• Journal of the Korean Ceramic Society
• /
• v.44 no.5 s.300
• /
• pp.141-143
• /
• 2007

Nanotubes and microtubes of ferroelectric lead zirconate titanate (PZT) were synthesized by means of a simple and convenient process called a template-wetting process. Nanoporous alumina and macroporous Si were used as template materials to fabricate the corresponding tubes. For the improvement of the wetting properties of the wetting solution, the PZT solution was mixed with a polymer. The polymer was removed completely during annealing. The grain growth processes of the PZT nanotubes during baking and furnace annealing were examined by means of field emission electron microscope (FE-SEM) and X-ray diffractometry (XRD).

• Proceedings of the KIEE Conference
• /
• 2009.04a
• /
• pp.27-29
• /
• 2009

본 연구에서는 Titanate Nanotube (TNT)를 LBL-SA (layer-by-layer self-assembling) method을 이용하여 전기변색 (electrochromism device, ECD) 소자에 적용하고자 하였다. TNT 분말은 10M NaOH와 $TiO_2$를 혼합한 후 autoclave에서 130$^{\circ}C$, 48시간 동안 수열합성하여 제조하였다. 주사전자현미경 (SEM)으로 TNT 분말의 형상을 관찰한 결과, 직경 20$\sim$30nm, 길이 500$\sim$600nm의 튜브 형상을 나타내었으며, X-선 회절시험 (XRD) 결과 층상구조로 확인되었다. 코팅 물질의 표면 전하를 이용한 LBL-SA method에 적용시키기 위해 수용액 중에서 TNT 입자 표면 전하를 TBAOH (tetrabutylammonium hydroxide)를 적정하여 제타 전위 값이 -40mV로 최대가 되도록 하였으며, 이때 pH 값은 9로 나타났다. 2전극 시스템을 이용하여 cycle voltammetry를 측정한 결과, -0.5$\sim$-1.5V 영역에서 산화환원전위 피크가 뚜렷하게 나타났으며, 짙은 갈색으로 변색되는 것을 확인하였다. 본 연구 결과로서 TNT 박막은 전기를 인가하였을 때 n-type 반도체 성질을 갖는 것으로 나타났으며, 앞으로 display 연구 분야에 적용할 수 있을 것으로 주목된다.

• Korean Chemical Engineering Research
• /
• v.44 no.2
• /
• pp.179-186
• /
• 2006

Two types of $TiO_2$, nanotube and nanoparticle, were used for the mesoporous coatings by doctor blade technique followed by calcining at $450^{\circ}C$. The coatings were used as working materials for dye-sensitized solar cells (DSCs) later on and their photovoltaic characterization was carried out. The nanoparticle was synthesized from hydrogen titanate nanotube by hydrothermal treatment at $180^{\circ}C$ for 24 hr. The solar energy conversion efficiency (${\eta}$) of DSCs prepared by this nanoparticle reached 8.07％ with $V_{OC}$ (open-circuit potential) of 0.81 V, $I_{SC}$ (short-circuit current) of $18.29mV/cm^2$, and FF (fill factor) of 66.95％, respectively. For the preparation of nanotube, the concentration of NaOH solution varied from 3 M to 5 M. In the case of DSCs fabricated with nanotubes from 3 M NaOH solution, the ${\eta}$ reached 6.19％ with $V_{OC}$ of 0.77 V, $I_{SC}$ of $12.41mV/cm^2$, and FF of 64.49％, respectively. On the other hand, in the case of 5 M solution, the photovoltaic ${\eta}$ was decreased with 4.09％ due to a loss of photocarriers. In conclusion, it is demonstrated that the solar energy conversion efficiency of DSCs made from $TiO_2$ nanoparticle showed best results among those under investigation.