• Proceedings of the Korean Society of Tribologists and Lubrication Engineers Conference
• /
• 2000.06a
• /
• pp.269-275
• /
• 2000

The fretting wear characteristics of TiN coated Zircaloy-4 tube were investigated experimentally The fretting wear experiment was performed using TiN coated Zircaloy-4 tube as the fuel rod cladding material and uncoated Zircaloy-4 tube as one of grids. TiN coating is probably one of the most frequently and successfully used PVD coatings for the mitigation of fretting wear. In this study, TiN coating by PVD was employed for improvement of Zircaloy-4 tube fretting characteristics. The fretting tester was designed and manufactured for this experiment. TiN coated Zircaloy-4 tube was used as the moving specimen, uncoated ZircaBoy-4 tube as the stationary one. The number of cycles, slip amplitude and normal load were selected as main factors of fretting wear. The results of this research showed that the wear volume of TiN coated Zircaloy-4 tube increased as number of cycles, normal load and slip amplitude increase but the quantity of volume was lower than the case of uncoated Zircaloy-4 tube pairs.

• Journal of the Korean Society for Heat Treatment
• /
• v.32 no.5
• /
• pp.224-229
• /
• 2019

PVD coating is a technology that can be applied to various industries, and is widely used for processing molds and machinery, improving performance of core parts, and extending the life. Therefore, there is a need for a research on a device and a process technology that can adjust the performance to suit each application. In this study, a PVD coating device with ion density control was used to deposit a coating layer on SKD 11, a cold die steel, with magnetron currents of 1 A, 2 A, 3 A at arc currents of 80 A, 100 A, 130 A. It examined the mechanical properties for each condition. Increasing the arc current and magnetron current could improve the thickness, adhesion, and hardness of the coating layer. Especially, When the magnetron current was high, it suppressed the droplets that could be generated by the high arc current, showing excellent surface uniformity and adhesion of the coating layer.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.8 no.3
• /
• pp.432-436
• /
• 2007

We have studied on the tribological characteristics of Plasma Vapour Deposition(PVD) coating method in Automotive Structural Materials. Coating materials were deposited by the Titanium carbide(TiC) and Titanium nitride(TiN). An experimental process was established to determine the tribological characteristics of friction and wear behaviour with the variation of applied load, temperature and the time with the Falex friction and wear test machine. It was improved that when the surface modification of hard coatings(TiC, TiN) was deposited steel, the tribological characteristics become better. It is argued that it is improved because of excellence of the anti-wear, the extreme pressure properties and tile heat stability.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.30 no.10 s.253
• /
• pp.1179-1186
• /
• 2006

This paper was designed to assess the adhesive properties of hard coatings on non-nitrided and nitrided various tool steels. Estimations of adhesion were done to scratch test which is mainly used in hard coating. The critical load$(L_c)$ between coating and substrate is defined through analysis of frictional load vs. normal load curve, signals of acoustic emission and optical observations. Coatings employed in this study are TiN, CrN and TiAlN, tools as substrates are STD11, STD61 and SKH51. It was classified to substrates with/without intermediate nitrided layer and hard coatings on substrate were deposited by arc PVD. Results showed that harder substrates and coatings give higher values of critical loads.

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 2005.10a
• /
• pp.186-189
• /
• 2005

This paper was designed to assess the adhesive properties of hard coatings on non-nitrided and nitrided various tool steels. Estimations of adhesion were done to scratch test which is mainly used in hard coating. The critical load(Lc) between coating and substrate is defined through analysis of frictional load vs. normal load curve, signals of acoustic emission and optical observations. Coatings employed in this study are TiN, CrN and TiAlN, tools as substrates are STD11, STD61 and SKH51. It was classified to substrates with/without nitrided layer and hard coatings on substrate were deposited by arc PVD. Results showed that harder substrates and coatings give higher values of critical loads.

• Transactions of Materials Processing
• /
• v.31 no.1
• /
• pp.11-16
• /
• 2022

In this paper, wear characteristics of PVD coatings were compared on the die surface for cold stamping of MART1470 steel sheet with the finite element analysis and the pin-on-disc wear test. Three types of PVD coatings (CrN, TiAlCrN, and MoS2TiCr(W)N) were considered for the tool surface made of STD11 material. The stamping process of an auto-body part was analyzed with the finite element method. Ranges of process variables for the wear test such as contact pressure, relative speed, and sliding distance were predicted from analysis results. In order to quantitatively analyze wear characteristics of each coating, the amount of wear was measured and compared according to process variables with the pin-on-disc wear test. The influence of each process variable was investigated and the wear characteristics of the three coating layers were quantitatively compared. It was confirmed that the wear characteristics of MoS₂TiCr(W)N coating were better than those of CrN and TiAlCrN. It was noted that the proposed prediction approach could predict and respond to the wear phenomenon occurring in the stamping process.

