
• /
• v.37 no.1
• /
• pp.9-16
• /
• 2012

The aim of this study was to evaluate surface characteristics and biological properties of the dentin -derived hydroxyapatite (HA) coating on titanium substrate. Dentinderived HA was obtained from extracted human teeth using a calcination method at $850^{\circ}C$. The commercially pure titanium (cp-Ti, ASTM Grade II) was used as a metallic substrate and a radio frequency magnetron sputtering method was employed as a coating method. Scanning electron microscopy (SEM) and energy dispersive X-ray analysis (EDX) were utilized to investigate the coating aspects and composition. Atomic forced microscopy (AFM) and a surface profiler were used to assess the surface morphology and roughness. Corrosion tests were performed in phosphate-buffered saline at a $36.5{\pm}1^{\circ}C$ in order to determine the corrosion behavior of the uncoated and coated specimens. The biocompatibility of dentin-derived HA coated specimens with fetal rat calvarial cells and human gingival fibroblasts was assessed by SEM and cell proliferation analysis. The results showed that the dentin-derived HA coatings appeared to cover thinly and homogeneously the surfaces without changing of the titanium substrate. The EDX analysis of this the coating surface indicated the presence of Ca and P elements. The mean surface roughness of cp-Ti and dentin-derived coating specimens was $0.27{\mu}m$ and, $1.7{\mu}m$, respectively. Corrosion tests indicated a stable passive film of the dentin-derived HA coating specimens. SEM observations of fetal rat calvarial cells and human fibroblast cells on coated surfaces showed that the cells proliferated and developed a network of dense interconnections. The cells on all specimens proliferated actively within the culture period, showing good cell viability. At day 1 and 3, dentin-derived coating specimens showed 89% and 93% cell viability, respectively, when normalized to cp-Ti specimens. These results suggest that dentin-derived HA coating using the RF magnetron sputtering method has good surface characteristics and biocompatibility.

• The Journal of Korean Academy of Prosthodontics
• /
• v.45 no.2
• /
• pp.169-181
• /
• 2007

Statement of problem: Titanium is well known as a proper metal for the dental restorations, because it has an excellent biocompatibility, resistance to corrosion, and mechanical property. However, adhesion between titanium and dental porcelains is related to the diffusion of oxygen to the reaction layers formed on cast-titanium surfaces during porcelain firing and those oxidized layers make the adhesion difficult to be formed. Many studies using mechanical, chemical and physical methods to enhance the titanium-ceramic adhesion have been actively performed. Purpose: This study meant to comparatively analyse the adhesion characteristics depending on different titanium surface coatings after coating the casts and wrought titanium surfaces with Au and TiN. Material and method: In this study, the titanium specimens (CP-Ti, Grade 2, Kobe still Co. Japan) were categorized into cast and wrought titanium. The wrought titanium was cast by using the MgO-based investment(Selevest CB, Selec). The cast and wrought titanium were treated with Au coating($ParaOne^{(R)}$., Gold Ion Sputter, Model PS-1200) and TiN coating(ATEC system, Korea) and the ultra low fusing dental porcelain was fused and fired onto the samples. Biaxial flection test was done on the fired samples and the porcelain was separated. The adhesion characteristics of porcelain and titanium after firing and the specimen surfaces before and after the porcelain fracture test were observed with SEM. The atomic percent of Si on all sample surfaces was comparatively analysed by EDS. In addition, the constituents of specimen surface layers after the porcelain fracture and the formed compound were evaluated by X-ray diffraction diagnosis. Result: The results of this study were obtained as follows : 1. The surface characteristics of cast and wrought titanium after surface treatment(Au, TiN, $Al_2O_3$ sandblasting) were similar and each cast and wrought titanium showed similar bonding characteristics. 2. Before and after the biaxial flection test, the highest atomic weight change of Si component was found in $Al_2O_3$ sandblasted wrought titanium(28.6at.% $\rightarrow$ 8.3at.%). On the other hand, the least change was seen in Au-Pd-In alloy(24.5at.% $\rightarrow$ 9.1at.%). 3. Much amount of Si components was uniformly distributed in Au and TiN coated titanium, but less amount of Si's was unevenly dispersed on Al2O3 sandblasting surfaces. 4. In X-ray diffraction diagnosis after porcelain debonding, we could see $Au_2Ti$ compound and TiN coating layers on Au and TiN coated surfaces and $TiO_2$, typical oxide of titanium, on all titanium surfaces. 5. Debonding of porcelain on cast and wrought titanium surface after the biaxial flection is considered as a result of adhesion deterioration between coating layers and titanium surfaces. We found that there are both adhesive failure and cohesive failure at the same time. Conclusion: These results showed that the titanium-ceramic adhesion could be improved by coating cast and wrought titanium surfaces with Au and TiN when making porcelain fused to metal crowns. In order to use porcelain fused to titanium clinically, it is considered that coating technique to enhance the bonding strength between coating kKlayers and titanium surfaces should be developed first.

