• Proceedings of the KIEE Conference
• /
• 2002.11a
• /
• pp.106-108
• /
• 2002

The composites were fabricated 61vol.% $\beta-SiC$ and 39vol.% $TiB_2$ powders with the liquid forming additives of l2wt% $Al_2O_3+Y_2O_3$ by pressureless annealing at $1700^{\circ}C,\;1750^{\circ}C,\;1800^{\circ}C$ for 4 hours respectively. The result of Phase analysis of composites by XRD revealed $\alpha-SiC$(6H), $TiB_2$, and YAG($Al_5Y_3O_{12}$) crystal phase. The relative density and the Young's modulus showed the highest value of 92.9701% and 92.884Gpa for composites by pressureless annealing temperature $1700^{\circ}C$ at room temperature.

• Journal of Korean Society for Atmospheric Environment
• /
• v.20 no.4
• /
• pp.451-463
• /
• 2004

The performance of disk-type catalytic filters impregnated by TiO$_2$ or TiO$_2$-3Al$_2$O$_3$ㆍ 2SiO$_2$ supports and V$_2$O$_{5}$ catalyst was evaluated for selective catalytic reduction (SCR) of NO with ammonia as a reductant. XRD, FT -IR, BET and SEM were used to characterize the catalytic filters prepared in this work. Optimal V$_2$O$_{5}$ loading and reaction temperature for V$_2$O$_{5}$/TiO$_2$ catalytic filters were 3-6 wt.% and 350-40$0^{\circ}C$ at GHSV 14,300 $hr^{-1}$ in the presence of oxygen, respectively. With increasing the V$_2$O$_{5}$ loading from 0.5 to 6 wt%, NO conversion increased from 24 to 96% at 40$0^{\circ}C$ and 14.300$hr^{-1}$, and maintained at 80% over in the V$_2$O$_{5}$ loading range of 3-6 wt.% and then dropped at V$_2$O$_{5}$ loading of 7wt.% over. In comparing V$_2$O$_{5}$/ TiO$_2$ and V$_2$O$_{5}$/ TiO$_2$-3Al$_2$O$_3$ㆍ2SiO$_2$ catalytic fillers, which have same 3wt.% V$_2$O$_{5}$ loading, the V$_2$O$_{5}$/ TiO$_2$-3A1$_2$O$_3$ㆍ2SiO$_2$ catalytic filter showed higher activity than V$_2$O$_{5}$/ TiO$_2$ catalytic filter, but higher differential pressure drops owing to its low air permeability. low air permeability.

• Journal of Korea Foundry Society
• /
• v.30 no.4
• /
• pp.147-150
• /
• 2010

An eco-friendly production technique of Al-8.6Ti-0.025C refiner was developed by melting a Al-Ti master alloy in a graphite crucible, in which the potential nucleation site, TiC effectively formed by the spontaneous in-situ reaction between excessive Ti and carbon from graphite crucible. The A3003 alloy refined by the Al-8.6Ti-0.025C showed effectively refined macrostructure and enhanced mechanical properties comparable to the commercial Al-Ti-B refiner. The effective refinement was achieved in a shorter compare to the melt-treating time commercial Al-Ti-B refiner.

• Journal of the Korean Ceramic Society
• /
• v.25 no.6
• /
• pp.704-712
• /
• 1988

In order to investigate the effect of the second phase on Al2O3 matrix, SiC whisker was dispersed in Al2O3 matrix as a second phase over the content range of 5vol% to 20vol%. To this mixture, Y2O3 or TiO2 powder was added as a sintering additive before isostatically pressing and pressureless sintering at 1800-190$0^{\circ}C$ for 90min in N2 atmosphere. With increasing SiC whisker content, relative densities of composites were decreased and the grain growth of Al2O3 was restricted. When Y2O3 was added as a sintering aid the sintering temperature was 180$0^{\circ}C$, the maximum values of flexural strength, hardness and fracture toughness were 537MPa, 12.1GPa, 3.7MPa.m1/2, respectively. However, when the sintering temperature was elevated to 190$0^{\circ}C$, maximum values of flexural strength, hardness and fracture toughness were 453MPa, 17.5GPa, 4.9MPa.m1/2, respectively. Improved mechanical properties are assumed to be attributed to the crack deflection by the second phase SiC whisker and whisker pullout mechanism.

