• The Korean Journal of Ceramics
• /
• 제4권4호
• /
• pp.387-393
• /
• 1998

The formation of titanium diboride ($TiB_2$ ) via the reduction of $TiO_2$ with boric oxide and carbon was studied in a partially reducing atmosphere of argon mixed with 4 vol.%H2. The effect of reaction time, temperature, partial pressure of nitrogen and $TiO_2/B_2_O3$ stoichiometric ratio on the reducibility of oxides has been studied. The phases formed were analysed by using X-ray rowder diffraction and scanning sosctron microscopic techniques. In this paper, we also investigated the presence of $CaC_2$ as a reducing agent on the reducibility of oxide mixtures and on the Ti-B-C-Ca-O phase equilibria. The morphology of $TiB_2$ formed in the presence of $CaC_2$ is compared with the microstructure of $TiB_2$ formed as a consequence of carbothermic reduction. The observed variation in $TiB_2$ crystals formed is also explained.

• 한국재료학회지
• /
• 제9권8호
• /
• pp.787-791
• /
• 1999

기계적합금법으로 Ti와 B의 혼합분말로부터 $TiB_2$분말을 제조하였고, Zr과 Ta의 Ti 치환 효과를 조사하였다. (Ti+B)의 혼합분말을 280시간 분쇄하여 $TiB_2$단일상을 얻었고 기계적합금화 도중 비정질상은 관찰되지 않았다. Ti의 일부를 원자반경이 Ti보다 큰 Zr으로 치환한 결과 기계적합금화에 걸리는 시간이 크게 감소한 반면에, 붕화물 생성열이 절대값이 $TiB_2$상보다 작은 Ta로 치환하면 280시간 분쇄하여도 단일상을 형성하지 못하였다.

• 한국세라믹학회지
• /
• 제34권11호
• /
• pp.1099-1106
• /
• 1997

In the present study, the effect of TiB2 addition on the sintering behavior of ZrB2 ceramics was studied with hot pressing under Ar atmosphere. Hot pressing experiments were carried out in graphite dies at the 1$700^{\circ}C$, 180$0^{\circ}C$ under Ar atmosphere. The sintering density increased with increasing TiB2 contents. With the addition of 10wt% TiB2 almost theoretical density could be achieved by hot-pressing at 180$0^{\circ}C$. Zr-Ti-Fe-B compound in liquid phase was observed from the EDS and WDS analysis. It was considered that sinterability was enhanced due to the mass transfer through liquid phase formed at the sintering temperature. In addition of TiB2, transition metal of groups IV, substitutional solid solution could be formed.

• 한국분말야금학회:학술대회논문집
• /
• 한국분말야금학회 2006년도 Extended Abstracts of 2006 POWDER METALLURGY World Congress Part2
• /
• pp.1084-1085
• /
• 2006

We studied formation of nanostructured $TiB_2$-Cu composites under shock wave conditions. We investigated the influence of preliminary mechanical activation (MA) of Ti-B-Cu powder mixtures on the peculiarities of the reaction between Ti and B under shock wave. In the MA-ed mixture the reaction proceeded completely while in the non-activated mixture the reagents remained along with the product . titanium diboride. The size of titanium diboride particles in the central part of the compact was 100-300 nm.

• 한국분말재료학회지
• /
• 제10권3호
• /
• pp.168-171
• /
• 2003

Interpenetrating phase composites of $TiB_2$-Cu system were produced via Spark-Plasma Sintering (SPS) oi nanocomposite powders. Under simultaneous action of pressure, temperature and electric current titanium diboride nanoparticles distributed in copper matrix move, agglomerate and form a fine-grained skeleton. Increasing SPS-temperature and he]ding time promote densification due to local melting of copper matrix When copper melting is avoided the compacts contain 17-20% porosity but titanium diboride skeleton is still formed representing the feature of SPS . High degree of densification and formation of titanium diboride network result in increased hardness of high-temperature SPS-compacts.