• The Journal of Korean Academy of Prosthodontics
• /
• v.45 no.5
• /
• pp.675-686
• /
• 2007

Statement of problem: Titanium nitride(TiN) coatings are the most general and popular coating method and used to improve the properties of metallic surface for industrial purposes. When TiN coating applied to the abutment screw, frictional resistance would be reduced, as a results, the greater preload and prevention of the screw loosening could be expected. Purpose: The purpose of this study was to investigate mechanical properties of TiN coated film of various coating thickness on the titanium alloy surface and to evaluate proper coating thickness. Material and method: 95 Titanium alloy (Ti-6Al-4V) discs of 15 mm in diameter and 3 mm in thickness were prepared for TiN coating and divided into 7 groups in this study. Acceding to coating deposition time (CDT) with TiN by using Arc ion plating, were divided into 7 groups : Group A (CDT 30min), Group B (CDT 60min), Group C (CDT 90min), Group D (CDT 120min), Group E (CDT 150min), Group F(CDT 180min) and Group G (no CDT) as a control group. TiN coating surface was observed with Atomic Force Microscope(AFM), field emission scanning electron microscopy(FE-SEM) and examined with scratch tester, wear tester. Result: 1. Coating thickness fir each coated group was increased in proportion to coating deposition time. 2. Surface of all coated groups except Group A was homogeneous and smooth. However, surface of none coated Group G had scratch. 3. Adhesion strength for each coated group was increased in proportion to coating deposition time. 4. Wear resistance for each coated group was increased in proportion to coating deposition time. 5. Surface roughness in Group A, B, C was increased in proportion to coating deposition time. But, surface roughness in Group D, E, F was showed decreased tendency in proportion to coating deposition time. Conclusion: According to coating deposition time, mechanical properties of TiN coated film were changed. It was considered that 120 minutes coating deposition time ($1.32{\mu}m$ in coating thickness) is necessary.

• Journal of Periodontal and Implant Science
• /
• v.38 no.3
• /
• pp.453-466
• /
• 2008

Purpose: The purpose of this research is to study about initial adhesion, proliferation and activation of osteoblast to titanium surface treated with machined, hydroxyapatite coating, resorbable blast material blasting and anodizing method. Material and Methods: After treating the titanium surface of each block with machined, impurities were removed and sterilized. The number of cells attached from cultured osteoblast of respective experimental groups were measured at 1, 4, 7, and 14day and alkaline phosphatase, calcium, and inorganic phosphate concentration of cultured solution was measured. Result: Anodizing group showed the highest rate of cell attachment and proliferation activity. RBM treated group showed the highest increasing on their alkaline phosphatase activity, on the calcium apposition, on inorganic phosphate apposition of 1 and 4 days in cultured osteoblast to compare with other groups. Conclusion: On the basis of these findings, we conclude that surface modification of titanium was profoundly effected on the attachment, proliferation and activation of osteoblast in initial stage osseointegration.

• Journal of the Korean Ceramic Society
• /
• v.45 no.10
• /
• pp.600-604
• /
• 2008

Although titanium-ceramic systems have gained substantial interests in dental prosthetic field, bonding problem between porcelain and titanium has not been solved. Main obstacle in titanium-porcelain bonding is excessive oxidation of titanium during porcelain firing. The effects of several coating materials on the bonding strength of titanium-porcelain system were investigated in this study. RF sputtering and electroplating of platinum significantly increased the bonding strength of porcelain-titanium specimen. However, coatings of Ni-Au, Ir, and ceramics(zirconia and hydroxyapatite) did not showed a significant effect on bonding strength. Platinum might be a promising material for the protective layer of excessive oxidation of titanium during porcelain firing, resulting in increase in the bonding strength.