• Journal of the Korean Ceramic Society
• /
• v.38 no.12
• /
• pp.1137-1143
• /
• 2001

In this study, glass-ceramics containing cordierite(2MgO$.$2Al$_2$O$_3$5SiO$_2$) as a major crystalline phase was prepared from MAS (MgO-Al$_2$O$_3$-SiO$_2$) glass system for the application to reflector. Glasses prepared with addition of TiO$_2$as a nucleating agent were crystallized by two-step heat treatment of nucleation and crystal growth. Then nucleation and crystal growth behavior were investigated and the influence of heat treatment schedule on the nature of crystal phases and the diffuse reflectance spectrum was investigated. As a result, cordierite and rutile were precipitated as a major crystalline phases for the glass-ceramics with the nucleation at 750$^{\circ}C$ for 3 hours and then crystallization at 1100$^{\circ}C$ for 5 hours, and this glass-ceramics showed the reflectance over 90% in 570∼2500nm specturm region.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.6 no.2
• /
• pp.275-285
• /
• 1996

The effect of heat-treatment on catalytic crystallization in $LI_2O-Al_2O_3-SiO_2$ glass system over its glass transition temperature was investigated. Glass composition $4Li_2O{cdot}22AL_2O_3{cdot}66SiO_2{cdot}2TiO_2{cdot}2.5ZrO_2{cdot}1.5P_2O_5{cdot}1.0Na_2O{cdot}1.0As_2O_3$ (wt%) was selected and heat-treated at different heating conditions to obtain transparent glass-ceramic. Nucleation and crystallization behaviour of this composition were estimated by differential thermal analysis (DTA) and X-ray diffractometer (XRD) and its thermal expansion coefficients were measured by Dilatometer. As a result, glass transition temperature was $730^{\circ}C$ and two maximum nucleation temperatures were estimated at $730^{\circ}C$ and 82$0^{\circ}C$ using JMA(Johson-Mehl-Avrami) equation by DTA. $ZrTiO_4$ $\beta$-Quartz solid solution and $\beta$-Spodumene crystals were identified by XRD. The optimum crystallization temperature was 92$0^{\circ}C$ and three step heating schedule was expected to be useful to obtain transparent glass-ceramic.

• Proceedings of the KIEE Conference
• /
• 2007.07a
• /
• pp.1303-1304
• /
• 2007

The composites were fabricated, respectively, using 61[vol.%]SiC-39[vol.%]$TiB_2$ and using 61[vol.%]SiC-39[vol.%]$ZrB_2$ powders with the liquid forming additives of 12[wt%] $Al_{2}O_{3}+Y_{2}O_{3}$ by hot pressing annealing at $1650[^{\circ}C]$ for 4 hours. Reactions between SiC and transition metal $TiB_2$, $ZrB_2$ were not observed in this microstructure. ${\beta}{\rightarrow}{\alpha}$-SiC phase transformation was occurred on the SiC-$TiB_2$ and SiC-$ZrB_2$ composite. The relative density, the flexural strength and Young's modulus showed the highest value of 98.57[%], 226.06[Mpa] and 86.38[Gpa] in SiC-$ZrB_2$ composite at room temperature respectively. The electrical resistivity showed the lowest value of $7.96{\times}10^{-4}[{\Omega}{\cdot}cm]$ for SiC-$ZrB_2$ composite at $25[^{\circ}C]$. The electrical resistivity of the SiC-$TiB_2$ and SiC-$ZrB_2$ composite was all positive temperature coefficient resistance (PTCR) in the temperature ranges from $25[^{\circ}C]$ to $700[^{\circ}C]$. The resistance temperature coefficient of composite showed the value of $6.88{\times}10^{-3}/[^{\circ}C]$ and $3.57{\times}10^{-3}/[^{\circ}C]$ for SiC-$ZrB_2$ and SiC-$TiB_2$ composite in the temperature ranges from $25[^{\circ}C]$ to $700[^{\circ}C]$.

