• Journal of the Korean Ceramic Society
• /
• v.42 no.8 s.279
• /
• pp.548-553
• /
• 2005

$TiO_2$ nanofibers were fabricated by annealing electrospun $TiO_2$/PVP nanofibers for 3 h at $500^{\circ}C$ in air. Size and uniformity of electrospun $TiO_2$ nanofiber diameters were evaluated via XRD and SEM by varying electric field, PVP concentration, Ti tetraisopropoxide concentration and precursor flow rate. Experimental results revealed that the effect of PVP concentration on size and uniformity of electrospun $TiO_2$ nanofiber diameters was most profound, however, the other effects were relatively small. Uniform fibers with no beads were observed for the electrospun anatase titania nanofibers with a diameter of 170 nm.

• Journal of Microbiology and Biotechnology
• /
• v.14 no.6
• /
• pp.1105-1113
• /
• 2004

Disinfection of a waterborne pathogenic protozoa, Giardia lamblia, by the conventional chlorine method has been known to be difficult. An alternative disinfection has been carried out by using a UV -light illuminating optical­fiber photoreactor. Light intensity diffused from one piece of a clad-removed optical-fiber was $1- 1.5{\mu}Em^{-2}s^{-1}$. Disinfection capability in a UV -light irradiated optical-fiber reactor suspended with 0.01 g $TiO_{2}\;dm^{-3}$ was 1.4 times that in the same reactor without $TiO_{2}$ photocatalysts. To resolve the absorption and scattering of UV light by the particles themselves as well as the difficulty of recycling particles in the slurry­type reactor, $TiO_{2}$ which was obtained by a hydrothermal method, was immobilized on clad-removed optical fibers. Such pretreatment of fiber surface resulted in an excellent transparency, which enhanced the UV light to diffuse laterally from a fiber surface. Coating time of the prepared solution by the hydrothermal method was not effective after more than two times. Disinfection capability in the $TiO_{2}$-immobilized optical-fiber reactor was $83\%$ in 1 h at $40^{\circ}C$, which was slightly higher than $76\%$ at $22^{\circ}C$ and $68\%$ at $10^{\circ}C$. Disinfection capability at $22^{\circ}C$ increased from $74\%$ at an initial pH of 3.4, through $76\%$ at pH 6.5, to $87\%$ at an initial pH of 10. Oxygen supply with air-flow rate of 5 $cm^3\;min^{-1}$ did not seem to increase the disinfection capability with UV /immobilized $TiO_2$.

• Korean Chemical Engineering Research
• /
• v.53 no.3
• /
• pp.276-281
• /
• 2015

Nanostructured $TiO_2-SiO_2$ materials have widely been used as anti-reflecting coating, optical-chemical sensors and catalysts because of their superior optical and thermal properties as well as chemical durability. Web type $SiO_2$ microfibers with nano-crystalline $TiO_2$ were prepared by electrospinning of Ti-PCS mixed solution and oxidation controlled heat-treatment, rather simple than sol-gel process. Nano-crystalline anatase phase were formed for the heat-treatment up to $1200^{\circ}C$ and they were finely dispersed in the amorphous $SiO_2$ matrix.

• Journal of the Korean Ceramic Society
• /
• v.54 no.1
• /
• pp.23-27
• /
• 2017

A series of $CeO_2-TiO_2$ composite samples with different Ce/Ti molar ratios were prepared by the paper template. Powder X-ray diffraction (XRD) and transmission electron microscopy (TEM) were used to confirm a face-centered cubic lattice of $CeO_2$ with Ce/Ti =8:2 or 9:1 and a two phase mixture of anatase titania and face-centered cubic ceria with Ce/Ti = 7 : 3. The field emission scanning electron microscopy (FESEM) results suggest that the products are micron braid structures consisting of fibers with diameters in a range of $1-6{\mu}m$ and lengths of several hundred micrometers. $N_2$ absorption-desorption testing shows that the composite at Ce/Ti molar fraction of 8 : 2 has the largest BET surface area (about $81m^2{\cdot}g^{-1}$). Compared to the pure $CeO_2$ sample, the composites show superior catalytic activity for $H_2$ reduction and CO oxidation. For the micron braid structure $CeO_2-TiO_2$ composite (Ce/Ti = 8 : 2), due to the high surface area and the solid solution with appropriate $Ti^{4+}$ incorporation, the CO conversion at about $280^{\circ}C$ was above 50% and at $400^{\circ}C$ was 100%.

• Korean Journal of Optics and Photonics
• /
• v.16 no.6
• /
• pp.490-493
• /
• 2005

We have experimentally studied supercontinuum generation in a photonic crystal fiber as a function of pump wavelength and intensity with 100 fs pulsewidth. A supercontinuum over 750 nm spectral width with amplitude variation less than 10 dB has been achieved. It was generated by coupling femtosecond pulses from a mode-locked Ti:Sapphire laser into a 2 m long photonic crystal fiber. Adjusting the parameters of the pump source, it was also possible to control different spectral features of the supercontinuum radiation.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2006.12a
• /
• pp.123-125
• /
• 2006

The $TiO_2$ sol was prepared hydrothermally in an autoclave from aqueous $TiOCl_2$ solutions as a starting precursor. Hollow fibers were obtained when the sol-gel-derived $TiO_2$ sol was treated chemically with a NaOH solution and subsequently heated in the autoclave under various conditions. A systematic analysis of the influence of different NaOH concentrations on the formation of nanotubes was carried out. The details of the nanotubular structure were investigated by using transmission electron microscopy (TEM), scanning electron microscopy (SEM) and X-ray diffraction (XRD). From the TEM images, the outer and the inner diameters of the tubes were measured to be about 8 and 4 nm, respectively, the lengths were measured to be several hundreds of nanometers.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.22 no.6
• /
• pp.274-278
• /
• 2012