• The Journal of Korean Academy of Prosthodontics
• /
• v.45 no.2
• /
• pp.203-215
• /
• 2007

Statement of problem: Titanium and its alloy, with their excellent bio-compatibility and above average resistance to corrosion, have been widely used in the field of dentistry. However, the excessive oxidization of titanium which occurs during the process of firing on porcelain makes the bonding of titanium and porcelain more difficult than that of the conventional metal-porcelain bonding. To solve this problem related to titanium-porcelain bonding, several methods which modify the surfaces, coat the surfaces of titanium with various pure metals and ceramics, to enable the porcelain adhesive by limiting the diffusion of oxygen and forming the adhesive oxides surfaces, have been investigated. Purpose: The purpose of this study was to know whether the titanium-porcelain bonding strength could be enhanced by treating the titanium surface with gold and TiN followed by fabrication of clinically applicable porcelain-fused-to-titanium crown Material and method: The porcelain-fused-to-titanium crown was fabricated after sandblasting the surface of the casting titanium coping with $Al_2O_3$ and treating the surface with gold and TiN coating followed by condensation and firing of ultra-low fusing porcelain. To compare with porcelain-fused-to-titanium crowns, porcelain-fused-to-gold crowns were fabricated and used as control groups. The bonding strengths of porcelain-fused-to-gold crowns and porcelain-fused-totitanium crowns were set for comparison when the porcelain was fractured on purpose to get the experimental value of fracture strength. Then, the surface were examined by SEM and each fracturing pattern were compared with each other Result:Those results are as follows. 1. The highest value of fracture strength of porcelain-fused-to-titanium crowns was in the order of group with gold coating, group with TiN coating, group with $Al_2O_3$ sandblasting. No statistically significant difference was found among the three (P>.05). 2. The porcelain-fused-to-gold crowns showed the highest value in bonding strength. The bonding strength of crowns porcelain-fused-to-titanium crowns of rest groups showed bonding strength reaching only 85%-94% of that of PFG, though simple comparision seemed unacceptable due to the difference in materials used. 3. The fracturing patterns between metal and porcelain showed mixed type of failure behavior including cohesive failure and adhesive failure as a similar patterns by examination with the naked eye and SEM. But porcelain-fused-to-gold crowns showed high incidence of adhesive failure and porcelain-fused-to-titanium crowns showed high incidence of cohesive failure. Conclusion: Above results proved that when fabricating porcelain-fused-to-titanium crowns, treating casting titanium surface with gold or TiN was able to enhance the bonding strength between titanium and porcelain. Mean value of masticatory force was found to showed clinically acceptable values in porcelain bonding strength in all three groups. However, more experimental studies and evaluations should be done in order to get better porcelain bonding strength and various surface coating methods that can be applied on titanium surface with ease.

• Journal of the Korean institute of surface engineering
• /
• v.38 no.1
• /
• pp.37-43
• /
• 2005

Nanosized titanium-colloid particles were prepared by sol-gel method. The physical properties, such as thermal stability, crystallite size and crystallinity according to synthesis condition have been investigated by TEM, XRD, SEM, TGA and DTA. In addition, Zinc phosphating has been studied in order to compare the phosphating characterization of prepared nanosized titanium-colloid particles. The major phase of all the prepared titanium-colloid particles was an amorphous structure regardless of synthesis temperature and the structure was composed of phoshate complex and titanium. The micrographs of HR- TEM showed that nanosized titanium-colloid particles possessed a spherical morphology with a narrow size distribution. The crystallite size of the titanium-colloid particles synthesized at 80℃ was 4-5 nm and increased to 8-10 nm with an increase of synthesis temperature (150℃). In addition, the coating weight increased with an increase of temperature of phosphating solution and when the concentration of titanium-colloid was 2.0 g/l, the coating weight was 1.0 g/㎡.