• The Korean Journal of Ceramics
• /
• 제4권3호
• /
• pp.227-230
• /
• 1998

Alumina($Al_2O_3$)-Titanium Diboride($TiB_2) particulate composites were fabricated by hot pressing of the powder mixture that was prepared from Self-propagating High Temperature Synthesis (SHS) product and commercial powders. Their propeties were examined in order to find feasibility of using SHS for making the high performance ceramic composite. $TiB_2 particles obtained by grinding the SHS product were finer than the commercial powders. Hot pressed sample containing the SHS products exhibited higher strength than the one prepared from the commercial powders.

• 한국분말야금학회:학술대회논문집
• /
• 한국분말야금학회 2006년도 Extended Abstracts of 2006 POWDER METALLURGY World Congress Part 1
• /
• pp.523-524
• /
• 2006

The $TiB_2$ dispersion strengthened copper alloy was attracted as thermal and electrical functional material for the high mechanical strength, high thermal stability and good conductivity of $TiB_2$. In the present study, the focus is on the synthesis of $TiB_2$ dispersed copper alloy by spark plasma sintering process using copper oxide and titanium diboride as raw materials. The mechanical, thermal and electrical properties of sintered bodies were discussed with the sintering parameters, and developed microstructure and phase of sintered bodies.

• 열처리공학회지
• /
• 제27권4호
• /
• pp.169-174
• /
• 2014

The effect of varying amounts of graphite and $TiB_2$ on the electrical conductivity of composite bipolar plates was systematically studied. In this study, Titanium diboride ($TiB_2$) which has a high electrical conductivity, was selected as a filler and a additive material instead of conventional graphite. For proper distribution of the filler and matrix materials, ball milling using alumina balls was conducted for 1h, and then the hot press method was applied for the preparation of composite samples. The results showed a rapid increase in the electrical conductivity of composite bipolar plates at the critical filler content. However, $TiB_2$ and graphite composite bipolar plates showed similar increases in the electrical conductivity even though $TiB_2$ has a higher electrical conductivity than graphite. In addition, it was also found that a small addition of $TiB_2$ to graphite filler could be very effective for increasing the electrical conductivity and flexural strength of the composite bipolar plate.

• 한국분말재료학회지
• /
• 제14권5호
• /
• pp.292-297
• /
• 2007

The present study was focused on the synthesis of a $TiB_2$ dispersed copper matrix composite material by the combination of the mechanical milling and plasma activated sintering processes. The $Cu/TiB_2$ mixed powder was prepared by the combination of the mechanical milling and reduction processes using the copper oxide and titanium diboride powder as the raw material. The synthesized $Cu/TiB_2$ mixed powder was sintered by the plasma activated sintering process. The hardness and electric conductivity of the sintered bodies were measured using micro vickers hardness and four probe method, respectively. The relative density of $Cu/TiB_2$ composite material sintered at $800^{\circ}C$ showed about 98% of theoretical density. The $Cu-1vol%TiB_2$ composite material has a hardness of about 130Hv and an electric conductivity of about 85% IACS. The hardness and electric conductivity of $Cu-3vol%TiB_2$ composite material were about 140 Hv and about 45% IACS, respectively.

• 한국분말재료학회지
• /
• 제10권6호
• /
• pp.443-447
• /
• 2003

Nano-sized $TiB_2$ was in situ synthesized in copper matrix through self-propagating high temperature synthesis (SHS) with high-energy ball milled Ti-B-Cu elemental mixtures as powder precursors. The size of $TiB_2$ particles in the product of SHS reaction decreases with time of preliminary mechanical treatment ranging from 1 in untreated mixture to 0.1 in mixtures milled for 3 min. Subsequent mechanical treatment of the product of SHS reaction allowed the $TiB_2$ particles to be reduced down to 30-50 nm. Microstructural change of $TiB_2$-Cu nanocomposite during spark plasma sintering (SPS) was also investigated. Under simultaneous action of pressure, temperature and electric current, titanium diboride nanoparticles distributed in copper matrix move, agglomerate and form a interpenetrating phase composite with a fine-grained skeleton.