$TiO_2$ can be used optically and is applied on many areas such as gas sensor, solar cell and photocatalysis. Electrospun nanofibers have received great interest for development and utilization in some novel applications, such as chemical sensors, dye-sensitized solar cell and photo catalysis. In this study, pure $TiO_2$ and Ga-doped $TiO_2$ nanofibers synthesized by a modified electrospinning method. The Ga doped $TiO_2$ solution is prepared by mixing poly vinyl pyrrolidone, ethyl alcohol, and titanium (IV) isopropoxide. By electrospinning these sols, nanofibers were fabricated. These fibers are heat-treated at $800^{\circ}C$ in air. The prepared pure $TiO_2$ and Ga-doped $TiO_2$ nanofibers samples were characterized by X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), scanning electron microscopy (SEM), transmission electron microscopy (TEM) and Raman spectroscopy.

• Computers and Concrete
• /
• v.22 no.5
• /
• pp.481-492
• /
• 2018

In this paper, a new hybrid fiber system (NHFS) is investigated for the application of slab. The steel fiber, polyvinyl alcohol (PVA) fiber and calcium carbonate ($CaCO_3$) whisker is added to form NHFS. The four-point bending test is carried out on the flexural properties of slab with plain, steel fiber, traditional hybrid fiber system (THFS) and NHFS reinforced cementitious composites. The flexural behavior is evaluated by ASTM C1018-97, JCI-SF4 and post-crack strength (PCS) technique. The evaluation parameters of flexural toughness such as toughness index (TI), equivalent flexural strength (EFS) and PCS are determined. The size of slab specimens is $15mm(thickness){\times}50mm(width){\times}200mm(length)$. The results show that adding $CaCO_3$ whisker to THFS can significantly improve the flexural strength, TI, EFS, PCS of the slab. The empirical relation between reinforcing index ($RI_v$) and flexural parameters show that flexural parameters of slabs increase first and then decrease; which indicates that optimum $RI_v$ values can be helpful in the considering the mix design of steel-PVA fibers-$CaCO_3$ whisker composites for achieving the desired flexural-related properties. The scanning electron microscopy is performed to observe the micro-morphological characteristics of the fracture surface, which proved the positive hybrid effect among the different fibers in cementitious composites. The NHFS can arrest the generation and propagation of the crack from micro to macro level.

• Proceedings of the Korean Society of Dyers and Finishers Conference
• /
• 2012.03a
• /
• pp.43-43
• /
• 2012

본 연구에서는 대량으로 손쉽게 구 할 수 있는 식물염료를 확보하여 새로운 천연색소자원을 탐색하기 위해서 진행되었으며, 시료의 최적 추출 조건을 확립하고 추출된 색소의 실크에 대한 염색 특성을 살펴 최적 염색조건을 설정하고, 염색견뢰도를 평가하여 수수 등겨 추출물의 천연색소로의 활용에 대한 기초 자료를 마련하고자 하였다. 수수 색소 추출 시 생산성과 편리성을 고려하여 추출은 pH 4, 추출온도 $60^{\circ}C$, 추출시간 24시간이 적정조건으로 제시되었으며, 수수 추출물에 함유되어 있는 탄닌의 최대흡수파장은 282nm로 나타났다. 견직물의 pH에 따른 염색 특성은 pH가 증가할수록 K/S값이 증가하여 염착량이 증가하였으며, 염색온도가 높을수록 염색시간이 길어질수록 염착량이 증가하는 경향을 보여주고 있다, 염색온도가 높을수록 염색시간이 경과될수록 색상은 $Y{\rightarrow}YR$로 변화되는 것을 알 수 있었으며 염색온도가 높을수록 채도가 증가하였다. 욕비가 클수록 염착량은 감소하였으나, 채도는 약간 증가하는 것을 알 수 있었다. 매염제 처리에 의한 색상변화에서는 Al, Ni 매염은 색상변화는 적었지만, Cu와 Fe 매염은 명도와 채도를 크게 감소시키고 아울러 색상도 Cu는 적갈색으로 Fe는 진회색으로 변화되었다. Sn과 Ti 매염에 의해서 명도는 약간 감소하고 채도는 약간 상승하여 연한 주황색으로 색상이 변화하였다. 설정된 조건에서 염색된 염색포의 일광견뢰도는 2~3급, 세탁견뢰도 변퇴색은 2~3급, 오염은 4~5급으로 나타났다. Fe로 매염된 염색포의 일광견뢰도는 증가하여 3~4급으로 나타났으며, 매염제 처리에 의한 세탁 견뢰도는 같거나 약간 증가되는 것으로 나타났다.

• Korean Journal of Materials Research
• /
• v.9 no.3
• /
• pp.315-321
• /
• 1999

Metal matrix composites have been extensively studied because of their excellent characteristics for structural application. $Al_2O_3$ and SiC have been used as a common reinforcement owing to their good mechanical properties. However the manufacturing cost of these ceramic reinforcement is expensive, so the use of the composites has been restricted to special purposes. In this study, we tested the application possibility as a reinforcement of $Al_2O_3$-TiC powder synthesized by SHS(Self-propagating High-temperature Synthesis) process to Al alloy matrix composite. Also, $Al_2O_3$ short fibers were added with the synthesized powders in order to apply to the Al matrix hybrid composites. Squeeze infiltration casting process was used to make the composite with 25vol% of reinforcement. Microstructure and crystal structure were examined by SEM, OM and XRD, also the mechanical properties were studied by the compressive test and wear test.