• Journal of the Korean Ceramic Society
• /
• v.32 no.9
• /
• pp.977-988
• /
• 1995

Several oxide (ZrO2, Al2TiO5, reactive Al2O3) and nonoxide (SiC, Si3N4, "ALON" (5AlN.9Al2O3)) additives were used as a microfiller for alumina based LCC (Low-Cement-Castable). High temperature prooperties (HMOR, softening under load) and the phase changes of developed LCC on various sintering temperatures were examined. In addition, thermal shock test and corrosion test were accomplished. Based on these data the effects of each microfiller on the properties of LCC were established comparing to those of the commercial LCC with amorphous silica as a microfiller. The castables, containing reactive alumina, ZrO2 and "ALON" (5AlN.9Al2O3) as a first portion, exhibited considerably higher HMOR-values over 100$0^{\circ}C$, better creep behavior, and thermal shock resistance than those of castables with amorphous silica. The LCC with 5% Al2TiO5 showed no corrosion against molten aluminum.nst molten aluminum.

• Proceedings of the Korean Vacuum Society Conference
• /
• 1999.07a
• /
• pp.86-86
• /
• 1999

본 연구에서는 마이크로파 유전체 소자로서의 응용 및 절연 산화막으로의 응용을 위해 마이크로파 유전체 세라믹으로 사용되어 온 MgTiO3 물질을 펄스 레이저로 박막을 제조하였다. MgTiO3 는 주로 고주파에서 높은 유전율을 갖고 높은 품질계수 (22.000 at 5 GHz) 혹은 낮은 유전손실을 갖으며 유전특성의 온도 안정성이 우수하여 유전체 세라믹 재료로 응용된다. MgTiO3 박막의 성장은 KrF(파장:248nm) 엑시머 레이저를 이용했으며 공정조건으로 박막의 성장온도는 500-75$0^{\circ}C$, 산소 압력은 10-5-200mTorr, 성장 후 냉각시 산소분위기는 200Torr, 레이저 에너지 밀도는 1.5-5J/cm2 등의 조건으로 박막을 성장하였다. MgTiO3 박막을 여러 가지 기판, 즉 Al2O3(r-plane), Si, Pt 위에 성장시켰으며 기판에 따라 에픽텍셜 혹은 다결정 상태를 갖는 ilmenite 구조로 성장되었다. PLD(Pulsed laser deposition)법에 의해 형성된 MgTiO3 박막을 보면, 우선 Al2O3(r-plane) 기판위에 성장된 경우 $700^{\circ}C$에서 에픽텍셜하게 성장하였으며, Si 기판 위에 성장된 경우 $650^{\circ}C$에서부터 (003)면으로 우선 배향된 단일상의 ilmenite 구조가 형성된다. Ptdnl에 성장된 경우 $600^{\circ}C$에서부터 (003)면으로 우선배향성을 가지며 $650^{\circ}C$에서 결정의 안정화를 이루었으나, MgTiO3 박막은 전기적 특성으로 유전특성 및 유전분산 특성 등이 측정 분석되어 MgTiO3 박막의 고주파 유전체로의 응용에 관한 가능성을 토의하였다.

• Journal of the Korean Society of Manufacturing Technology Engineers
• /
• v.9 no.6
• /
• pp.170-177
• /
• 2000

Dense $Al_2$O$_3$-30%TiC and Si$_3$N$_4$ ceramic tool materials with various grain size were produced by sintering-HIP treatment and by gas-pressure sintering. The fracture toughness was measured by indentation fracture and indentation strength method for both ceramics with various grain size. The effect of the grain size on the fracture toughness was evaluated, and the correlation between fracture toughness and mechanical properties such as hardness, Young\`s modulus and flexural strength of these ceramic were also investigated. The highest fracture toughness of around 6.7 MPa.m(sup)1/2 was obtained in Si$_3$N$_4$ ceramics with grain size of 1.58${\mu}{\textrm}{m}$. With a larger grain size of $Al_2$O$_3$-30%TiC and Si$_3$N$_4$ ceramics, the fracture toughness was generally increased. The increased fracture toughness of these ceramic also improved the flexural strength although the hardness decreased considerably. Similar results were obtained in grain size and mechanical properties on both $Al_2$O$_3$-30%TiC and Si$_3$N$_4$ ceramic tool materials.