• Proceedings of the Korean Vacuum Society Conference
• /
• 1996.06a
• /
• pp.175-176
• /
• 1996

ppt/Ti/SiO2/Si 기판상에 고주파 마그네트론 스퍼터링 방식으로 ppZT 박막[두 께:3000$\AA$]을 증착하고 RTA 방식으로 후속 열처리[열처리온도:550~$650^{\circ}C$]를 실시하여 직 경 0.2mm 소자의 FECApps(ferroelectric cappacitors)를 제작하였다. 증착된 ppZT 박막을 강 유전성 pperovskite 결정상으로 만들기 위해 ppZT 박막의 열처리조건을 연구하였으며, 열처리 방식에 따른 ppZT 박막의 결정특성(상형상, 형상관찰, 성분분석 등)과 커패시터 소자의 전기 적 특성($\varepsilon$r,tan$\delta$,pp-E hysteresis curves, 누설전류 등)을 비교, 분석하였다.

• Bulletin of the Korean Chemical Society
• /
• v.31 no.2
• /
• pp.360-364
• /
• 2010

$Li_4Ti_5O_{12}$ thin film with inverse hemispheric structure was fabricated on a Pt/Ti/$SiO_2$/Si substrate by the sol-gel and dip coating method for use as an anode for 3-dimensional (3D) thin-film batteries. Polystyrene (PS) beads of 400 nm diameter were used to prepare the template for the inverse hemispheric structure. A coating solution prepared using precursor sources was dropped on the template-deposited substrates, which were then calcinated at $400^{\circ}C$. The template was removed by calcination, and the inverse hemispheric structure was successfully formed by an annealing process. The cyclic performance during high-rate charge/discharge processes of the $Li_4Ti_5O_{12}$ film with inverse hemispheric structure was superior to that of the flat $Li_4Ti_5O_{12}$ film.

• Journal of the Korean Vacuum Society
• /
• v.8 no.4A
• /
• pp.425-431
• /
• 1999

$Pb(Zr_{0.52}, Ti_{0.48})O_3$ (PZT) thick films as an actuating material with conducting oxides, $(La_{0.5}Sr_{0.5}) CoO_3$ (LSCO), have been fabricated by sol-gel method for Optical Micro-Electro-Mechanical System (MEMS) devices, in which PZT/LSCO/SiO2 structures were used. In order to improve the adhesion to LSCO solution in order to enhance the wetting behavior of a water-based LSCO precursor solution and further to improve the adhesion between LSCO and $SiO_2$ layers. PZT films were made using 1-3 propanediol based precursor solution which has a high viscosity and a boiling point appropriate for thick film fabrication. In the precursor solution, Ti-propoxied and Zr-propoxied are partially substituted with acetylacetone to achieve the solution stability while maintaining reactivity. Crack free PZT films (0.8~1$\mu\textrm{m}$) have been successfully fabricated at crystallization temperatures above $700^{\circ}C$. Dielectric constants and dielectric losses of the PZT films were 900~1200and 2~5%, respectively. Piezoelectric constant $d_{33}$ of the PZT films constrained by a substrate were 200pm/V at 100kV/cm.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2013.08a
• /
• pp.306-306
• /
• 2013

p-type Si(100)기판위에 Al2O3 박막을 증착하고 Si/SiO2 박막을 연속 증착하여 태양전지를 제작하였다. Si/SiO2 박막을 연속으로 증착하면 양자 구속이 일어나고 이로 인한 유효밴드 갭이 증가하게 되고, tunnel effect와 계면에서의 passivation 효과를 기대할 수 있다. 이런 효과들을 이용하여 고효율 태양전지를 기대 할 수 있다. 본 연구에서는 Remote Plasma Atomic Layer Deposition(RPALD)를 이용하여 Al2O3를 증착하였고 RF-Magnetron Sputter와 e-beam Evaporator 장비를 이용하여 Si/SiO2을 증착하였다. 전극으로는 Ti/Ag와 Al을 이용하였다. Solar simulator 장비를 이용하여 cell의 전기적 특성 평가를 평가하였고(Fig. 1) QE 측정장비를 통해 파장대의 따른 광학적 측정을 하였다(Fig. 2). ellipsometer 장비와 ${\alpha}$-step 장비로 박막과 전극의 두께를 측정하였고 4-point prove 장비를 이용하여 면저항, 저항율을 측정 평가하였다. 또한 I-V, C-V 측정 결과 터널링 현상이 일어나는 것을 확인 하였으며, Si/SiO2 다중 박막을 연속 증착 할수록 cell 효율이 더 좋게 나온다는 것을 확인하였다.