• Journal of Advanced Marine Engineering and Technology
• /
• v.19 no.3
• /
• pp.62-69
• /
• 1995

In order to investigate the effect of TiN coating on corrosion fatigue behavior of metal, the rotary bending corrosion fatigue tests were carried out in 3% NaCl solution by using the round bar specimens of high-speed steel, SKH-9, coated with TiN by PVD method. From the experimental results, fatigue strength of TiN coating steel in air was obvious improvement as compared with that of the substrate because of the restriction of dislocation movement in near surface of the substrate by hard thin film. In 3% NaCl solution, corrosion fatigue life of TiN coating specimen in high stress level was improvement same as in air. But in low stress level, corrosion fatigue life of TiN coating one was equivalent to that without coating, due to much crack initiated from corrosion pits formed at the substrate by failure of coating layer.

• Journal of the Korean institute of surface engineering
• /
• v.34 no.5
• /
• pp.435-444
• /
• 2001

WC-( $Ti_{1-x}$ A $l_{x}$) N coatings of constant changing Al concentration were deposited on S45C substrates by high-ionization sputtered PVD method. The Al concentration could be controlled by using evaporation source for Al and fixing the evaporation rate of the metals (i.e, WC- $Ti_{0.86}$A $l_{0.14}$N, WC- $Ti_{0.72}$A $l_{0.28}$N, and WC- $Ti_{0.58}$A $l_{0.42}$N). The corrosion behavior of WC-( $Ti_{1-x}$ A $l_{x}$)N coatings in a deaerated 3.5% NaCl solution was investigated by electrochemical corrosion tests and surface analyses. The measured galvanic corrosion currents between coating and substrate indicated that WC- $Ti_{0.72}$A $l_{0.28}$N coating showed the best resistance of the coating tested. The results of potentiodynamic polarization tests showed that the WC- $Ti_{0.72}$A $l_{0.28}$N coating deposited with 32W/c $m^2$ of Al target revealed higher corrosion resistance. This indicated that the WC- $Ti_{0.72}$A $l_{0.28}$N coating is effective in improving corrosion resistance. In EIS, the WC- $Ti_{0.72}$A $l_{0.28}$N coating showed one time constant loop and increased a polarization resistance of coating ( $R_{coat}$) relative to other samples. Compositional variations of WC-( $Ti_{1-x}$ A $l_{x}$)N coatings were analyzed by EDS and XRD analysis was performed to evaluate the crystal structure and compounds formation behavior. Surface morphologies of the films were observed using SEM and AFM. Scratch test was performed to measure film adhesion strength.strength. adhesion strength.strength.

• Journal of the Korean institute of surface engineering
• /
• v.31 no.6
• /
• pp.400-406
• /
• 1998

Tool life characteristics were investigated for the TiN coated (PVD) tungsten carbide cutting tools to improve the tool life Experimental variables for Tin coating were coating time and cathode bias voltage and cuting variables were cutting speed and feel rate. As a experiment result, TiN coated tool was extended about from 2.14 to 2.7 times than that of not coated tungsten carbide tools. Also, coating thinkness is much affected to tool life.

• Tribology and Lubricants
• /
• v.17 no.6
• /
• pp.453-458
• /
• 2001

The fretting wear of a nuclear fuel rod it a dangerous phenomenon. In this study, TiN coating was used to reduce the fretting wear of Zircaloy-4 tube, a nuclear fuel rod cladding material. TiN coating is probably one of the molt frequently and successfully used PVD coatings for the mitigation of fretting wear. The fretting tester was designed and manufactured for this experiment. The number of cycles, slip amplitude and normal load were selected as main factors of fretting wear. The results of this research showed that wear volume was improved 1.3∼3.2 times with TiN coating. The worn surfaces were observed by SEM. Wear mechanism at lower slip amplitude was the brittle cracks and rupture of TiN coating. However, adhesive and abrasive wear were mainly observed on most surfaces at higher slip amplitude.