• The Transactions of The Korean Institute of Electrical Engineers
• /
• v.56 no.10
• /
• pp.1786-1790
• /
• 2007

The $(SrCa)TiO_3(SCT)$ thin films are deposited on Pt-coated electrode ($Pt/TiN/SiO_2/Si$) using RF sputtering method at various deposition temperature. The dielectric constant of SCT thin films were increased with the increase of deposition temperature, and changed almost linearly in temperature ranges of $-80{\sim}+90[^{\circ}C]$. Also, SCT thin films was observed the phenomena of dielectric relaxation with the increase of frequency, and the relaxation frequency was observed above 200[kHz]. V-I characteristics of SCT thin films show the increasing leakage current with the increases of deposition temperature. The conduction mechanism of the SCT thin films observed in the temperature range of $25{\sim}100[^{\circ}C]$ can be divided into three characteristic regions with different mechanism by the increasing current. The region 1 below 0.8[MV/cm] shows the ohmic conduction. The region 2 can be explained by the Child's law, and the region 3 is dominated by the tunneling effect.

• Proceedings of the KIEE Conference
• /
• 1999.07d
• /
• pp.1501-1503
• /
• 1999

The $(Sr_{0.85}Ca_{0.15})TiO_3$(SCT) thin films are deposited on Pt-coated electrode$(Pt/TiO_2/SiO_2/Si)$ using RF sputtering method. Ag, Cu, Al, Pt films for the formation of top eletrode were doposited on SCT thin films by thermal evaporator and sputtering. The effects of top electodes have be studied on SCT samples with a variety of top electrode materials.

• The Journal of the Acoustical Society of Korea
• /
• v.6 no.4
• /
• pp.55-63
• /
• 1987

Modified $PbTiO_3$ piezoelectric ceramics added with 0.2, 0.25, 0.3 mol of $CaCO_3$ and 0.04 mol of $(Co_{\frac{1}{2}}W_{\frac{1}{2}})$ and 0.05 mol of $MnO_2$ and NiO have been fabricated. These ceramics can be poled sufficiently within 10 minutes at $100^{\circ}C$ under about d.c. field of 40 kv/cm. Detailed measurement was performed on dielectric constants, cutie temperatures, elastic and piezoelectric properties and coupling factors for the fabricated ceramics. The most value of the piezoelectric coupling factors was coupling factor of thickness mode kt and its value for 0.25 mol of Ca was about $45\%$. Dielectric constants of $\varepsilon_{33}^T$ and $\varepsilon_{11}^T$ for 0.25 mol of Ca were 242 and 260, and coupling factor ratio (kt/Kp) and Qm were 6 and 357 respectively.

• Journal of information and communication convergence engineering
• /
• v.4 no.4
• /
• pp.147-150
• /
• 2006

The thin film of PbTiO3 is fabricated at substrate temperature of 100-150$^{\circ}C$. The infrared spectrum of the ferroelectric thin film is measured as temperature of thermal treatment, 400 - 550$^{\circ}C$. According to infrared spectrum analysis, there are absorption bands at a nearby wave number of 1000 $\sim$ 400 cm-l and the thin film treated by temperature of 550$^{\circ}C$ has absorption bands of wave number 500 cm-l similar to infrared response property of PbTiO3 powder. The pyroelectric infrared detector is fabricated after deposition of Pt and PbTiO3 thin film on Si wafer by sputtering machine. The measured remnant polarization are 11.5-12.5$\muC/cm2$, breakdown electric field Ec is 100-120KV/cm, and voltage responsivity and detectivity is -280V/W, -108cm Hz/W.

• Proceedings of the KIEE Conference
• /
• 1991.07a
• /
• pp.204-208
• /
• 1991

In this paper, the radiation properties of a far-Infrared using a PTC thermistor, the $BaTiO_3$+1.63mol% $Al_2O_3$+3.75mol% $SiO_2$+1.25mol% $TiO_2$(1/3 $Al_2O_3+xSiO_2$+(1-x) $TiO_2$; total x: 6.67mol%) ceramics, in order to progress the grade resistivity characteristics, by adding an ethanol solution of $Mn(NO_3){\cdot}6H_2O$ was investigated. The ceramics was fabricated by wet-mill method. The sintering temperature read 1300-1350$[^{\circ}C]$ and the holding time was 3 hours. The quantity of $Sb_2O_3$ and $Al_2O_3$ for an activation of the far-infrared radiation in ceramics was doped. In sintering, R-T property was measured by varying the grade temperature. The anatase-lighting apparatus and microstructures by using XRD and SEM were observed. $Sb_2O_3$. oxides additive. affected the semiconducting and emissivity and MnO was devoted an increase of resistivity. The specimen which only $Sb_2O_3$ is added to was high appeared far-infrared emissivity and Mno was not affacted the far-infrared radiation. The ceramics shows that it is effective in the structure of the human bodies as organic bodies and can be applied as electron device.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 1998.06a
• /
• pp.139-142
• /
• 1998

PLZT thin films were fabricated with different Zr/Ti ratios by pulsed laser deposition. PLZT films deposited on Pt/Ti/SiO$_2$/Si substrate. This PLZT thin films of 5000${\AA}$. thickness were crystallized at 600$^{\circ}C$, 200 mTorr O$_2$ press. 2/55/45 PLZT thin film showed a maximum dielectric constant value of $\varepsilon$$\_$r/=1500, and dielectric loss was 0.O$_3$. At 2/70/30 PLZT thin film, Coercive field and remnant polarization was respectively 19[kV/cm], 8[${\mu}$C/$\textrm{cm}^2$].